GROWTH MODE OF Cu-RICH PARTICLES ON LASER-ABLATED YBa2Cu3O7 THIN FILMS

The microstructure of the laser-ablated YBa₂Cu₃O₇ (YBCO) thin film deposited on heated (100) SrTiO₃ substrate was examined by transmission electron microscope. The par-ticles on the film mainly consist of CuO and few CuYO₂. Most of these non-superconducting particles nucleate on or near the surface of the film and protrude about 100-400 nm in height, A large amount of a-axis YBCO grains also exist in the film, which nucleate at the substrate surface and grow perpendicularly above the c-axis YBCO film. The YBCO thin film deposited under low oxygen pressure has very different microstructure compared with YBCO thin film deposited under high oxygen pressure.     

插入二氧化铈薄膜提高MOD-YBa2Cu3O7-x厚膜超导性能的研究

YBa₂Cu₃O_7-x(YBCO)膜存在“厚度效应”: 随着厚度增加, YBCO薄膜的临界电流密度下降, 尤其是YBCO薄膜的厚度超过1 μm时, 它的临界电流密度急剧下降. 本文在YBCO薄膜之间引入极薄的二氧化铈(CeO₂)薄膜, 成功制备出结构为YBCO/YBCO/CeO₂/YBCO的超导厚膜. 所制备的厚度为2 μm的YBCO膜临界电流密度为1.36 MA/cm² (77 K, 自场), 其性能比相同厚度的纯YBCO膜有了较大幅度的提升. 研究表明CeO₂薄膜起到了传递织构、松弛应力的作用.     

EFFECTS OF THE QUALITY OF SUBSTRATE ON THE STRUCTURE AND SUPERCONDUCTING PROPERTIES OF Yba2Cu3O7-x THIN FILM

We have systematically investigated the structures, morphologies, microwave surface resistance, DC performances and the substrate qualities of three YBa₂Cu₃O_7-x(YBCO) thin films 30mm in diameter. The three samples deposited by the same process have been proved of different properties. It has been shown that the structure and superconducting properties of the thin film depend strongly on the quality of substrate.     

Effect of different oxidizing gases on the in-situ growth of YBa2Cu3O7−δ films by pulsed laser deposition

The effectiveness of oxygen (O₂), nitrous oxide (N₂O), and nitrogen dioxide (NO₂) as oxidizing agents during in-situ growth of YBa₂Cu₃O_7−δ (YBCO) films on (100) SrTiO₃ substrates by pulsed laser deposition has been studied as a function of deposition temperature (700–800°C), and laser wavelength (193,248 and 355 nm), for a wide range of oxidizer gas pressure (0.1–200 mTorr). In general, the superconducting transition temperature of the films has been found to increase with increasing oxidant pressure, with zero-resistance temperature ≈90 K only obtained in films prepared in a relatively high pressure (150–200 mTorr) of oxidizer gas. At lower pressures, the transition temperature while being depressed is quite sensitive to the nature of the oxidant, the laser wavelength and the deposition temperature. Nevertheless, independent of the oxygen source or other growth parameters, an almost linear decrease in transition temperature with a corresponding increase in the c-axis lattice parameter has been observed for all the film. YBCO films have also been deposited in a low pressure background (≤ 1 mTorr) using a combination of atomic oxygen and pulsed molecular oxygen. The results are discussed in terms of the oxygen requirement for kinetic and thermodynamic stability of YBCO during growth of the film by pulsed laser deposition.     

PREPARATION OF a-AXIS ORIENTED YBa2Cu3Ox THIN FILMS

The a-axis oriented YBa₂Cu₃O_x(YBCO) thin films could be grown on (100) SrTiO₃(STO) substrates with STO buffer layers by dc and rf magnetron sputtering either by low-ering the deposition temperature, or by using a self-template technique. For the latter, the resistivity of the thin film at 290K along the substrate [001] direction is about four times larger than that in the [010] direction. The zero resistance temperatures T_c0 are 89 K in both directions. So high quality a-axis oriented YBCO thin films can be prepared by the self-template technique. Also the T_c0 increase monotonously with the reduction of the thickness of the YBCO seed layer.     

Aspects of annealing and free surface crystallization of YBCO thin films

We describe a method of high temperature annealing in which the control of oxygen partial pressure is the principal experimental determinant in obtaining highly c oriented thin films of YBa₂Cu₃O_{7 − δ} on YSZ. Film crystallization, morphology and substrate interactions are discussed with detailed reference to the equilibria existing in the YBCO system. A model based on the melt-assisted crystallization of the precursor tetragonal compound, beginning at the free film surface, is used to explain the observed c texturing. Excellent Josephson coupling between grains of YBa₂Cu₃O_{7 − δ} in our films is related to melt-assisted growth. We discuss the adverse effects of annealing in pure oxygen at high temperatures.     

SiO2 passivation film effects on microwave characteristics of YBa2Cu3O7−x-based resonators

SiO₂ film coated as a passivation layer for YBa₂Cu₃O_7−x (YBCO)-based microwave devices is investigated by measuring the microwave characteristics of microstrip line resonators. The SiO₂ film is deposited with its 0.3 to 0.4 μm thickness by a sputtering method using Ar + 30%O₂ plasma. These deposition conditions do not degrade the microwave characteristics and the critical temperature (T_c). Next, the SiO₂ film coated resonators are compared with the uncoated ones for two kinds of degradation conditions: a 200°C annealing in air, and an exposure to air at 85°C and 85% RH (relative humidity). We find that the SiO₂ passivation film prevents the YBCO thin film from the surface degradation and reacting with water.     

Improved initial epitaxial growth of superconducting YBa2Cu3O7 thin films on Y–ZrO2 substrates with a La1.85Sr0.15CuO4 buffer layer

Epitaxial thin films of YBa₂Cu₃O₇ (YBCO) have been deposited on Y–ZrO₂ (YSZ) substrates by means of the pulse laser deposition technique. It has been found that the initial epitaxy of YBCO thin films grown on YSZ can be significantly improved by using La_1.85Sr_0.15CuO₄ (LSCO) as a buffer layer. X-ray diffraction measurements show that the epitaxial YBCO films have single in-plane orientation with YBCO [100]LSCO [100] and LSCO [100]YSZ [110]. The real-time resistance measurements reveal that with LSCO buffer layers the initial formation of the YBCO ultra-thin films changes from the island growth to the layer-by-layer growth.     

Perpendicularly oriented barium ferrite thin films with low microwave loss,prepared by pulsed laser deposition

Barium ferrite(Ba M) thin films are deposited on platinum coated silicon wafers by pulsed laser deposition(PLD).The effects of deposition substrate temperature on the microstructure,magnetic and microwave properties of Ba M thin films are investigated in detail.It is found that microstructure,magnetic and microwave properties of Ba M thin film are very sensitive to deposition substrate temperature,and excellent Ba M thin film is obtained when deposition temperature is 910℃ and oxygen pressure is 300 m Torr(1 Torr = 1.3332×10~2Pa).X-ray diffraction patterns and atomic force microscopy images show that the best thin film has perpendicular orientation and hexagonal morphology,and the crystallographic alignment degree can be calculated to be 0.94.Hysteresis loops reveal that the squareness ratio(M_r/M_s) is as high as 0.93,the saturated magnetization is 4004 Gs(1 Gs = 10~4T),and the anisotropy field is 16.5 kOe(1 Oe = 79.5775 A·m~(-1)).Ferromagnetic resonance measurements reveal that the gyromagnetic ratio is 2.8 GHz/kOe,and the ferromagnetic resonance linewith is108 Oe at 50 GHz,which means that this thin film has low microwave loss.These properties make the Ba M thin films have potential applications in microwave devices.     

High TcYBa2Cu3O7−δ superconducting transition-edge microbolometers

High T_c superconducting thin film YBa₂Cu₃O_7−δ (YBCO) bolometers have been fabricated on various substrates such as MgO, LaAlO₃, YSZ and Si using laser ablation technique. Performance of these IR bolometers operating with a Joule-Thomson refrigerator has been investigated. Measurements of the responsivity and low frequency noise near T_c in the current biased YBCO bolometers show that reliable devices can be fabricated. Measured noise equivalent power (NEP), for YBCO/YSZ bolometer, reaches 6 × 10⁻¹⁰W/Hz^1/2 at 165 Hz and has a responsivity of 60 V/W with a blackbody source. This performance is comparable to that of the optimized pyroelectric detectors. The characteristics of YBCO films deposited on Si substrates reveal that superconducting thin film multi-elements or focal plane array with silicon integrated readout circuit are feasible. Such bolometers exhibit NEP of 7 × 10⁻⁹W/Hz^1/2, and significant improvement appears possible. Electrical measurements show no noticeable film degradation after the bolometer is exposed to atmosphere for three months.     

Pulsed laser deposition of Pb(Zr0.52Ti0.48)O3 thin film on cobalt ferrite nano-seed layered Pt(111)/Si substrate: effect of oxygen pressure

The effect of oxygen pressure during pulsed laser deposition of Pb(Zr_0.52Ti_0.48)O₃ (PZT) thin films on CoFe₂O₄ nano-seed layered Pt(111)/Si substrate was investigated. The PZT film deposited at oxygen pressure lower than 25 mTorr is identified as both perovskite and pyrochlore phases and the films deposited at high oxygen pressure (50-100 mTorr) show the single-phase perovskite PZT that has a perfect (111)-orientation. In addition, the film deposited at P_O2 of 50 mTorr has a uniform surface morphology, whereas the film deposited at P_O2 of 100 mTorr has a non-uniform surface morphology and more incompacted columnar cross-section microstructure. The polarization of film deposited at 100 mTorr is higher than that deposited at 50 mTorr, but shift of the hysteresis loop along the electrical field axis in the film deposited at P_O2 of 100 mTorr is larger than that of the film deposited at P_O2 of 50 mTorr.     

GaSb基PECVD法制备SiO2薄膜的应力研究

为了实现在GaSb衬底上获得低应力的SiO₂薄膜,研究了等离子体增强化学气相沉积法（PECVD）在晶格失配较大的GaSb衬底上沉积SiO₂薄膜的应力情况。通过改变薄膜沉积时的工艺条件,如反应温度、射频功率、反应压强、气体流量比,并基于曲率法模型,对镀膜前后的曲率半径进行了实验测量,利用Stoney公式计算相关应力值并绘制应力变化曲线。详细讨论了PECVD工艺条件的改变对SiO₂薄膜应力所产生的影响。同时通过在Si衬底上沉积SiO₂薄膜,对比分析了导致薄膜应力产生的因素及变化过程。实验结果表明,在沉积温度为300℃、射频功率为20 W、腔体压强为90 Pa、气体流量比SiH₄/N₂O为125/70 cm³·min^-1的工艺参数下,PECVD法在GaSb衬底上沉积的SiO₂薄膜应力相对较小。     

光学玻璃基底原子层同质材料沉积薄膜光谱及激光诱导损伤特性研究

通过原子层沉积技术在熔石英玻璃表面制备了同质材料的单层SiO₂薄膜,对光学薄膜的物理化学性质和强激光辐照下的激光诱导损伤性能进行了深入研究。实验中采用双叔丁基氨基硅烷（BTBAS）和臭氧（O₃）作为反应前驱体,在熔石英光学元件表面进行了SiO₂薄膜的原子层沉积工艺研究,以不同沉积温度条件制备了一系列膜样品。首先对原子层沉积特性和薄膜均匀性展开了研究,发现薄膜生长厚度与沉积循环次数之间符合线性生长规律,验证了制备薄膜的原子级逐层生长特性,并且表面沉积膜层的均匀性很好,其测得膜厚波动不超过2%。然后针对不同温度条件下沉积的SiO₂薄膜,对其粗糙度及各类光谱特性展开了研究,对比结果表明：样品的表面粗糙度在镀膜后有轻微的降低;薄膜样品在200～1 000 nm范围内具有出色的透过率,均超过90%并逐渐趋近于93.3%,且其透射光谱与在裸露熔石英衬底上测得的光谱没有明显差异;镀膜前后荧光光谱和傅里叶变换红外光谱的差异证实了原子层沉积SiO₂膜中点缺陷（非桥键氧、氧空位、羟基等）的存在,这将会影响薄膜耐损伤性能。最后对衬底和膜样品进行了紫外激光诱导损伤测试,损伤阈值的变化表明熔石英元件表面沉积薄膜后的激光损伤性能有所降低,其零概率损伤阈值从31.8 J·cm-2减小到20 J·cm-2左右,与光谱缺陷情况表征相符合。薄膜中点缺陷部位会吸收紫外激光能量,导致局域温度升高,进而出现激光诱导损伤现象并降低抗激光损伤阈值。在选定的沉积温度范围内,较高温度条件下沉积的SiO₂薄膜其激光诱导损伤性能更好,可以控制沉积温度条件使得元件的抗损伤性能更为接近衬底本身,后续有望通过其他反应参数的优化来获得薄膜抗损伤性能的进一步提升。     

The effect of Ag or Au overlayers on underlying YBa2Cu3O7 thin films

Although Ag and Au are commonly used to provide low-resistance contacts to YBa₂Cu₃O₇ (YBCO), their effect on the electrical properties of the underlying YBCO has been largely neglected. Epitaxial YBCO thin films on LaAlO₃ substrates were used in this study. Thin (50 nm) and thick (1 μm) layers of Ag or Au were deposited as overlayers, and in some cases annealed in oxygen at 550–650°C. Compared to samples with no metal overlayers, for both Ag and Au the normal-state parameters changed (resistivity, its temperature coefficient, and the transition width), whereas the transition temperature and critical current density remained unaltered. These results are encouraging for the use of these metals as contacts and/or conducting overlayers on YBCO.     

High pyroelectric Ba0.65Sr0.35TiO3 thin films with Ba0.65Sr0.35RuO3 seeding-layer for monolithic ferroelectric bolometer

Ba_0.65Sr_0.35TiO₃ (BST) thin films were deposited by RF sputtering with a very thin Ba_0.65Sr_0.35RuO₃ (BSR) seeding-layer on Pt/Ti/SiO₂/Si substrate. The crystallization of BST thin films and the surface morphology of BSR seeding-layer were characterized by X-ray diffraction (XRD) and atomic force microscopy (AFM), respectively. XRD patterns show that the BSR seeding-layer affected the orientation of BST thin film, which is highly a-axis textured. It was also found that the BSR seeding-layer had a marked influence on the dielectric properties of BST thin films. Comparing with BST thin films directly deposited on Pt electrode, the dielectric relaxation can be suppressed and dielectric constant increased due to a possible reduction of interface oxygen vacancies at BST/BSR interface. Moreover, J–V measurement indicates that the leakage current density of BST thin films on BSR seeding-layer were greatly reduced compared with that of BST thin films directly on Pt electrodes. The pyroelectric coefficient of BST thin films with BSR seeding-layer is 7.57 × 10⁻⁷ C cm⁻² K⁻¹ at 6 V/μm at room temperature (RT). Our results reveal that high pyroelectric property of BST thin film could be achievable using BSR seeding-layer as a special buffer.     

高压退火对0.65PMN-0.35PT薄膜结构、形貌及电学性能的影响

利用射频磁控溅射技术在LaNiO₃/SiO₂/Si(100)基底上制备了厚 度约为250 nm的0.65PMN-0.35PT(PMN-PT)薄膜. 研究高压氧氛围退火方式对PMN-PT薄膜晶体结构、形貌以及电学性能的影响. 经过XRD测试发现,在高压氧气氛围中, 温度为400℃下退火后的PMN-PT薄膜具有纯的钙钛矿相结构, 具有完全的(100)择优取向, 且衍射峰尖锐, 表明经过高压退火后的薄膜结晶极为充分. SEM表面形貌测试结果显示, 经高压退火处理的PMN-PT薄膜表面呈现出棒状或泡状的形貌. 铁电性能测试表明: 氧气氛围压强4 MPa, 退火时间4h的PMN-PT薄膜样品具有较好的铁电性能, 其剩余极化强度P_r达到10.544 μC/cm², 且电滞回线形状较好, 但漏电流较大, 这可能是由于其微结构所导致.同时介电测试发现: PMN-PT薄膜样品具有极好的介电性能, 其在1 kHz下测试的介电常数ε_r达到913, 介电损耗tgδ 较小, 仅为0.065. 关键词： 射频磁控溅射 高压退火 0.65PMN-0.35PT 介电     

低能离子对高温超导YBa_2Cu_3O_(7-δ)薄膜的表面改性和机理

低能氩离子束轰击并后退火处理的离子束表面改性,会影响高温超导薄膜的表面结构和超导特性,但是其中的深刻微观机理不清楚.本文通过连续改变离子束轰击时间,系统研究了离子束表面改性对于超导膜结构和临界电流密度的影响.通过扫描电子显微镜、X射线衍射、J_(c-scanning)测试表征样品的结构特性和超导特性,并得出内应变、氧空位缺陷等参量.研究表明,经过表面改性的钇钡铜氧(YBa_2Cu_3O_(7-δ),YBCO)薄膜,随轰击时间增加表面形貌会变得更加均匀致密,a轴晶粒消失,并且临界电流密度有了显著的提高.由化学键收缩配对模型分析得出,临界电流密度的提高与薄膜内应变增大和引发的局部YBCO结构中Cu—O键收缩有关.     

TEM investigation of YBa2Cu3O7 thin films on SrTiO3 bicrystals

YBa₂Cu₃O₇ films in c-axis orientation on bicrystalline SrTiO₃ substrates are investigated by TEM. The films and the substrates are examined in cross-section and in plane view. The grain boundary of the bicrystal substrate contains (110) faceted voids, but is otherwise straight on a nanometer scale. Contrary to this, the film grain boundary is not straight grain boundary can be up to 100 nm for a 100 nm thick film. The deviation from the intended position of the YBCO grain boundary can already occur at the film/substrate interface where it can be as much as ±50 nm.     

高温氢退火还原V2O5制备二氧化钒薄膜及其性能的研究

过渡金属氧化物二氧化钒(VO₂)在温度340 K附近会发生金属绝缘体的转变(metal-insulator transition, MIT). 基于金属绝缘体的转变性质, VO₂薄膜材料具有很好的应用前景. 本文首先采用脉冲激光沉积制备了高质量的V₂O₅薄膜, 再通过高温氢退火还原V₂O₅薄膜制备出VO₂多晶薄膜. 研究了不同的退火温度、退火时间、退火气氛对VO₂薄膜制备的影响, 采用X射线衍射、X射线光电子能谱、变温电阻特性测量等手段对样品进行分析, 发现在H₂(5%)/Ar退火气氛下, 在一定的退火温度范围内(500–525 ℃), 退火 3 h, 得到了B相和M相共存的VO₂薄膜, 具有M相的VO₂的MIT特性, 而相同退火温度下退火时间达到4.5 h, 薄膜完全变成B相的VO₂. 通过纯Ar气氛下对B相VO₂再退火, 得到了转变温度为350 K, 电阻突变接近4个数量级的M相的VO₂薄膜. 实现了VO₂的B相和M相的相互转变. 关键词： 2薄膜')" href="#">VO₂薄膜 金属绝缘体转变 氢退火