分子筛的酸处理对Mo/HZSM-5催化甲烷无氧芳构化反应性能的影响

 采用HNO3溶液对HZSM-5分子筛进行预处理,并以处理后的分子筛为载体制备了Mo/HZSM-5 催化剂. 结果表明,改性的Mo/HZSM-5催化剂在甲烷无氧脱氢芳构化反应中表现出很好的稳定性,显著地抑制了积炭物种在催化剂表面的形成. SEM,XRD和1H MAS NMR等表征结果表明,酸处理在一定程度上降低了HZSM-5分子筛的结晶度,使部分Al物种脱离骨架结构,迁移到骨架外形成新的表面Al羟基,从而使HZSM-5分子筛上B酸中心的数目明显减少. 未经改性的Mo/HZSM-5催化剂表面,平均每个晶胞中有1.12个B酸位,而改性的Mo/HZSM-5催化剂表面,平均每个晶胞中仅有0.88个B酸位. 这表明过多的酸性位存留在催化剂上会引起积炭的生成,降低催化剂的稳定性.     

高温水蒸气处理对ZnHZSM-5活性中心的影响

应用X-射线衍射、能谱表面分析和吡啶吸附红外光谱研究了高温水蒸气处理对HZSM-5和ZnHZSM-5催化剂的影响，并以丙烷芳构化作为探针反应考查了催化活性中心的变化．高温水蒸气处理对分子筛的结晶度影响不大，但水蒸气处理使得分子筛骨架铝脱出，脱出的铝在表面富集，分子筛锌交换位的骨架铝脱出较难，脱铝导致分子筛的酸性减弱．高温水蒸气处理后的HZSM-5和ZnHZSM-5催化剂的丙烷反应活性都降低，在ZnHZSM－5上丙烯的选择性增加，反映了具有脱氢活性的锌的强L酸中心数目相对B酸中心减少较少，进一步说明了处于离子交换位的锌离子对骨架铝有保护作用     

A New Way to Obtain Mo/HZSM-5 Catalyst with High Activity and Selectivity for Methane Dehydro-aromatization 一种制备高活性和高稳定性甲烷无氧芳构化Mo/HZSM-5的新方法

 采用气相化学沉积法对HZSM-5分子筛的外表面进行选择性修饰,然后将它作为载体制备Mo/HZSM-5 催化剂,并应用于甲烷无氧脱氢芳构化反应. 改性的催化剂比未改性的催化剂表现出更好的甲烷转化活性、芳烃选择性和稳定性,明显地抑制了积碳的生成. 利用核磁氢谱对催化剂进行了表征. 在未经改性的Mo/HZSM-5催化剂表面,平均每个晶胞中含有1.12个B酸中心, 而在改性后的催化剂表面,平均每个晶胞中只有0.61个B酸位. 说明在甲烷无氧芳构化反应中,少量的B酸中心即可达到反应要求,过多的酸性位只会导致更多积碳物种的生成,从而加快催化剂失活速度,降低其稳定性.     

硅烷化处理对Mo/HZSM-5催化剂上甲烷脱氢芳构化活性的影响

 结合催化剂的活性评价及固体高分辨核磁共振谱、X射线光电子能谱和X射线荧光光谱和热重等技术,考察了硅烷化处理对Mo/HZSM-5催化剂上甲烷脱氢芳构化活性的影响. 结果表明,采用大分子有机硅烷对HZSM-5分子筛进行硅烷化处理,除去了分子筛外表面的酸性位,并使分子筛本身发生了脱铝. 硅烷化处理使Mo/HZSM-5催化剂在进行甲烷脱氢芳构化反应时催化剂上总的积碳量明显减少,从而提高了催化剂的活性.     

硅烷化处理对Moo/HZSM-5催化剂上甲烷脱氢芳构化活性的影响

结合催化剂的活性评价及固体高分辨核磁共振谱、X射线光电子能谱和X射线荧光光谱和热重等技术,考察了硅烷化处理对Mo/HZSM-5催化剂上甲烷脱氢芳构化活性的影响.结果表明,采用大分子有机硅烷对HZSM-5分子筛进行硅烷化处理,除去了分子筛外表面的酸性位,并使分子筛本身发生了脱铝.硅烷化处理使Mo/HZSM-5催化剂在进行甲烷脱氢芳构化反应时催化剂上总的积碳量明显减少,从而提高了催化剂的活性.     

Mo/HZSM-5催化剂载体对甲烷无氧芳构化反应的影响

着重研究了挤条成型的纳米Mo/HZSM-5催化剂在甲烷无氧芳构化反应中的催化性能.结果表明,Al2O3载体的加入减少了催化剂的B酸量,对甲烷无氧芳构化反应不利,导致甲烷转化率降低,并且催化剂积碳严重.通过适量添加SiO2载体,减少Al2O3载体的量,可以使催化剂的B酸量提高,从而可提高甲烷转化率,并且可降低催化剂的积碳量.     

HZSM-5沸石中Lewis酸与Brönsted酸协同作用下的甲基环己烷开环反应

由于水蒸气处理HZSM-5生成的骨架外铝在分子筛中体现Lewis酸性, 分子筛中骨架外铝物种的可移动性导致Lewis酸与分子筛本身的Brönsted酸在空间上具有临近性. 当甲基环己烷分子在HZSM-5的笼中转化时, Lewis酸与Brönsted酸的协同作用加快了甲基环己烷分子的转化速率, 且骨架外铝物种浓度越高, 这种协同效应越明显. 而产物的选择性只与催化剂的孔道结构有关, 与水蒸气处理所导致的酸性质的变化无关.     

碳四烃在改性HZSM-5分子筛上芳构化研究

研究了炼厂混合C_4烃在Zn、Ga、Cr、La改性的HZSM-5分子筛催化剂上的芳构化反应,采用TPD和IR测定了催化剂的表面酸性质。结果表明,用Zn(3%)和Zn(2%)Ga(1%)改性的HZSM-5分子筛具有较好的芳构化性能;各改性HZSM-5分子筛催化剂芳构化性能变化与表面酸性有关,总酸量下降,芳构化活性下降,强B酸中心减少,深度裂解反应减少;Zn的单组分和双组分改性的HZSM-5分子筛催化剂芳构化活性的增高与表面强L酸浓度增加和吡啶吸附IR谱中的1615cm~(-1)吸收峰出现有关。     

甲烷无氧芳构化反应催化剂Mo/HZSM-5的H2-TPR研究

 采用H2-TPR技术研究了不同方法制备的Mo/HZSM-5催化剂,并借助 1H MAS NMR等表征手段对Mo/HZSM-5催化剂还原过程中可能出现的6个TPR谱峰进行了详细归属,首次指认了分布于分子筛孔道内并与B酸性位相互作用的Mo物种的还原峰. 此外,还考察了各种Mo基催化剂在甲烷无氧芳构化反应中的催化性能. 结果表明,与B酸中心相互作用的Mo物种比其他形式的Mo物种具有更好的活性和稳定性.     

预处理条件对Mo/HZSM-5和Mo-Zn/HZSM-5甲烷芳构化性能的影响

甲烷无氧芳构化 ,具有选择性高、技术简单及产物易分离等特点 ,已引起人们的广泛关注 [1,2 ] .Mo/HZSM- 5是芳构化的良好催化剂 ,为了探讨预处理条件对反应的影响 ,我们对不同预处理条件下的 Mo/HZSM- 5及 Zn改性的 Mo/HZSM- 5催化剂上的甲烷无氧芳构化反应进行了研究 ,并以热重法对催化剂的稳定性进行了表征 .1实验部分1 .1原料和试剂钼酸铵 ( A.R.级 ) ,乙酸锌 ( A.R.级 ) ,铵型ZSM- 5分子筛 (硅铝比为 5 0～ 70 ) .1 .2催化剂制备铵型 ZSM- 5分子筛于 81 3K、空气气氛下焙烧3h,即成 HZSM- 5分子筛 .以一定浓度的钼酸铵溶液…     

Propane Aromatization over Mo／HZSM—5 Catalysts

Impregnation,mechanical mixing and hydrothermal treatment methods were used to introduce molybdenum species into the HZSM-5 zeolite ,the structure and surface acidity of the catalysts were studied by means of XRD,FT-IR ,NH3-TPD,TPR and XPS,The effects of Mo content and reaction time on stream on the aromatization of propane were investigated,It was found that the performance of the Mo/HZSM-5 catalst prepared by the hydrothermal treatment method was much better than that of the other two catalysts,For example ,under the reaction conditions of 823 K and 600h^-1, propance conversion and aromatics selectivity over the catalyst prepared by hydrothermal pretreatment could reach 89.17% and 78.56%,respectively,XRD and XPS results showed that the Mo species in the catalysts prepared by hydrothermal treatment were highly dispersed on the surface of the HZSM-5,and lartger amounts of them could penetrate into the HZSM-5 channel ,as compared with the other two kinds of catalysts,These factors may be responsibled for their high activities for propane aromatization,IR and NH3-TPD studies indicated that the number of Broensted acid centers decreased and the Lewis acid centers increased after Mo was introduced into the HZSM-5 zeolite.     

Propane Aromatization over Mo/HZSM-5 Catalysts

Impregnation, mechanical mixing and hydrothermal treatment methods were used to introduce molybdenum species into the HZSM-5 zeolite. The structure and surface acidity of the catalysts were studied by means of XRD, FT-IR, NH3-TPD, TPR and XPS. The effects of Mo content and reaction time on stream on the aromatization of propane were investigated. It was found that the performance of the Mo/HZSM-5 catalyst prepared by the hydrothermal treatment method was much better than that of the other two catalysts. For example, under the reaction conditions of 823 K and 600 h-1, propane conversion and aromatics selectivity over the catalyst prepared by hydrothermal pretreatment could reach 89.17% and 78.56%, respectively. XRD and XPS results showed that the Mo species in the catalysts prepared by hydrothermal treatment were highly dispersed on the surface of the HZSM-5, and larger amounts of them could penetrate into the HZSM-5 channel, as compared with the other two kinds of catalysts. These factors may be responsi     

Properties and Characterization of Modified HZSM—5 Zeolites

Physicochemical and catalytic properties of phosphorus and boron modified HZSM-5 zeolites treated with 100% steam at 673K were investigated.The acidity and distribution of acidic sites were studied by infrared spectroscopy using pyridine as probe molecule and temperature programmed desortion (TPD) of ammonia.The structure of the samples was characterized by XRD,and the textural properties of the catalysts were determined by nitrogen isothermal adsorption-desorption measurements and scanning electron microscopy(SEM).The XRD results show that the modified samples have no novel crystalline phase,indicating a high dispersion of phosphorus and boron species.After treatment,the microporous volume and surface area of the samples markedly decrease,implying the bolockage of the channel.The nitrogen adsorption-desorption measurements suggest that the isothermal type of all samples is a combination of isothermal type Ⅰ and Ⅳ，and all hysteresis loops resemble the H4-type in the IUPAC classification.The total acidity of the modified samples,determined by pyrldine adsorption IR and TPD of ammonia,decreases in contrast to that of the parent HZSM-5.The conversion of n-heptane over P and B steammodified HZSM-5 is higher than that of P and B-modified HZSM-5 zeolites but lower than that of the parent HZSM-5.     

酸碱改性HZSM-5分子筛上甲醇制取均四甲苯的研究

对HZSM-5分子筛进行"酸碱两步改性",制备得到了H(0.2)-Na-ZSM-5、H(0.5)-Na-ZSM-5、H(0.2)-K-ZSM-5和H(0.5)-K-ZSM-5四种催化剂。通过XRD、NH₃-TPD、ICP、FT-IR与Py-IR方法对催化剂进行表征,并在连续流动固定床反应装置上对催化剂进行评价。实验结果表明,H(0.2)-K-ZSM-5催化剂由于其孔径变大、弱的B酸量增多,从而提高了均四甲苯的选择性。     

水对改性HZSM-5催化联苯甲基化反应的影响

以纳米(n(SiO₂)/n(Al₂O₃)=26) 分子筛为母体, 采用水热处理、水热处理结合酸洗等方法对其进行改性, 并以联苯(BP)与甲醇的烷基化为探针反应, 在固定床反应器上考察了反应体系中生成的水及通入的水对改性HZSM-5催化性能的影响, 并通过吡啶吸附傅里叶变换红外(FTIR)光谱、热重(TG)分析对改性前后样品的酸性及反应后样品积炭量进行了表征. 结果表明, 水热处理及水热处理结合酸洗都提高了催化剂的稳定性,酸洗后效果更好. 在改性的HZSM-5 催化联苯甲基化反应体系中, 不通水的条件下, 联苯的转化率随时间呈抛物线变化; 通水后, 联苯转化率30 h 内稳定在8.6%左右, 4-甲基联苯(4-MBP)的选择性增加至约60%; 通水条件下升高反应温度至500℃, 联苯的转化率在反应30 h后达最高点, 选择性稳定在58%左右. 水的存在不仅改善了催化剂的活性及稳定性, 还能提高对位选择性.     

磷酸和水蒸气联合改性的HZSM-5的物化表征及催化研究

研究了磷和水蒸气联合改性HZSM-5样品的物化和催化性能。XRD和IR研究表明，没有新的晶相出现。NH3-TPD研究样品的酸性表明，经过磷改性后的样品的酸量明显下降。经过水热处理的样品的BET比表面明显降低，这可能归因于磷物种和铝物种对孔道的堵塞。氮吸附－脱附等温线研究表明，等温线为I型和IV型的复合型，滞后环为H4型。联合改性样品的正庚烷裂化转化率高于仅仅由水蒸气改性样品的正庚烷裂化转化率，从而显示出磷物种对沸石分子筛高温水蒸气脱铝的抑制作用。     

水蒸气处理对HZSM-5分子筛催化剂的酸性及孔结构的影响

通过XRD，NH3-TPD，IR，比表面与孔结构测定等方法，研究了HZSM-5分子筛（硅铝比为38）在不同温度下进行水热处理时的酸性与孔结构。结果表明，随着水热处理温度的提高，HZSM-5分子筛的结晶度稍有增大；酸性明显减弱，弱酸位增多，强酸位相对减少；IR谱图上有一定的蓝移；比表面与微孔体积减小，介孔体积增大。     

KCl,NaCl在HZSM—5分子筛上的分散研究

HZSM-5沸石分子筛是六十年代末发展起来的,具有高硅铝比,高催化活性和高热稳定性等特点,被广泛地应用于石油冶炼中的柴油临氢降解,加氢脱腊生成润滑油,催化重整和石油化学工业中的合成乙苯,甲苯歧化等项目[1]。近年来,对HZSM-5分子筛的改性研究比较活跃[2],但对盐类在其表面的分散研究还未见报道。本文选择了KCl、NaCl两种盐类,研究了他们在HZSM-5分子筛上的分散阈值,临界分散温度等性质。1　实验部分KCl、NaCl均为分析纯试剂,HZSM-5分子筛(SiO2/Al2O3=38)系南开大学化工厂的产品,使用前于550℃烘4小时。干混法制样:按0.02∶1,0…     

HZSM－5改性的研究

ＨＺＳＭ－５改性的研究张谦和，何瑞德，胡杰南（中国科学院山西煤炭化学研究所太原０３０００１）关键词ＨＺＳＭ－５，改性，酸性，吸附，扩散自从中孔ＺＳＭ－５沸石分子筛问世以来，许多文献报道了用改性ＨＺＳＭ－５催化剂可使烷基苯烷基转移过程中表现出高对位选择...     

水热处理Zn/HZSM-5催化剂对丙烷芳构化反应的影响

考察了水热处理对Ｚｎ／ＨＺＳＭ－５催化剂丙烷芳构化反应的影响,并采用ＦＴ－ＩＲ手段,研究了处理温度对催化剂表面酸性的影响,结果表明,随着水热处理温度的升高,单位晶胞中的Ｂ酸中心数减少,而上酸中心数增加,丙烷的转化率和芳烃选择性升高,水热处理温度为４００℃时达到最大值,此时催化剂的脱氢中心Ｚｎ＾２＋与聚合,环化的Ｂ酸中心为最佳匹配状态,随着处理温度的进一步升高、Ｂ酸中心数显著下降,丙烷的转化率和芳烃