Intrinsic Surface Reaction Constant in 1-pK Model of Mg-Fe Hydrotalcite-like Compounds

The relationship among intrinsic surface reaction constant (K) in 1-pK model, point of zero net charge (PZNC) and structural charge density (σst) for amphoteric solid with structural charges was established in order to investigate the effect of σst on pK. The theoretical analysis based on 1-pK model indicates that the independent PZNC of electrolyte concentration (c) exists for amphoteric solid with structural charges. A common intersection point (CIP) should appear on the acid-base titration curves at different c, and the pH at the CIP is pHPZNC. The pK can be expressed as pK=-pHPZNC log[(1 2αPZNC)/(1-2αPZNC)], where αPZNC≡σst/eNANs, in which e is the elementary charge, NA the Avogadro‘s constant and Ns the total density of surface sites. For solids without structural charges, pK=-pHPZNC. The pK values of hydrotalcite-like compounds (HTlc) with general formula of [Mg1-xFex(OH)2](Cl,OH)x were evaluated. With increasing x, the pK increases, which can be explained based on the affinity of metal cations for H^- or OH^- and the electrostatic interaction between charging surface and H^- or OH^-.     

甲酰胺对有序介孔二氧化硅形貌的影响

At room temperature and in acidic solution, ordered mesoporous silicas with particular morphology were synthesized using cetylpyridinium chloride as the template and formamide as the cosolvent. Scanning electron microscope (SEM), small angle X-ray diffraction (SXRD), and nitrogen adsorption techniques were used to characterize the as-synthesized and calcined samples. Results showed that the samples had hexagonal mesostructure analogous to MCM-41 and relatively narrow pore-size distributions (BJH). Besides, BET surface areas of the samples were in the range of 1 000～1 250 m²·g^-1 and high total pore volumes were up to 1.367 cm³·g^-1. Addition of formamide affected obviously mesostructures and the morphology of the mesoporous silica. Furthermore, with the increase of the concentration of formamide, the unit-cell constant decreased and particle shape changed from gyroids to fibers.     

合成介孔纳米晶体氧化锆的新方法(英文)

通过一种新颖的方法,即软模板-固液技术(CSSL)合成具有高比表面积的介孔纳米晶体氧化锆.首先,通过软模板法以1-十六烷基-3-甲基咪唑溴(C16mim+Br-)为结构导向剂,硫酸锆为无机前驱物合成了介观相氧化锆杂化物,然后该杂化物与固体硝酸铜无机盐研磨并进行热处理.在600℃焙烧后所得到的氧化锆材料具有蠕虫状介孔结构,且孔壁由尺寸约为2.50nm的四方相氧化锆纳米粒子组成.该材料的比表面积为240.0m2·g-1,孔径为4.10nm.与之对应,使用单一的软模板法在相同的温度焙烧后,所得到的氧化锆材料介孔结构坍塌,比表面积仅为9.5m·2g-1.     

Zn-Mg-Al型类水滑石纳米颗粒制备及晶体结构

采用液相非稳态共沉淀法合成了锌镁铝类水滑石(Zn-Mg-Al-HTlc)颗粒,考察了其化学组成、晶体结构、粒子形貌及原料配比的影响等.结果表明,Zn-Mg-Al-HTlc样品中的n(Zn)/n(Zn+Mg+Al)比原料配比低,而n(Mg)/n(Zn+Mg+Al)基本无变化.n(Al)/n(Zn+Mg+Al)(x)在0.22～0.40范围内是纯类水滑石相,超出此范围时出现异相;x<0.22时出现ZnO相;x>0.40时出现Al(OH)₃相.所制备的Zn-Mg-Al-HTlc颗粒的晶胞参数a=0.27～0.32nm,c=2.27～2.42nm,层间距在0.75～0.81nm之间,层间通道的高度约0.30nm.样品颗粒均为较规则的六边形片状粒子.XRD-Scherrer公式计算结果表明,粒子的平均晶粒度在30～45nm之间.TEM结果表明,平均颗粒度随x的值趋于减小,x<0.33时平均颗粒度基本小于100nm.x值相近,Zn含量增加,平均颗粒度有增大趋势;n(Zn)/n(Al)相近,Mg含量增加,平均颗粒度有减小趋势.     

Al-Mg MMH溶胶和钠土悬浮体的相互作用机理

通过流变参数、电泳淌度和pH值的测定,研究了无机盐(CaCl₂、KCl、NaCl)和pH值对铝镁混合金属氢氧化物与钠土悬浮体间相互作用的影响。发现随着混合金属氢氧化物含量的增加,钠土体系的pH值逐渐降低,而动切力(YP)先上升,经最大值后逐渐下降;当钠土体系为NaCl所饱和时,相同混合金属氢氧化物加量下YP的上升幅度明显减小,在实验混合金属氢氧化物浓度范围内,YP未出现峰值。混合金属氢氧化物/钠土体系的YP随pH值的变化曲线呈抛物线形,加入相同浓度的无机盐,△YP、△pH(绝对值)按CaCl₂KCl～NaCl次序递减。     

镁铝氢氧化物正电溶胶结构研究

镁铝氢氧化物正电溶胶结构研究韩书华，张春光，侯万国，孙德军，王果庭（山东大学胶体与界面化学研究所，济南，２５０１００）关键词镁铝氢氧化物，正电溶胶，共沉淀镁铝氢氧化物是一种层状的氢氧化物。Ｂｕｒｂａ等［１］提出将镁铝氢氧化物与钠质蒙脱土作用可得到抑制...     

萘基桥联有机-无机杂化介孔材料的合成及其光学性质

以短链阳离子三聚表面活性剂C₁₀H₂₁N⁺(CH₃)₂(CH₂)₂N⁺(CH₃)(C₁₀H₂₁)(CH₂)₂N⁺(CH₃)₂C₁₀H₂₁]·3Br^?为结构导向剂, 通过2,7-二(3-三乙氧硅基氨丙酯基)萘(NIS)和四乙氧基硅烷(TEOS)共缩聚, 制备了有序的萘基桥联的杂化周期性介孔有机硅(PMOs). 样品通过X射线衍射(XRD)、高分辨透射电镜(HRTEM)、氮气吸附-脱附、差示扫描量热/热重分析(DSC/TGA)表征. 结果表明, 当NIS占NIS和TEOS总量40% (摩尔分数)时, 可以形成具有结晶态孔壁的有序介孔杂化材料. 当NIS含量低于或高于40%时, 分别形成无定形孔壁的有序介孔杂化材料和无孔杂化材料. 随着孔壁中萘基基团的增加, 由于有机基团之间π-π堆积作用增强, 杂化介孔材料显示良好的热稳定性. 由于在二氧化硅骨架中嵌入荧光萘基基团, 杂化有机-无机有序介孔材料显示了激基缔合物的光学行为. 随萘基基团含量的增加, 杂化材料的紫外吸收峰发生蓝移, 形成H聚集体; 由于聚集引起的荧光淬灭, 杂化材料的荧光量子产率明显降低.     

助表面活性剂对介孔二氧化硅孔径的影响

在十六烷基三甲基溴化铵(CTAB)与硝酸形成的胶束体系中,分别加入正戊醇与正辛胺作助表面活性剂,合成出介孔二氧化硅.经小角XRD和N₂气体吸附与脱附实验证实,随着CTAB与正戊醇摩尔比的增加,介孔二氧化硅的孔径增加;而随CTAB与正辛胺摩尔比的增加,介孔二氧化硅的孔径减小.主要原因是正戊醇增大了CTAB胶束体积,从而导致介孔二氧化硅的孔径增加.而在CTAB与正辛胺的混合胶束中,正辛胺同硅酸盐作用力比CTAB强,导致介孔二氧化硅的孔径减小.     

模板法合成六方介孔SiO2

模板法合成六方介孔SiO2;六方结构;低聚表面活性剂     

氢氧化铝镁钠米颗粒的零电荷点及电荷密度研究

探讨了电位滴定(PT)法测定的零电荷点的物理意义, 认为是零净电荷点(ZPNC)。并对零净电荷点pH(pHZPNC), 零可变电荷点pH(pHZPVC), 永久电荷密度(σP), 可变电荷密度(σV)和净电荷密度(σT)之间的关系进行了理论分析。用PT法测定了氢氧化铝镁纳米颗粒的pHZPNC和σP, 探讨了电解质浓度和pH对各电化学性质的影响规律。另外, 还考察了CO3^2^-对PT法测定结果的影响。