C2轴手性双胍催化叶立德和不饱和吖内酯的串联反应研究

本文成功合成了4种基于联二萘酚骨架的手性双胍-酰胺类催化剂,并将其应用于邻羟基苯甲醛亚甲胺叶立德与不饱和吖内酯的1,3-偶极环加成和分子内串联反应。研究表明,在室温下以CHCl_3作为溶剂、轴手性胍(1b,10(mol)%)作为催化剂,反应12h,能以较好的收率(73%～88%)和较高的对映选择性(72%～86%)得到苯并吡喃衍生物。     

Simulation of near-infrared photodiode detectors based on β-FeSi_2/4H-SiC heterojunctions

In this paper,we propose a near-infrared p-type β-FeSi2/n-type 4H-SiC heterojunction photodetector with semiconducting silicide(β-FeSi2) as the active region for the first time.The optoelectronic characteristics of the photodetector are simulated using a commercial simulator at room temperature.The results show that the photodetector has a good rectifying character and a good response to near-infrared light.Interface states should be minimized to obtain a lower reverse leakage current.The response spectrum of the β-FeSi2/4H-SiC detector,which consists of a p-type β-FeSi2 absorption layer with a doping concentration of 1×1015cm-3 and a thickness of 2.5 μm,has a peak of 755 mA/W at 1.42 μm.The illumination of the SiC side obtains a higher responsivity than that of the β-FeSi2 side.The results illustrate that the β-FeSi2/4H-SiC heterojunction can be used as a near-infrared photodetector compatible with near-infrared optically-activated SiC-based power switching devices.     

联萘酚多氢键硫脲催化合成1,4-二氢吡啶衍生物

本文合成了三种具有多氢键的联萘酚轴手性硫脲催化剂,并将其用于催化合成1,4-二氢吡啶衍生物。结果显示,所合成的新型多氢键硫脲均表现出较好的催化作用,能有效地提高1,4-二氢吡啶衍生物的收率和对映选择性。所有新化合物结构均经过~1H NMR、~(13)C NMR、IR、熔点等表征所确认。     

Optically controlled SiCGe/SiC heterojunction transistor with charge-compensation layer

A novel optically controlled SiCGe/SiC heterojunction transistor with charge-compensation technique has been simulated by using commercial simulator.This paper discusses the electric field distribution,spectral response and transient response of the device.Due to utilizing p-SiCGe charge-compensation layer,the responsivity increases nearly two times and breakdown voltage increases 33%.The switching characteristic illustrates that the device is latch-free and its fall time is much longer than the rise time.With an increase of the light power density and wavelength,the rise time and fall time will become shorter and longer,respectively.In terms of carrier lifetime,a compromise should be made between the responsivity and switching speed,the ratio of them reaches maximum value when the minority carrier lifetime equals 90 ns.     

6H-SiC单晶锭边缘的多晶环控制

6H-SiC晶体生长过程中单晶锭边缘形成的多晶环影响单晶体的品质.本研究制定了以改进坩埚系统结构为主、调整线圈与坩埚相对位置为辅的多晶环厚度控制方案,利用自制设备进行了6H-SiC晶体生长验证实验,实验结果显示所生长6H-SiC单晶体不但周边和表面光滑,未有多晶出现,还实现了显著的扩径生长.     

SiC单晶片的取向研磨

优质晶体生长常常需要籽晶或衬底偏离常规结晶取向.为便于按任意偏向角度研磨晶片,本实验室设计并应用了晶片取向研磨夹具及相应的研磨工艺.本文介绍了该夹具和工艺的工作原理、技术要点以及对技术指标的鉴定情况.测试结果表明,研磨取向误差范围可控制在5;之内,研磨片厚度偏差小于5 μm、粗糙度Ra=0.12 μm.     

SiC晶体的PVT生长系统及测温盲孔对热场的影响

实验中研究了不同结构参数的测温盲孔对晶体生长面热场的影响,结果分析表明:径向温度梯度和轴向温度梯度与测温盲孔的深度和半径近似成正比关系,但测温盲孔尺寸变化对径向温度梯度和轴向温度梯度的影响效果不同;改变测温盲孔尺寸适于调节径向温度梯度;测温盲孔半径和深度的增加均可导致坩埚盖上SiC多晶生长速率提高.     

用热壁CVD法在SiC衬底上生长SiCGe合金的热场分析与设计

采用有限元法,对热壁CVD法SiCGe合金生长炉中加热组件的感应加热和温度分布进行了研究.分析了感应线圈匝数和石墨衬托的厚度对磁矢势和温度分布的影响,获取了感应线圈数越多感应生成焦耳热越大且越均匀的结论,得出了随石墨厚度的增加升温速率而增加,相反轴向温度均匀性而变差的设计准则.模拟结果表明选取16匝线圈和10mm左右的石墨壁厚为优化的设计参数.     

两种非晶碳化硅薄膜发光二极管

利用硅烷与甲烷的混合气在射频电场下的等离子体反应,淀积不同导电类型的非晶碳化硅薄膜,制成了p-i-n结注入型和均匀材料的碰撞电离型两种大面积发光二极管。本文报导这两种非晶发光器件的结构设计及光谱特性,并对器件的发光机现进行了讨论。     

SiC1-xGex/SiC 异质结光电二极管特性的研究

使用二维器件模拟软件Medici, 对SiC_1-xGe_x/SiC异质结的光电特性进行了模拟.设计了N型重掺杂SiC层的厚度为1 μm, P型轻掺杂SiC_1-xGe_x层厚为0.4 μm, 二者之间形成突变异质结.在反向偏压3 V、光强度为 0.23 W/cm²的条件下, p-n+ SiC_0.8Ge_0.2/SiC和p-n+ SiC_0.7Ge_0.3/SiC敏感波长λ分别可以达到0.64 μm和0.7 μm, 光电流分别为7.765×10^－7 A/μm和7.438×10^－7 A/μm; 为了进一步提高SiC_1-xGe_x/SiC 异质结的光电流, 我们把p-n+两层结构改进为p-i-n三层结构.在同样的偏压、光照条件下, p-i-n SiC_0.8Ge_0.2/SiC和p-i-n SiC_0.7Ge_0.3/SiC的光电流分别达到1.6734×10－6 A/μm和1.844×10－6 A/μm.