Monolith Manganese-Based Catalyst Supported on ZrO2-TiO2 for NH3-SCR Reaction at Low Temperature

Monolith catalysts were prepared using TiO₂ and ZrO₂-TiO₂ as supports with MnO₂ as active component and Fe₂O₃ as promoter. The catalytic activities at low temperature and stability at high temperature for selective catalytic reduction of NO_x with NH₃ (NH₃-SCR) in the presence of excessive O₂ were studied after the catalysts calcined at different temperatures. The catalysts were characterized by X-ray diffraction (XRD), specific surface area measurements (BET), oxygen storage capacity (OSC), and temperature programmed reduction (H₂-TPR). The results indicated that the catalyst supported on ZrO₂-TiO₂ had excellent stability at high temperature, and possessed high specific surface area and oxygen storage capacity, and had strong redox property. The results of the catalytic activities indicated that the monolith manganese-based catalyst using ZrO₂-TiO₂ as support had evidently improved the activity of NH₃-SCR reduction reaction at low temperature, and it showed great potential for practical application.