ＬＲＳ，ＸＲＤ，ＸＰＳ结果表明，仲钼酸铵浸渍仅经干燥的Ｚｒ（ＯＨ）４，再焙烧制得的固体超强酸（ＭｏＯ３／ＺｒＯ２（Ｉ））与浸渍晶态ＺｒＯ２制得的部分氧化催化剂（ＭｏＯ３／ＺｒＯ２（Ⅱ）中，活性组分的存在形式明显不同，在ＭｏＯ３／ＺｒＯ２（Ⅱ）中，ＭｏＯ３以二维聚钼酸根和Ｍｏ－Ｏ－Ｚｒ表面物种两种表面态存在于介稳的四方ＺｒＯ２上，后者在ＬＲＳ谱中表现为～８１４ｃｍ＾－１的宽峰，ＭｏＯ３含量超过一定值     

制备方法对MoO3/ZrO2结构的影响及MoO3/ZrO2固体超强酸的结构特征Ⅱ.活性组分存在形态?

ＬＲＳ，ＸＲＤ，ＸＰＳ结果表明，仲钼酸铵浸渍仅经干燥的Ｚｒ（ＯＨ）４，再焙烧制得的固体超强酸（ＭｏＯ３／ＺｒＯ２（Ｉ））与浸渍晶态ＺｒＯ２制得的部分氧化催化剂（ＭｏＯ３／ＺｒＯ２（Ⅱ）中，活性组分的存在形式明显不同，在ＭｏＯ３／ＺｒＯ２（Ⅱ）中，ＭｏＯ３以二维聚钼酸根和Ｍｏ－Ｏ－Ｚｒ表面物种两种表面态存在于介稳的四方ＺｒＯ２上，后者在ＬＲＳ谱中表现为～８１４ｃｍ＾－１的宽峰，ＭｏＯ３含量超过一定值     

SO^2—4／TiO2和SO^2—4／Fe2O3固体超强酸研究

用ＸＲＤ、ＴＧ－ＤＴＧ、ＳＥＭ和化学分析等手段研究了浸渍Ｈ２ＳＯ４的无定形ＴｉＯ２和Ｆｅ２Ｏ３在焙烧过程中的晶化、相变、失水及失硫情况，总结出ＳＯ＾２－４／ＭｘＯｙ型固体超强酸具有与ＳＯ＾２－４／ＺｒＯ２体系相同的形成规律。用ＩＲ光谱和常温正戊烷异构化反应对ＳＯ＾２－４／ＴｉＯ２／Ｆｅ２Ｏ３的超强酸性进行了表征，表明它们与ＳＯ＾２－４／ＺｒＯ２体系具有相似的表面酸位结构，无水状态主要为Ｌ酸位，吸水     

镝对固体超强酸催化剂ZrO2-Dy2O3/SO42--HZSM-5的酸性和稳定性的影响

合成了固体超强酸催化剂ＺｒＯ２－Ｄｙ２Ｏ３／ＳＯ４＾２－,并将其负载于分子筛ＨＺＳＭ－５上,制成复合型固体超强酸催化剂ＺｒＯ２－Ｄｙ２Ｏ３／ＳＯ４＾２－ＨＺＳＭ－５）以下简称催化剂ＺＤＳＨ）,采用Ｈａｍｍｅｔｔ批示剂法,吸附吡淀的ＴＰＤ法,考察催化剂ＺＤＳＨ的酸强度及其分布;通过热重分析（ＴＧＡ）、差热分析（ＤＴＡ）方法,考察镝对催化剂ＺＤＳＨ稳定性的作用;运用红外光谱（ＩＲ）法,分析催化剂ＺＤＳ     

以ZrO2-Al2O3为载体的Co-Mo-K耐硫水煤气变换催化剂

采用沉淀法和浸渍法分别制备了ＺｒＯ２－Ａｌ２Ｏ３复合载体和Ｃｏ－Ｍｏ－Ｋ耐硫变换催化剂。研究了ＺｒＯ２对Ｃｏ－Ｍｏ－Ｋ面硫变换催化剂活性及热稳定性的影响。利用ＸＲＤ、ＢＥＴ、ＴＧ、ＸＰＳ等手段对催化剂及其载体的结构、吸硫吸水性能和氧化还原性能进行了表征。结果表明以ＺｒＯ２－Ａｌ２Ｏ３代替传统的γ－Ａｌ２Ｏ３作为Ｃｏ－Ｍｏ－Ｋ耐硫变换催化剂的载体,可提高催化剂的活性,尤其是低温活性,并可改善催化剂的     

硫化态K—MoO3／γ—Al2O3催化剂表面物种的XPS研究

采用Ｘ光光电子能谱及曲线氦合手段对硫化态Ｋ－ＭｏＯ３／Ａｌ２Ｏ３合成醇催化剂进行了研究，分别考察负载量及硫化前不同条件预处理对催化剂表面的Ｓ、Ｍｏ组分的物种形式及各物种相对含量的影响，以及表面不同组分的相对组成。结果表明，根据其电子结合能变化，Ｓ组分可区分为ＳＯ＾２－４、ＳＯ３、Ｓ＾０、ＭｏＳ２、ＭｏＳ２－ｘ等六种存在形式不同的物种；Ｍｏ组分可分为Ｍｏ＾６＋、Ｍｏ＾５＋、ＭｏＳ＾２＋、ＭｏＳ２、Ｍ     

固体超强酸催化剂ZrO2-Dy2O3/SO42--HZSM-5的制备及结构性能关系的研究

合成了分子筛复合超强酸催化剂ＺｒＯ２－Ｄｙ２Ｏ３／ＳＯ＾２－４－ＨＺＳＭ－５;以柠檬酸和正丁醇的酯化反应为探针,运用Ｈａｍｍｅｔｔ指示剂法、ＢＥＴ、ＸＲＤ和ＡＥＳ等方法,考察了催化剂的制备条件与结构性能的关系。结果表明,Ｄｙ２Ｏ３与ＺｒＯ２的质量比为０．０３：１时,催化剂性能较好;最适宜焙烧温度为５５０℃,在此温度下制得的催化剂具有较大的比表面积和较强的酸性,催化剂中的ＺｒＯ２以四方晶形存在,该催     

SO4^2—／ZrO2和SO4^2—／Al2O3—ZrO催化剂上的正戊烷反应

研究了添加Ａｌ对ＳＯ４＾２－／ＺｒＯ２超强酸样品的晶化,比表面、硫含量、超强酸性和正戊烷反应性能的影响,考察了活化温度、反应温度、Ａｌ含量和载Ｐｔ对催化剂活性和选择性的影响。ＳＯ４＾２／Ａｌ２Ｏ３－ＺｒＯ２催化剂的酸强度与ＳＯ４＾２－／ＺｒＯ２基本相当,但超强酸位经后者多,未载Ｐｔ时正戊烷反应活性和稳定性明显高于后者,负载Ｐｔ后,正戊烷异构化选择性和稳定性大大提高,但Ｐｔ／ＳＯ４＾２－／Ａｌ２Ｏ３     

MoO3在Ga2O3上的分散研究

采用ＸＲＤ,ＬＲＳ,ＦＴ－ＩＲ,ＵＶ－ＤＲＳ和ＴＰＲ研究了ＭｏＯ３在体载体Ｇａ２Ｏ３上的分散情况。结果表明：ＭｏＯ３的分散状态受Ｇａ２Ｏ３表面结构的影响,ＭｏＯ３在Ｇａ２Ｏ３上的分散容量约为８．４μｍｏｌ／ｍ＾２;低于该分散容量时,Ｍｏ＾６＋主要以高分散态存在于Ｇａ２Ｏ３表面,而高于该分散容量时,除在分散态的Ｍｏ－Ｏ物种外,还有残余的ＭｏＯ３晶相出现。ＴＰＲ结果表明：ＭｏＯ３低于分散容量时,体系中     

制备方法对MoO_3／ZrO_2结构的影响及MoO_3／ZrO_2固体超强酸的结构特征 Ⅱ．活性组分存在形态的研究

ＬＲＳ，ＸＲＤ，ＸＰＳ结果表明，仲钼酸铵浸渍仅经干燥的Ｚｒ（ＯＨ）４再焙烧制得的固体超强酸（ＭｏＯ３／ＺｒＯ２（Ⅰ））与浸渍晶态ＺｒＯ２制得的部分氧化催化剂（ＭｏＯ３／ＺｒＯ２（Ⅱ）中，活性组分的存在形式明显不同．在ＭｏＯ３／ＺｒＯ２（Ⅱ）中，ＭｏＯ３以二维聚钼酸根形式单层分散在ＺｒＯ２上（其中单斜ＺｒＯ２为主），在～９５０ｃｍ－１处出现特征拉曼宽峰，超出单层分散容量的部分以晶态ＭｏＯ３形式存在．在ＭｏＯ３／ＺｒＯ２（Ⅰ）中，活性相以二维聚钼酸根和Ｍｏ—Ｏ—Ｚｒ表面物种两种表面态存在于介稳的四方ＺｒＯ２上，后者在ＬＲＳ谱中表现为～８１４ｃｍ－１的宽峰；ＭｏＯ３含量超过一定值时，多余的ＭｏＯ３在５５０℃即与四方ＺｒＯ２发生反应形成体相Ｚｒ（ＭｏＯ４）２．Ｍｏ—Ｏ—Ｚｒ表面物种中，Ｍｏ（Ⅵ）是四配位的，与四方ＺｒＯ２结合很强，它很可能与ＭｏＯ３／ＺｒＯ２具有超强酸性有密切关系．     

WO3／ZrO2固体强酸催化剂上异丁烷—丁烯烷基化反应的研究：Ⅲ.超 …

制备了以超细ＺrＯ２为载体的ＷＯ３／ＺrＯ２、ＳＯ４＾２－／ＺrＯ２、ＭoＯ３／Ｚr Ｏ２固体强酸催化剂,并用ＸＲＤ、ＤＴＡ－ＴＧ、Ｈ２－ＴＰＲ、ＮＨ３－ＴＰＤ等方法表征了其晶型结构、表面状态和酸性。结果表明,超细ＺrＯ２中的Ｔ－晶相所占比例虽有所下降,但具有更大的比表面积、酸强度和对金属氧化物的负载能力,且酸强度随焙烧温度升高而增强,表明其表面状态亦有较大变化。研究了以超细ＺrＯ２为载体的固体强酸催化     

Catalysis of SO42--ZrO2/TiO2 nanometer solid superacid

Superacid catalyst SO42--ZrO2/TiO2 was applied in esterification of Acetic Acid and Butanol. The particle size of ZrO2 in the catalyst was about 12.5 nm. In catalyst preparation conditions, the effect factor order on catalytic activity is H2SO4 concentration ＞ calcination temperature ＞ ZrO2 supported content. The optimum preparation condition is as follows: ZrO2 content 3.5g/g; calcination temperature 600℃, and H2SO4 concentration 0.5mol/L. The catalytic activity is 96.5 vol%.SO42-/MxOy solid superacid is a kind of green catalyst, whose application perspective is bright. In this paper, SO42--ZrO2/TiO2 solid superacid was prepared with nanometer compound carrying method. The acidic strength of catalysts was measured with the following Hammett indicators, 2,4-dinitrofluorobenzene (H0=-14.52) and p-nitrochlorobenzene (H0=-12.70). Catalytic activity was evaluated with esterification reaction of Acetic Acid and Butanol. Reaction temperature was at 105℃, and reaction time was only 1h. The conversion rate of Acetic Acid was analyzed by a gas chromatograph (GC-14C SHIMADZU in Japan)The experimental results showed that H2SO4 concentration had more influences on catalytic activity than other two factors, calcination temperature and ZrO2 supported content. Since sulfur absorbed on the surface of metal oxides is necessary to the acidity of SO42-/MxOy solid superacid,H2SO4 concentration in impregnation solution is needed enough high. But, it can't be too much high,otherwise, Zirconium sulfate formed on the catalyst surface will be harmful influences on catalytic activity. In researched cover, 0.5mol/L H2SO4 concentration is the most suitable, and the catalyst prepared with this concentration has very strong acidity.The optimum preparation condition is as follows: ZrO2 content 3.5g/g; calcination temperature 600℃, and H2SO4 concentration 0.5mol/L. In the catalyst prepared with above conditions, the acidic strength (H0) of the catalyst is smaller than ＜-14.52, and catalytic activity is 96.5 vol%. When it was re-used in esterification reaction, catalytic activity decreased gradually with re-used times increasing(seen in Table 1). But after catalyst is used repeatedly up to five times, catalytic activity (84.3 vol %)is still higher than that of H2SO4 catalyst.The X-ray diffraction patterns showed that ZrO2 supported in TiO2 belonged tetragonal zirconia phases. Through the calculation of Scherrer formula, the particle size of ZrO2 in the catalyst is about 12.5 nm. After SO42- promoted nanometer ZrO2/TiO2 compound carrier, the diffraction peaks of tetragonal zircoma become broader and the strength weaker. It shows that adding SO4 ions restrains the crystallization of ZrO2, diminishes the size of particles. This might be why SO42--ZrO2/TiO2 has high catalytic activity and stability in acidic catalysis reaction.     

MoO3/SiO2催化剂的异丁烷选择氧化反应性能

分别采用浸渍法和溶胶－凝胶法制备了MoO3/SiO2催化剂，用XRD，TPR，IR，TPD和活性评价等手段对催化剂的影响，晶格氧活泼性，化学吸附性能和异丁烷选择氧化反应性能进行了研究。结果表明，催化剂表面由Lewis碱位Mo=M,Mo-O-Mo中的晶格氧和Lewis酸位Mo^6 构成，在MoO3/SiO2催化剂上，异丁烷主要通过甲基的H双位吸附在表面的Lewis碱位Mo=O上；在常压条件下，异丁烷选择氧化产物主要为异丁烷，甲基丙烯醛和甲基丙烯酸，其中深度氧化产物CO2主要由吸附的异丁烯继续反应生成；采用溶胶－凝胶法制备的MoO3/SiO2催化剂，可得到较高的异丁烷转化率和含氧有机物选择性。     

引入SiO2对SO4^2—／ZrO2超强酸体系的影响

用共沉淀法和负载法制备了一系列SO4^2-/ZrO2催化剂,详细研究了添加SiO2对SO4^2-/ZrO2超强酸样品的晶化、比表面、硫含量、超强酸性和异丙苯裂解及异丙醇脱水反应的影响。引入SiO2会延迟ZrO2的晶化和晶相转变,减弱SO4^2-/ZrO2体系的超强酸性,但对提高样品的异丙苯裂解和异丙醇脱水反应活性有利。     

固体超强酸对合成辛基多苷的催化作用

SO2 -4 /ZrO2 固体超强酸用作合成辛基多苷 (OctylPolyglycosides)的催化剂 ,具有活性高、选择性好、易与产品分离、无污染、可重复利用等优点。文中主要讨论SO2 -4 /ZrO2 ,SO2 -4 /ZrO2 MoO3、SO2 -4 /ZrO2 Fe2 O3、以及SO2 -4 /ZrO2 SiO2 固体超强酸在合成辛基多苷反应中的不同催化活性。实验证明 :同一制备条件下的不同催化剂其活性不同 ,且SO2 -4 /ZrO2 的活性、选择性最好 ,可使葡萄糖的转化率高达 96%。     

固体超强酸SO2-4-MoO3-TiO2的制备及其催化酯化性能研究

In this paper a new solid superacid catalyst SO2-4-MoO3-TiO2 was prepared.The activity of the catalyst in esterification of acetic acid and iso-amyl alcohol was measured and compared with that of SO2-4-TiO2 and MoO3-TiO2.The results showed that SO2-4-MoO3-TiO2 had better catalytic performance than SO2-4-TiO2 and MoO3-TiO2.There was evident coordination between MoO3 and SO2-4 when they coexisted on TiO2.     

固体超强酸SO_4~(2-)-MoO_3-TiO_2的制备及其催化酯化性能研究

ＳＯ2 -4 ＭｘＯｙ 型固体超强酸自问世以来一直受到人们的广泛关注 ,已对其进行了大量的研究。该类催化剂的酸强度高 ,在烷基化、酰基化、裂解、醇脱水、异构化、酯化等反应中有很高的催化活性。最常用的氧化物基体是ＺｒＯ2 和ＴｉＯ2 ,最好的促进剂是ＳＯ2 -4 。也有用ＭｏＯ3作促进剂的[1～3] ,得到相应的超强酸催化剂。作者在ＳＯ2 -4 ＴｉＯ2 超强酸的基础上 ,将ＭｏＯ3和ＳＯ2 -4 同时负载在ＴｉＯ2基体上 ,得到ＳＯ2 -4 ＭｏＯ3 ＴｉＯ2 固体超强酸 ,以乙酸异戊酯的合成为探针反应考察了该催化剂的催化酯化活性 ,并与ＳＯ2 -4 …     

低温陈化超声波共沉淀制备SO4^2-/ZrO2-La2O3催化剂

低温陈化超声波共沉淀法制得SO4^2-/ZrO2-La2O3前驱体,经H2SO4处理,在不同温度下焙烧得到纳米晶催化剂SO4^2-/ZrO2-La2O3;用Hammett指示剂法测定其酸性．用XRD、BET、TEM、IR和XPS对样品进行表征,其催化活性用醋酸和甘油的酯化反应进行了评价．结果表明经超声波搅拌和低温（-15℃）陈化,650℃焙烧4h得到的固体超强酸表现出较高催化活性．     

MoO3和Nb2O5助剂对Pt/ZrO2催化剂上短链烷烃燃烧反应的不同促进作用

贵金属Pt催化剂具有高活性和热稳定性,广泛应用于催化挥发性有机物的完全氧化反应(燃烧反应).短链烷烃(甲烷、乙烷、丙烷等)化学性质稳定,是最难氧化的一类有机物,常用作考察燃烧反应催化剂性能的模型反应物.然而,目前报道的研究工作通常仅限于针对某一种烷烃底物的催化燃烧,系统考察催化剂以及助剂对不同短链烷烃的催化燃烧活性鲜有报道.在短链烷烃中,甲烷只有C–H键;而其它烷烃除了C–H键;还有C–C键.因此,研究催化剂对甲烷、乙烷和丙烷燃烧反应催化性能的差异性,对于认识催化剂上C–H键和C–C键的活化具有非常重要的意义.本文制备了MoO3或Nb2O5修饰的Pt/ZrO2催化剂并用于短链烷烃的燃烧反应.研究发现,MoO3助剂对甲烷燃烧有明显的抑制作用,但对乙烷,丙烷和正己烷燃烧反应具有促进作用,促进作用随着烷烃碳链的增长逐渐增加;Nb2O5助剂对甲烷、乙烷、丙烷和正己烷燃烧反应均具有促进作用,然而促进作用随着碳链的增长而逐渐减弱.MoO3和Nb2O5助剂的不同促进作用与助剂影响催化剂表面酸性以及Pt物种的氧化或还原态有关.NH3-TPD结果表明,MoO3助剂可以显著增加Pt/ZrO2催化剂表面强酸位点数量,而Nb2O5助剂可以显著增加Pt/ZrO2催化剂表面中强酸位点数量.HTEM结果表明,两种助剂的添加都不会明显改变Pt物种的颗粒尺寸.在Pt-Mo/ZrO2催化剂上,MoO3覆盖部分Pt物种形成丰富的Pt-MoO3界面,促进了金属Pt物种和强表面酸性位点的生成,提高了丙烷燃烧反应活性;Pt-Nb/ZrO2催化剂上载体表面的部分Nb2O5被Pt物种包覆,使得生成的表面Pt-Nb2O5界面低于Pt-Mo/ZrO2催化剂,但由于催化剂表面酸性位的提升,也促进了丙烷燃烧反应活性的提高.XPS结果表明,在甲烷燃烧反应中,Pt-Nb/ZrO2催化剂上Ptn+物种能够更加稳定地存在,这可能是Nb2O5助剂提高Pt-Nb/ZrO2催化剂上甲烷燃烧活性的关键.而Pt-Mo/ZrO2催化剂上Ptn+物种在甲烷反应中可以更容易地被还原,并且由于MoO3的包裹导致暴露的Pt位点数量降低,使催化剂催化甲烷燃烧的活性受到抑制.可见,MoO3助剂更有利于C–C键活化,而Nb2O5助剂更有利于高键能的C–H键活化.综上,本文系统性地研究MoO3助剂和Nb2O5助剂对Pt/ZrO2催化剂上不同短链烷烃的燃烧反应的影响,证实了两种助剂的促进作用与碳链长度的关系是截然不同的.     

SO4 2- /ZrO2酸性及其催化液化性能研究

通过沉淀 浸渍法制备了一系列SO4 2－/ZrO2固体酸催化剂,利用NH3-TPD、FT-IR及间歇式高压加氢实验考察了SO4 2－/ZrO2固体酸的酸性和催化液化性能。对SO4 2－/ZrO2固体酸的结构进行了XRD、BET及TG/DTA表征。结果表明,SO4 2－/ZrO2固体酸表面酸中心强度呈非均一化、连续分布,中强酸是SO4 2－/ZrO2主要的酸中心;煤液化反应中,SO4 2－/ZrO2固体酸催化作用主要表现为催化裂解,酸中心越强,催化活性越高;提高SO4 2－/ZrO2焙烧温度,有利于提高酸中心强度及强酸中心分布、增大煤的转化率;650℃焙烧3h ,SO4 2－/ZrO2催化活性最高,煤液化转化率达到76.77%。