物理法和化学法制备的单层ZrO2膜的激光损伤行为差异

 分别采用电子束热蒸发技术和溶胶-凝胶技术在K9基片上镀制了光学厚度相近的ZrO₂单层薄膜,测试了两类薄膜的激光损伤阈值。分别采用透射式光热透镜技术、椭偏仪、原子力显微镜和光学显微镜研究了两类薄膜的热吸收、孔隙率、微观表面形貌、激光辐照前薄膜的杂质和缺陷状况以及激光辐照后薄膜的损伤形貌。实验结果表明：两类薄膜的不同损伤形貌与薄膜的热吸收与微观结构有关， 物理法制备的ZrO₂膜结构致密紧凑，膜层的杂质和缺陷多；化学法制备的ZrO₂膜结构疏松多孔，膜层纯净杂质少，激光损伤阈值达26.9 J/cm²；因物理法制备的ZrO₂膜拥有更大的热吸收(115.10×10^-6)和更小的孔隙率(0.20)，其激光损伤阈值较小(18.8 J/cm²)，损伤主要为溅射和应力破坏，而化学法制备的ZrO₂膜的损伤主要为剥层。理论上对实验结果进行了解释。     

铜膜和铁膜污染物诱导熔石英表面损伤行为的对比研究

采用人工溅射的方式分别在熔石英基片上镀制了光学厚度相近的铜膜和铁膜污染物。研究了熔石英基底在355nm波长的激光损伤阈值。分别采用透射式光热透镜技术、椭偏仪、原子力显微镜和光学显微镜研究了两类薄膜的热吸收、膜层厚度、表面微观形貌以及激光辐照后薄膜的损伤形貌。实验结果表明：熔石英表面的金属膜状污染物均导致基片损伤阈值下降,位于前表面的污染物引起的损伤阈值下降更为严重,约为23％。两种污染物薄膜引起基底的损伤形貌、基底损伤阈值的下降幅度与薄膜的热吸收系数与微观结构有关。从热力学响应角度,结合损伤形貌对污染物诱导熔石英表面形貌的损伤机理进行了讨论。     

单层SiO2物理膜与化学膜激光损伤机理的对比研究

采用离子束溅射沉积技术和溶胶-凝胶技术在K9基片上镀制了厚度相近的SiO₂单层介质膜，用表面热透镜技术对两类膜层分别进行了热吸收及实时动态热畸变实验测试，结合散射光阈值测试及实验前后膜层的显微观测，对相同基底、相同膜层材料而采用不同方法镀制的光学膜层，发现化学膜的强激光损伤阈值远高于相应物理膜；从热力学响应及膜层特性差异的角度揭示了化学膜层的强激光损伤阈值远高于相应物理膜层的微观机理，即物理膜具有高吸收下的致密膜层快传导的基底热冲击效应，而化学膜则有低吸收下的疏松空隙填充慢传导的延缓效应，大量的实验数据及现象都证实了这一结论. 关键词： 强激光辐照损伤 损伤形貌 热冲击 热吸收     

SiO2内保护层对LiB3O5晶体倍频增透膜损伤阈值的影响

 利用离子辅助电子束沉积方法在LiB₃O₅基底上镀制了不加SiO₂内保护层和加SiO₂内保护层的倍频增透膜，测量了两类薄膜在波长1 064 nm多脉冲辐照下的激光损伤阈值，获得了两种不同的损伤形貌，并对损伤原因作了初步探讨。实验结果表明：保护层的加入把由基底膜层界面缺陷吸收所决定的阈值改变到由HfO₂膜层内缺陷吸收所决定的阈值，显著提高了倍频增透膜的抗激光损伤能力。     

表面Al膜污染物诱导熔石英表面损伤特性

在熔石英表面人工溅射一层Al膜污染物,分别测试污染前后熔石英基片在355 nm波长激光辐照下的损伤阈值,并采用透射式光热透镜技术、椭偏仪和光学显微镜研究了污染物Al膜的热吸收、厚度以及激光辐照前后熔石英的损伤形貌。用355 nm波长的脉冲激光分别辐照位于污染的熔石英和洁净的熔石英前后表面的损伤点,并用显微镜在线采集损伤增长图样,测试损伤点面积。实验表明:熔石英前表面的金属Al膜污染物导致基片损伤阈值的下降约30%,后表面的污染物导致基片下降约15%,位于熔石英样片后表面损伤点面积随激光辐照次数呈指数增长,而位于前表面的损伤点面积与激光脉冲辐照次数呈线性增长关系;带有污染的熔石英样片的增长因子比洁净的熔石英样片的增长因子高30%。     

化学法制备的HfO2薄膜的激光损伤阈值研究

 采用化学法制备了HfO₂介质膜，研究了热处理、紫外辐照以及Al₂O₃复合对HfO₂介质膜激光损伤阈值的影响。采用红外光谱（FTIR）和X射线衍射仪对薄膜进行了表征，并用输出波长为1.064 μm、脉宽为10 ns的电光调Q激光系统测试薄膜的激光损伤阈值。实验结果表明：采用150 ℃左右的温度对薄膜进行热处理可以提高薄膜的激光损伤阈值，所获得的薄膜的激光损伤阈值高达42.32 J/cm²，比热处理前的激光损伤阈值提高了82%；无机材料Al₂O₃的适量添加能够提高薄膜的激光损伤阈值，其中HfO₂与Al₂O₃的最佳质量配比约为95∶5；另外，对薄膜进行适当的紫外辐照也可改善HfO₂ 薄膜以及HfO₂-Al₂O₃复合薄膜的抗激光损伤性能。紫外辐照对提高HfO₂-Al₂O₃复合薄膜的激光损伤阈值效果尤为显著，辐照40 min后的激光损伤阈值达到44.33 J/cm²，比紫外辐照前的激光损伤阈值提高了90%。     

高损伤阈值三倍频分离膜

 设计了Nd：YAG激光用三倍频分离膜,膜层材料为SiO₂和HfO₂。经过优化,膜系在355 nm处的反射率在99%以上,在532 nm和1 064 nm处透射率也在99%以上。采用电子束蒸发技术,在熔融石英基底上制备了样品,经测量,制备的分离膜光学性能与设计值接近。分离膜在355 nm激光辐照下的损伤阈值为5.1 J/cm²,并用微分干涉显微镜表征了薄膜损伤形貌。     

HfO2/SiO2双色膜在1 064 nm和532 nm激光辐照下的损伤特性

 采用电子束蒸发的方式,制备了有氧化硅内保护层和没有氧化硅内保护层的1 064 nm高透过、532 nm高反射的HfO₂/SiO₂双色膜,测量了它们的光学性能以及在基频和倍频激光辐照下的抗损伤性能。结果表明:氧化硅内保护层提高了双色膜在基频光辐照下的损伤阈值,对双色膜在倍频光辐照下的损伤阈值无明显影响。通过观察薄膜的损伤形貌,分析破斑的深度信息结合驻波场分布,对两类双色膜在基频光和倍频光下的损伤机制做了初步探讨。分析表明:氧化硅内保护层提高了膜基界面的抗损伤性能,从而提高了双色膜在基频光下的损伤阈值。     

单层SiO2物理膜与化学膜激光损伤机理的对比研究

采用离子束溅射沉积技术和溶胶-凝胶技术在K9基片上镀制了厚度相近的SiO2单层介质膜,用表面热透镜技术对两类膜层分别进行了热吸收及实时动态热畸变实验测试,结合散射光阈值测试及实验前后膜层的显微观测,对相同基底、相同膜层材料而采用不同方法镀制的光学膜层,发现化学膜的强激光损伤阈值远高于相应物理膜;从热力学响应及膜层特性差异的角度揭示了化学膜层的强激光损伤阈值远高于相应物理膜层的微观机理,即物理膜具有高吸收下的致密膜层快传导的基底热冲击效应,而化学膜则有低吸收下的疏松空隙填充慢传导的延缓效应,大量的实验数据及现象都证实了这一结论.     

氧分压对ZrO2薄膜激光损伤阈值的影响

 在不同的氧分压下用电子束热蒸发的方法制备了ZrO₂薄膜。分别通过X射线衍射、光学光谱、热透镜技术、抗激光辐照等测试，对所制备样品的微结构、折射率、吸收率及激光损伤阈值进行了测量。实验结果表明，薄膜中晶粒主要是四方相为主的多晶结构，并且随着氧分压的增加，结晶度、折射率以及弱吸收均逐渐降低。薄膜的激光损伤阈值开始随着氧分压增加从18.5J/cm²逐渐增加，氧分压为9×10^-3Pa时达到最大，值为26.7 J/cm²，氧分压再增加时则又降低到17.5 J/cm²。由此可见，氧分压引起的薄膜微结构变化是ZrO₂薄膜激光损伤阈值变化的主要原因。     

Effect of ammonia treatment on laser-induced damage of nano-porous silica film

The sol-gel monolayer silica films on K9 glass substrates were prepared with the dip method, and then treated in saturated ammonia gas. The laser-induced damage threshold (LIDT) of silica films with and without ammonia treatment was measured. Properties of the films were analyzed by using Stanford photo-thermal solutions (SPTS), ellipsometry, atomic force microscopy (AFM), and optical microscopy to study the effect of ammonia treatment on laser-induced damage of sol-gel monolayer silica film under laser irradiation. The experimental results showed that compared with the as-grown silica film, the silica film with ammonia treatment had larger absorption and smaller porous ratio, and it had smaller LIDT. Considering the improved abrasion resistance of films with ammonia treatment, a trade-off is always needed between abrasion resistance and LIDT in practice.     

Experimental research of laser-induced damage of the monolayer ZrO2 PVD and sol–gel films

Monolayer zirconia physical vapor deposition (PVD) and sol–gel films on K9 glass substrates were prepared by electron beam evaporation and spin coating methods, respectively. The laser-induced damage threshold (LIDT) of each film was measured. Properties of the films were analyzed using Stanford photo-thermal solutions (SPTS), ellipsometry, atomic force microscopy (AFM) and optical microscopy to study the damage mechanism of films under laser irradiation. The experimental results showed that, compared with the monolayer zirconia sol–gel film, the monolayer zirconia PVD film had larger absorption and smaller porous ratio, and that it had smaller LIDT. The different damage morphologies of films were influenced by their different absorption and microstructure characteristics. The zirconia sol–gel film is more suitable for applications involving high-power lasers.     

Influence of porosity on laser damage threshold of sol–gel ZrO2 and SiO2 monolayer films

Monolayer ZrO₂ sol–gel and physical vapor deposition (PVD) films were prepared by spin method and electron beam evaporation method, respectively. Monolayer sol–gel SiO₂ films were prepared with the dip-coating method from acid and base catalyzed SiO₂ sols, respectively. Some of the SiO₂ base films were subsequently treated in saturated ammonia gas for 20 h. The laser induced damage threshold (LIDT) of each film was measured. Properties of the films were analyzed by using Stanford photo-thermal solutions (SPTSs), ellipsometer, atomic force microscopy (AFM) and optical microscopy. The experimental results showed that porous ratio is an essential factor to decide the LIDT for sol–gel films, which benefits the pressure exerted on the film or substrate by the moving particle to dissipate. The films with lower thermal absorption and higher porous ratio have higher LIDT.     

二氧化硅增透膜微观结构与激光损伤阈值的调控

采用溶胶-凝胶技术制备了二氧化硅增透膜,通过向溶胶中添加高分子聚乙烯醇缩丁醛（PVB）,调控胶体的粒径,进而控制膜层微观结构,研究膜层微观结构与激光损伤阈值的关系。纳米粒度仪和扫描探针显微镜测试表明:PVB加入溶胶后,控制了二氧化硅胶粒的生长,使二氧化硅胶粒生长更均匀,因而膜层的微观结构更均匀。当PVB质量分数为1%时,胶体粒径为15 nm,分散系数小于0.1。用该胶体镀膜,膜层均匀,表面粗糙度小于3.25 nm。并且PVB加入后增加了膜层胶粒间的黏附性,使得膜层强度增大。PVB加入使膜层的激光损伤阈值有所增加。当PVB的添加量为1%时,膜层的激光损失阈值从30.0 J/cm2增加到40.1 J/cm2。膜层激光损伤阈值的增加与膜层微观均匀性和物理强度的增加有关。     

Structural and optical properties of laser irradiated nano structured cadmium oxide thin film synthesized by sol-gel spin coating method

Cadmium oxide CdO nanostructured thin films are synthesized using sol-gel spin coating method. The prepared samples of CdO thin films are irradiated with 10 mJ laser from pulsed Q-Switched Nd:YAG laser at 1064 and 532 nm wavelength. The samples were exposed to 45 pulses of 7 ns pulse duration. Morphology and structural analysis were carried out with scanning electron microscope (SEM) micrographs and X-ray diffraction (XRD) patterns. Optical investigations were obtained with spectrometer and fluorospectrometer from Shimadzu. SEM micrographs confirm the nanostructure of the CdO film and indicate agglomeration of nanoparticles with laser irradiation. XRD patterns show decrease in the intensity of orientation peaks after laser irradiation. Variation in band gap energy, absorption peaks, and photoluminescence spectra with laser irradiation are observed.     

原子层沉积HfO_2薄膜的激光损伤特性分析

以目前激光惯性约束聚变中应用最广泛的高折射率材料二氧化铪(HfO2)为研究对象,在熔石英基底上分别采用TEMAH和HfCl4前驱体制备了HfO2薄膜,沉积温度分别为100,200和300℃。采用椭偏仪和激光量热计对薄膜的光学性能进行了测量分析,采用X射线衍射仪(XRD)对薄膜的微结构进行了测量。最后在小口径激光阈值测量平台上按照1-on-1测量模式对薄膜的损伤阈值进行了测试,并采用扫描电子显微镜(SEM)对损伤形貌进行了分析。研究表明,用同一种前驱体源时,随着沉积温度升高,薄膜折射率增加,吸收增多,损伤阈值降低。在相同温度下,采用有机源制备的薄膜更容易在薄膜内部形成有机残留,导致薄膜吸收增加,损伤阈值降低。采用HfCl4作为前驱体源在100℃制备氧化铪薄膜时,损伤阈值能够达到31.8J/cm2(1064nm,3ns)。     

HfO_2/SiO_2薄膜的激光预处理作用研究北大核心CSCD

激光预处理是提高激光薄膜抗激光损伤阈值的重要手段。对电子束蒸发方式镀制的HfO2/SiO2反射膜采用大口径激光进行了辐照,并采用激光量热计测量了激光辐射前后的弱吸收值。采用聚焦离子束(FIB)技术分析了激光辐照后薄膜的损伤形态并探究了损伤原因,首次采用扫描电镜拍摄到了节瘤部分喷发时的形貌图,并对其进行了FIB分析,为进一步了解节瘤的损伤过程提供了依据。实验发现,激光辐照过后的激光薄膜弱吸收明显降低,激光预处理有效减少了引起薄膜吸收的缺陷,存在明显的清洗效应;在本实验采用的HfO2/SiO2反射膜中,激光预处理技术对于祛除位于基底上种子形成的节瘤是有效的,原因是激光辐射过后该节瘤进行了预喷发并不会对后续激光产生影响;而激光预处理技术对位于膜层中间的可能是镀膜过程中材料飞溅引起的缺陷是无效的,需要通过其他手段对该类节瘤进行祛除。