Evolution of the 251 cm-1 infrared phonon mode with temperature in Ba0.6K0.4Fe2As2

The far-infrared optical reflectivity of an optimally doped Ba1-xKxFe2As2(x =0.4) single crystal is measured from room temperature down to 4 K. We study the temperature dependence of the in-plane infrared-active phonon at 251 cm-1 . This phonon exhibits a symmetric line shape in the optical conductivity, suggesting that the coupling between the phonon and the electronic background is weak. Upon cooling down, the frequency of this phonon continuously increases, following the conventional temperature dependence expected in the absence of a structural or magnetic transition. The intensity of this phonon is temperature independent within the measurement accuracy. These observations indicate that the structural and magnetic phase transition might be completely suppressed by chemical doping in the optimally doped Ba0.6K0.4Fe2As2 compound.     

Evolution of the 251 cm-1 temperature in infrared phonon mode with Ba0.6K0.4Fe2As2

The far-infrared optical reflectivity of an optimaUy doped Ba1-xKxFe2As2 （x = 0.4） single crystal is measured from room temperature down to 4 K. We study the temperature dependence of the in-plane infrared-active phonon at 251 em-1. This phonon exhibits a symmetric line shape in the optical conductivity, suggesting that the coupling between the phonon and the electronic background is weak. Upon cooling down, the frequency of this phonon continu- ously increases, following the conventional temperature dependence expected in the absence of a structural or magnetic transition. The intensity of this phonon is temperature independent within the measurement accuracy. These observa- tions indicate that the structural and magnetic phase transition might be completely suppressed by chemical doping in the optimally doped Bao.6Ko.4Fe2As2 compound.     

Nanosecond-time-resolved infrared spectroscopic study of fast relaxation kinetics of protein folding by means of laser-induced temperature-jump

Elucidating the initial kinetics of folding pathways is critical to the understanding of the protein folding mechanism. Transient infrared spectroscopy has proved a powerful tool to probe the folding kinetics. Herein we report the construction of a nanosecond laser-induced temperature-jump （T-jump） technique coupled to a nanosecond timeresolved transient mid-infrared （mid-IR） spectrometer system capable of investigating the protein folding kinetics with a temporal resolution of 50 ns after deconvolution of the instrumental response function. The mid-IR source is a liquid N2 cooled CO laser covering a spectral range of 5.0μm （2000 cm^-1）-6.5μm （1540 cm^-1）. The heating pulse was generated by a high pressure H2 Raman shifter at wavelength of 1.9μm. The maximum temperature-jump could reach as high as 26±1℃. The fast folding/unfolding dynamics of cytochrome C was investigated by the constructed system, providing an example.     

缺氧YBCO的c方向电荷动力学

我们利用激光沉积法在斜切的钛酸锶基片上制备了缺氧(110)取向的YBa2Cu3O7-δ薄膜.由于在这种薄膜中的c轴躺在基片的表面上,从而为我们研究沿c方向的某些独特的物理性质提供了便利.在这里我们报道了所测量的在不同温度及磁场下这种薄膜沿c方向的远红外偏振反射谱.结果表明在温度Tc以上,沿c方向运动的载流子浓度很低.由于载流子之间弱的相干性以及较大的热涨落,反射边得到展宽.随着超导的出现,沿着c方向运动的载流子之间的相干性得到加强,这表现为一个在100波数附近等离子体边的出现.磁场下的测量表明磁场对等离子体边的位置影响很小,这种现象与已有的理论预言不相符合,我们认为导致这种现象的原因是超导体中磁通涡旋的钉扎作用.     

Structural and Electrical Characteristics of Pb（Zr0.53,Ti0.47）O3 Thin Films Deposited on Si （100） Substrates

Pb(Zr0.53, Ti0.47)O3 (PZT) films were directly deposited on Si substrates without a buffer layer by pulsed laser deposition. Only(110)-oriented PZT peaks (other than Si substrate peaks) were observed from the XRD data. The electrical properties of the PZT/Si capacitor were characterized in terms of both the capacitance versus voltage (C-V) and current versus voltage (I-V) measurements. The clockwise trace of the C-V curve shows ferroelectric polarization switching, as is expected. From the I-V curves, the Schottky emission and spacecharge-limited-current behaviour are found to be the mainly leakage current mechanism in a certain electric field range in the negative and positive bias, respectively.     

Temperature dependent phonon modes and ionicity of LiGaO2 single crystal

This paper reports that polarized far-infrared reflectivity measurements have been done on LiGaO2 single crystal along two crystalline taxes at different temperatures. The temperature dependent frequencies of the longitudinal and transverse optical phonon have been obtained from the real part of optical conductivity and the loss function respectively. A small Drude component is observed at frequency below 300 cm^-1 which could arise from Li ions or oxygen deficiencies. The ionicity of LiGaO2 has been studied from the analysis of the Born effective charge of different ions.     

La0.33Pr0.34Ca0.33MnO3薄膜的应变效应

采用脉冲激光沉积法分别在(100)LaAlO₃和(100)SrTiO₃基片上生长了La_0.33Pr_0.34Ca_0.33MnO₃薄膜,并通过磁测量和电输运测量对生长在不同基片上的La_0.33Pr_0.34Ca_0.33MnO₃薄膜的物性进行了研究.结果表明,基片和薄膜之间的压应力导致La_{关键词： 钙钛矿锰氧化物 相分离 电荷有序}     

Matching effect in superconducting NbN thin film with a square lattice of holes

A square hole array is fabricated over a micro-bridge of NbN thin film by electron beam lithography and reactive ion milling. Magneto-resistance is measured across the micro-bridge filled with a hole array near the superconducting transition temperature. It is found that magneto-resistance minima occur when the number of vortices is an integer multiple or a fractional multiple of the number of holes. The temperature and the current dependences of the matching effect are studied.     

Interstitial vortex in superconducting film with periodic hole arrays

The response of superconducting Nb films with a diluted triangular and square array of holes to a perpendicular magnetic field are investigated.Due to small edge-to-edge separation of the holes,the patterned films are similar to multi-connected superconducting islands.Two regions in the magnetoresistance R(H) curves can be identified according to the field intervals of the resistance minima.Moreover,in between these two regions,variation of the minima spacing was observed.Our results provide strong evidence of the coexistence of interstitial vortices in the islands and fluxoids in the holes.     

Raman scattering studies on the collapsed phase of CaCo_2As_2

In this work,Raman scattering measurements have been performed on the collapsed phase CaCo_2As_2 crystals.At least 8 Raman modes were observed at room temperature though CaCo_2As_2 is structurally similar to other 122 compounds like BaFe_2As_2.Two Raman modes are assigned to the intrinsic A_(1g)and B_(1g)of this material system respectively.The other ones are considered to originate from the local vibrations relevant to cobalt vacancies.Careful polarized measurements allow us to clearly resolve the four-fold symmetry of the B_(1g)mode,which put strong constraints on possible point group symmetries of the system with Co vacancies.The temperature-dependent measurements demonstrate that the anomalies in both frequency and width of the B_(1g)mode occur around Neel temperature T_N.The anomalies are considered to be related to the gap opening near the magnetic transition.The study may shed light on the structural and magnetic changes and their correlations with superconductivity in 122 systems.