镧掺杂BaSnO3薄膜的电学和光学特性

利用射频磁控溅射法在(LaAlO₃)_0.3(SrAl_0.5Ta_0.5O₃)_0.7 (001)单晶基底上生长了镧掺杂BaSnO₃外延薄膜. 通过Hall效应和热电势测量证实了镧掺杂BaSnO₃薄膜具有n型简并半导体特征, 并且基于载流子浓度和Seebeck系数计算出电子的有效质量为0.31m₀ (m₀为自由电子质量). 镧掺杂BaSnO₃薄膜在可见波段具有良好的透明性(透过率大于73%). 基于介电模型对薄膜的透过率曲线进行拟合, 从拟合结果中不仅得到了薄膜的厚度为781.2 nm, 能带宽度为3.43 eV、 带尾宽度为0.27 eV和复光学介电常数随波长的变化规律, 而且也强力地支持了基于电学参数计算电子有效质量的正确性.     

掺杂Y2O3和BaCeO3提高MOD-YBCO超导性能的研究

本文通过在前驱液中添加过量钇盐和铈的有机盐,采用三氟乙酸盐-金属有机沉积法(TFA-MOD) 在铝酸镧单晶基体上制备了含有纳米氧化钇和纳米铈酸钡的YBCO薄膜. 与纯YBCO薄膜相比,掺杂Y₂O₃/BaCeO₃的YBCO膜的临界转变温度几乎保持不变,为91 K左右. 而掺杂Y₂O₃/BaCeO₃的YBCO膜的临界电流密度达到5.0 MA/cm² (77 K, 0T), 是纯YBCO膜临界电流密度的1.5倍.薄膜中的Y₂O₃和BaCeO₃可能在YBCO内部起到了 有效的钉扎磁通作用. 关键词： 钇钡铜氧薄膜 2O₃和纳米BaCeO₃')" href="#">纳米Y₂O₃和纳米BaCeO₃ 磁通钉扎 三氟乙酸盐-金属有机沉积     

In2O3/SnO2薄膜的制备及光谱反射性能研究

开展了在伪装网基布上镀In₂O₃/SnO₂薄膜的性能研究,系统分析了薄膜厚度对其光谱反射性能的影响;总结了薄膜厚度对In₂O₃/SnO₂薄膜表面形貌、光谱反射辐射性能的影响规律,为In₂O₃/SnO₂薄膜的红外伪装应用奠定了基础理论和实验依据. 关键词： 2O₃/SnO₂薄膜')" href="#">In₂O₃/SnO₂薄膜 红外反射特性 红外发射率 可见光—近红外透过率     

氧压对SrTiO3和SrNb0.2Ti0.8O3薄膜晶格参数的影响及激光感生热电电压效应

采用脉冲激光沉积技术制备了SrTiO₃和SrNb_0.2Ti_0.8O₃薄膜.X射线衍射分析表明在LaAlO₃(100)单晶平衬底上生长的SrTiO₃及SrNb_0.2Ti_0.8O₃薄膜是沿［001］取向的近外延生长.随着氧压在一定范围内逐渐增大,SrTiO₃薄膜的晶格参数减小,而SrNb_0.2Ti_0.8O₃薄膜的晶格参数先减小后增大.同时摸索出制备具有二维电子气超晶格(SrTiO₃/SrNb_0.2Ti_0.8O₃)_L的最佳氧压为1.0×10^-2Pa.另外在LaAlO₃(100)倾斜衬底上制备的SrNb_0.2Ti_0.8O₃薄膜中观察到激光感生热电电压效应. 关键词： 0.2Ti_0.8O₃薄膜')" href="#">SrNb_0.2Ti_0.8O₃薄膜 晶格参数 激光感生热电电压 脉冲激光沉积     

关于MgB2/Al2O3超导薄膜电阻转变和各向异性的研究

利用电子束蒸发方法将MgB₂超导薄膜沉积到Al₂O₃(001)衬底上.采用标准的四引线法研究了磁场平行和垂直超导薄膜ab平面下的电阻转变.一个激活能模型 U(T,H)=U₀(1-T/(T_c+δ))ⁿ(1-H/H 关键词： 2/Al₂O₃')" href="#">MgB₂/Al₂O₃ 超导体 电阻转变 各向异性     

热原子层沉积钛掺杂氧化镓薄膜的光学性能

在250℃的低温下，以三甲基镓、四(二甲氨基)钛为前躯体源，O₃为反应气体，采用热原子层沉积制备了Ti掺杂Ga₂O₃(TGO)薄膜。Ga₂O₃和TiO₂的生长速率分别为0.037 nm/cycle和0.08 nm/cycle,TGO薄膜厚度低于理论计算值。X射线光电子能谱仪测试结果表明膜中Ti浓度随Ga₂O₃/TiO₂循环比减少而增加，O 1s、Ga 2p和Ti 2p的峰位置向较低的结合能移动，这是因为Ti原子取代了Ga原子的某些位点引起了结合能降低，表明Ti元素成功掺杂到Ga₂O₃薄膜中。TiO₂和Ga₂O₃的芯能级光谱分析表明薄膜中存有Ti⁴⁺和Ga³⁺离子。TGO薄膜的O 1s芯能级光谱中Ga-O键随着Ti-O键含量增加而下降，表明T...     

磁控溅射制备Y2O3-TiO2薄膜形貌的研究

室温下采用射频磁控溅射法,在硅衬底上制备了Y₂O₃-TiO₂氧化物复合薄膜.利用XRD(X-ray diffraction)和AFM( atomic force microscopy)分析观察了退火前后样品的物相、形貌等变化,讨论了致密薄膜的生长机理.实验发现,溅射功率越大,薄膜的平整度和致密度越好.对热处理前后样品的结晶结构和表面形貌的分析结果显示,在本实验参数范围内,随着溅射功率的增大,更多的Y₂O_{3关键词： 2}O₃-TiO₂薄膜')" href="#">Y₂O₃-TiO₂薄膜 表面形貌 原子力显微镜 磁控溅射     

Si掺杂β-Ga2O3的第一性原理计算与实验研究

采用基于密度泛函理论(DFT)的第一性原理平面波超软赝势(USPP)法, 在广义梯度近似(GGA)下计算了本征β-Ga₂O₃和Si掺杂β-Ga₂O₃的能带结构、电子态密度、差分电荷密度和光学特性. 在蓝宝石衬底(0001)晶面上用脉冲激光沉积(PLD)法制备了本征β-Ga₂O₃和Si掺杂β-Ga₂O₃薄膜, 测量了其吸收光谱和反射光 关键词： 第一性原理 超软赝势 密度泛函理论 2O₃')" href="#">Si掺杂β-Ga₂O₃     

金属有机物化学气相沉积法生长Ga2（1-x）In2xO3薄膜的结构及光电性能研究

采用金属有机物化学气相沉积（MOCVD）法在蓝宝石（0001）衬底上制备出了Ga_2（1-x）In_2xO₃（x=01—09）薄膜,研究了薄膜的结构、电学和光学特性以及退火处理对薄膜性质的影响.测量结果表明：当In组分x=02时,样品为单斜β-Ga₂O₃结构;x=05的样品,薄膜呈现非晶结构,退火处理后薄膜结构得到明显的改善 关键词： 金属有机物化学气相沉积 2（1-x）In_2xO₃薄膜')" href="#">Ga_2（1-x）In_2xO₃薄膜 蓝宝石衬底 退火     

YBCO半导体薄膜及Bolometer特性

就Si为衬底的钇钡铜氧(分子式：Y₁Ba₂Cu₃O_7-δ ,δ≥05,简称YBCO)薄膜的半导体性质,及用于红外测辐射热计(Bolometer)的探 测性能进行了研究.通过测定温度电阻系数(TCR)和霍尔(Hall)系数,并采用XRD、拉曼散射 光谱等手段分析了YBCO半导体薄膜的微观结构和光谱响应特性,认为该薄膜是非制冷红外焦 平面的新型探测元材料. 关键词： YBCO半导体薄膜 测辐射热计 温度电阻系数     

调制掺杂GaAs/N-AlGaAs异质结的制备及输运性质

本文报道利用垂直束源式的分子束外延设备,生长了高质量的调制掺杂GaAs/N-AIGaAs异质结构,液氦温度下的二维电子迁移率达4.26×10⁵cm²/V·s(非光照)、5.9×10⁵cm²/V·S(光照)。用脉冲磁场下的磁声子共振测量,得到了二维电子的有效质量,并研究了异质结构中二维电子的低场迁移率增强特性及低温强磁场下的量子霍耳效应。 关键词：     

溶胶-凝胶法制备Li-N双掺p型ZnO薄膜的结构、光学和电学性能

采用溶胶-凝胶法在n型Si(100)衬底上沉积Li-N双掺杂ZnO薄膜,经X射线衍射和扫描电镜图片分析,所制备薄膜具有多晶纤锌矿结构和高的c轴择优取向.室温下霍尔效应测试结果显示Li-N双掺杂ZnO薄膜具有p型导电特性.在Li掺杂量为15.0at%,Li/N（摩尔比）为1∶1,700℃退火等优化条件下得到的最佳电学性能结果是：电阻率为0.34 Ω·cm,霍尔迁移率为16.43 cm²/V·s,载流子浓度为2.79×10¹⁹ cm^{-3关键词： Li-N双掺 p型ZnO薄膜 溶胶-凝胶 性能}     

Quantum transport studies of electron accumulation layers in InSe bulk crystals

Summary Experiments show that the Hall resistivityρ _xy of InSe bulk crystals is quantized into integer multiples ofh/e ². Quantum Hall effect in InSe is explained as a result of plane defects in InSe crystals. The electrons in bulk InSe are localized at these defects at low temperatures forming regions with two-dimensional conductivity. Concentration of electrons in these regions isN _2D=2·10¹¹ cm⁻² and their mobility μ=2·10⁴cm²/V·s. To speed up publication, the authors of this paper have agreed to not receive the proofs for correction.     

High-performance amorphous indium gallium zinc oxide thin-film transistors with sol-gel processed gate dielectric and channel layer fabricated using microwave irradiation

In this study, we fabricated high-performance a-IGZO TFTs by forming Al₂O₃ and a-IGZO thin films for gate insulator and active channel layer, respectively, using a sol-gel process. MWI for low thermal budget process was used to condensate Al₂O₃ and a-IGZO films, which was compared with the CTA. It is found that the MWI is superior process to the conventional method in terms of precursor and solvent decomposition and has proven to be more effective for eliminating residual organic contaminants. In addition, the MWI-treated Al₂O₃ and IGZO films have smoother surfaces, higher visible light transmittance, lower carbon contamination and impurities than the CTA-treated films. We have demonstrated that a-IGZO TFTs with sol-gel solution-processed Al₂O₃ gate insulator and a-IGZO channel layer can achieve a field effect mobility of 69.2 cm²/V·s, a subthreshold swing of 86.2 mV/decade and a large on/off current ratio of 1.48 × 10⁸, by the MWI process even at temperatures below 200 °C. In addition, the MWI-treated a-IGZO TFTs have excellent resistance to electron trapping and good stability to positive and negative gate-bias stress. Therefore, the sol-gel processed a-IGZO TFTs with Al₂O₃ gate oxide and the MWI treatment with a low thermal budget are promising for emerging transparent flat panel displays applications.     

调制掺杂GaAs/AlGaAs 2DEG材料持久光电导及子带电子特性研究

在掺Si的GaAs/AlGaAs二维电子气(2DEG)结构中，得到μ_2K=1.78×10^{6cm2/(V·s)的高迁移率.在低温(2K)和高磁场(6T)的条件下，对样品进行红 光辐照，观察到持久光电导(PPC)效应，电子浓度在光照后显著增加.通过整数量子霍尔效应 (IQHE)和Shubnikov-de Haas (SdH)振荡的测量，研究了2DEG的子带电子特性.样品在低温光 照后2DEG中第一子带和第二子带的电子浓度同时随电子总浓度的增加而增加；而且电子迁移 率也明显提高.同时，通过整数霍尔平台的宽度对光照前后电子的量子寿命变短现象作了理 论分析. 关键词： 二维电子气 量子霍尔效应 SdH振荡 持久光电导效应}     

用激光分子束外延在Si衬底上外延生长高质量的TiN薄膜

采用激光分子束外延技术,利用两步法,在Si单晶衬底上成功地外延生长出TiN薄膜材料.原子力显微镜分析结果显示, TiN薄膜材料表面光滑,在10 μm×10 μm范围内,均方根粗糙度为0842nm.霍耳效应测量结果显示,TiN薄膜在室温条件下的电阻率为36×10^-5Ω·cm,迁移率达到5830 cm²/V·S,表明TiN薄膜材料是一种优良的电极材料.X射线θ—2θ扫描结果和很高的迁移率均表明,高质量的TiN薄膜材料被外延在Si衬底 关键词： 激光分子束外延 TiN单晶薄膜 外延生长     

Preparation of ferromagnetic semiconducting HgCr2Se4 thin films by molecular-beam deposition

Summary Polycrystalline thin films of the ferromagnetic semiconductor HgCr₂Se₄ have been prepared for the first time on insulating MgAl₂O₄ single-crystal substrates by molecular-beam deposition and subsequent annealing with HgSe. The optimum conditions for preparing single-phase thin films of HgCr₂Se₄ were obtained. The magnetoresistance and Hall effects of these films were measured from 77 to 295 K in magnetic fields up to 1.19·10⁶ A/m. It becomes evident that these electrical properties of the films are affected by the interdiffusion layers in the films near the substrates or the magnetically disordered layers such as amorphous or grain boundaries in the films. Paper presented at the ?V International Conference on Ternary and Multinary Compounds?, held in Cagliari, September 14–16, 1982.     

In2O3 透明薄膜晶体管的制备及其电学性能的研究

采用磁控溅射方法在玻璃衬底上生长了In₂O₃晶体薄膜.该薄膜具有(111)晶面择优取向,晶粒尺寸达到33 nm.利用光刻工艺制作了以In₂O₃晶体薄膜为沟道层的底栅式薄膜晶体管.In₂O₃薄膜晶体管具有良好的栅压调制特性,场效应迁移率达到6.3 cm²/(V·s),开关电流比为3×10³,阈值电压为-0.9 V.结果表明,In相似文献   

Hf-sputtered indium oxide films doped with tin

Indium oxide films doped with tin (ITO-films) have been hf-sputtered from an 80 at-%In₂O₃/20 at-%SnO₂ target onto glass substrates. The sputter atmosphere contained mainly argon (10⁻²Torr) with addition of oxygen (0≦p _{O 2}≦2·10⁻²Torr). The sputtered films aren-conductors. The conductivity and density of charge carriers depend on the oxygen content of the sputter gas. They could be varied by two orders of magnitude. In air or in oxygen atmosphere the films oxidize at the surface and for a certain depth beneath the surface, thus decreasing the conductivity. The Hall mobility of the sputtered films is smaller (≈10 cm²V⁻¹ s⁻¹) than one observes at ITO films produced by CVD sparaying or other methods. The conductivity of as sputtered films approached maximum values of about 1000Ώ⁻¹cm⁻¹.     

基于氧化铟锡的无结低电压薄膜晶体管

在室温下制备了基于氧化铟锡(ITO)的底栅结构无结薄膜晶体管. 源漏电极和沟道层都是同样的ITO薄膜材料,没有形成传统的源极结和漏极结, 因而极大的简化了制备流程,降低了工艺成本.使用具有大电容的双电荷层SiO₂作为栅介质, 发现当ITO沟道层的厚度降到约20 nm时, 器件的栅极电压可以很好的调控源漏电流. 这些无结薄膜晶体管具有良好的器件性能: 低工作电压(1.5 V), 小亚阈值摆幅(0.13 V/dec)、 高迁移率(21.56 cm²/V·s)和大开关电流比(1.3× 10⁶). 这些器件即使直接在大气环境中放置4个月, 器件性能也没有明显恶化:亚阈值摆幅保持为0.13 V/dec,迁移率略微下降至18.99 cm²/V·s,开关电流比依然大于10⁶.这种工作电压低、工艺简单、 性能稳定的无结低电压薄膜晶体管非常有希望应用于低能耗便携式电子产品以及新型传感器领域.