国产航空煤油裂解催化剂Pt/ZrxTixAl1-2xO2的性能

采用共沉淀法制备了一系列Zr_xTi_xAl_1-2xO₂复合氧化物载体材料,考察了其作为裂解催化剂载体对航空煤油裂解反应的影响.?采用全自动吸附仪、X射线衍射、扫描电镜/能谱仪联用、NH₃-程序升温脱附等手段对催化剂进行了表征.?结果表明,当ZrO₂：TiO₂：Al₂O₃质量比为1：1：3时催化剂具有最大的比表面积和孔容;具有最强的表面酸性和最集中的强酸中心密度,且具有良好的再生功能.?实验结果表明,载体ZrO₂：TiO₂：Al₂O₃质量比为1：1：3时催化剂上650?℃裂解产气量较热裂解提高了2.1倍,700?℃时提高1.4倍.?另外,该系列载体材料经1000?℃焙烧5?h后,所制得的催化剂几乎失去了催化活性.     

Ce0.5Zr0.5O2修饰的Ni/SiC、Fe/SiC和Co/SiC催化燃烧甲烷性能

以铈锆固溶体（Ce_0.5Zr_0.5O₂）修饰的高比表面积SiC为载体,采用两步浸渍法制备了Ni、Fe和Co基催化剂,研究了其在煤层气催化燃烧脱氧中的催化活性和稳定性. 利用X射线衍射（XRD）、X射线光电子能谱（XPS）、电感耦合等离子体质谱（ICP-MS）、高分辨透射电子显微镜（HRTEM）、比表面积（BET）、热重分析（TGA）和H₂程序升温还原（H₂-TPR）对催化剂进行了表征. 分析结果表明,Ni、Fe和Co部分进入Ce_0.5Zr_0.5O₂固溶体晶格内部,导致催化剂体相形成更多的缺陷;同时Ce_0.5Zr_0.5O₂固溶体有助于加速金属氧化物和金属之间氧化还原过程的进行,促进了氧吸附、传输和对甲烷的活化. 另外,SiC和Ce_0.5Zr_0.5O₂固熔体良好的抗积碳性能,有效避免了催化剂在富甲烷反应气氛中因积碳而失活,从而使三种催化剂均具有优良的催化燃烧脱氧活性和稳定性. 其中,Co/Ce_0.5Zr_0.5O₂/SiC活性最高,可在320 ℃活化催化甲烷,并在410 ℃实现完全脱氧.     

Ce0.5+xZr0.4-xLa0.1O2-Al2O3催化剂催化燃烧柴油车碳烟

采用共沉淀法制备了系列Ce_0.5+xZr_0.4-xLa_0.1O₂-Al₂O₃催化剂, 其中0≤x≤0.4且Ce_0.5+xZr_0.4-xLa_0.1O₂与Al₂O₃的质量比为1:1. 考察了该系列催化剂对柴油车排放碳烟的催化燃烧性能, 并用低温N2吸附-脱附、X射线衍射(XRD)、X射线光电子能谱(XPS)、氢气程序升温还原(H₂-TPR)和氧气程序升温脱附(O₂-TPD)等手段对催化剂进行了表征. 研究结果表明该系列催化剂均形成了具有立方萤石结构的固溶体. 当x=0.2时, Ce³⁺离子在催化剂表面有一定的富集, 此时催化剂具有最大的β氧脱附峰和最好的表面还原性能, 同时具有良好的催化碳烟氧化活性, 碳烟在该催化剂的起燃温度为360 °C, 具有较好的应用前景.     

ZrxTixAl1-2xO2的制备及其在三效催化剂上的应用

Zr_0.5Ti_0.5O₂(ZT) and Zr_0.25Ti_0.25Al_0.5O₂(ZTA) mixed oxides were prepared by co-precipitation method and characterized by low temperature adsorption-desorption， XRD and NH₃-TPD. The activity of Pt/Zr_0.5Ti_0.5O₂ and Pt/ Zr_0.5Ti_0.5Al_0.5O₂ catalysts was evaluated using the simulated gases. The results show that ZTA samples exhibit higher specific surface area， larger pore volume and proper surface acidic amount and acidity in comparison with ZT. The results of the catalytic test indicate that Pt/ZT and Pt/ZTA catalysts exhibit excellent low-temperature catalytic activity and lower light-off temperatures of hydrocarbon， carbon monoxide and nitrogen oxides， especially better conversion for nitrogen oxides (NO_x). The addition of Al₂O₃ into ZT enhanced the anti-aging property of Pt/ ZTA catalysts due to the excellent textural， structural， surface acidity and thermal stability.     

Zr/Ti摩尔比对锶锆钛复合氧化物在可见光下光催化性能的影响

通过分步沉积法制备了不同Zr/Ti 摩尔比的锶锆钛(SZT)复合氧化物催化剂, 以X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)、紫外-可见(UV-Vis)漫反射光谱等表征手段考察不同Zr/Ti 摩尔比下SZT催化剂的结构形态, 以可见光下光催化降解亚甲基蓝为模型反应考察样品的光催化活性. 结果表明: Zr/Ti 摩尔比<1 时SZT催化剂发生Zr⁴⁺与Ti⁴⁺同质替换, 引起晶格缺陷, 光催化活性小幅提高; Zr/Ti 摩尔比≥1 时SZT催化剂产生SrZrO₃/Ti_nO_2n-1 (n=4, 9)的新晶相, Ti_nO_2n-1 (n=4, 9)的存在有利于光生电子-空穴的传导与分离, 可大幅提高催化剂光催化活性. 其中, SZT-5/5 表现出最高的光催化活性, 其一级反应速率常数达到0.2133 min^-1, 是同等光照条件下纯SrTiO₃样品(0.0158 min^-1)的13.5倍.     

CeZrYLaO对Fe基整体式稀薄甲烷催化燃烧性能的影响

采用共沉淀法制备了高性能低铈储氧材料Ce_0.35Zr_0.55Y_0.07La_0.03O_1.95(OSM,储氧材料)和胶溶法制备了耐高温、高比表面的La-Al₂O₃并以它们为载体,制备了一系列整体式铁基催化剂。考察了该系列催化剂对甲烷稀薄燃烧的催化性能,并用低温N₂吸附-脱附,储氧能力(oxygen storage capacity,OSC),XRD,XPS和H₂-TPR等测试手段对载体和催化剂进行了表征。活性测试结果表明所制得的整体式催化剂Fe/OSM+La-Al₂O₃可在50 000 h^-1的高空速条件下使含量为1%的甲烷在474 ℃起燃,565 ℃完全转化;低温氮吸附-脱附测试结果表明,所制得的Ce_0.35Zr_0.55Y_0.07La_0.03O_1.95经1 050 ℃焙烧5 h后的BET比表面积达33 m²·g^-1,孔容为0.14 mL·g^-1;La-Al₂O₃经1 050 ℃焙烧5 h后的BET比表面积达125 m²·g^-1,孔容为0.46 mL·g^-1,是优良的催化剂载体;OSC测试结果表明,加入储氧材料(oxygen storage material(OSM))能增加催化剂的储氧性能,有利于催化活性的提高;XRD测试结果表明,OSM以均一固溶体存在;XPS测试结果表明,Fe₂O₃与OSM载体之间的相互作用最强;H₂-TPR测试结果表明,加入OSM能增加催化剂的还原性能,从而提高了催化活性。     

一种具有低SO2氧化活性并满足欧V排放标准的柴油车氧化型催化剂

制备了具有高性能的稀土储氧材料Ce_0.75Zr_0.25O₂-Al₂O₃,Ti_0.9Zr_0.1O₂复合材料和Cr改性的β分子筛(Cr-β分子筛),并以此制备了单Pt型柴油车尾气净化氧化型催化剂.低温N₂吸附-脱附、储氧量测试结果表明,Ce_0.75Zr_0.25O₂-Al₂O₃样品具有较大的比表面积和优异的储氧性能,Ti_0.9Zr_0.1O₂复合材料也具有优越的织构性能.催化剂对HC和CO具有较高的催化活性,可使SOF在140℃开始转化,且具有较低的SO₂氧化活性.在YC4F国Ⅳ柴油机的测试结果表明,经该催化剂处理后的尾气排放能够满足欧Ⅴ排放标准对HC和CO排放要求.     

Cr掺杂对K2La2Ti3O10光催化活性的影响

通过溶胶-凝胶法制备了层状钙钛矿结构的K₂La₂Ti₃O₁₀及Cr掺杂的K₂La₂Ti₃O₁₀，采用X-射线衍射(XRD)、紫外可见漫反射光谱(DRS)、X射线光电子能谱(XPS)等对K₂La₂Ti₃O₁₀及Cr掺杂K₂La₂Ti₃O₁₀进行了表征。以I^-为电子给体、分别在紫外和可见光辐射下研究了K₂La₂Ti₃O₁₀及Cr掺杂K₂La₂Ti₃O₁₀光催化分解水的产氢活性。采用第一性原理，计算了Cr掺杂对K₂La₂Ti₃O₁₀半导体能带结构和态密度的影响，从电子结构的变化揭示了掺杂引起光催化活性差异的原因。结果表明，Cr的掺入能够改善和提高K₂La₂Ti₃O₁₀的光解水的产氢活性；Cr改善和提高K₂La₂Ti₃O₁₀的光解水的产氢活性存在一个最佳的掺杂浓度；当Cr与Ti的物质量的比为0.02∶1时，紫外光催化分解水产氢速率为1 500 μmol·L^-1·h^-1，可见光催化分解水产氢速率为83.6 μmol·L^-1·h^-1，分别为K₂La₂Ti₃O₁₀掺杂改性前产氢速率的26和5倍。     

高比表面CexZr1-xO2复合氧化物的制备及表征

分别采用共沉淀法和阴离子表面活性剂模板法制备了Ce_xZr_1-xO₂复合氧化物。采用XRD、AFM、FTIR以及N₂吸附-脱附等方法对样品进行了表征。结果表明，共沉淀法合成的样品在500 ℃煅烧2 h后，生成了立方相Ce_0.75Zr_0.25O₂和四方相Ce_0.5Zr_0.5O₂固溶体，比表面积为62.1 m²·g^-1，孔体积为0.097 cm³·g^-1；以阴离子表面活性剂十二烷基苯磺酸钠(SDBS)为模板剂，乙二胺为助模板剂合成的样品在500 ℃煅烧2 h后，生成了纯四方相Ce_0.5Zr_0.5O₂固溶体，比表面积为180 m²·g^-1，孔体积为0.182 cm³·g^-1。结果表明，以阴离子表面活性剂SDBS为模板剂，可以合成高比表面积且具有介孔结构的Ce_0.5Zr_0.5O₂复合氧化物；加入乙二胺作为助模板剂可明显的提高比表面积和孔体积。     

Cd3Al2Ge3O12: Mn2+磷光体的发光和长余辉性能

采用传统的高温固相法合成了Cd₃Al₂Ge₃O₁₂: Mn²⁺长余辉发光材料, 利用X射线粉末衍射仪、荧光光谱仪、热释光谱计量仪等手段对粉末样品进行了表征。研究了以Zr⁴⁺离子作为辅助激活剂离子, 对发光材料Cd₃Al₂Ge₃O₁₂: Mn²⁺余辉性能的影响。分析结果表明, 样品位于500~700 nm的黄光宽带发射峰源于Mn²⁺的⁴T₁(⁴G)→⁶A₁(⁶S)跃迁发射结果。并且观察到了由Cd₃Al₂Ge₃O₁₂基质向激活剂离子Mn²⁺的能量传递。共掺杂Zr⁴⁺离子后样品发射峰位没有明显变化, 但是余辉亮度衰减曲线表明适量的Zr⁴⁺离子掺杂可延长Cd₃Al₂Ge₃O₁₂: Mn²⁺的余辉时间。通过对热释光谱的分析, 解释了双掺杂荧光粉余辉性能增强的原因, Zr⁴⁺的掺杂在材料中引入了深度更为合适的缺陷陷阱, 可有效存储光能, 增强余辉的时间和强度。     

CuO/Ti0.5Zr0.5O2催化剂对NO+CO反应的催化作用

环境治理是当今社会面临的一大主要问题。目前,城市空气污染日趋严重,特别是工厂和汽车排放的大量未燃烧的烃类、CO、NOx是主要的空气污染物。其中,氮氧化物(NOx)排放状况尤其严重,它的排放会给环境和人们生活带来严重危害,因此,如何有效地消除NOx已成为目前环境保护中一个非常     

Al含量对Pt-SO2-4 /ZrO2-Al2O3固体超强酸催化

通过向SO^2-₄ /ZrO₂催化剂中同时引入适量的Pt和Al₂O₃, 制备出了具有较高催化性能和稳定性的Pt-SO^2-₄ /ZrO₂-Al₂O₃型固体超强酸催化剂. 以正戊烷异构化反应为探针, 考察了Al含量对催化剂性能的影响; 并采用X射线衍射(XRD)、比表面积测定(BET)、红外(IR)光谱、程序升温还原(TPR)、热重-差热分析(TG-DTA)和氨-程序升温脱附(NH₃-TPD)手段对催化剂进行了表征. 结果表明, Al能够提高ZrO₂的晶化温度, 抑制硫的分解, 增加催化剂的比表面积, 增强硫氧键的结合, 提高催化剂的还原性能, 增加催化剂的酸强度和酸总量. 当Al₂O₃含量(质量分数, w)为5.0%时, Pt-SO^2-₄ /ZrO₂-Al₂O₃固体超强酸催化剂的催化活性最好, 在100 h内异戊烷收率可稳定在52.0%以上, 选择性在98.2%以上.     

Preparation of ZrO2-TiO2-CeO2 and Its Application in the Selective Catalytic Reduction of NO with NH3

TiO₂,ZrO₂-TiO₂,andZrO₂-TiO₂-CeO₂ were prepared by co-precipitation method and characterized by X-ray diffraction (XRD), specific surface area measurements (BET), temperature programmed desorption (NH₃-TPD), oxygen storage capacity (OSC), and temperature programmed reduction (H₂-TPR). The results showed that ZrO₂-TiO₂-CeO₂ exhibited large number of surface strong acid, possessed some oxygen storage capacity, and strong redox property. The three materials were used as supports and the monolith catalysts were prepared with 1% (w) V₂O₅ and 9% (w)WO₃ for selective catalytic reduction (SCR) of NO with ammonia in the presence of excessive O₂, and the results of catalytic activity showed that the catalyst used ZrO₂-TiO₂-CeO₂ as support yielded nearly 100% NO conversion at 275 °C at a gas hourly space velocity (GHSV) of 10000 h⁻¹, and it had the best catalytic activity and showed great potential for practical application.     

Catalytic methanol decomposition to carbon monoxide and hydrogen over Pd/CeO2-ZrO2-La2O3 with different Ce/Zr molar ratios

The catalytic behaviors of Pd (1.4 wt%) catalysts supported on CeO₂-ZrO₂-La₂O₃ mixed oxides with different Ce/Zr molar ratios were investigated for methanol decomposition. Nitrogen adsorption-desorption (BET), X-ray photoelectron spectroscopy (XPS), H₂ temperature-programmed reduction (H₂-TPR), X-ray diffraction (XRD) and Pd dispersion analysis were used for their characterization. Pd/Ce_0.76Zr_0.18 La_0.06O_1.97 catalyst showed the highest BET surface area, best Pd dispersion capability and strongest metal-support interaction. Moreover, XPS showed that there was lattice defect oxygen or mobile oxygen. According to the result of O 1s measurements the lattice defect oxygen or mobile oxygen helped to maintain Pd in a partly oxidized state and increased the activity for methanol decomposition. The Pd/Ce_0.76Zr_0.18La_0.06O_1.97 catalyst exhibited the best activity. A 100% conversion of methanol was achieved at around 260 °C, which was about 20-40 °C lower than other catalysts     

Structure Evolution Process of Ce0.65Zr0.25Y0.1O1.95 Prepared by Oxidation-Coprecipitation Method

Ce_0.65Zr_0.25Y_0.1O_1.95 oxides were prepared by oxidation-coprecipitation method using ammonia and salvolatile as precipitators. The as-prepared samples were thermally treated at different temperatures and characterized by thermogravimetry-differential scanning calorimetry (TG-DSC), Fourier transform-infrared (FT-IR) spectrometry, X-ray diffraction (XRD), and specific surface area measurements (BET). The results showed that the hydroxyl and carboxyl groups coexisted in the precipitate and a perfect solid solution was gradually formed with an increase in calcination temperature. The physisorbed water was lost from 100 to 170 °C, hydroxyl groups were removed from 250 to 300 °C, and the carboxyl groups were eliminated from 420 to 500 °C. A structure model was further proposed to understand the Ce_0.65Zr_0.25Y_0.1O_1.95 structure evolution process in depth.     

Ultrasonic-assisted synthesis of PMMA/Ni0.5Zn0.5Fe2O4 nanocomposite in mixed surfactant system

PMMA/Ni_0.5Zn_0.5Fe₂O₄ nanocomposite with superparamagnetic behavior was synthesized by in situ emulsion polymerization of methylmethacrylate (MMA) monomer in the presence of Ni_0.5Zn_0.5Fe₂O₄ colloidal suspension assisted by ultrasonic irradiation. The obtained samples were characterized by X-ray diffraction (XRD), Fourier transform infrared spectra (FT-IR), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). XRD and FT-IR spectra confirmed the formation of PMMA/Ni_0.5Zn_0.5Fe₂O₄ nanocomposite. TEM images showed that Ni_0.5Zn_0.5Fe₂O₄ nanoparticles with the particle sizes of about 12 nm were well dispersed in the polymer matrix. The nanocomposite at room temperature exhibited superparamagnetic behavior under applied magnetic field. The formation mechanism of PMMA/Ni_0.5Zn_0.5Fe₂O₄ nanocomposite was proposed as well.     

ZnO添加量对Pd/Zr0.5Al0.5O1.75催化剂净化稀燃天然气汽车尾气性能的影响

以掺杂不同含量ZnO的Zr_0.5Al_0.5O_1.75为载体,制备了系列1.5%Pd催化剂.在模拟稀燃天然气汽车尾气条件下,测试了催化剂的活性和抗水性,并用N₂吸附-脱附、X射线衍射、H₂程序升温还原和X射线光电子能谱等手段对催化剂进行了系统表征.研究结果表明,ZnO的添加及添加量对催化剂的活性和抗H₂O性有明显影响,其中以ZnO添加量为15%时制备的复合氧化物为载体的催化剂活性最佳.当模拟尾气中不含H₂O时,该催化剂对甲烷的起燃温度（T₅₀）和完全转化温度（T₉₀）分别为278和314℃;在含H₂O时,该催化剂的T₅₀和T₉₀分别为342和371℃.     

Monolith Manganese-Based Catalyst Supported on ZrO2-TiO2 for NH3-SCR Reaction at Low Temperature

Monolith catalysts were prepared using TiO₂ and ZrO₂-TiO₂ as supports with MnO₂ as active component and Fe₂O₃ as promoter. The catalytic activities at low temperature and stability at high temperature for selective catalytic reduction of NO_x with NH₃ (NH₃-SCR) in the presence of excessive O₂ were studied after the catalysts calcined at different temperatures. The catalysts were characterized by X-ray diffraction (XRD), specific surface area measurements (BET), oxygen storage capacity (OSC), and temperature programmed reduction (H₂-TPR). The results indicated that the catalyst supported on ZrO₂-TiO₂ had excellent stability at high temperature, and possessed high specific surface area and oxygen storage capacity, and had strong redox property. The results of the catalytic activities indicated that the monolith manganese-based catalyst using ZrO₂-TiO₂ as support had evidently improved the activity of NH₃-SCR reduction reaction at low temperature, and it showed great potential for practical application.