Identification and elimination of inductively coupled plasma-induced defects in AlxGa1 - xN/GaN heterostructures 下载免费PDF全文
By using temperature-dependent Hall,variable-frequency capacitance-voltage and cathodoluminescence (CL) measurements,the identification of inductively coupled plasma (ICP)-induced defect states around the Al x Ga 1-x N/GaN heterointerface and their elimination by subsequent annealing in Al x Ga 1-x N/GaN heterostructures are systematically investigated.The energy levels of interface states with activation energies in a range from 0.211 to 0.253 eV below the conduction band of GaN are observed.The interface state density after the ICP-etching process is as high as 2.75×10 12 cm 2 ·eV 1.The ICP-induced interface states could be reduced by two orders of magnitude by subsequent annealing in N 2 ambient.The CL studies indicate that the ICP-induced defects should be Ga-vacancy related. 相似文献
3.
4.
研究发展了用肖特基电容电压特性数值模拟确定调制掺杂AlxGa1-xN/GaN异质结中极化电荷的方法.在调制掺杂的Al0.22Ga0.78N/GaN异质结上制备了Pt肖特基接触,并对其进行了C-V测量.采用三维费米模型对调制掺杂的Al0.22Ga0.78N/GaN异质结上肖特基接触的C-V特性进行了数值模拟,分析了改变样品参数对C-V特性的影响.利用改变极化电荷、n-AlGaN
关键词:
xGa1-xN/GaN异质结')" href="#">AlxGa1-xN/GaN异质结
极化电荷
电容电压特性
数值模拟 相似文献
5.
在1.5K低温和0~9T的高磁场下研究了AlGaG/GaN异质结二维电子气的磁输运性质.实验结果在4块样品中都观察到了Shubnikov-da HaSS振荡的双周期行为.表明异质结的三角势阱中有两个子带被电子占据.通过电子子带占据时电子浓度分配的线形行为得到第二子带被占据的阈值浓度为7.2×1012cm-2.通过对不同样品量子散射时间和输运迁移率的研究,说明在1.5K下远程离化施主散射在量子散射时间中起主要作用. 相似文献
6.
7.
Frequency-dependent capacitance-voltage (C-V) measurements have been performed on modulation-doped Al0.22 Ga0.78N/GaN heterostructures to investigate the characteristics of the surface states in the AlxGa1-xN barrier. Numerical fittings based on the experimental data indicate that there are surface states with high density locating on the AlxGa1-xN barrier. The density of the surface states is about 10^12cm^-2eV^-1, and the time constant is about 1μs. It is found that an insulating layer (Si3N4) between the metal contact and the surface of AlxGa1-xN can passlvate the surface states effectively. 相似文献
8.
利用脉冲激光淀积法(PLD)在α-Al2O3衬底上淀积了ZnO薄膜, 通过ZnO和α-Al2O3固相反应制备了具有ZnAl2O4覆盖层的α-Al2O3衬底. X射线衍射谱(XRD)表明ZnAl2O4薄膜随反应时间由单一(111)取向转变为多晶取向, 然后变为不完全的(111)择优取向. 同时扫描电子显微镜(SEM)照片表明ZnAl2O4表面形貌随反应时间由均匀的岛状结构先变为棒状结构, 然后再变为突起的线状结构. 另外, XRD谱显示低温制备的ZnAl2O4在高温下不稳定. 在ZnAl2O4覆盖的α-Al2O3衬底上利用光加热低压MOCVD法直接生长了GaN薄膜. XRD测量表明随ZnAl2O4厚度增加GaN由c轴单晶变为多晶, 单晶GaN的摇摆曲线半高宽为0.4°. 结果表明薄ZnAl2O4覆盖层的岛状结构有利于GaN生长初期的成核, 从而提高了GaN的晶体质量. 相似文献
9.
With the solid phase reaction between pulsed-laser-deposited (PLD) ZnOfilm and α-Al2O3 substrate, ZnAl2O4/α-Al2O3 complex substrates were synthesized. X-ray diffraction (XRD) spectra show that as the reaction proceeds, ZnAl2O4 changes from the initial (111)-oriented single crystal to poly-crystal, and then to inadequate (111) orientation. Corresponding scanning electron microscope (SEM)images indicate that the surface morphology of ZnAl2O4 transforms from uniform islands to stick structures, and then to bulgy-line structures. In addition, XRDspectra present that ZnAl2O4 prepared at low temperature is unstable at the environment of higher temperature. On the as-obtained ZnAl2O4/α-Al2O3 substrates, GaN films were grown without any nitride buffer using light-radiation heating low-pressure MOCVD (LRH-LP-MOCVD). XRD spectra indicate that GaN film on this kind of complex substrate changes from c-axis single crystal to poly-crystal as ZnAl2O4 layer is thickened. For the single crystal GaN, its full width at half maximum (FWHM) of X-ray rocking curve is 0.4°. Results indicate that islands on thin ZnAl2O4 layer can promote nucleation at initial stage of GaN growth, which leadsto the (0001)-oriented GaN film. 相似文献
10.
桑立雯 ;秦志新 ;岑龙斌 ;沈波 ;张国义 ;李书平 ;陈航洋 ;刘达艺 ;康俊勇 ;成彩晶 ;赵鸿燕 ;鲁正雄 ;丁嘉欣 ;赵岚 ;司俊杰 ;孙维国 《中国物理快报》2008,25(1):258-261
We report AlGaN-based back-illuminated solar-blind Schottky-type ultraviolet photodetectors with the cutoff- wavelength from 280nm to 292nm without bias. The devices show low dark current of 2.1× 10^-6A/cm^2 at the reverse bias of 5 V. The specific detectivity D* is estimated to be 3.3 × 10^12cmHz^1/2 W^-1 . To guarantee the performance of the photodetectors, the optimization of AlGaN growth and annealing condition for Schottky contacts were performed. The results show that high-temperature annealing method for Ni/Pt Schottky contacts is effective for the reduction of leakage current. 相似文献