Characteristics of pentacene organic thin film transistor with top gate and bottom contact

High performance pentacene organic thin film transistors (OTFT) were designed and fabricated using SiO₂ deposited by electron beam evaporation as gate dielectric material. Pentacene thin films were prepared on glass substrate with S--D electrode pattern made from ITO by means of thermal evaporation through self-organized process. The threshold voltage V_TH was --2.75± 0.1V in 0---50V range, and that subthreshold slopes were 0.42± 0.05V/dec. The field-effect mobility (μ_EF) of OTFT device increased with the increase of V_DS, but the μ_EF of OTFT device increased and then decreased with increased V_GS when V_DS was kept constant. When V_DS was --50V, on/off current ratio was 0.48× 10⁵ and subthreshold slope was 0.44V/dec. The μ_EF was 1.10cm²/(V.s), threshold voltage was --2.71V for the OTFT device.     

对以并五苯和酞菁铜为不同有源层的有机薄膜晶体管特性研究

通过扫描电镜和X射线衍射对SiO₂衬底上生长并五苯和酞菁铜薄膜的表面形貌进行表征,并得到在SiO₂衬底上生长的并五苯薄膜是以岛状结构生长,其大小约为100nm,且薄膜有较好的结晶取向,呈多晶态存在. 酞菁铜薄膜则没有表现出明显的生长机理,其呈非晶态存在. 还对通过掩膜的方法制作得以酞菁铜和并五苯为有源层的顶栅极有机薄膜晶体管的特性进行了研究. 有源层的厚度为40nm,绝缘层SiO₂的厚度为250nm,器件的沟道宽长比(W/关键词： 有机薄膜晶体管 并五苯薄膜 酞菁铜薄膜 μ_EF)')" href="#">场效应迁移率(μ_EF)     

有机阱结构器件在反向偏压调制下光致发光猝灭的研究

实验过程中制备了3种不同周期的有机阱结构器件,分别用N,N’-diphenyl-N,N’-bis(1-napthyl)-1,1’-biphenyll-4,4’-diamine(NPB)和4,4,N,N’-dicarbazolebiphenyl(CBP)作为电子的势阱和势垒。讨论了3个器件在反向偏压调制下的光致发光的猝灭。研究结果显示在作者所制备的器件中NPB层中激子的猝灭速度要比CBP层中的激子猝灭速度快。这主要是因为NPB层中的有效电场要比CBP层中的有效电场强。当所制备的有机阱结构器件的周期数增加时,在相同的反向电场下,NPB和CBP层中的激子猝灭速度会随之增加,因为实验中制备的这3个器件为Ⅱ型量子阱结构,激子在这种阱结构器件中会随着阱周期数的增加而变得越来越不稳定,因此周期数较大的器件猝灭现象比较明显。     

磷光材料fac-tris(2-phenylpyridinato-N，C2′)iridium(Ⅲ)对不同荧光材料的敏化作用及发光机制分析

在荧光材料中掺杂合适的磷光敏化剂,可以大大提高荧光有机电致发光器件(OLED)的效率。选择磷光材料知fac-tris(2-phenylpyridinato-N,C^2′)iridium(Ⅲ)(Ir(ppy)3)分别与荧光材料4-(dicyanomethylene)-2-t-butyl-6-(1,1,7,7-tetramethyljulolidyl-9-enyl(DCJTB)、5,6,11,12,-tetraphenylnaphthacene(Rubrene)掺杂作为发光层,当掺杂质量比合适时,磷光材料的发光消失,得到了纯正的荧光材料的发光。同时,对磷光材料的敏化作用及发光机制进行了分析,比较了Ir(ppy)3对两种不同荧光材料的敏化作用强弱,发现Ir(ppy)3对荧光材料Rubrene的敏化作用更强。对影响敏化作用的因素进行了分析,推测其原因与磷光材料和荧光材料的相容性质有关。     

Electroluminescence quenching mechanism in Rubrene doped host-guest system

In this paper, the electroluminescence quenching mechanism in a 5,6,11,12-tetraphenylnaphthacene (Rubrene) doped host--guest system is studied by utilizing a specially designed organic light-emitting diode with an emission layer consisting of a few periodic host/guest structures. Tris-(8-hydroxyquinoline) aluminium (Alq₃) and Rubrene are used as the host and the guest, respectively. The thickness variation of the guest layer in each period enables the study of the effect of molecule aggregation, and the thickness variation of the host layer suggests a long range quenching mechanism of dipole--dipole interaction. The long range quenching mechanism is a F?rster process, and the F?rster radius of Rubrene is between 3 and 10~nm.     

量子阱结构对有机电致发光器件效率的影响

实验中共制备了五种有机量子阱结构电致发光器件,分别对这五种量子阱结构器件的电致发光特性进行了研究,分析了量子阱结构的周期数和势垒层的厚度对器件电学性能的影响.实验结果表明适当周期数的量子阱结构器件的亮度和电流效率比传统的三层结构器件的要大,主要原因是量子阱结构对电子和空穴的限制作用,这种限制作用提高了电子和空穴在发光层中形成激子和复合的概率,从而提高了发光的亮度和效率.当改变阱结构器件中势阱层的厚度时,也会对器件的亮度和效率产生影响,采用适当的势阱层厚度能够提高器件的亮度和效率. 关键词： 量子阱结构 电致发光 电流效率 光谱