 考察了Ni－B／SiO2非晶态催化剂在高压液相硝基苯加氢制苯胺反应中的催化活性和选择性．研究表明,该催化剂不仅具有很高的催化活性,而且对苯胺的选择性较高,优于RaneyNi以及其它Ni基催化剂．晶化导致催化剂失活．载体的存在不仅能提高催化剂的分散度,而且能对非晶态结构起稳定化作用;将催化剂保存在乙醇中可保持其活性不变．结合催化剂的表征,讨论了Ni－B／SiO2非晶态催化剂的催化性能与其结构的关系．     

苯部分加氢制环己烯新型Ru-B/MOF催化剂

制备了多种金属-有机骨架(MOF)材料,采用浸渍-化学还原法制备了非晶态Ru-B/MOF催化剂,考察了它们在苯部分加氢反应中的催化性能.催化性能评价结果表明,这些催化剂的初始反应速率(r0)顺序为Ru-B/MIL-53(Al)Ru-B/MIL-53(Al)-NH2Ru-B/UIO-66(Zr)Ru-B/UIO-66(Zr)-NH2Ru-B/MIL-53(Cr)Ru-B/MIL-101(Cr)Ru-B/MIL-100(Fe),环己烯初始选择性(S0)顺序为Ru-B/MIL-53(Al)≈Ru-B/MIL-53(Cr)Ru-B/UIO-66(Zr)-NH2Ru-B/MIL-101(Cr)Ru-B/MIL-53(Al)-NH2Ru-B/UIO-66(Zr)≈Ru-B/MIL-100(Fe).催化性能最好的Ru-B/MIL-53(Al)催化剂上的r0和S0分别为23 mmol·min-1·g-1和72%.采用多种手段,对催化性能差异最为显著的Ru-B/MIL-53(Al)和Ru-B/MIL-100(Fe)催化剂的物理化学性质进行了表征.发现MIL-53(Al)载体能够更好地分散Ru-B纳米粒子,粒子的平均尺寸为3.2 nm,而MIL-100(Fe)载体上Ru-B纳米粒子团聚严重,粒径达46.6 nm.更小的粒径不仅能够提供更多的活性位,而且也有利于环己烯选择性的提高.对Ru-B/MIL-53(Al)催化剂的反应条件进行了优化,在180°C和5 MPa的H2压力下,环己烯得率可达24%,展示了MOF材料用作苯部分加氢催化剂载体的良好前景.     

壳聚糖表面修饰的SiO2负载Ni-B非晶态合金的制备及催化性能

以壳聚糖(CS)对SiO2进行表面修饰, 采用浸渍还原法制备了负载型Ni-B非晶态合金催化剂(Ni-B/CS/SiO2), 并采用XRD、FTIR、电感耦合等离子体发射光谱(ICP)、BET、XPS、TEM、SAED等表征方法研究了催化剂的非晶性质、原子组成、尺寸分布及粒径大小等. 考察了催化剂对糠醇加氢制四氢糠醇反应的催化性能, 并与没有壳聚糖修饰的Ni-B/SiO2催化剂及Raney Ni催化剂进行了对比. 结果表明, 加入壳聚糖制得的Ni-B/CS/SiO2催化剂的活性组分Ni-B团簇粒径更小, 表面活性组分浓度更高, 催化活性更高.     

负载型Ru基催化剂用于丙酮常压气相加氢

采用气相脉冲法，首次将非晶态Ru-B合金催化剂用于催化丙酮常压气相加氢反应．研究结果表明负载型Ru-B合金催化剂在较低的反应温度下表现出了很高的活性及生成异丙醇的选择性；负载在γ-Al2O3上的非晶态Ru-B合金与晶态的Ru相比，活性及异丙醇的产率都有很大提高；采用不同载体的非晶态Ru-B合金催化剂活性不同，在所选定的反应温度下，以膨润土为载体的Ru-B合金催化剂的活性与异丙醇的产率均高于以γ-Al2O3作载体的．用程序升温还原(TPR)，程序升温脱附(TPD)，等离子体发射光谱(ICP)等方法对催化剂表面性质及含量进行了表征．     

Ni-P/SiO_2催化剂晶化过程及其加氢活性研究

采用化学还原法制备了负载型Ni－P／SiO2非晶态合金催化剂．应用ICP、BET、氢氧滴定法、XRD、SEM、XPS研究了上述催化剂在高温晶化过程中的表面结构、表面形貌和表面电子态的变化。测定了Ni－P／SiO2非晶态合金晶化前后对其液相苯甲醛加氢反应催化活性和选择性,并讨论了非晶态合金催化剂晶化过程中结构变化对催化性能的影响．     

Ni-Mo2N/SiO2复合纳米催化剂的制备及其对四氢萘加氢的催化活性

采用程序升温氮化法制备了Mo2N/SiO2,在此基础上负载Ni盐,制备了Ni-Mo2N/SiO2复合纳米催化剂,并考察了催化剂对四氢萘加氢的催化活性.结果表明,与Ni2Mo3N/SiO2及Ni/SiO2催化剂相比,Ni-Mo2N/SiO2复合催化剂具有较高的催化活性.采用"分离床"方法研究了Ni和Mo2N对四氢萘加氢活性的影响.通过X射线粉末衍射、透射电镜、氢吸附、元素分析和比表面积测定等技术对Ni-Mo2N/SiO2催化剂进行了表征.结果表明,与Ni/SiO2催化剂相比,Ni-Mo2N/SiO2复合催化剂中Ni的分散度并未提高;催化活性的提高归因于Ni与Mo2N在四氢萘加氢中的协同作用.氮化物的引入增加了芳烃吸附活性位的数目.提出了四氢萘在Ni-Mo2N/SiO2催化剂上的可能加氢机理.     

非晶态铁基固体碱催化剂的酯交换性能

通过化学还原法和共沉淀法分别制备了非晶态和晶态的FeCeOx/SiO2固体碱催化剂。与晶态的FeCeOx/SiO2相比,非晶态的FeCeOx/SiO2催化剂对梨醇酯与甲醇的酯交换活性显著提高。通过电感耦合等离子体质谱(ICP-MS)、N2吸附-脱附、透射电子显微镜(TEM)结合选区电子衍射(SAED)、X射线衍射(XRD)、X射线光电子能谱(XPS)、CO2-TPD和NH3-TPD等对催化剂进行表征。结果表明催化剂的活性与其碱性密切相关,非晶态FeCeOx/SiO2显示出相对于晶态FeCeOx/SiO2更强的碱性。使用非晶态FeCeOx/SiO2催化剂进行梨醇酯酯交换反应,在130℃下反应10 h,梨醇酯的转化率达到95%,异戊烯醇的选择性达到96%。在重复使用10次后,催化剂活性基本不变。对新鲜的和套用10次后的FeCeOx/SiO2催化剂进行X射线衍射分析,表明该催化剂在套用10次后仍未晶化,证实其具有良好的稳定性,说明该催化剂在非均相催化酯交换反应中具有应用价值。     

Pd-SiW12/SiO2催化乙烯气相直接氧化制乙酸:SiO2孔结构的影响

采用二三种不同孔结构的Si02制备了Pd-SiW12/SiO2催化剂,通过x射线衍射、N2物理吸附、吡啶吸附红外光谱以及H2脉冲化学吸附对催化剂进行了表征,并考察了Pd-SiW12/SiO2催化剂上乙烯直接氧化制乙酸反应性能.结果表明,以孔径较大的粗孔硅胶为载体制备的Pd-SiW12/SiO2催化剂显示出最高的催化活性,乙酸收率为145.2g/(L·h).这是由于Pd在粗孔硅胶载体表面良好的分散使其具有较高的催化活性.     

微波辅助Ni-B/SiO2非晶态催化剂的制备及其在硝基苯加氢中催化性能的研究

采用微波辐射干燥浸渍法获得的Ni2 /SiO2,再由液相KBH4还原制备Ni-B/SiO2非晶态催化剂,在液相硝基苯加氢反应中,该催化剂对苯胺的选择性为100%,催化活性显著高于由传统加热法制备的Ni-B/SiO2.根据XRD、XPS、SEM和氢吸附等表征,两种催化剂具有相似的活性中心本质,催化性能的不同主要归因于分散度的区别.与传统加热法相比,微波加热具有受热均匀以及增强Ni2 与载体SiO2相互结合力的特点,导致Ni-B/SiO2(MW)分散度增加,并能减少催化反应过程中活性相的脱落流失,延长催化剂使用寿命.     

Co-B/SBA-15非晶态催化剂应用于肉桂醛选择性加氢的研究

以介孔材料SBA-15作为载体,采用浸渍法制备Co-B/SBA-15非晶态催化剂,该样品仍然保持SBA-15特有的有序规整孔道结构,Co-B非晶态合金颗粒均匀分布在孔道内壁,采用普通SiO2载体制备的Co-B/ SiO2,Co-B颗粒主要分布在外表面.在肉桂醛选择性加氢制肉桂醇中,Co-B/SBA-15的催化活性和对肉桂醇的最佳得率显著高于Co-B/SiO2,主要归因于活性位的高分散,规整的孔道结构,以及独特的活性位团簇结构和电子态.     

超细Pd—B／SiO2非晶态合金加氢反应的催化活性

采用浸渍法并通过ＫＢＨ４还原制备超细Ｐｄ－Ｂ／ＳｉＯ２非晶态合金催化剂,以硝基苯加氢生成苯胺为目标反应,考察了上述催化剂的活性和选择性及热稳定性,并与晶态Ｐｄ－Ｂ／ＳｉＯ２和Ｐｄ／ＳｉＯ２催化剂及非负载型Ｐｄ－Ｂ非晶态合金催化剂进行了比较。     

Liquid phase glucose hydrogenation to -glucitol over an ultrafine Ru-B amorphous alloy catalyst

A Ru-B amorphous alloy catalyst in the form of ultrafine particles was prepared by chemical reduction of RuCl₃ with borohydride in aqueous solution, whose amorphous structure was confirmed by XRD, DSC, and SAED. Heating pretreatment resulted in the rapid crystallization and the deep decomposition of the Ru-B amorphous alloy as well as the abrupt decrease in the surface area due to the gathering of small particles at high temperature. XPS spectra revealed that partial electrons transferred from the alloying B to the metallic Ru in the as-prepared Ru-B sample. In comparison with other catalysts, the as-prepared Ru-B amorphous catalyst exhibited excellent activity and perfect selectivity to -glucitol as well as superior lifetime during the liquid phase glucose hydrogenation, showing its potential application in industrial process. The higher activity of the Ru-based catalysts than that of other metal catalysts, such as Co-B and Ni-B amorphous catalysts as well as Raney Ni catalysts, demonstrated that the metallic Ru was more active than both metallic Ni and Co for the glucose hydrogenation. Meanwhile, the Ru-B amorphous catalyst exhibited higher activity than its corresponding crystallized Ru-B and pure Ru powder catalysts, showing the promoting effects of both the amorphous structure and the electronic interaction between the metallic Ru and the alloying B, which was briefly discussed based on the kinetic studies and various characterizations.     

Hydrogenation of phenylpyruvic acid to phenylalanine catalyzed by Ni-B/SiO2

Phenylalanine （Phe） is a significant amino acid that cannot be synthesized by human themselves but must be taken from environment. It was initially found that the nanosized amorphous Ni-B/SiO2 alloy prepared by the chemical reduction method was an effective catalyst for the preparation of Phe from phenylpyruvic acid （PPA） by amination and hydrogenation. It has been found that the amorphous Ni-B/SiO2 alloy catalyst exhibits superior activity and selectivity to the traditional catalysts Raney Ni and Urushibara nickel. The effects of reaction time, amounts of catalysts and ammonia solution, reaction temperature, and H2 pressure on the reaction have been investigated systematically. The results indicated that the yield of Phe was 97.9%, and the selectivity for Phe reached 98.9% when the reaction was carried out for 3 h at 333 K and 2.0 MPa of H2 with m（Cat.） ： m（PPA） = 0.6 ： 1.0 and n（NH3） ： n（PPA） = 3 ： 1. The catalysts were characterized by XRD, AAS, XPS, BET, and TEM, and the relationship between the catalyst structure and the catalytic activity was discussed in detail. It was found that the reason why Ni-B/SiO2 amorphous alloy catalyst was much more active for the preparation of Phe could be accounted for by the presence of electron-rich Ni due to electron donation from alloying B; the smaller size of Ni-B particles, the larger specific surface area of Ni-B/SiO2.     

金前驱液pH值对Au-Pd/SiO2催化剂上噻吩加氢脱硫活性的影响

考察了金前驱液的pH值对Au-Pd/SiO2双金属催化剂用于噻吩加氢脱硫反应活性的影响,应用N2吸附,X-光粉末衍射(XRD)、程序升温还原(TPR)等技术对该催化剂的物性与结构进行了表征.发现当金前驱液的pH值为7时制得的双金属催化剂具有较好的加氢脱硫活性,并具有最小的孔径,该催化剂以PdO相与Au0相共存.与Pd/SiO2催化剂相比,Au-Pd/SiO2催化剂的稳定性明显提高.虽然AuxPdy合金相的生成对提高双金属催化剂的脱硫活性不利,但能明显改善催化剂的抗硫中毒能力.     

担载型钌催化剂吸附CO性能的原位红外研究

用原位红外研究了ＣＯ的吸附与脱附，ＣＯ／Ｈ２的共吸附及反应，考察了焙烧温度对Ｒｕ／Ａｌ２Ｏ３及Ｒｕ／ＳｉＯ２催化剂的影响，结果表明，经不同温度焙烧的催化剂样品，其吸附性能有很大差别。随着焙烧温度的升高，金属－载体相互作用增强，导致ＣＯ吸附量减少。Ｒｕ／Ａｌ２Ｏ３吸附的ＣＯ较稳定，而Ｒｕ／ＳｉＯ２吸附的ＣＯ在高温易脱附。各不同ＣＯ吸会态间、多重态更易发生反应。在未焙烧的Ｒｕ／ＳｉＯ２低ＣＯ／Ｈ２反应     

SiO2改性的V2O5-MoO3/ TiO2催化剂抗碱中毒性能研究

以陶瓷为骨架,用溶胶凝胶法和浸渍法制备了V₂O₅-MoO₃/ TiO₂催化剂,并用SiO₂进行改性。采用浸渍法模拟碱K中毒,研究了SiO₂改性前后催化剂中毒脱硝效率的变化,并通过BET、H₂-TPR、NH₃-TPD等技术手段对催化剂进行了表征。结果表明,加入SiO₂后,催化剂的比表面积明显提高。SiO₂改性后新鲜催化剂还原温度向低温方向迁移10 ℃左右,氧化还原能力得到了提高,其表面酸强度和酸量也得到较大的提高。反应评价结果表明,SiO₂改性可以提高催化剂抗碱中毒的性能。     

高选择性苯乙酮加氢Ni-Sn-B/SiO2非晶态催化剂的制备及表征

采用化学还原法制备了一系列三元非晶态Ni-Sn-B／SiO2催化剂,并考察了Sn含量对催化剂的苯乙酮选择加氢制备苯乙醇反应的活性及选择性的影响,同时对Sn改性前后的催化剂进行了系统的表征．XRD结果表明,Sn物种在催化剂表面高度分散,没有改变催化剂的非晶态结构．SEM结果也表明Sn的修饰并不改变非晶态合金的特征形貌．在苯乙酮加氢反应中,当Sn／SiO2=10wt％时,羰基加氢产物苯乙醇的得率可高达97．5％,且苯环加氢产物仅为0．5％,显示了良好的羰基加氢选择性．结合XPS结果,我们将该催化剂优异的催化性能归因于非晶态合金独特的电子结构、活性组分的高度分散及催化剂中Sn氧化物对羰基的选择性活化．