磁控溅射制备的W,WSi2,Si单层膜和W/Si,WSi2/Si多层膜应力

采用直流磁控溅射技术制备了厚度约100 nm的W,WSi2,Si单层膜和周期约为20 nm,Si膜层厚度与周期的比值为0.5的W/Si,WSi2/Si周期多层膜.利用台阶仪对镀膜前后基底表面的面形进行了测试,计算并比较了不同膜系的应力值.结果表明:W单层膜表现出较大的压应力,而W/Si周期膜则表现为张应力.WSi2单层...     

Mo/Si aperiodic multilayer broadband reflective mirror for 12.5-28.5-nm wavelength range

Aperiodic molybdenum/silicon (Mo/Si) multilayer designed as a broadband reflective mirror with mean reflectivity of 10% over a wide wavelength range of 12.5-28.5 nm at incidence angle of 5° is developed using a numerical optimized method. The multilayer is prepared using direct current magnetron sputtering technology. The reflectivity is measured using synchrotron radiation. The measured mean reflectivity is 7.0% in the design wavelength range of 12.5-28.5 nm. This multilayer broadband reflective mirror can be used in extreme ultraviolet measurements and will greatly simplify the experimental arrangements.     

多层膜劳厄透镜对8keV X射线的聚焦性能模拟研究

基于多层膜技术的劳厄(Laue)透镜能实现硬X射线纳米级聚焦,在X射线微纳分析领域具有重要的应用前景.基于衍射动力学理论,分析了X射线在多层膜劳厄透镜中的传播,计算了不同结构的多层膜劳厄透镜对8 keVX射线的聚焦性能.结果表明,最外层厚度为5 nm的倾斜多层膜劳厄透镜可获得5.7 nm的聚焦光斑和26%的平均衍射效率...     

Multilayers with high-reflectivity at 19.5 nm and low-reflectivity at 30.4 nm

The multilayer （ML） mirror with high-reflectivity （HR） at a specific emission line of 19.5 nm （Fe line） and low-reflectivity （LR） at 30.4 nm （He line） is needed to be designed and fabricated for observing the image of sun. Based on a variety of optimizations utilized different structures, the design is performed and the final results demonstrate that the reflectivity at 30.4 nm does not achieve minimum value when the reflectivity at 19.5 nm reaches the maximum value. The tradeoff should be done between the HR at 19.5 nm and LR at 30.4 nm. One optimized mirror is fabricated by direct current magnetron sputtering and characterized by grazing-incident X-ray diffraction （XRD） and synchrotron radiation （SR）. The experimental results demonstrate that the ML achieves the reflectivity of 33.3% at 19.5 nm and of 9.6× 10-4 at 30.4 nm at the incident angle of 13°.     

辐射驱动内爆流线实验测量

内爆速度的测量是惯性约束聚变研究中的核心问题, 是判断聚变点火反应的关键物理量. 在神光II激光装置上, 利用KB显微镜配合时间分辨为10 ps的条纹相机, 对1600 J激光能量注入, 3倍频, 脉宽为1 ns黑腔辐射驱动CH靶球, 获得了清晰的辐射驱动内爆流线轨迹X射线图像. 通过流线轨迹图像给出了最大内爆速度为160 km/s. 利用Multi1D程序对内爆压缩流线和壳层速度变化进行了模拟, 实验数据和理论模拟较符合.     

Hard X-ray one dimensional nano-focusing at the SSRF using a WSi2 /Si multilayer Laue lens

The multilayer Laue lens (MLL) is a novel diffraction optics which can realize nanometer focusing of hard X-rays with high efficiency. In this paper, a 7.9 μm-thick MLL with the outmost layer thickness of 15 nm is designed based on dynamical diffraction theory. The MLL is fabricated by first depositing the depth-graded multilayer using direct current (DC) magnetron sputtering technology. Then, the multilayer sample is sliced, and both cross-sections are thinned and polished to a depth of 35-41 μm. The focusing property of the MLL is measured at the Shanghai Synchrotron Facility (SSRF). One-dimensional (1D) focusing resolutions of 205 nm and 221 nm are obtained at E=14 keV and 18 keV, respectively. It demonstrates that the fabricated MLL can focus hard X-rays into nanometer scale.     

B_4C/Mo/Si high reflectivity multilayer mirror at 30.4 nm

The B4C/Mo/Si high reflectivity multilayer mirror was designed for He-Ⅱradiation (30.4 nm) using the layer-by-layer method. The theoretical peak reflectivity was up to 38.2% at the incident angle of 5℃. The B4C/Mo/Si multilayer was fabricated by direct current magnetron sputtering and measured at the National Synchrotron Radiation Laboratory (NSRL) of China. The experimental reflectivity of the B4C/Mo/Si multilayer at 30.4 nm was about 32.5%. The promising performances of the B4C/Mo/Si multilayer mirror could be used for the construction of solar physics instrumentation.     

液体表面的遮光效应及其应用

首次发现了液体介质表面的遮光效应,讨论了遮光半径与液体介质性质的关系.基于这一发现,建立了一种测量液体折射率的新方法,该方法具有实时、自动化、高精度等特点.     

X射线Kirkpatrick-Baez显微镜用超反射镜的研制

 介绍了一种可应用于X射线Kirkpatrick-Baez（KB）显微镜的光学元件—X射线超反射镜。选用的W和B₄C作为镀膜材料，膜对数为20，采用单纯型调优的方法实现了X射线超反射镜设计，用磁控溅射的方法在Si基片上完成了W/B₄C X射线超反射镜的制备。采用高分辨率X射线衍射仪（8 keV）测量了X射线超反射镜的反射特性。制备的X射线超反射镜在掠入射角分别为1.052°和1.143°处，反射角度带宽为0.3°，反射率达到20%，可满足KB型显微镜的要求。     

Design, Fabrication and Measurement of Ni/Ti Multilayer Used for Neutron Monochromator

Ni/Ti multilayers, which can be used for neutron monochromators, are designed, fabricated and measured. Firstly, their reflectivities are simulated based on the Nevot-Croce model. Reflectivities of two Ni/Ti multilayer mirrors with periods d = 10.3 nm （M1） and d = 7.8 nm （M2） are calculated. In the calculation, the reflectivity of the Ni/Ti multilayer is taken as a function of the gazing angle with different roughness factors δ =1.0 nm and = 1.5 nm. Secondly, these two multilayers are fabricated by the direct current magnetron sputtering technology. Thirdly their structures are characterized by small-angle x-ray diffraction. The roughness factors are fitted to be 0.68 nm and 1.16nm for M1 and M2, respectively. Finally their reflective performances are measured on the V14 neutron beam line at the Berlin Neutron Scattering Centre （BENSC）, Germany. The experimental data show that the grazing angle of the reflected neutron intensity peak increases, but the reflected neutron intensity decreases, with the decreasing periods of the multilayers.