两个基于2,5-二甲氧基对苯二甲酸和咪唑衍生物的超分子钴配位聚合物的结构及光催化反应

本文以咪唑衍生物为配体,通过水热合成法与钴离子制备出两个配位聚合物:{[Co(DTA)(1,4-DIB)(H₂O)]·H₂O}_n(1)和[Co(DTA)(1,3-BMIB)]_n(2)(1,4-DIB=1,4-二(1H-咪唑-1-基)苯; 1,3-BMIB=1,3-二(4-甲基-1H-咪唑-1-基)苯;H₂DTA=2,5-二甲氧基对苯二甲酸)。利用X射线单晶衍射、粉末衍射、热失重、元素分析、红外光谱以及固体紫外-可见光谱等对两个配合物进行了表征。结构分析证实配合物1和2是通过二维结构堆积成的三维超分子化合物。粉末衍射测试则显示两个配合物在水中有很好的稳定性。固体紫外-可见光谱显示两个配合物属半导体材料,对紫外-可见光有很强的吸收作用。在光催化实验中,配合物1和2可加快亚甲基蓝的降解速度。     

基于2,5-二溴对苯二甲酸配体的锌/钴配合物合成、晶体结构及性质

将有机物2,5-二溴对苯二甲酸(H₂L₁)和2,2′-联吡啶(L₂)作为双配体,使用溶剂热法和七水合硫酸锌(ZnSO₄·7H₂O)、六水合硝酸钴(Co(NO₃)₂·6H₂O)分别反应,得到配合物[Zn(L₁)(L₂)(H₂O)]_n(1)和配合物[Co(L₁)(L₂)(H₂O)]_n(2)。采用单晶X射线衍射、元素分析、红外光谱、紫外光谱、荧光光谱、热重分析等测试方法对这两种物质进行分析研究。单晶测试结果表明配合物1是单斜晶系,以Zn²⁺配位连接L^2-₁与L₂形成一维链状结构,各条链在分子间氢键和π…π共轭作用下有规律地堆叠形成三维网络结构。配合物2是三斜晶系,Co1离子和Co1ⁱ离子由H₂L₁上的羧酸氧原子O4和O4ⁱ连接,形成双齿螯合的配位结构单元,以Co²⁺配位连接 L^2-₁和L₂形成二维网格结构,各层在O—H…O分子间氢键和范德瓦耳斯力作用下有规律的堆叠形成三维网络结构。配合物1和2均含有芳香杂环、羧基杂环和氮杂环,具有良好的荧光性质和热稳定性,最大发射波长分别为345 nm和333 nm。     

Cu2O/TiO2-Bi2WO6三元复合催化剂的制备及光催化性能研究

采用水热法制备花状Bi2 WO6,并利用超声分散法制备了Cu2 O/TiO2-Bi2 WO6复合光催化剂,通过FESEM、XRD、XPS、FI-IR、UV-vis DRS和PL对光催化剂进行了分析和表征.表征结果证明:花状Bi2 WO6表面负载着碎片状的TiO2和立方体Cu2 O形成Cu2 O/TiO2-Bi2 WO6复合光催化剂;以短链脂肪酸(SCFAs)为牺牲剂,考察复合光催化剂的光催化产生氢气和烷烃的性能.实验结果表明:Cu2 O/TiO2-Bi2 WO6复合光催化剂以乙酸为牺牲剂,主要产氢气和甲烷,降解率高达91.82;;以丙酸为牺牲剂,产物主要是乙烷和丁烷,降解率高达90.70;;以丁酸为牺牲剂,除了氢气,甲烷,乙烷,丙烷,丁烷外,气体产物还含有一定量的戊烷,其降解率高达91.50;.结合反应液中间产物的成分进行检测,由此推断出光催化反应的可能机理.     

煤直接液化油中混合酚的分离研究

利用分子筛择形特点，对煤直接液化油中的混合酚实施高效分离。本研究选取间甲酚和对甲酚作为分离煤直接液化油馏分段混合酚的模型化合物，采用化学液相沉积法对HZSM-5吸附剂的孔口结构进行改变，分析分子筛硅铝比及颗粒粒径对模型化合物间甲酚和对甲酚吸附分离性能的影响，以获得高性能固相吸附剂，并将其应用于180-190℃馏分段混合酚分离。结果表明，当分子筛硅铝比为25、粒径为3-5 μm时，分子筛的孔口结构调节效果最优；当正硅酸乙酯的最小用量为0.2 mL/g时，固相吸附剂的吸附量为0.03 g/g，对甲酚选择性高于95%。由于外表面沉积物对吸附剂的孔口结构变化，导致对甲酚选择性的提高。进一步采用HZSM-5（1）吸附剂对真实煤直接液化油混合酚的分离中发现，苯酚和对甲酚的选择性均达到100%。     

Surface passivation in n-type silicon and its application in silicon drift detector

Based on the surface passivation of n-type silicon in a silicon drift detector(SDD), we propose a new passivation structure of SiO2/Al2O3/SiO2 passivation stacks. Since the SiO2 formed by the nitric-acid-oxidation-of-silicon(NAOS)method has good compactness and simple process, the first layer film is formed by the NAOS method. The Al2O3 film is also introduced into the passivation stacks owing to exceptional advantages such as good interface characteristic and simple process. In addition, for requirements of thickness and deposition temperature, the third layer of the SiO2 film is deposited by plasma enhanced chemical vapor deposition(PECVD). The deposition of the SiO2 film by PECVD is a low-temperature process and has a high deposition rate, which causes little damage to the device and makes the SiO2 film very suitable for serving as the third passivation layer. The passivation approach of stacks can saturate dangling bonds at the interface between stacks and the silicon substrate, and provide positive charge to optimize the field passivation of the n-type substrate.The passivation method ultimately achieves a good combination of chemical and field passivations. Experimental results show that with the passivation structure of SiO2/Al2O3/SiO2, the final minority carrier lifetime reaches 5223 μs at injection of 5×10¹⁵ cm^-3. When it is applied to the passivation of SDD, the leakage current is reduced to the order of nA.     

YBa2Cu1-xCox(Cu1-yZny)2Oz体系的Co,Zn共同掺杂效应

本文报道通过对YBa₂Cu_1-xCo_x(Cu_1-yZn_y)₂O_z(0≤x,y≤0.1)体系晶体结构、氧含量、正常态电阻-温度关系、Hall效应以及超导临界温度等的综合测量,发现随着Co和Zn含量的增加,体系经历了从正交结构的超导金属向四方结构的非超导半导体的转变,超导临界温度T_c和载流子浓度n_h均迅速下降,Co 关键词：     

6066Al/SiCp复合材料内耗性能研究

用粉末冶金方法制备了6066Al合金和不同SiCp含量的6066Al/SiCp复合材料,用多功能内耗仪在200～600 K温度区间内测试了所研究材料在升温过程中的内耗变化趋势,探讨了6066 Al /SiCp复合材料在不同温度区间的内耗机制.结果表明6066Al/SiCp的内耗值比6066Al合金内耗值高,特别是在高温阶段比6066Al合金内耗值高得多;6066Al/SiCp和6066Al合金在300～470 K时的内耗主要是位错与第二相颗粒交互作用引起的位错内耗,在高温下内耗主要由Al/Al、Al/SiC的界面微滑移引起.     

应力对M-Z型InP/InGaAsP-EAM偏振

采用Agilent 81910A光子全参量测试仪,首次实验研究了InP/In1－xGaxAs1－yPy-MQW（Multiple-Quantum-Well,MQW）材料与衬底间因应力而产生的M-Z型光调制器的PDL影响以及由此引起的由差分群时延(Differential Group Delay,DGD)表征的偏振模色散(Polarization Mode Dispersion,PMD).研究结果表明,半导体MQW光调制器的PDL与DGD是一致的.因此在半导体光器件的制作过程中,应尽可能地减小衬底与波导芯层之间的因残存应力的存在造成对光器件的高速性能的不利影响.