以PEG为模板剂水热合成高比表面介孔Ce0．5Zr0．51O2固溶体

以PEG-4000为模板剂,采用水热法制备了具有萤石型立方相结构的Ce0.5Zr0.5O2固溶体,考察了共沉淀pH、PEG-4000添加量、水热温度、焙烧温度对样品的物相、比表面积、孔径分布、N2吸附脱附特性等的影响。结果表明：当PEG／（Ce＋zr）（摩尔比）为0．3,共沉淀pH值约为10,120℃下水热反应12h,烧结温度为500℃时,所得产品的比表面积为146．7m^2·g^-1,平均孔径为12．50nm。     

Preparation and Characterization of Mesoporous Ce0.5Zr0.5O2 Mixed Oxide

Mesoporous （MSU） Ce0.5Zr0.5O2 mixed oxide with a high specific surface area has been synthesized under weak acidic condition in the presence of an anionic surfactant, sodium dodecylbenzenesulfonate. The effect of the pH value on the formation of mesostructure and the thermal stability of the material has been evaluated. The products were characterized by transmission electron microscopy, powder X-ray diffraction and nitrogen adsorption-desorption measurements. The results showed that the as-prepared Ce0.5Zr0.5O2 mixed oxide possessed a specific surface area of 163.3 m^2·g^-1, which had a cubic fluorite-type structure and possessed specific surface areas of 148.4 and 62.4 m^2·g^-1 after calcination at 500 and 800 ℃ for 2 h, respectively. The material showed excellent thermal stability.     

以PEG为模板剂水热合成高比表面介孔Ce0.5Zr0.5O2固溶体

以PEG-4000为模板剂,采用水热法制备了具有萤石型立方相结构的Ce0.5Zr0.5O2固溶体,考察了共沉淀pH、PEG-4000添加量、水热温度、焙烧温度对样品的物相、比表面积、孔径分布、N2吸附脱附特性等的影响.结果表明:当PEG/(Ce+Zr)(摩尔比)为0.3,共沉淀pH值约为10,120℃下水热反应12 h,烧结温度为500℃时,所得产品的比表面积为146.7 m2·g-1,平均孔径为12.50 nm.     

高比表面CexZr1-xO2复合氧化物的制备及表征

分别采用共沉淀法和阴离子表面活性剂模板法制备了Ce_xZr_1-xO₂复合氧化物。采用XRD、AFM、FTIR以及N₂吸附-脱附等方法对样品进行了表征。结果表明，共沉淀法合成的样品在500 ℃煅烧2 h后，生成了立方相Ce_0.75Zr_0.25O₂和四方相Ce_0.5Zr_0.5O₂固溶体，比表面积为62.1 m²·g^-1，孔体积为0.097 cm³·g^-1；以阴离子表面活性剂十二烷基苯磺酸钠(SDBS)为模板剂，乙二胺为助模板剂合成的样品在500 ℃煅烧2 h后，生成了纯四方相Ce_0.5Zr_0.5O₂固溶体，比表面积为180 m²·g^-1，孔体积为0.182 cm³·g^-1。结果表明，以阴离子表面活性剂SDBS为模板剂，可以合成高比表面积且具有介孔结构的Ce_0.5Zr_0.5O₂复合氧化物；加入乙二胺作为助模板剂可明显的提高比表面积和孔体积。