Catalytic methanol decomposition to carbon monoxide and hydrogen over Pd/CeO2-ZrO2-La2O3 with different Ce/Zr molar ratios |
| |
Authors: | Hairong Wang Yaoqiang Chen Qiulin Zhang Qingchao Zhu Maochu Gong Ming Zhao |
| |
Institution: | aKey Laboratory of Green Chemistry & Technology of Ministry Education, College of Chemistry, Sichuan University, Chengdu 610064, Sichuan, China |
| |
Abstract: | The catalytic behaviors of Pd (1.4 wt%) catalysts supported on CeO2-ZrO2-La2O3 mixed oxides with different Ce/Zr molar ratios were investigated for methanol decomposition. Nitrogen adsorption-desorption (BET), X-ray photoelectron spectroscopy (XPS), H2 temperature-programmed reduction (H2-TPR), X-ray diffraction (XRD) and Pd dispersion analysis were used for their characterization. Pd/Ce0.76Zr0.18 La0.06O1.97 catalyst showed the highest BET surface area, best Pd dispersion capability and strongest metal-support interaction. Moreover, XPS showed that there was lattice defect oxygen or mobile oxygen. According to the result of O 1s measurements the lattice defect oxygen or mobile oxygen helped to maintain Pd in a partly oxidized state and increased the activity for methanol decomposition. The Pd/Ce0.76Zr0.18La0.06O1.97 catalyst exhibited the best activity. A 100% conversion of methanol was achieved at around 260 °C, which was about 20-40 °C lower than other catalysts |
| |
Keywords: | methanol decomposition palladium CeO2-ZrO2-La2O3 XPS hydrogen carbon monoxide |
本文献已被 维普 ScienceDirect 等数据库收录! |
| 点击此处可从《天然气化学杂志》浏览原始摘要信息 |
| 点击此处可从《天然气化学杂志》下载免费的PDF全文 |