Zr对CuO/ZnO/Al_2O_3前驱体物相、催化剂结构及其合成甲醇性能的影响

采用并流共沉淀法,在CuO/ZnO/Al2O3三元催化剂中加入第四组分Zr,考察了沉淀温度对四元催化剂的前驱体物相组成及浆态床合成甲醇催化活性的影响。通过XRD、DTG、TPR、FTIR、CO-TPD、XPS、HR-TEM等对所制备催化剂及其前驱体的微观结构进行了表征。研究表明:Zr促进了绿铜锌矿(Cu,Zn)5(CO3)2(OH)6物相的生成,使催化剂前驱体中绿铜锌矿含量增加,焙烧后的催化剂铜锌协同作用增强,CuO分散度提高,CuO晶粒平均直径只有4.18nm,同时还原温度显著降低为150℃,CO吸附能力增强,结果显著提高了浆态床合成甲醇催化活性和稳定性。与CuO/ZnO/Al2O3三元催化剂相比,80℃沉淀制备的含4%Zr的CuO/ZnO/Al2O3/ZrO2四元催化剂的甲醇时空收率提高了8.67%,失活率降低了65.12%。     

溶剂极性对微波辐射老化制备前驱体及CuO/ZnO/Al2O3催化剂结构的影响

在制备CuO/ZnO/Al2O3催化剂的老化过程中,采用微波辐射老化技术,着重研究了溶剂极性对前躯体物相组成,烧后CuO/ZnO/Al2O3催化剂结构及其在浆态床合成甲醇工艺中催化性能的影响。通过XRD、DTG、H2-TPR,FTIR、HR-TEM和XPS对前驱体及催化剂表征表明,沉淀母液在微波辐射条件下进行老化,溶剂的极性对前躯体物相组成及催化剂结构影响显著。随着溶剂极性的增大,Zn2+/Cu2+取代Cu2(CO3)(OH)2/Zn5(CO3)2(OH)6中Cu2+/Zn2+的取代反应增强,使得前躯体中(Cu,Zn)5(CO3)2(OH)6和(Cu,Zn)2(CO3)(OH)2物相的含量增多,结晶度提高,导致烧后CuO/ZnO/Al2O3催化剂中CuO-ZnO协同作用增强,且CuO晶粒减小,表面Cu含量增加,催化剂活性和稳定性提高。水溶剂的极性最大,制备的催化剂活性和稳定性最好,甲醇的时空收率(STY)和平均失活率分别为320 mg.g-1.h-1和0.11%.d-1。     

老化时间对Cu/ZnO/Al2O3合成甲醇催化剂性能的影响

并流共沉淀法制备了CuO/ZnO/Al2O3催化剂前驱体及催化剂，用XRD、TG－DTG、TPR、N2吸附及加压微反活性评价技术，考察了母料老化时间对催化剂前驱体物相组成及焙烧后物料中CuO－ZnO间的作用和物化性能的影响，提出了催化剂母料物相随老化时间的变化。研究表明，老化时间对催化剂活性的影响是通过改变催化剂比表面积及形成CuO ZnO固溶体的结果。     

微波辐射对浆态床合成甲醇CuO/ZnO/Al2O3催化剂前驱体晶相转变的影响

在微波辐射条件下,对CuO/ZnO/Al2O3催化剂的沉淀母液进行老化,通过XRD、TG、H2-TPR,FTIR、HR-TEM和XPS对前驱体及催化剂微观结构的进行表征,探讨了CuO/ZnO/Al2O3催化剂前驱体晶相转变过程中微波辐射的作用。结果表明,微波辐射有利于Cu2+取代Zn5(CO3)2(OH)6中Zn2+的同晶取代反应。微波辐射的老化过程中,首先发生Cu2+取代Zn5(CO3)2(OH)6中Zn2+生成(Cu,Zn)5(CO3)2(OH)6的同晶取代反应,并于1.0 h内基本完成;随着老化时间继续延长,主要进行Zn2+取代Cu2(CO3)(OH)2中Cu2+生成(Cu,Zn)2(CO3)(OH)2的同晶取代反应,同时(Cu,Zn)5(CO3)2(OH)6进一步结晶。与常规老化1 h制备的前驱体相比,微波辐射老化1.0 h制备的前驱体含有较多的(Cu,Zn)5(CO3)2(OH)6物相,有助于增强焙烧后CuO/ZnO/Al2O3催化剂中CuO-ZnO协同作用,提高表面铜含量,进而提高CuO/ZnO/Al2O3催化剂在浆态床合成甲醇的催化活性和稳定性,在400 h浆态床合成甲醇评价期间,甲醇时空收率最大达318.9 g.kg-1.h-1,失活率仅为0.11%.d-1。     

浆态床合成甲醇CuO/ZnO/Al2O3催化剂的表面性质

采用并流共沉淀法制备了不同Cu/Zn摩尔比的CuO/ZnO/Al2O3催化剂,考察了其浆态床CO加氢合成甲醇的催化性能.通过N2吸附-脱附、X射线衍射、程序升温还原及X射线光电子能谱等方法对催化剂表面性质进行了表征.结果表明,催化剂具有体相和表面高分散两种不同还原性质的CuO,表面CuO的含量及其与ZnO的相互作用使催化剂活性增大.当催化剂中Cu/Zn≤1时,随着铜含量的增加,表面高分散的CuO量增加,CuO和ZnO之间相互作用增强,催化剂的活性也随之增大;当催化剂Cu/Zn>1时,增加的铜量主要体现为体相CuO含量的增加,且ZnO结晶度提高,CuO和ZnO之间的相互作用减弱,催化剂的活性随铜含量增大而减小.     

Fe2O3含量对Cu-Fe/铝土矿水煤气变换催化剂结构和性能的影响

利用具有高比表面积和介孔结构的改性铝土矿为载体,采用并流共沉淀法制备不同Fe2O3含量的Cu-Fe/铝土矿催化剂。以水煤气变换反应为探针反应,考察了催化剂性能。利用X射线荧光元素分析(XRF)、X射线粉末衍射(XRD)、H2程序升温还原(H2-TPR)、CO程序升温脱附(CO-TPD)和X射线光电子能谱(XPS)等对催化剂进行了表征。结果表明:负载的Fe2O3能显著提高CuO/改性铝土矿催化剂的水煤气变换活性特别是热稳定性能,且随负载的Fe2O3含量增加而提高,当负载量为20%时达到最佳。其原因是负载的Fe2O3和CuO之间发生了相互作用,形成了类似于CuFe2O4复合氧化物,且随负载的Fe2O3含量的增加而增强,这种相互作用同时促进了CuO和Fe2O3的还原,抑制了CuO的烧结,进而提高了催化剂的性能。     

沉淀剂对悬浮共沉淀法制备二甲醚催化剂的影响

以无水乙醇为溶剂,将Cu、Zn和Al的硝酸盐并流共沉淀在HZSM-5分子筛的悬浮溶液中,一步合成CuO-ZnO-Al2O3/HZSM-5双功能催化剂.研究了沉淀剂的种类、加入顺序和加入量对催化剂活性的影响.结果表明,以适量的草酸作沉淀剂,采用悬浮液并流共沉淀法制备的双功能催化剂,对CO2加氢直接合成二甲醚有较高的催化性能:在固定床反应器中,温度为270℃,压力为3.0 MPa,空速为4 800 h-1的反应条件下,CO2的单程转化率达到28.7%,二甲醚的选择性达到53.2%.BET、XRD、TPR、TPD和N2O滴定等对催化剂结构表征结果表明,双功能复合催化剂CuO-ZnO-Al2O3/HZSM-5的结构影响CO2加氢合成二甲醚的催化性能.     

合成ZnO纳米阵列及刺突状CuO/ZnO异质结

采用低温水热法在掺氟SnO₂ (FTO)导电玻璃表面制备ZnO纳米阵列, 研究了前驱体溶液浓度摩尔配比对ZnO纳米阵列形貌、光学性能及其生长机理的影响. 研究发现, 随着前驱体溶液浓度摩尔配比的增加, ZnO纳米阵列形貌及光学性能也随之变化. ZnO纳米阵列高度逐渐降低, ZnO纳米阵列直径和光学带隙值大体上出现先增大后降低的趋势. 而当前驱体溶液(Zn(NO₃)₂:环六亚甲基四胺(HMT, C₆H₁₂N₄))浓度摩尔配比为5:5时, 其光学禁带值(3.2 eV)接近于理论值. 结果显示制备ZnO纳米阵列的最优浓度摩尔配比为5:5. 随后选用最优浓度摩尔配比下制备的ZnO纳米阵列为基底, 通过一种两步溶液法成功在其表面制备刺突状CuO/ZnO异质结.从场发射扫描电镜(FE-SEM)结果中可以清楚看见, 大量的CuO纳米粒子沉积在ZnO纳米阵列表面形成刺突状异质结结构.研究发现该CuO/ZnO纳米异质结相对于纯ZnO纳米阵列在紫外光下光催化性能明显增加. 最后, 讨论了CuO/ZnO纳米异质结光催化机理.     

CuO/Mn2O3 /γ-Al2O3催化剂的制备、表征及其在CO氧化反应中的性能研究

采用浸渍法在γ-Al2O3载体上分步负载改性剂Mn2O3和活性组分CuO,制备了一系列不同配比的CuO/Mn2O3/γ-Al2O3催化剂,并运用CO+O2模型反应、XRF、XRD、H2-TPR、in-situ FTIR等手段表征了催化剂的活性和物理化学性质。活性测试结果表明,锰氧化物对γ-Al2O3载体的改性能有效地提高CuO/γ-Al2O3催化剂在CO+O2模型反应中的催化活性。XRD结果表明,锰氧化物对γ-Al2O3载体的改性可以促进氧化铜在载体表面的分散,从而提高了分散态氧化铜的含量,不过这与活性变化的趋势并不完全一致。进一步结合H2-TPR、in-situ FTIR表征结果 ,我们发现,分散态铜、锰氧化物的还原性质也是影响其催化活性的重要因素,催化剂中分散态铜、锰物种越容易被还原,其对CO+O2模型反应的催化活性就越高。     

陈化时间对CuO/ZnO/CeO2/ZrO2甲醇水蒸气重整制氢催化剂性能的影响

采用共沉淀法制备了CuO/ZnO/CeO₂/ZrO₂甲醇水蒸气重整催化剂,探讨了陈化时间对催化剂性能的影响.结果发现,延长陈化时间能增加催化剂的表面铜原子数和改善催化剂的还原性能,但与此同时也降低了催化剂的储放氧性能.延长陈化时间,CuO/ZnO/CeO₂/ZrO₂催化剂的氢产率随表面铜原子数的增加而成线性增长.另一方面,重整尾气中的CO含量也随着储放氧能力的下降而增加.综合考虑产氢率和重整尾气中CO含量,最佳陈化时间为2h,此时,CuO/ZnO/CeO₂/ZrO₂催化剂表现出了最佳性能.     

Characterization and evaluation of Fe2O3/Al2O3 oxygen carrier prepared by sol–gel combustion synthesis

The sol-gel combustion synthesis (SGCS) for oxygen carrier (OC) to be used in chemical looping combustion (CLC) was first designed and experimented in this work, which is a new method of OC synthesis by combining sol-gel technique and solution combustion synthesis. Cheap hydrated metal nitrates and urea were adopted as precursors to prepare Fe₂O₃/Al₂O₃ OC at the molar ratio to unity (Fe1Al1), which was characterized through various means, including Fourier transforms infrared (FTIR) spectroscopy, thermogravimetric analysis (TGA), differential thermal analysis (DTA), X-ray diffractor (XRD), and N₂ isothermal adsorption/desorption method. FTIR analysis on the chemical structure of the dried gel of Fe1Al1 indicated that urea was partly hydrolyzed and the hydrated basic carbonate was formed by the combination of groups such as (Fe(_1−yAl_y)_1−xO_1−3x, CO₃²⁻ and -OH-. By analyzing the staged products during SGCS, calcination was found as a necessary step to produce Fe₂O₃/Al₂O₃ OC with separate phases of α-Fe₂O₃ and α-Al₂O₃. Through TGA-DTA, the decomposition of the dried gel was found to undergo five stages. The analysis of the evolved gases from the gel decomposition using FTIR partially confirmed the staged decomposition and assisted a better understanding of the mechanism of SGCS. XRD identification further substantiated the necessity of calcination to synthesize Fe₂O₃/Al₂O₃ OC with separate phases of α-Fe₂O₃ and α-Al₂O₃, though it was not necessary for the synthesis of single phase α-Fe₂O₃ and α-Al₂O₃. Structural characterization performed on N₂ adsorption analyzer displayed that the pore shape of Fe1Al1 particles was heterogeneous. Finally, H₂ temperature-programmed reduction (TPR) of Fe1Al1 products in TGA indicated that the reduction reaction of Fe1Al1 OC after calcination was a single step reaction from α-Fe₂O₃ to Fe, and calcination benefited to improve the transfer rate of the lattice oxygen from the OC to fuel H₂. Furthermore, four times of reduction and oxidization (redox) reaction by alternating with H₂ and air demonstrated the synthesized OC had good reactivity and sintering-resistance, much suitable to be used in the realistic CLC. Overall, the SGCS method was found superior to other existent methods to prepare Fe₂O₃/Al₂O₃ OC for CLC application.     

表面助剂改性对Cu/ZnO/Al2O3甲醇合成催化剂性能的影响

采用共沉淀-后浸渍方法制备了表面助剂改性的Cu/ZnO/Al₂O₃ (CZA)甲醇合成催化剂, 在固定床反应器上以合成气为原料分别考察了三种助剂(Zr、Ba和Mn)对CZA催化剂性能的影响; 以Zr为助剂时反应温度的影响; 并进行了催化稳定性试验. 利用粉末X射线衍射(XRD)、低温氮气吸脱附(N₂-sorption)、氧化亚氮(N₂O)反应吸附技术、X射线光电子能谱(XPS)、氢气程序升温吸脱附(H₂-TPD)、扫描电子显微镜(SEM)和高分辨透射电子显微镜(HR-TEM)技术对催化剂进行了表征.结果显示: 以Zr或Ba作为助剂能够明显提高CZA催化剂耐热前后的甲醇时空收率(STY); Mn的引入降低了CZA催化剂的耐热前活性; Zr的引入降低了CZA催化剂最高活性温度点, 增强了CZA催化剂的催化稳定性; 还原态CZA催化剂表面Cu⁰和ZnO都能吸附活化氢气, Cu⁰与ZnO的强相互作用有利于提高催化剂的性能, 耐热后催化剂性能的降低归因于Cu晶粒的长大. 在实验和表征结果基础上,提出了CZA催化剂上合成气制甲醇的“双向同步催化反应历程”.     

Straightforward Synthesis of Mn3O4/ZnO/Eu2O3-Based Ternary Heterostructure Nano-Photocatalyst and Its Application for the Photodegradation of Methyl Orange and Methylene Blue Dyes

Zinc oxide-ternary heterostructure Mn₃O₄/ZnO/Eu₂O₃ nanocomposites were successfully prepared via waste curd as fuel by a facile one-pot combustion procedure. The fabricated heterostructures were characterized utilizing XRD, UV–Visible, FT-IR, FE-SEM, HRTEM and EDX analysis. The photocatalytic degradation efficacy of the synthesized ternary nanocomposite was evaluated utilizing model organic pollutants of methylene blue (MB) and methyl orange (MO) in water as examples of cationic dyes and anionic dyes, respectively, under natural solar irradiation. The effect of various experimental factors, viz. the effect of a light source, catalyst dosage, irradiation time, pH of dye solution and dye concentration on the photodegradation activity, was systematically studied. The ternary Mn₃O₄/ZnO/Eu₂O₃ photocatalyst exhibited excellent MB and MO degradation activity of 98% and 96%, respectively, at 150 min under natural sunlight irradiation. Experiments further conclude that the fabricated nanocomposite exhibits pH-dependent photocatalytic efficacy, and for best results, concentrations of dye and catalysts have to be maintained in a specific range. The prepared photocatalysts are exemplary and could be employed for wastewater handling and several ecological applications.     

应用原位漫反射红外-质谱技术研究CuO/Al2O3催化剂表面酸性及其反应性能

应用原位漫反射红外-质谱联用、程序升温和暂态响应技术研究了CuO/Al₂O₃催化剂表面酸性及其反应性能. 实验结果表明, CuO/Al₂O₃催化剂表面呈Lewis酸性, 硫化不仅可增强CuO/Al₂O₃催化剂的Lewis酸性, 而且可产生新的Brønsted酸性位; 吸附于Lewis酸性位的NH₃具有选择性催化还原(SCR)活性. 而在硫化样Cu8(400S)中Lewis和Brønsted酸性位同时存在的情况下, 吸附于Lewis和Brønsted酸性位的氨均具有SCR活性, 且后者较前者弱; CuO/Al₂O₃催化剂上的SCR反应遵循Eley-Rideal机理, 即SCR反应发生于吸附态NH₃与气相NO之间.     

Ce0.5Zr0.5O2修饰的Ni/SiC、Fe/SiC和Co/SiC催化燃烧甲烷性能

以铈锆固溶体（Ce_0.5Zr_0.5O₂）修饰的高比表面积SiC为载体,采用两步浸渍法制备了Ni、Fe和Co基催化剂,研究了其在煤层气催化燃烧脱氧中的催化活性和稳定性. 利用X射线衍射（XRD）、X射线光电子能谱（XPS）、电感耦合等离子体质谱（ICP-MS）、高分辨透射电子显微镜（HRTEM）、比表面积（BET）、热重分析（TGA）和H₂程序升温还原（H₂-TPR）对催化剂进行了表征. 分析结果表明,Ni、Fe和Co部分进入Ce_0.5Zr_0.5O₂固溶体晶格内部,导致催化剂体相形成更多的缺陷;同时Ce_0.5Zr_0.5O₂固溶体有助于加速金属氧化物和金属之间氧化还原过程的进行,促进了氧吸附、传输和对甲烷的活化. 另外,SiC和Ce_0.5Zr_0.5O₂固熔体良好的抗积碳性能,有效避免了催化剂在富甲烷反应气氛中因积碳而失活,从而使三种催化剂均具有优良的催化燃烧脱氧活性和稳定性. 其中,Co/Ce_0.5Zr_0.5O₂/SiC活性最高,可在320 ℃活化催化甲烷,并在410 ℃实现完全脱氧.     

氧化锌表面包覆Sn6O4(OH)4的制备及其在锌镍电池中的应用

采用水热-共沉淀法在氧化锌表面包覆锡化合物,利用扫描电子显微镜（SEM）、X射线衍射（XRD）和能谱分析对制备的包覆ZnO材料进行表征。结果表明：XRD表明附着在氧化锌表面的是Sn₆O₄（OH）₄,且结晶度较好;SEM测试显示在pH=12条件下,Sn₆O₄（OH）₄能够很好地附着在氧化锌颗粒表面;能谱分析显示组成物中的元素包含Zn、Sn、O三种元素。利用循环伏安曲线、电化学阻抗谱（EIS）、倍率充放电技术对包覆ZnO材料进行了电化学性能的测试,结果表明：包覆Sn₆O₄（OH）₄的ZnO可以提高锌负极的耐蚀性能,增大电荷转移电阻（R_ct）;锌电极覆Sn₆O₄（OH）₄量为3%时充放电效率最佳,在0.2C充放循环40次后充放电循环保持率仍有70%。     

氧化锌表面包覆Sn_6O_4(OH)_4的制备及其在锌镍电池中的应用

采用水热-共沉淀法在氧化锌表面包覆锡化合物,利用扫描电子显微镜(SEM)、X射线衍射(XRD)和能谱分析(EDS)对制备的包覆ZnO材料进行表征。结果表明:XRD表明附着在氧化锌表面的是Sn_6O_4(OH)_4,且结晶度较好;SEM测试显示在p H=12条件下,Sn_6O_4(OH)_4能够很好地附着在氧化锌颗粒表面;EDS显示组成物中的元素包含Zn、Sn、O三种元素。利用循环伏安曲线(CV)、电化学阻抗谱(EIS)、倍率充放电技术对包覆ZnO材料进行了电化学性能的测试,结果表明:包覆Sn_6O_4(OH)_4的ZnO可以提高锌负极的耐蚀性能,增大电荷转移电阻(Rct);锌电极覆Sn_6O_4(OH)_4量为3%时充放电效率最佳,在0.2C充放循环40次后充放电循环保持率仍有70%。     

微波加热液相均匀沉淀法制备纳米Sb2O3阻燃剂(英)

Antimonyoxide(Sb2O3)isanimportantadditiveflameretardant.Itisextensivelyusedinflameretar鄄danttreatmentofpolyolefine,polyvinylchloride,polyesterandtextiles.TheefficiencyofhalogenatedflameretardantcanbeenhancedbycooperatingwithSb2O3.ThesizeofSb2O3hasgreatef…