Effect of substrate temperature and pressure on properties of microcrystalline silicon films

In this paper intrinsic microcrystalline silicon films have been prepared by very high frequency plasma enhanced chemical vapour deposition (VHF-PECVD) with different substrate temperature and pressure. The film properties were investigated by using Raman spectra, x-ray diffraction, scanning electron microscope (SEM), and optical transmittance measurements, as well as dark conductivity. Raman results indicate that increase of substrate temperature improves the microcrystallinity of the film. The crystallinity is improved when the pressure increases from 50Pa to 80Pa and the structure transits from microcrystalline to amorphous silicon for pressure higher than 80Pa. SEM reveals the effect of substrate temperature and pressure on surface morphology.     

Zr-Cu Amorphous Films Prepared by Magnetron Co-sputtering Deposition of Pure Zr and Cu

ZrxCu100-x amorphous films are prepared on Si （111） substrates by magnetron co-sputtering of pure Zr and Cu. It is found that the glass forming ability （GFA） of the films increases with x when x is in the range from 35 to 65 and with the best glass forming ability at x = 65. It is therefore different from the bulk counterparts, for which only x = 35 and 50 were reported to have high glass forming ability during casting. The structure of the films is sensitive to the substrate temperature and the sputtering argon pressure.     

Deposition of Diamond-Like carbon Films by High-Intensity Pulsed Ion Beam Ablation at Various Substrate Temperatures

Diamond-like carbon (DLC) films have been deposited on to Si substrates at substrate temperatures from 255℃ to 400O℃ by a high-intensity pulsed-ion-beam (HIPIB) ablation deposition technique. The formation of DLC is confirmed by Raman spectroscopy. According to an x-ray photoelectron spectroscopy analysis, the concentration of sp^3 carbon in the films is about 40% when the substrate temperature is below 300℃ C. With increasing substratetemperature from 25℃ to 400℃, the concentration of sp^3 carbon decreases from 43% to 8%. In other words,sp3 carbon is graphitized into sp^2 carbon when the substrate temperature is above 300℃. The results of xray diffraction and atomic force microscopy show that, with increasing the substrate temperature, the surface roughness and the friction coefficient increase, and the microhardness and the residual stress of the films decrease.     

Influence of the deposition parameters on the transition region of hydrogenated silicon films growth

Hydrogenated microcrystalline and amorphous silicon thin films were prepared by very high frequency plasmaenhanced chemical vapour deposition （VHF PECVD） by using a mixture of silane and hydrogen as source gas. The influence of deposition parameters on the transition region of hydrogenated silicon films growth was investigated by varying the silane concentration （SC）, plasma power （Pw）, working pressure （P）, and substrate temperature （Ts）. Results suggest that SC and Ts are the most critical factors that affect the film structure transition from microcrystalline to amorphous phase. A narrow region in the range of SC and Ts, in which the rapid phase transition takes place, was identified. It was found that at lower P or higher Pw, the transition region is shifted to larger SC. In addition, the dark conductivity and photoconductivity decrease with SC and show sharp changes in the transition region. It proposed that the transition process and the transition region are determined by the competition between the etching effect of atomic hydrogen and the growth of amorphous phase.     

Nanoscale superconductivity of ?-Ga islands grown by molecular beam epitaxy

We report on the preparation and superconductivity of metastable γ-Ga islands on Si(111) substrate. The Ga grows in a typical Volmer-Weber mode at a low temperature of 110 K, resulting in formation of Ga nanoislands at various sizes with the identical γ-phase. In-situ low temperature scanning tunneling spectra reveal quantized electronic states in ultrathin Ga islands. It is found that both the lateral size and thickness of the Ga islands strongly suppress the superconductivity. Due to substantial surface energy contribution, the transition temperature Tc scales inversely with the island thickness and the minimum thickness for the occurrence of superconductivity is calculated to be two monolayers.     

Effects of Substrate Temperature on Helium Content and Microstructure of Nanocrystalline Titanium Films

Helium-charged nanocrystalline titanium films have been deposited by HeAr magnetron co-sputtering. The effects of substrate temperature on the helium content and microstructure of the nanocrystalline titanium films have been studied. The results indicate that helium atoms with a high concentration are evenly incorporated in the deposited titanium films. When the substrate temperature increases from 60℃ to 350℃ while the other deposition＇parameters are fixed, the helium content decreases gradually from 38.6 at.% to 9.2at.%, which proves that nanocrystalline Ti films have a great helium storage capacity. The 20 angle of the Bragg peak of （002） crystal planes of the He-charged Ti film shifts to a lower angle and that of （100） crystal plane is unchanged as compared with that of the pure Ti film, which indicates that the lattice parameter c increases and a keeps at the primitive value. The grain refining and helium damage result in the diffraction peak broadening.     

Fabrication of VO_2 thin film by rapid thermal annealing in oxygen atmosphere and its metal–insulator phase transition properties

Vanadium dioxide thin films have been fabricated through sputtering vanadium thin films and rapid thermal annealing in oxygen. The microstructure and the metal–insulator transition properties of the vanadium dioxide thin films were investigated by X-ray diffraction, X-ray photoelectron spectroscopy, and a spectrometer. It is found that the preferred orientation of the vanadium dioxide changes from(1ˉ11) to(011) with increasing thickness of the vanadium thin film after rapid thermal annealing. The vanadium dioxide thin films exhibit an obvious metal–insulator transition with increasing temperature, and the phase transition temperature decreases as the film thickness increases. The transition shows hysteretic behaviors, and the hysteresis width decreases as the film thickness increases due to the higher concentration carriers resulted from the uncompleted lattice. The fabrication of vanadium dioxide thin films with higher concentration carriers will facilitate the nature study of the metal–insulator transition.     

Superconductivity of bilayer titanium/indium thin film grown on SiO_2/Si(001)

Bilayer superconducting films with tunable transition temperature(Tc) are a critical ingredient to the fabrication of high-performance transition edge sensors. Commonly chosen materials include Mo/Au, Mo/Cu, Ti/Au, and Ti/Al systems. Here in this work, titanium/indium(Ti/In) bilayer superconducting films are successfully fabricated on SiO_2/Si(001)substrates by molecular beam epitaxy(MBE). The success in the epitaxial growth of indium on titanium is achieved by lowering the substrate temperature to-150?C during indium evaporation. We measure the critical temperature under a bias current of 10 μA, and obtain different superconducting transition temperatures ranging from 645 m K to 2.7 K by adjusting the thickness ratio of Ti/In. Our results demonstrate that the transition temperature decreases as the thickness ratio of Ti/In increases.     

Temperature dependences of optical properties,chemical composition,structure,and laser damage in Ta2O5 films

Ta2O5 films are prepared by e-beam evaporation with varied deposition temperatures,annealing temperatures,and annealing times.The effects of temperature on the optical properties,chemical composition,structure,and laserinduced damage threshold(LIDT) are systematically investigated.The results show that the increase of deposition temperature decreases the film transmittance slightly,yet annealing below 923 K is beneficial for the transmittance.The XRD analysis reveals that the film is in the amorphous phase when annealed below 873 K and in thehexagonal phase when annealed at 1073 K.While an interesting near-crystalline phase is found when annealed at 923 K.The LIDT increases with the deposition temperature increasing,whereas it increases firstly and then decreases as the annealing temperature increases.In addition,the increase of the annealing time from 4 h to 12 h is favourable to improving the LIDT,which is mainly due to the improvement of the O/Ta ratio.The highest LIDT film is obtained when annealed at 923 K,owing to the lowest density of defect.     

Optical Properties of ZnFe2O4—SiO2 Granular Films Prepared by Radio—Frequency Magnetron Sputtering

We report on the optical properties of ZnFe2O4-SiO2 granular films prepared on quartz substrates by the radio-frequency magnetron sputtering method.Post-annealing was performed at different temperatures under flow oxygen atmosphere.The morphology and Structures of ZnFe2O4 nanoparticles were characterized by x-ray different line types in the optical absorption curves of ZnFe2O4-SiO2 granular films.The critical transition of line types occurs when ZnFe2O4 changes from amorphous to crystalline,and the transition temperature increases with the increasing content of ZnFe2O4.There is an obvious blueshift of the optical absorption edge of the granular films with the decreasing annealing temperature.     

衬底温度和硼掺杂对p型氢化微晶硅薄膜结构和电学特性的影响

以B₂H₆为掺杂剂,采用射频等离子体增强化学气相沉积技术在玻璃衬底上制备p型氢化微晶硅薄膜.研究了衬底温度和硼烷掺杂比对薄膜的微结构和暗电导率的影响.结果表明：在较高的衬底温度下很低的硼烷掺杂比即可导致薄膜非晶化;在实验范围内,随着衬底温度升高薄膜的晶化率单调下降,暗电导率先缓慢增加然后迅速下降,变化趋势与硼烷掺杂比的影响极为相似.最后着重讨论了p型氢化微晶硅薄膜的生长机理. 关键词： p型氢化微晶硅薄膜 衬底温度 晶化率 电导率     

Visible photoluminescence from silicon-incorporated diamond like carbon films synthesized via direct current PECVD technique

Silicon-incorporated diamond like carbon (Si-DLC) films were deposited via DC plasma-enhanced chemical vapor deposition (PECVD) on glass and alumina substrates at a substrate temperature of 473 K. The precursor gas used was acetylene and for silicon incorporation tetraethyl orthosilicate dissolved in methanol was used. Silicon atomic percentage in the films was varied from 0% to 19.3% as measured from energy dispersive X-ray analysis. Fourier transformed infrared spectroscopy studies depicted the presence of Si-C, Si-H and Si-H₂ bonding within the films. The binding energies of C 1s, Si 2s and Si 2p were determined from X-ray photoelectron spectroscopic studies. UV-vis-NIR spectroscopic studies were used to determine the optical gaps as well as the Urbach parameters of the samples. Room temperature photoluminescence study showed a broad peak centered at around 467 nm. Also the peak intensity was found to increase monotonically with Si percentages. The results are discussed in terms of the electronic structure of a-C:H, the doping induced defect states and the enhanced carbon dangling bonds via the formation of more sp³ hybridized carbon network.     

The optoelectronic properties of silicon films deposited by inductively coupled plasma CVD

Hydrogenated amorphous and microcrystalline silicon films were deposited by inductively coupled plasma chemical vapor deposition (ICP-CVD) at low substrate temperatures using H₂-diluted SiH₄ as a source gas. High-density plasma generated by inductively coupled excitation facilitates the crystallization of silicon films at low temperatures, and microcrystalline silicon films were obtained at the substrate temperature as low as 180 °C. The columnar structure of the films becomes more and more compact with an increase of their crystallinity. The reduction of hydrogen content in the films causes a narrowing of the optical bandgap and an enhancement of the absorption with increasing the substrate temperature. The microcrystalline silicon films show two electronic transport mechanisms: one is related to the density of state distribution in the temperature region near room temperature and the other is the variable range hopping between localized electronic states close to the Fermi level below 170 K. A reasonable explanation is presented for the dependence of the optoelectronic properties on the microstructure of the silicon films. The films prepared at a substrate temperature of 300 °C have highly crystalline and compact columnar structure, high optical absorption coefficient and electrical conductivity, and a low hydrogen content of 3.8%.     

Structural and luminescent characteristics of pulsed laser deposited Eu3+-doped Y2O3 thin films

Thin films of Eu-doped Y₂O₃ were deposited using the pulsed laser ablation technique on amorphous fused silica substrates. The effect of oxygen partial pressure (pO₂) and substrate temperature on the structural and optical characteristics of the deposited films were investigated. All the deposited films were crystalline, showing preferred orientation along the (111) plane, irrespective of oxygen partial pressure and substrate temperature. The film deposited at 0.005?mbar pO₂ exhibited better crystallinity with minimum FWHM at a substrate temperature of 600°C. All the films deposited at various substrate temperatures and different partial pressure (at 600°C) exhibited a red luminescence peak at 615?nm corresponding to the ⁵D₀–⁷F₁ transition in Eu³⁺. Photoluminescence excitation spectra exhibited two bands, one corresponding to band to band excitation (212?nm) of the host and the other to charge transfer band excitation (245?nm). A microstructure analysis revealed that surface roughness of the as-deposited films increases with increase in oxygen partial pressure.     

Monte Carlo simulation of growth of porous SiOx by vapor deposition

A random network model containing defects has been developed and applied to the deposition of amorphous SiOx films on a flat substrate. A new Monte Carlo procedure enables dangling bonds to migrate and annihilate. The degree of porosity in the films is found to increase with oxygen content. As the oxygen content increases a larger fraction of pore surfaces is covered with oxygen, and the density of dangling bonds on pore surfaces decreases. Oxygen plays the role of a surfactant, lowering the energies of pore surfaces and enhancing the porosity of amorphous SiO2 compared to amorphous Si.     

The influence of substrate temperature variation on tungsten oxide thin film growth in an HFCVD system

Tungsten oxide (WO₃) thin films were deposited by a modified hot filament chemical vapor deposition (HFCVD) technique using Si (1 0 0) substrates. The substrate temperature was varied from room temperature to 430 °C at an interval of 100 °C. The influence of the substrate temperature on the structural and optical properties of the WO₃ films was studied. X-ray diffraction and Raman spectra show that as substrate temperature increases the film tends to crystallize from the amorphous state and the surface roughness decreases sharply after 230 °C as confirmed from AFM image analysis. Also from the X-ray analysis it is evident that the substrate orientation plays a key role in growth. There is a sharp peak for samples on Si substrate due to texturing. The film thickness also decreases as substrate temperature increases. UV-vis spectra show that as substrate temperature increases the film property changes from metallic to insulating behavior due to changing stoichiometry, which was confirmed by XPS analysis.     

Evolution of infrared spectra and optical emission spectra in hydrogenated silicon thin films prepared by VHF-PECVD

A series of hydrogenated silicon thin films with varying silane concentrations have been deposited by using very high frequency plasma enhanced chemical vapor deposition (VHF-PECVD) method. The deposition process and the silicon thin films are studied by using optical emission spectroscopy (OES) and Fourier transfer infrared (FTIR) spectroscopy, respectively. The results show that when the silane concentration changes from 10% to 1%, the peak frequency of the Si—H stretching mode shifts from 2000 cm ^{- 1} to 2100 cm ^{- 1}, while the peak frequency of the Si—H wagging—rocking mode shifts from 650 cm ^{- 1} to 620 cm ^{- 1}. At the same time the SiH^*/H_α intensity ratio in the plasma decreases gradually. The evolution of the infrared spectra and the optical emission spectra demonstrates a morphological phase transition from amorphous silicon (a-Si:H) to microcrystalline silicon (μc-Si:H). The structural evolution and the μc-Si:H formation have been analyzed based on the variation of H_α and SiH^* intensities in the plasma. The role of oxygen impurity during the plasma process and in the silicon films is also discussed in this study.     

过渡区p型氢化硅氧薄膜结构和光电特性的研究

采用射频等离子体增强化学气相沉积技术,利用二氧化碳(CO_2)、氢气(H_2)、硅烷(SiH_4)和乙硼烷(B_2H_6)作为气源,制备出一系列p型氢化硅氧薄膜.利用拉曼光谱、傅里叶变换红外光谱和暗电导测试,研究了不同二氧化碳流量对薄膜材料结构和光电特性的影响,获得了从纳米晶相向非晶相转变的过渡区P层.研究表明:随着二氧化碳流量从0增加到1.2 cm~3·min~(-1),拉曼光谱的峰值位置从520 cm~(-1)逐渐移至480 cm~(-1).材料红外光谱表明,随着二氧化碳流量的增加,薄膜中的氧含量逐渐增加,氢键配置逐渐由硅单氢键转换为硅双氢键.P层SiO:H薄膜电导率从3S/cm降为8.3×10~(-6)S/cm.所有p型SiO:H薄膜的光学带隙(Eopt)都在1.82—2.13 eV之间变化.在不加背反射电极的条件下,利用从纳米晶相向非晶相转变的过渡区P层作为电池的窗口层,且在P层和I层之间插入一定厚度的缓冲层,制备出效率为8.27%的非晶硅薄膜电池.     

氢化非晶硅激光结晶温场控制模型

氢化非晶硅在低速激光扫描下,可以得到四个结晶区,即微晶区,固相结晶区,过冷液相结晶区和液相激光结晶区。对氢化非晶硅激光结晶提出了一种温场控制模型,可用以解释结晶特点,揭示结晶过程。 关键词：