Ti/Pr0.7Ca0.3MnO3/La0.67Sr0.33MnO3/Pt异质结电致电阻效应的改善

采用脉冲激光沉积技术制备了Ti/Pr_0.7Ca_0.3MnO₃/Pt和Ti/Pr_0.7Ca_0.3MnO₃/La_0.67Sr_0.33MnO₃/Pt异质结并研究了La_0.67Sr_0.33MnO₃功能插层对异质结电致电阻特性的影响. 实验结果表明La_0.67Sr_0.33MnO₃功能层的引入有效提高了器件的电阻转变特性,尤其是电阻转变率和疲劳性得到了极大的改善. 对La_0.67Sr_0.33MnO₃插层改善电致电阻转变特性的机理进行了定性的分析. 关键词： 电致电阻效应 电阻转变比率 疲劳特性     

电脉冲对多晶La0.7Ca0.3MnO3比热的影响

对电脉冲诱导的不同电阻态下La_0.7Ca_0.3MnO₃样品的比热进行了研究.实验结果表明,电脉冲导致La_0.7Ca_0.3MnO₃样品比热随电阻状态发生可逆变化.比热随电阻状态的减小而减小.低温比热拟合及不同电阻状态下的比热差与温度关系说明,声子对比热的贡献不随电阻状态变化,磁性和载流子对比热的贡献是导致La_0.7Ca_0.3MnO₃样品比热变化的原因.电脉冲诱导O离子沿一维扩展性缺陷的电化学迁移,导致材料中局部区域的O离子浓度发生变化.O离子浓度的变化导致载流子浓度的变化,同时载流子浓度的变化将使得低温下磁性耦合强度发生变化,从而导致比热发生变化. 关键词： 0.7Ca_0.3MnO₃')" href="#">La_0.7Ca_0.3MnO₃ 比热 氧离子迁移     

La1-xCaxMnO3的巨磁电阻效应

通过测量La_2/3Ca_1/3MnO₃，La_0.6Ca_0.4MnO₃单相多晶样品的磁电阻、电阻与温度的依赖关系，发现在La_1-xCa_xMnO₃体系中随x的变化，其磁电阻峰和电阻峰都发生了位移．作者认为体系中Mn⁴⁺含量是受Ca含量调制的，正是Mn⁴⁺含量的变化，导致磁性 关键词：     

成分调制的La1－xSrxMnO3复合隧道结

利用磁控溅射和Sr成分的调制以及原位热处理方法，在10mm×10mm大小的(001) 取向SrTiO_３单晶衬底上制备出三明治结构为La_0.7Sr_0.3MnO３(100nm)/La_0.96Sr_0.04MnO_３ (5nm)/ La0.7Sr_0.3MnO_３ (100nm) 的隧道结外延薄膜，然后再次 利用磁控溅射方法，在三层单晶膜上方继续沉积Ir_２２Mn_７８(15n m)/Ni_７９Fe_２１(5nm)/Pt(20nm)等金属三层膜.最后利用深紫外曝 光和Ar离子束刻蚀等微加工技术，制备出长短轴分别为12和6μm或者8和4μm大小的椭圆形L a_１-xSr_xMnO_３成分调制的复合磁性隧道结.在4.2K和 外加磁场8 T的测试下，La_１-xSr_xMnO_３成分调制的复 合磁性隧道结其隧穿磁电阻(TMR)比值达到3270%, 直接从实验上证实了铁磁性La_{0.7Sr0.3MnO３金属氧化物的自旋极化率（97%）可接近100％，具 有很好的半金属性质. 关键词： １-x}Sr_xMnO_３')" href="#">La_１-xSr_xMnO_３ 半金属 成分调制 复合磁性隧道 结 隧穿磁电阻     

La0.33Pr0.34Ca0.33MnO3薄膜的应变效应

采用脉冲激光沉积法分别在(100)LaAlO₃和(100)SrTiO₃基片上生长了La_0.33Pr_0.34Ca_0.33MnO₃薄膜,并通过磁测量和电输运测量对生长在不同基片上的La_0.33Pr_0.34Ca_0.33MnO₃薄膜的物性进行了研究.结果表明,基片和薄膜之间的压应力导致La_{关键词： 钙钛矿锰氧化物 相分离 电荷有序}     

钙钛矿型稀土锰氧化物La2/3Ca1/3MnO3中Mn位的Ti替代效应

研究了钙钛矿型锰氧化物La_2/3Ca_1/3Mn_1-xTi_xO₃(0≤x≤0.3)的结构、磁性和输运性质.发现Ti替代Mn强烈地抑制了La_2/3Ca_1/3MnO₃的铁磁性和金属电导,并很大地提高了磁电阻值.在低掺杂情况下(x≤0.04),1%的Mn被Ti替代,居里温度T_C和金属-绝缘体转变温度T_p分别平均下降了31和26.5K.当x=0.06时,铁磁态过渡为团簇玻璃态,并在x=0.20时完全变为自旋玻璃态.指出由于Ti的掺入而引起的磁稀释作用以及局域晶格畸变是产生上述结果的主要原因. 关键词：     

La0.9Sr0.1MnO3薄膜中电流效应研究

用直流磁控溅射法在(100)LaAlO₃衬底上制备了La_0.9Sr_0.1MnO₃薄膜.经退火处理后薄膜的原子力显微镜形貌观测和X射线衍射分析显示具有比较好的质量.电阻率-温度关系表明La_0.9Sr_0.1MnO₃薄膜在281 K处发生金属绝缘体转变.电流在0.01—4 mA范围内，薄膜的峰值电阻率随电流增大而减小，在4 mA下获得了30.5%的峰值电阻率变 关键词： 掺杂锰氧化合物 0.9Sr_0.1MnO₃薄膜')" href="#">La_0.9Sr_0.1MnO₃薄膜 电流诱导效应 相分离理论     

脱氧La0.5Ca0.5MnO3样品的铁磁-反铁磁转变和电阻率变化

研究了氧空位对La_0.5Ca_0.5MnO₃ （LCMO）多晶块材的电输运和磁性质的影响. 随着氧空位的增加, 样品在高温段的电阻率一直增加, 并满足绝热小极化子模型, 而低温段的电阻率先下降后上升, 并出现明显的dR/dT>0的行为, 直至最后变为绝缘的. 氧空位的增加抑止了反铁磁相的出现, 使得脱氧的LCMO样品不发生反铁磁转变, 进一步增加氧空位则会抑制铁磁相. 关键词： 0.5Ca_0.5MnO₃')" href="#">La_0.5Ca_0.5MnO₃ 反铁磁相变 铁磁相变 脱氧     

La2/3Ca1/3MnO3薄膜的光致电阻率变化特性

射频磁控溅射法制备了La_2/3Ca_1/3MnO₃纳米薄膜(LCMO).该薄膜发生FM-PM相变的转变点温度为T_c≈308K（近似为电阻峰值温度T_p）；在不同温度下的光电导性质实验表明所制备的LCMO薄膜在连续激光作用时低温段（Tc）表现为光致电阻率增大效应，即ΔR/R＞0，并在R-T曲线拐点附近取得极大值，（ΔR/R）_max=43.5%；当T>T关键词： 钙钛矿薄膜 光响应 电子自旋 小极化子     

多晶La0.7Sr0.3MnO3的低温输运性质和磁电阻效应

详细研究了由纳米晶粒组成的块体多晶La_0.7Sr_0.3MnO₃(LSM)的电阻率和磁电阻效应,以及它们的温度依赖性.随着温度从室温降低,电阻率(ρ)在250K附近存在一最大值,低于该温度后,样品表现为金属导电特性,随后在50K附近存在一极小值.也就是说在低于50K的温度范围内,随着温度降低ρ反而升高,表现为绝缘体性的导电特性.经研究发现,这种随温度降低ρ反而增加的现象与隧穿效应的理论模型(lnρ∝T^-1/2)符合得很好 关键词： 0.7Sr_0.3MnO₃')" href="#">多晶La_0.7Sr_0.3MnO₃ 隧道效应 隧道磁电阻效应     

Electrical and magnetic behavior of La0.7Ca0.3MnO3/La0.7Sr0.2Ca0.1MnO3 composites

The electrical transport properties and the magnetoresistance of La_0.7Ca_0.3MnO₃/La_0.7Sr_0.2Ca_0.1MnO₃ composites are investigated as a function of sintering temperature. On the basis of an analysis by X-ray powder diffraction and scanning electron microscopy we suggest that raising the sintering temperature enhanced the interfacial reaction and creates interfacial phases at the boundaries of the La_0.7Ca_0.3MnO₃ and La_0.7Sr_0.2Ca_0.1MnO₃. Results also show that in 3 kOe, and at the Curie temperature, the magnetoresistance value of 14% was observed for the composite sintered at 1300 °C. Based on the phenomenological equation for conductivity under a percolation approach, which depends on the phase segregation of ferromagnetic metallic clusters and paramagnetic insulating regions, we fitted the experimental resistivity—temperature data from 50-300 K and find that the activation barrier decreases as temperature is increased.     

Effects of the surface layer of La2/3Ca1/3MnO3 thin films

The surface layer effects on transport in epitaxial La_2/3Ca_1/3MnO₃ thin films are studied. It was found that the two-probe resistance is nonlinear which is enhanced with decreasing temperature. Similar to the resistance of intrinsic La_2/3Ca_1/3MnO₃ thin films reported in the literature, the apparent dynamic contact resistance behaves semiconducting at high temperatures, passes through a peak, and displays a metallic behavior. At lowest temperatures, the curve of the contact resistance versus temperature shows a little upturn. The temperature dependent work function difference between the surface layer and the thin film underneath, together with the tunneling process across either the resulting charge depleted layer or the semiconducting surface layer is used to explain our observations.     

Temperature-dependent photoluminescence in La2/3Ca1/3MnO3

Visible photoluminescence and its temperature dependence of La_2/3Ca_1/3MnO₃ in the temperature range 138-293 K were measured. It was observed that the main broad band centered at ∼1.77 eV with the shoulders at ∼1.57 and ∼1.90 eV existed in the entire temperature range. It can be well fitted by three Gaussian curves B₁, B₂ and B₃ centered at ∼1.52, ∼1.75 and ∼1.92 eV, respectively. The intensities of the peak B₁ and B₂ vary as temperature increases. In the entire temperature range, the intensity of B₁ increases with increasing temperature, whereas that of B₂ decreases. The photoluminescence mechanisms for La_2/3Ca_1/3MnO₃ are presented based on the electronic structures formed by the interactions among spin, charge and lattice, in which B₁ was identified with the charge transfer excitation of an electron from the lower Jahn-Teller split e_g level of a Mn³⁺ ion to the e_g level of an adjacent Mn⁴⁺ ion, B₂ is assigned to the transition between the spin up and spin down e_g bands separated by Hund's coupling energy E_J and B₃ is attributed to the transition, determined by the crystal field energy E_C, between a t_2g core electron of Mn³⁺ to the spin up e_g bands of Mn⁴⁺ by a dipole allowed charge transfer process.     

La0.67Ca0.33MnO3薄膜皮秒光电效应

在1064 nm波长脉冲激光（脉宽25 ps）的照射下，钙钛矿氧化物薄膜La0.67Ca0.33MnO3/SrTiO3具有超快光电效应，对激光脉冲显示ps量级的响应时间，上升沿响应时间300 ps，半高宽700 ps，同时，对激光能量的响应灵敏度为500 mV/mJ。     

机械合金化La0.7Ca0.3MnO3的晶化动力学及磁电阻研究

通过机械合金化方法制备了单相La_0.7Ca_0.3MnO₃化合物.球磨形成的非晶态结构在920K退火时转变为钙钛矿型相结构.根据质量作用定律,讨论了非晶晶化动力学行为,其晶化转变激活能约为265kJ/mol.同时研究了化合物的电阻特性,发现低温下样品的电阻ρ与温度T的关系为ρ∝T²,随退火温度的升高,ρ-T²曲线斜率下降.在远离居里温度处的低温磁电阻可用Δρ/ρ₀=p₁-p₂T^3/2-p₃T描述. 关键词：     

Reversal transient laser-induced voltages in La2/3Ca1/3MnO3 films

This paper reports that the transient laser-induced voltages have been observed in La2/3Ca1/3MnO3 thin films on MgO （001） in the absence of an applied current. A peak voltage of - 0.15 V was detected in response to 0.015J pulse of 308 nm laser. It is demonstrated that the signal polarity is reversed when the films are irradiated through the substrate rather than at the air/film interface. Off-diagonal thermoelectricity may support the inversion of the signal when the irradiation direction is reversed.     

Magnetoresistance and transport properties of different impurity doped La0.67Ca0.33MnO3 composite

An enhanced magnetoresistance and a two-fold effect result from impurity dopant were observed in composites of La_0.67Ca_0.33MnO₃/YSZ and La_0.67Ca_0.33MnO₃/Fe₃O₄. Where YSZ represents yttria-stabilized zirconia and the doping level of both YSZ and Fe₃O₄ is 1 mol%. Different electrical and magnetic transport properties, in particular a lower field magnetization behavior, were observed between pure La_0.67Ca_0.33MnO₃ and the impurity doped La_0.67Ca_0.33MnO₃ composites. Compared with pure La_0.67Ca_0.33MnO₃, a possible interpretation is presented by considering the influences of YSZ and Fe₃O₄ on the structure of grain boundaries and/or surfaces of La_0.67Ca_0.33MnO₃grains.     

La0.8-xCa0.2MnO3纳米颗粒的居里温度与磁热效应

采用溶胶凝胶法制备了系列La_0.8-xCa_0.2MnO₃多晶样品,用X射线衍射分析确定了样品的钙钛矿结构,用透射电子显微镜观察了样品的形貌及粒径分布情况,用PAR155型振动样品磁强计测量了样品的磁性随外场和温度的变化,确定样品的居里温度并计算了各样品的磁熵变.磁测量及计算结果表明制备的各样品的居里温度在180—260K的范围内且随焙烧温度和La³⁺离子空位浓度的不同而变化,不同温度焙烧的样品均有较大的磁熵变值,其中1100℃焙烧的La_0.77Ca_0.2MnO₃,多晶样品在240.5K,H=1.0T的外场下的磁熵变达3.76J/kg·K,对实验结果做了定性的分析.该材料具有较高的居里温度和较大的磁熵变,所需外场强度适中,电阻率高,性能稳定,适合做高温磁制冷材料. 关键词： 钙钛矿 居里温度 磁热效应