Effect of double AlN buffer layer on the qualities of GaN films grown by radio-frequency molecular beam epitaxy

This paper reports that the GaN thin films with Ga-polarity and high quality were grown by radio-frequency molecular beam epitaxy on sapphire （0001） substrate with a double A1N buffer layer. The buffer layer consists of a high-temperature （HT） A1N layer and a low-temperature （LT） A1N layer grown at 800℃ and 600℃, respectively. It is demonstrated that the HT-A1N layer can result in the growth of GaN epilayer in Ga-polarity and the LT-A1N layer is helpful for the improvement of the epilayer quality. It is observed that the carrier mobility of the GaN epilayer increases from 458 to 858cm^2/V.s at room temperature when the thickness of LT-A1N layer varies from 0 to 20nm. The full width at half maximum of x-ray rocking curves also demonstrates a substantial improvement in the quality of GaN epilavers by the utilization of LT-A1N layer.     

利用MOCVD在r面蓝宝石上生长的α面GaN中两步AlN缓冲层的优化

采用两步AlN缓冲层(一层低温AlN和一层高温AlN)在r面蓝宝石衬底上生长了非极性的α面GaN,并利用高分辨X射线衍射和光致荧光谱对所生长的材料进行了研究.两步AIN缓冲层在我们之前的工作中已被证明比单步高温AlN或低温GaN缓冲层更有利于减小材料各向异性和提高晶体质量,本文进一步优化了两步AlN缓冲层的结构,并得到...     

Influence of AlN buffer layer thickness on structural properties of GaN epilayer grown on Si (111) substrate with AlGaN interlayer

We present the growth of GaN epilayer on Si (111) substrate with a single AlGaN interlayer sandwiched between the GaN epilayer and AlN buffer layer by using the metalorganic chemical vapour deposition. The influence of the AlN buffer layer thickness on structural properties of the GaN epilayer has been investigated by scanning electron microscopy, atomic force microscopy, optical microscopy and high-resolution x-ray diffraction. It is found that an AlN buffer layer with the appropriate thickness plays an important role in increasing compressive strain and improving crystal quality during the growth of AlGaN interlayer, which can introduce a more compressive strain into the subsequent grown GaN layer, and reduce the crack density and threading dislocation density in GaN film.     

利用MOCVD在r面蓝宝石上生长的α面GaN中两步AlN缓冲层的优化

采用两步AlN缓冲层(一层低温AlN和一层高温AlN)在r面蓝宝石衬底上生长了非极性的α面GaN,并利用高分辨X射线衍射和光致荧光谱对所生长的材料进行了研究.两步AIN缓冲层在我们之前的工作中已被证明比单步高温AlN或低温GaN缓冲层更有利于减小材料各向异性和提高晶体质量,本文进一步优化了两步AlN缓冲层的结构,并得到了各向异性更小,晶体质量更好的α面GaN薄膜.分析表明,两步AlN缓冲层中的低温AlN层在减小各向异性中起着关键作用.低温AlN层能抑制了优势方向(c轴)的原子迁移,有利于劣势方向(m轴)的原子迁移,从而减小了Al原子在不同方向迁移能力的差异,并为其后的高温AlN缓冲层和GaN层提供"生长模板",以得到各向异性更小、晶体质量更好的α面GaN材料.     

Growth of AlGaN Epitaxial Film with Chemical Vapour High A1 Content by Metalorganic Deposition

A high-Al-content AlGaN epilayer is grown on a low-temperature-deposited AlN buffer on （0001） sapphire by low pressure metalorganic chemical vapour deposition. The dependence of surface roughness, tilted mosaicity, and twisted mosaicity on the conditions of the AlGaN epilayer deposition is evaluated. An AlGaN epilayer with favourable surface morphology and crystal quality is deposited on a 2Onto low-temperature-deposited AlN buffer at a low V/Ⅲ flow ratio of 783 and at a low reactor pressure of 100 Torr, and the adduct reaction between trimethylaluminium and NH3 is considered.     

MOCVD生长Si衬底上HT-AlN缓冲层低生长压力对GaN薄膜的影响

采用金属有机化学气相沉积（MOCVD）技术在Si（111）衬底上外延GaN薄膜,对高温AlN（HT-AlN）缓冲层在小范围内低生长压力（6.7~16.6 kPa）条件下对GaN薄膜特性的影响进行了研究。研究结果表明GaN外延层的表面形貌、结构和光学性质对HT-AlN缓冲层的生长压力有很强的的依赖关系。增加HT-AlN缓冲层的生长压力,GaN薄膜的光学和形貌特性均有明显改善,当HT-AlN缓冲层的生长压力为13.3 kPa时,得到无裂纹的GaN薄膜,其（002）和（102）面的X射线衍射峰值半高宽分别为735 arcsec和778 arcsec,由拉曼光谱计算得到的张应力为0.437 GPa,原子力显微镜（AFM）观测到表面粗糙度为1.57 nm。     

氮化铝单晶薄膜的ECR PEMOCVD低温生长研究

采用电子回旋共振等离子体增强金属有机物化学气相沉积（ECR－PEMOCVD）技术，在c轴取向的蓝宝石即α Al2O3（0001）衬底上，以氮化镓（GaN）缓冲层和外延层作为初始层，分别以高纯氮气（N2）和三甲基铝(TMAl)为氮源和铝源低温生长氮化铝（AlN）薄膜.并利用反射高能电子衍射（RHEED）、原子力显微镜（AFM）和x射线衍射（XRD）等测量结果，研究了氢等离子体清洗、氮化和GaN初始层对六方AlN外延层质量的影响，从而获得解理性与α Al2O3衬底一致的六方相AlN单晶薄膜，其XRD半高宽为1 关键词： AlN 氢等离子体清洗 氮化 GaN     

Influence of AlN Buffer Thickness on GaN Grown on Si(111) by Gas Source Molecular Beam Epitaxy with Ammonia

Hexagonal GaN is grown on a Si(111) substrate with AlN as a buffer layer by gas source molecular beam epitaxy (GSMBE) with ammonia. The thickness of AlN buffer is changed from 9 to 72nm. When the thickness of AlN buffer is 36nm, the surface morphology and crystal quality of GaN is optimal. The in-situ reflection high energy electron diffraction (RHEED) reveals that the transition to a two-dimensional growth mode of AlN is the key to the quality of GaN. However, the thickness of AlN buffer is not so critical to the residual in-plane tensile stress in GaN grown on Si(111) by GSMBE for AlN thickness between 9 to 72nm.     

Influence of double A1N buffer layers on the qualities of GaN films prepared by metal-organic chemical vapour deposition

<正>In this paper we report that the GaN thin film is grown by metal-organic chemical vapour deposition on a sapphire (0001) substrate with double AlN buffer layers.The buffer layer consists of a low-temperature(LT) AlN layer and a high-temperature(HT) AlN layer that are grown at 600℃and 1000℃,respectively.It is observed that the thickness of the LT-AlN layer drastically influences the quality of GaN thin film,and that the optimized 4.25-min-LT-AlN layer minimizes the dislocation density of GaN thin film.The reason for the improved properties is discussed in this paper.     

蓝宝石表面处理对氮化镓光学性质的影响

采用化学方法腐蚀部分c面蓝宝石衬底,在腐蚀区域形成一定的图案,利用LP-MOCVD在经过表面处理的蓝宝石衬底上外延生长GaN薄膜.利用GaN薄膜光学透射谱,结合椭偏测量得到的折射率色散公式,计算得到GaN薄膜厚度,与椭偏光谱结果几乎一致;在经过表面处理的蓝宝石衬底上外延生长的GaN薄膜表现出更优异的光学质量和结晶质量,其透射谱具有更高的透射率和更大的调制深度,而且其光致发光谱中的黄光带几乎可以忽略.     

Nonpolar a-plane GaN grown on r-plane sapphire using multilayer AlN buffer by metalorganic chemical vapor deposition

Mirror-like and pit-free non-polar a-plane (1 1 −2 0) GaN films are grown on r-plane (1 −1 0 2) sapphire substrates using metalorganic chemical vapor deposition (MOCVD) with multilayer high-low-high temperature AlN buffer layers. The buffer layer structure and film quality are essential to the growth of a flat, crack-free and pit-free a-plane GaN film. The multilayer AlN buffer structure includes a thin low-temperature-deposited AlN (LT-AlN) layer inserted into the high-temperature-deposited AlN (HT-AlN) layer. The results demonstrate that the multilayer AlN buffer structure can improve the surface morphology of the upper a-plane GaN film. The grown multilayer AlN buffer structure reduced the tensile stress on the AlN buffer layers and increased the compressive stress on the a-plane GaN film. The multilayer AlN buffer structure markedly improves the surface morphology of the a-plane GaN film, as revealed by scanning electron microscopy. The effects of various growth V/III ratios was investigated to obtain a-plane GaN films with better surface morphology. The mean roughness of the surface was 1.02 nm, as revealed by atomic force microscopy. Accordingly, the multilayer AlN buffer structure improves the surface morphology and facilitates the complete coalescence of the a-plane GaN layer.     

The influence of SixNy interlayer on GaN film grown on Si(111) substrate

A method to drastically reduce dislocation density in a GaN film grown on an Si(111) substrate is newly developed. In this method, the Si_xN_y interlayer which is deposited on an AlN buffer layer in situ is introduced to grow the GaN film laterally. The crack-free GaN film with thickness over 1.7 micron is grown on an Si(111) substrate successfully. Synthesized GaN epilayer is characterized by X-ray diffraction (XRD), atomic force microscope (AFM), and Raman spectrum. The test results show that the GaN crystal reveals a wurtzite structure with the <0001> crystal orientation and the full width at half maximum of the X-ray diffraction curve in the (0002) plane is as low as 403 arcsec for the GaN film grown on the Si substrate with an Si_xN_y interlayer. In addition, Raman scattering is used to study the stress in the sample. The results indicate that the Si_xN_y interlayer can more effectively accommodate the strain energy. So the dislocation density can be reduced drastically, and the crystal quality of GaN film can be greatly improved by introducing Si_xN_y interlayer.     

AlN缓冲层对Si基GaN外延薄膜性质的影响

采用金属有机化合物化学气相沉积（MOCVD）方法制备了不同AlN缓冲层厚度的GaN样品,研究了AlN缓冲层厚度对GaN外延层的应力、表面形貌和晶体质量的影响。研究结果表明：厚度为15 nm的AlN缓冲层不仅可以有效抑制Si扩散,而且还给GaN外延层提供了一个较大的压应力,避免GaN薄膜出现裂纹。在该厚度AlN缓冲层上制备的GaN薄膜表面光亮、无裂纹,受到的张应力为0.3 GPa,（0002）和（1012）面的高分辨X射线衍射摇摆曲线峰值半高宽分别为536 arcsec和594 arcsec,原子力显微镜测试得到表面粗糙度为0.2 nm。     

The effect of low temperature AlN interlayers on the growth of GaN epilayer on Si (111) by MOCVD

Low temperature (LT) AlN interlayers were used to effectively reduce the tension stress and micro-cracks on the surface of the GaN epilayer grown on Si (111) substrate. Optical Microscopy (OM), Atomic Force Microscopy (AFM), Surface Electron Microscopy (SEM) and X-Ray Diffraction (XRD) were employed to characterize these samples grown by metal-organic chemical vapor deposition (MOCVD). In addition, wet etching method was used to evaluate the defect of the GaN epilayer. The results demonstrate that the morphology and crystalline properties of the GaN epilayer strongly depend on the thickness, interlayer number and growth temperature of the LT AlN interlayer. With the optimized LT AlN interlayer structures, high quality GaN epilayers with a low crack density can be obtained.     

Characteristics of GaN epilayer grown on Al2O3 with AlN buffer layer by molecular beam epitaxy

Double crystal rocking curve (DCRC), atomic force microscopy (AFM), scanning electron microscopy (SEM), and photoluminescence (PL) measurements on GaN epilayers grown with various thicknesses (3.4, 8.5, 17, 34, and 51 nm) of the AlN buffer layer were carried out to investigate the surface, the structural, and the optical properties of the GaN epilayers. The results of the DCRC, AFM, SEM, and PL measurements showed that the GaN epilayer grown on a 3.4 nm AlN buffer layer had the best quality. These results indicate that GaN active layers grown on 3.4 nm AlN buffer layers hold promise for potential applications in optoelectronic devices.     

Effects of AlN nucleation layer thickness on crystal quality of AlN grown by plasma-assisted molecular beam epitaxy

In this paper,the effects of thickness of AlN nucleation layer grown at high temperature on AlN epi-layer crystalline quality are investigated.Crack-free AlN samples with various nucleation thicknesses are grown on sapphire substrates by plasma-assisted molecular beam epitaxy.The AlN crystalline quality is analysed by transmission electron microscope and x-ray diffraction (XRD) rocking curves in both (002) and (102) planes.The surface profiles of nucleation layer with different thicknesses after in-situ annealing are also analysed by atomic force microscope.A critical nucleation thickness for realising high quality AlN films is found.When the nucleation thickness is above a certain value,the (102) XRD full width at half maximum (FWHM) of AlN bulk increases with nucleation thickness increasing,whereas the (002) XRD FWHM shows an opposite trend.These phenomena can be attributed to the characteristics of nucleation islands and the evolution of crystal grains during AlN main layer growth.     

Structural characterization of Al_(0.55)Ga_(0.45)N epitaxial layer determined by high resolution x-ray diffraction and transmission electron microscopy

Structural characteristics of Alo.55 Gao.45N epilayer were investigated by high resolution x-ray diffraction(HRXRD)and transmission electron microscopy(TEM);the epilayer was grown on GaN/sapphire substrates using a high-temperature A1 N interlayer by metal organic chemical vapor deposition technique.The mosaic characteristics including tilt,twist,heterogeneous strain,and correlation lengths were extracted by symmetric and asymmetric XRD rocking curves as well as reciprocal space map(RSM).According to Williamson-Hall plots,the vertical coherence length of AlGaN epilayer was calculated,which is consistent with the thickness of AlGaN layer measured by cross section TEM.Besides,the lateral coherence length was determined from RSM as well.Deducing from the tilt and twist results,the screw-type and edge-type dislocation densities are 1.0×10~8 cm~(-2) and 1.8×10~(10) cm~(-2),which agree with the results observed from TEM.     

磁控反应溅射AlN缓冲层对GaN基LED器件性能的影响

以直流磁控反应溅射法(RMS)在图形化蓝宝石衬底上制备的AlN薄膜作为缓冲层,采用金属有机化学气相沉积法(MOCVD)外延生长了GaN基LED。与MOCVD生长的低温GaN缓冲层相比,RMS制备的AlN缓冲层具有表面更平整、颗粒更小的形核岛,有利于促进GaN外延的横向生长,减少了形核岛合并时的界面数量和高度差异,降低了缺陷和位错产生的几率。研究结果表明,溅射AlN缓冲层取代传统低温GaN缓冲层后,外延生长的GaN材料具有更高的晶体质量,LED器件在亮度、漏电和抗静电能力等光电特性上均有明显提升。     

Si(111)衬底上生长有多缓冲层的六方GaN晶格常数计算和应变分析

利用卢瑟福背散射/沟道技术和高分辨率X射线衍射技术对在Si(111)衬底上利用金属有机化合物气相外延技术(MOVPE)生长有多缓冲层的六方GaN外延膜进行结晶品质计算、晶格常数计算和应变分析. 实验结果表明：GaN外延膜的结晶品质为χ_min=1.54%，已达到完美晶体的结晶品质(χ_min=1%—2%)；GaN外延膜的水平方向和垂直方向晶格常数分别为：a_epi＝0.31903nm，c_epi=0.51837nm，基本达到G 关键词： GaN 高分辨X射线衍射 卢瑟福背散射/沟道 弹性应变     

SiO2对多层GaN外延片热应力分布影响的仿真分析

为了研究SiO2对多层结构GaN外延片的热应力的影响,以直径d为40 mm的GaN外延片为研究对象,利用有限元分析法分别对蓝宝石/AlN/GaN和蓝宝石/SiO2/AlN/GaN这两种光阴极组件外延片表面热应力进行理论计算和仿真。在其他结构参数相同的情况下,分别分析了两种光阴极组件外延片径向和厚度方向的应力分布,分析了外延片热应力分布及影响因素。分析结果显示:在1 200 ℃的生长温度下,径向区域内的热应力分布比较均匀,厚度方向的热应力均在衬底和外延层的界面上发生突变。最后分析了外延片生长温度、蓝宝石衬底和GaN、AlN过渡层厚度对表面热应力的影响。