Nanostructured BiVO4 Derived from Bi-MOF for Enhanced Visible-light Photodegradation

BiVO4,a promising visible-light responding photocatalyst,has aroused extensive research interest because of inexpensiveness and excellent chemical stability.However,its main drawback is the poor photoinduced charge-transfer dynamics.Building nanostructures is an effective way to tackle this problem.Herein,we put forward a new method to prepare nanostructured BiVO4 from Bi-based metal-organic frameworks[Bi-MOF(CAU-17)]precursor.The as-prepared material has a rod-like morphology inherited from the Bi-MOF sacrificial template and consists of small nanoparticle as building blocks.Compared with its counterparts prepared by conventional methods,MOF-derived nanostructured BiVO4 shows better light absorption ability,narrower bandgap,and improved electrical conductivity as well as reduced recombination.Consequently,BiVO4 nanostructure demonstrates high photocatalytic activity under visible light towards the degradation of methylene blue.Methylene blue can be degraded up to 90%within 30 min with a reaction rate constant of 0.058 min-1.Moreover,the cycling stability of the catalyst is excellent to withstand unchanged degradation efficiency for at least 5 cycles.     

La单掺4H-SiC电子结构和光学性质的第一性原理研究

采用基于密度泛函理论的第一性原理计算方法，对未掺杂及La掺杂4H-SiC的电子结构和光学性质进行理论计算。计算结果表明，未掺杂4C-SiC其禁带宽度为2.257 eV。La掺杂后带隙宽度下降为1.1143eV，导带最低点为G点，价带最高点为F点，是P型间接半导体。掺杂La原子在价带的低能区间贡献比较大，而对价带的高能区和导带的贡献比较小。未掺杂4H-SiC在光子能量为6.25 eV时，出现一个介电峰，这是由于价带电子向导带电子跃迁产生。而La掺杂后，出现3个介电峰，分别对应的光子能量为0.47eV、2.67eV、6.21eV，前两个介电峰是由于价带电子向杂质能级跃迁产生，第三个介电峰是由于价带电子向导带电子跃迁产生。La掺杂后4H-SiC变成负介电半导体材料。未掺杂4h-SiC的静态介电常数为2.01，La掺杂的静态常数为12.01。     

改变激发环境调控Ho3+离子的上转换发光特性

稀土掺杂上转换发光材料的发光特性不仅依赖于基质材料本身,而且与其激发条件密切相关.本文主要是以Ho^3+离子为研究对象,在NaYF4和LiYF4这两种不同的基质中,研究其在不同激发条件下的上转换发光特性.通过共聚焦显微光谱测试系统,对比Ho^3+离子在NaYF4和LiYF4微米晶体中的发光特性.实验结果发现:Ho^3+离子在这两种不同基质中均展现出较强的荧光发射.然而,当激发功率增加时,在单颗粒个LiYF4微米晶体中,当激发功率增加时,Ho^3+离子则发射出较强绿光及微弱的红光,红绿比变化并不明显,其蓝光发射强度也相对较弱.当激发这两种微米粉末晶体时,结果发现:Ho^3+离子均发射较强的绿光发射并伴有微弱红光发射,两种晶体中的发射特性极其相似.由此可见,在常规测试条件下,一些特殊发光现象是很难被观测到的.同时,通过对其光谱特性的分析,对Ho^3+离子的发光机理进行了研究.     

Thermal stress reduction of GaAs epitaxial growth on V-groove patterned Si substrates

We investigate the thermal stresses for GaAs layers grown on V-groove patterned Si substrates by the finite-element method. The results show that the thermal stress distribution near the interface in a patterned substrate is nonuniform,which is far different from that in a planar substrate. Comparing with the planar substrate, the thermal stress is significantly reduced for the Ga As layer on the patterned substrate. The effects of the width of the V-groove, the thickness, and the width of the SiO₂ mask on the thermal stress are studied. It is found that the SiO₂ mask and V-groove play a crucial role in the stress of the Ga As layer on Si substrate. The results indicate that when the width of V-groove is 50 nm, the width and the thickness of the SiO₂ mask are both 100 nm, the Ga As layer is subjected to the minimum stress. Furthermore,Comparing with the planar substrate, the average stress of the Ga As epitaxial layer in the growth window region of the patterned substrate is reduced by 90%. These findings are useful in the optimal designing of growing high-quality Ga As films on patterned Si substrates.     

煤直接液化油中混合酚的分离研究

利用分子筛择形特点，对煤直接液化油中的混合酚实施高效分离。本研究选取间甲酚和对甲酚作为分离煤直接液化油馏分段混合酚的模型化合物，采用化学液相沉积法对HZSM-5吸附剂的孔口结构进行改变，分析分子筛硅铝比及颗粒粒径对模型化合物间甲酚和对甲酚吸附分离性能的影响，以获得高性能固相吸附剂，并将其应用于180-190℃馏分段混合酚分离。结果表明，当分子筛硅铝比为25、粒径为3-5 μm时，分子筛的孔口结构调节效果最优；当正硅酸乙酯的最小用量为0.2 mL/g时，固相吸附剂的吸附量为0.03 g/g，对甲酚选择性高于95%。由于外表面沉积物对吸附剂的孔口结构变化，导致对甲酚选择性的提高。进一步采用HZSM-5（1）吸附剂对真实煤直接液化油混合酚的分离中发现，苯酚和对甲酚的选择性均达到100%。     

平面硅异质结太阳电池的光吸收增强的研究

钙钛矿/硅叠层太阳电池可以充分利用太阳光谱,提高光电转换效率.平面硅异质结太阳电池可以作为叠层电池的底电池,其性能直接影响叠层电池的性能表现.采用传统反应热蒸发技术,在低温(170 ℃)条件下制备了掺锡氧化铟薄膜,并在170 ℃的氧气氛围下后退火处理,对ITO薄膜的特性进行了详细的表征和分析.结果表明:后退火工艺改善了ITO的结晶特性,使得材料的光学特性和电学特性得到明显提高,将其应用于平面硅异质结太阳电池,短路电流密度得到极大提高,尤其红外光响应改善明显.引入MgF2薄膜作为减反射层,进一步增强了电池的光响应,转换效率达到19.04;.     

高压辅助法制备红外非线性AgGaGe5Se12、AgGaGeS4晶体

AgGaGe5 Se12、AgGaGeS4非线性晶体在中远红外激光具有良好的应用前景.合成高纯多晶是制备可器件化单晶元件的关键.但S、Se易挥发、高温下饱和蒸气压高,易导致石英坩埚的爆炸,组分偏离化学计量比.为此,本文采用一种新型的高压辅助法合成出大尺寸高纯的多晶原料,解决了石英坩埚爆炸和组份偏离问题,并在此基础上进行了单晶的生长过程.多晶X射线粉末衍射测试结果与模拟图谱或者标准PDF卡片一致;X射线荧光光谱分析得到各元素百分含量非常接近化学计量比,AgGaGe5 Se12中Ag、Ga、Ge、Se各占7.86;、5.08;、23.80;、63.26;,AgGaGeS4中Ag、Ga、Ge、S各占28.22;、18.24;、19.52;、34.02;;单晶透过率测试得到AgGaGe5 Se12、AgGaGeS4透过率分别为60;、70;,证明此方法制备的AgGaGe5 Se12、AgGaGeS4晶体性能优良,展现了该方法在多晶合成的应用潜力.     

减反膜对单晶硅太阳能电池性能的影响分析

在太阳能电池效率的评价中，电池材料、掺杂浓度、扩散长度等都是比较重要的参数，合理地改变相关参数可以优化太阳能电池的性能，提高电池效率。此外，在太阳能电池表面镀一层具有减反作用的光学薄膜（简称减反膜）也是提高电池效率的重要手段。以提高电池效率为目标，对单晶硅太阳能电池的掺杂浓度和扩散长度等微观参数进行计算优化，分析了掺杂浓度和扩散长度变化对电池效率的影响。并在此基础上分析了不同类型的减反膜对于电池效率的影响，给出了最佳减反膜材料及其膜系厚度，并且结合镀膜后电池量子效率的变化验证了其准确性。结果表明，在优化电池掺杂浓度和扩散长度的基础上，选择合适的减反膜，电池效率最高可达20.35%，相比于优化前提高了8.25%。     

H2SO4-H2O中硝酸铜对脱硫石膏晶须生长的影响

以处理后的脱硫石膏为原料,在H₂SO₄-H₂O体系中以Cu(NO₃)₂为晶形控制剂采用水热法制备脱硫石膏晶须,探讨了Cu(NO₃)₂对脱硫石膏晶须生长的影响机理。结果表明:Cu(NO₃)₂对脱硫石膏有明显促溶作用,其中Cu²⁺可减小溶液中各离子的活度系数,使溶液中的Ca²⁺浓度增大。NO^-₃通过静电作用在Ca²⁺周围聚集并对SO^2-₄产生屏蔽作用,导致脱硫石膏继续溶解并使Ca²⁺和SO^2-₄的浓度处于相对稳定状态,有利于半水脱硫石膏晶体的形核与生长。此外,Cu²⁺还可在晶须的生长过程中选择性吸附在晶须表面,生成CuSO₄,促进了脱硫石膏的结晶生长,最终在Cu(NO₃)₂用量为2.0%(质量分数)时制备的脱硫石膏晶须长径比约为73。