Large inverse and normal magnetocaloric effects in HoBi compound with nonhysteretic first-order phase transition

HoBi single crystal and polycrystalline compounds with NaCl-type structure are successfully obtained, and their magnetic and magnetocaloric properties are studied in detail. With temperature increasing, HoBi compound undergoes two magnetic transitions at 3.7 K and 6 K, respectively. The transition temperature at 6 K is recognized as an antiferromagnetic-to-paramagnetic (AFM-PM) transition, which belongs to the first-order magnetic phase transition (FOMT). It is interesting that the HoBi compound with FOMT exhibits good thermal and magnetic reversibility. Furthermore, a large inverse and normal magnetocaloric effect (MCE) is found in HoBi single crystal in the $H|| [100]$ direction, and the positive $\Delta S_{\rm M}$ peak reaches 13.1 J/kg$\cdot$K under a low field change of 2 T and the negative $\Delta S_{\rm M}$ peak arrives at $-18 $ J/kg$\cdot$K under a field change of 5 T. These excellent properties are expected to be applied to some magnetic refrigerators with special designs and functions.     

钐配合物有序分子膜的激光诱导荧光研究

用Langmuir-Blodgett(LB)膜方法组装了可发红色荧光的钐配合物有序分子膜。用时间分辨技术得到了其激光诱导荧光光谱,并分析了荧光光谱的精细结构,计算了有序分子膜中钐离子的能级常数,测定了配合物中心离子的荧光寿命,从分子内及分子间能量转移机理上研究了分子存在状态、膜中组分对钐配合物荧光寿命及能级常数的影响。     

Zn-Mg-Al型类水滑石纳米颗粒制备及晶体结构

采用液相非稳态共沉淀法合成了锌镁铝类水滑石(Zn-Mg-Al-HTlc)颗粒,考察了其化学组成、晶体结构、粒子形貌及原料配比的影响等.结果表明,Zn-Mg-Al-HTlc样品中的n(Zn)/n(Zn+Mg+Al)比原料配比低,而n(Mg)/n(Zn+Mg+Al)基本无变化.n(Al)/n(Zn+Mg+Al)(x)在0.22～0.40范围内是纯类水滑石相,超出此范围时出现异相;x<0.22时出现ZnO相;x>0.40时出现Al(OH)₃相.所制备的Zn-Mg-Al-HTlc颗粒的晶胞参数a=0.27～0.32nm,c=2.27～2.42nm,层间距在0.75～0.81nm之间,层间通道的高度约0.30nm.样品颗粒均为较规则的六边形片状粒子.XRD-Scherrer公式计算结果表明,粒子的平均晶粒度在30～45nm之间.TEM结果表明,平均颗粒度随x的值趋于减小,x<0.33时平均颗粒度基本小于100nm.x值相近,Zn含量增加,平均颗粒度有增大趋势;n(Zn)/n(Al)相近,Mg含量增加,平均颗粒度有减小趋势.     

剪切速率对Fe-Al-Mg-MMH/钠质蒙脱土悬浮体触变性的影响

研究了测定条件对Fe-Al-Mg型混合金属氢氧化物（简称MMH）/钠质蒙脱土（简 称MT）混合悬浮体及纯MT体系触变性的影响，主要考察了高速剪切分散后，剪切速 率（D_L）对粘度（η）～时间（t）变化趋势的影响。发现纯的MT体系和MMH/MT质 量比（R）为0.013的Fe-Al-Mg-MMH/MT体系在所研究的D_L下（10，170，511和1 022 s~(-1)）都呈现为正触变性，D_L不影响触变性类型。R = 0.051的体系，低 D_L时（10和170 s~(-1)）呈现复合触变性，高D_L时（511和1 022 s~(-1)）呈现 正触变性；R = 0.091的体系在低D_L时（10和170 s~(-1)）呈现负触变性，在高 D_L时（511和1 022 s~(-1)）呈现复合触变性。D_L增加，各体系η逐渐降低。对 D_L影响触变性的机理进行了深入探讨。     

pH值对Fe-Al-Mg-MMH/钠质蒙脱土悬浮体触变性的影响

研究了pH值对Fe-Al-Mg型混合金属氢氧化物／钠质蒙脱土（简称MMH／MT）悬浮体触变性的影响。发现pH值能影响其触变性类型：m(MMH)/m(MT)(下文中以R表示）较低时（0，0．013和0．051），随着pH增高，体系有由负触变性－复合触变性－正触谱性转变的趋势；而R较高的体系（R＝0．091），随pH的增高，体系由复合触变性向负触变性转化。探讨了各种触变性产生的原因和pH的影响机理。     

钙钛矿型La_(0.2)Pb_(0.4)Sr_(0.4)FeO_3的制备及其气敏性

采用溶胶-凝胶法首次制备出平均粒径为22.3 nm的La0.2Pb0.4Sr0.4FeO3的晶体,这种复合晶体是正交的钙钛矿型结构.通过对其导电性和气敏性的研究,发现La0.2Pb0.4Sr0.4FeO3材料是一种p型半导体材料,并且在175℃下对甲醛具有很好的气敏性.     

超高性能钕铁硼表面镀渗处理研究

通过磁控溅射进行钕铁硼磁体表面重稀土Tb镀膜,再经过渗扩热处理获得了综合性能近80[H_cj/kOe+(BH)_max/MGOe]的超高性能磁体,分析了其内在机制。借助扫描电镜背散射电子成像技术,研究了热处理温度对磁体磁性能和微观组织的影响,并探讨了晶界扩散法矫顽力提高的机理和微观结构变化规律。结果表明,经镀渗处理后磁体的矫顽力明显提高,剩磁无明显降低,温度稳定性得以显著改进,显微组织结构有了明显的优化,形成连续均匀薄层晶界富Nd相组织有效的包裹主相,能够有效降低相邻晶粒的磁耦合效应。Tb富集在2∶14∶1晶粒的表面区域而不是中心,不仅通过增强局部磁晶各向异性场来增加矫顽力,而且还保持了剩磁。     

La-Ca-(Mn,Fe)-O大磁阻材料的低温特性

研究了低温下Ｌａ－Ｃａ－（Ｍｎ,Ｆｅ）－Ｏ的磁性及磁阻特性。发现随着铁离子替代锰离子,材料中的铁磁作用关弱,的主作用增强。在铁替代锰量为１／１０的样品中,在磁化曲线及磁阻变化的关系上,发现了“弯曲“现象,并给出了物理解释,还发现少量的铁离子替代锰离子可提高材料的低温磁阻比值。     

剪切速率对Fe-Al-Mg-MMH/钠质蒙脱土悬浮体触变性的影响

研究了测定条件对Fe-Al-Mg型混合金属氢氧化物（简称MMH）/钠质蒙脱土（简 称MT）混合悬浮体及纯MT体系触变性的影响，主要考察了高速剪切分散后，剪切速 率（D_L）对粘度（η）～时间（t）变化趋势的影响。发现纯的MT体系和MMH/MT质 量比（R）为0.013的Fe-Al-Mg-MMH/MT体系在所研究的D_L下（10，170，511和1 022 s~(-1)）都呈现为正触变性，D_L不影响触变性类型。R = 0.051的体系，低 D_L时（10和170 s~(-1)）呈现复合触变性，高D_L时（511和1 022 s~(-1)）呈现 正触变性；R = 0.091的体系在低D_L时（10和170 s~(-1)）呈现负触变性，在高 D_L时（511和1 022 s~(-1)）呈现复合触变性。D_L增加，各体系η逐渐降低。对 D_L影响触变性的机理进行了深入探讨。     

Nd-Fe(Co,Nb)-B交换耦合磁体的磁性

用熔体快淬法结合热处理制备了高性能纳米复合永磁合金Nd₉Fe_85.5-xCo_xNb₁B_4.5(0≤x≤16).最佳磁性能对应的成分为Nd₉Fe_81.5Nb₁B_4.5,其永磁性能如下：最大磁能积(BH)_max＝156kJ/m³,剩磁J_r＝1.11T 关键词：