Comparison of the formation epitaxial graphenes on Si- and process and properties of C-face 6H-SiC substrates

In this paper,the epitaxial graphene layers grown on Si-and C-face 6H-SiC substrates are investigated under a low pressure of 400 Pa at 1600 C.By using atomic force microscopy and Raman spectroscopy,we find that there are distinct differences in the formation and the properties between the epitaxial graphene layers grown on the Si-face and the C-face substrates,including the hydrogen etching process,the stacking type,and the number of layers.Hopefully,our results will be useful for improving the quality of the epitaxial graphene on SiC substrate.     

N型4H-SiC同质外延生长

利用水平式低压热壁CVD (LP-HW-CVD) 生长系统,台阶控制生长和衬底旋转等优化技术,在偏晶向的4H-SiC Si(0001) 晶面衬底上进行4H-SiC同质外延生长,生长温度和压力分别为1550℃和10⁴ Pa,用高纯N₂作为n型掺杂剂的4H-SiC原位掺杂技术,生长速率控制在5μm/h左右.采用扫描电镜(SEM)、原子力显微镜(AFM),傅里叶变换红外光谱(FTIR)和Hg/4H-SiC肖特基结构对同质外延表面形貌、厚度、掺杂浓度以及均匀性进行了测试.实验结果表明,4H-SiC同质外延在表面无明显缺陷,厚度均匀性1.74%, 1.99% 和1.32%(σ/mean),掺杂浓度均匀性为3.37%,2.39%和2.01%.同种工艺条件下,样品间的厚度和掺杂浓度误差为1.54%和3.63%,有很好的工艺可靠性. 关键词： 4H-SiC 同质外延生长 水平热壁CVD 均匀性     

Effect of Carbonized Conditions on Residual Strain and Crystallinity Quality of Heteroepitaxial Growth 3C-SiC Films

Heteroepitaxial growth of SiC on n-Si（111） substrates is performed by a low pressure chemicaJ vapor deposition process. The effects of different carbonized temperature and carbonized time on the crystalline quality and the residual strain of 3C-SiC films are discussed. The results show that the residual strain is obviously reduced and the crystalline quality is greatly improved at the best carbonized temperature of 1000℃ and the carbonized time of 5 min. Under these optimized carbonization conditions, thick epitaxial films of about 15 μm with good crystalline quality and low residual strain can be obtained.     

Formation of the intermediate semiconductor larger for the Ohmic contact to silicon carbide using Germanium implantation

By formation of an intermediate semiconductor layer (ISL) with a narrow band gap at the metallic contact/SiC interface, this paper realises a new method to fabricate the low-resistance Ohmic contacts for SiC. An array of transfer length method (TLM) test patterns is formed on N-wells created by P⁺ ion implantation into Si-faced p-type 4H-SiC epilayer. The ISL of nickel-metal Ohmic contacts to n-type 4H-SiC could be formed by using Germanium ion implantation into SiC. The specific contact resistance ρ_c as low as 4.23× 10^-5~Ωega \cdotcm² is achieved after annealing in N₂ at 800~°C for 3~min, which is much lower than that (>900~°C) in the typical SiC metallisation process. The sheet resistance R_sh of the implanted layers is 1.5~kΩega /\Box. The technique for converting photoresist into nanocrystalline graphite is used to protect the SiC surface in the annealing after Ge⁺ ion implantations.     

Edge termination study and fabrication of a 4Hben SiC junction barrier Schottky diode

The 4H-SiC junction barrier Schottky (JBS) diodes terminated by field guard rings and offset field plate are designed, fabricated and characterized. It is shown experimentally that a 3-μm P-type implantation window spacing gives an optimum trade-off between forward drop voltage and leakage current density for these diodes, yielding a specific on-resistance of 8.3 mΩ·cm². A JBS diode with a turn-on voltage of 0.65 V and a reverse current density less than 1 A/cm² under 500 V is fabricated, and the reverse recovery time is tested to be 80 ns, and the peak reverse current is 28.1 mA. Temperature-dependent characteristics are also studied in a temperature range of 75 ℃-200 ℃. The diode shows a stable Schottky barrier height of up to 200 ℃ and a stable operation under a continuous forward current of 100 A/cm².     

Fabrications and characterizations of high performance 1.2 kV,3.3 kV,and 5.0 kV class 4H–SiC power SBDs

In this paper, 1.2 kV, 3.3 kV, and 5.0 kV class 4H–SiC power Schottky barrier diodes(SBDs)are fabricated with three N-type drift layer thickness values of 10 μm, 30 μm, and 50 μm, respectively. The avalanche breakdown capabilities,static and transient characteristics of the fabricated devices are measured in detail and compared with the theoretical predictions. It is found that the experimental results match well with the theoretical calculation results and are very close to the 4H–SiC theoretical limit line. The best achieved breakdown voltages(BVs) of the diodes on the 10 μm, 30 μm, and 50 μm epilayers are 1400 V, 3320 V, and 5200 V, respectively. Differential specific-on resistances(R_(on-sp)) are 2.1 m?·cm~2,7.34m?·cm~2, and 30.3 m?·cm~2, respectively.     

Study of （Ga,Mn）N prepared by Mn-ion implantation using optical techniques

This paper reports that （Ga, Mn）N is prepared using implantation of 3at.% Mn Ions into undoped GaN. Structural characterization of the crystals was performed using x-ray diffraetion（XRD）. Detailed XRD measurements have revealed the characteristic of Mn-ion implanted GaN with a small contribution of other compounds. With Raman spectroscopy measurements, the spectra corresponding to the intrinsic GaN layers demonstrate three Raman active excitations at 747, 733 and 566 cm-1 identified as EI（LO）, A1 （LO） and E~, respectively. The Mn-doped GaN layers exhibit additional excitations at 182, 288, 650 725, 363, 506cm^-1 and the vicinity of E~ mode. The modes observed at 182, 288, 650 725em 1 are assigned to macroscopic disorder or vacancy-related defects caused by Mn-ion implantation. Other new phonon modes are assigned to Mnx-Ny, Gax-Mny modes and the local vibrational mode of Mn atoms in the （Ga, Mn）N, which are in fair agreement with the standard theoretical results.     

Comparison of the formation process and properties of epitaxial graphenes on Si- and C-face 6Hben SiC substrates

In this paper, the epitaxial graphene layers grown on Si- and C-face 6H-SiC substrates are investigated under a low pressure of 400 Pa at 1600 ℃. By using atomic force microscopy and Raman spectroscopy, we find that there are distinct differences in the formation and the properties between the epitaxial graphene layers grown on the Si-face and the C-face substrates, including the hydrogen etching process, the stacking type, and the number of layers. Hopefully, our results will be useful for improving the quality of the epitaxial graphene on SiC substrate.     

Investigation of 4H—SiC metal—insulation—semiconductor structure with Al2O3/SiO2 stacked dielectric

Atomic layer deposited (ALD) Al₂O₃/dry-oxidized ultrathin SiO₂ films as high-k gate dielectric grown on the 8° off-axis 4H-SiC (0001) epitaxial wafers are investigated in this paper. The metal-insulation-semiconductor (MIS) capacitors, respectively with different gate dielectric stacks (Al₂O₃/SiO₂, Al₂O₃, and SiO₂) are fabricated and compared with each other. The I-V measurements show that the Al₂O₃/SiO₂ stack has a high breakdown field ( ≥ 12 MV/cm) comparable to SiO₂, and a relatively low gate leakage current of 1× 10^-7 A/cm² at electric field of 4 MV/cm comparable to Al₂O₃. The 1-MHz high frequency C-V measurements exhibit that the Al₂O₃/SiO₂ stack has a smaller positive flat-band voltage shift and hysteresis voltage, indicating less effective charge and slow-trap density near the interface.