超声浸渍对费托合成Co/Zr/SiO2催化剂性能的影响

采用超声浸渍法制备了费托合成Co/Zr/SiO2催化剂,考察了超声波功率对催化剂费托反应性能的影响,并运用N2物理吸附、X射线衍射、H2程序升温脱附、H2程序升温还原和透射电子显微镜对催化剂进行了表征,结果表明,超声波处理可以增大催化剂的比表面积,减小金属Co的粒径,并使其较为均匀地分散于载体表面,其中以高功率超声波作...     

溶剂诱导翻转Pickering乳液用于原位循环使用酶催化剂

Separation and recycling of catalysts are crucial for realizing the objectives of sustainable and green chemistry but remain a great challenge, especially for enzyme biocatalysts. In this work, we report a new solvent-induced reversible inversion of Pickering emulsions stabilized by Janus mesosilica nanosheets (JMSNs), which is then utilized as a strategy for the in situ separation and recycling of enzymes. The interfacial active solid particle JMSNs is carefully characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), nitrogen sorption experiments, Fourier transform infrared (FT-IR) spectroscopy, and thermogravimetric analysis (TGA).The JMSNs are demonstrated to show order-oriented mesochannels with a large specific surface area, and the hydrophobic octylgroup is selectively modified on one side of the nanosheets. Furthermore, the inversion is found to be a fast process that is strongly dependent on the interfacial activity of the solid emulsifier JMSNs. Such a phase inversion is also a general process that can be realized in various oil/water phasic systems, including ethyl acetate-water, octane-water, and cyclohexane-water systems. By carefully analyzing the capacity of JMSNs with different surface wettabilities for phase inversion, a triphase contact angle (θ) close to 90° and a critical oil-water ratio of 1 : 2 are identified as the key factors to achieve solvent-induced phase inversion via a catastrophic phase inversion mechanism. Importantly, this reversible phase inversion is suitable for the separation and recycling of enzyme biocatalysts that are sensitive to changes in the reaction medium. Specifically, during the reaction, the organic substrates are dissolved in the oil droplets and the water-soluble catalysts are dispersed in the water phase, while a majority of the product is released into the upper oil phase and the enzyme catalyst is confined inside the water droplets in the bottom layer after phase inversion. The perpendicular mesochannels of JMSNs provide a highly accessible reaction interface, and their excellent interfacial activity allows for more than 10 rounds of consecutive phase inversions by simply adjusting the ratio of oil to water in the system. Using the enzymatic hydrolysis kinetic resolution of racemic acetate as an example, our Pickering emulsion system shows not only a 3-fold enhanced activity but also excellent recyclability. Because no sensitive chemical reagents are used in this phase inversion process, the intrinsic activities of the catalysts can be preserved even after seven cycles. The current study provides an alternative strategy for the separation and recycling of enzymes, in addition to revealing a new innovative application for Janus-type nanoparticles.     

溶胶-凝胶法制备MoP/SiO2催化剂加氢脱硫催化活性的研究

以正硅酸乙酯为硅源,以钼酸铵和磷酸二氢铵为钼源和磷源,采用溶胶-凝胶法,经干燥、焙烧,程序升温还原制备得到二氧化硅负载磷化钼(MoP)催化剂。以噻吩、二苯并噻吩为模型化合物,对负载催化剂的加氢脱硫活性进行评价,考察了负载量、反应压力、反应温度等因素对催化活性的影响。实验结果表明,MoP/SiO₂催化剂Mo的最佳负载量为20%,升高反应压力和温度均有利于提高二苯并噻吩的转化率,但降低了产物中联苯的含量。     

巯基功能化介孔材料高效锚定钯负载型催化剂的制备及其苯酚加氢催化性能

以含巯基官能团有机硅烷修饰的介孔材料MCM-41和SBA-15为载体, 采用浸渍-氢气还原法制备了高分散和高活性的负载型Pd催化剂. X射线衍射、N₂吸附-脱附和透射电子显微镜表征结果显示, 所制Pd催化剂Pd-SH-MCM-41和Pd-SH-SBA-15具有很好的长程有序结构、分布均匀的孔径、高比表面积及高度分散的Pd颗粒. 苯酚加氢反应结果表明, 以Pd-SH-MCM-41和Pd-SH-SBA-15为催化剂时, 在80℃, 1.0MPa反应1h, 苯酚转化率达99%以上, 环己酮选择性为98%. 它们的催化活性为商业Pd/C催化剂的5倍, Pd/MCM-41和Pd/SBA-15催化剂的3倍. 这可归因于介孔材料表面修饰的巯基官能团对Pd的锚定作用, 避免了Pd颗粒的团聚, 使其高度分散在介孔材料上.     

热处理对富硅氧化硅薄膜中硅纳米晶形成的影响

采用磁控溅射法制备了富硅氧化硅薄膜, 然后分别经过一步热处理、两步热处理和快速热处理制备了镶嵌有硅纳米晶的氧化硅薄膜. 实验结果表明, 在硅含量为～ 42.63 at.%的富硅氧化硅薄膜中, 三种热处理均能形成10¹²/cm²量级的硅纳米晶. 其中在两步热处理中, 硅纳米晶的密度最高, 达到2.2× 10¹²/cm², 并且尺寸均匀、结晶完整性好; 一步热处理后的样品中, 硅纳米晶密度较低, 并且部分纳米晶结晶不充分; 快速热处理后的样品中, 硅纳米晶密度最低、尺寸分布不均匀, 并且存在孪晶结构. 分析认为, 热处理初始阶段的形核过程对纳米晶的密度及微观结构有着重要的影响, 两步热处理中的低温段促进了纳米晶的成核, 有助于形成高密度高质量硅纳米晶.     

Magnetic Tunnel Junctions with MgO／Al-O Composite Barriers

Magnetic tunnel junctions (MTJs) with structures of Ta(5 nm)/Cu(30nm)/Ta(5 nm)/Ni79Fe21 (5 nm)/Ir22Mn78 (12 nm)/Co62Fe20B18 (4 nm)/MgO(d)/Al(0.8 nm)-oxide/Co62Fe20B18 (6 nm)/Cu(30 nm)/Ta(5 nm) on a thermally oxidized Si wafer substrate were fabricated by magnetron sputtering and photolithographic patterning method. The tunnel magnetoresistance (TMR) and the bias dependence of TMR at room temperature for the MTJs with different thickness d of MgO are investigated. TMR values of over 50% as high as those of the MTJs with pure Al-O barrier and the TMR-voltage curve asymmetries, which vary with the increase of d, are observed in the MTJs with hybrid barriers after annealing at 265℃ for an hour. The dependences of TMR, resistance and coercivity of the MTJs with composite barriers on temperature are also investigated.     

Pd/MoO3-TiO2/SiO2光催化CO2与C2H6合成烃类氧化物的反应性能

 采用化学反应改性和等体积浸渍法制备了负载型Pd/MoO3-TiO2/SiO2催化剂,并用IR,FT-Raman,TPD-MS,UV-Vis DRS和活性评价等方法研究了催化剂的表面结构、光吸收性能、化学吸附性能及光催化CO2与C2H6合成烃类氧化物的反应性能. 结果表明,SiO2负载的MoO3和TiO2之间存在着强相互作用,并能部分形成Mo-O-Ti键联,使得两种氧化物微粒均匀分布于载体表面; 表面MoO3和TiO2的复合作用使TiO2/SiO2的吸光带边红移,扩展了其吸光域,Pd的引入明显提高了固体材料的可见光吸收率; CO2和C2H6能较好地吸附在催化剂表面,在紫外光的激发下,CO2吸附态能解离生成CO,而C2H6单位吸附态能部分转化为C和H同时吸附在两个晶格氧上的双位吸附态; 光促CO2和C2H6反应主要生成丙醛、乙醇和乙醛; 在合适的条件下,烃类氧化物的选择性可超过90%.     

TiO2/SiO2/γ-Fe2O3-SiO2磁性光催化剂的制备与表征

 A γ-Fe2O3-SiO2 composite was prepared by sol-gel method followed by calcination at 700 ℃ for 30 min starting from tetraethoxysilane and iron nitrate. Upon further coating with SiO2 and TiO2, a TiO2/SiO2/γ-Fe2O3-SiO2 magnetic photocatalyst was obtained. XRD results show that Fe in the composite converts to the γ-Fe2O3 phase up to a processing temperature of 700 ℃, and further increase in temperature results in the formation of the α-Fe2O3 phase. The TiO2/SiO2/γ-Fe2O3-SiO2 samples obtained are monodisperse spherical particles with 200～250 nm diameter, well coated firstly by an amorphous SiO2 layer and then by an anatase TiO2 layer. The TiO2/SiO2/γ-Fe2O3-SiO2 particles retain their magnetic property well and show high activity for the photocatalytic degradation of salicylhydroxamic acid.     

CO2气氛下负载型Cr2O3催化剂上乙苯脱氢制苯乙烯反应

 采用浸渍法制备了负载型Cr2O3/Al2O3和Cr2O3/SiO2催化剂,并考察了催化剂在CO2气氛下催化乙苯脱氢制苯乙烯反应的活性. 结果表明,Cr2O3/Al2O3的催化活性高于Cr2O3/SiO2. 这可能是由于Cr2O3在Al2O3载体表面的分散度大大高于在SiO2表面的分散度. 催化剂的催化活性与Cr2O3的负载量有关,在w(Cr2O3)=25%时,Cr2O3/Al2O3的催化活性最高. CO2气氛对乙苯脱氢反应有明显的促进作用; 在CO2气氛下,Cr6+物种可能是催化乙苯脱氢反应活性位的前驱体.     

Ru-B/SiO2非晶态催化剂应用于液相葡萄糖加氢制山梨醇

 采用浸渍法结合KBH4还原法制备了Ru-B/SiO2非晶态催化剂(3.14%Ru),并将其用于液相葡萄糖加氢制山梨醇反应. 结果表明,该催化剂具有良好的热稳定性,且其催化活性远高于Raney Ni和Ni-B/SiO2非晶态催化剂,山梨醇的选择性接近于100%,显示出良好的工业化应用前景. 通过与晶态Ru-B/SiO2及Ru/SiO2的催化活性进行比较,并结合ICP,XRD,DSC,SEM,XPS及氢吸附等表征结果,初步讨论了非晶态合金结构和表面电子态对催化剂活性的促进作用.