Growth of Indium Nanorods by Magnetron Sputtering

Indium nanorods are grown on silicon substrates by using magnetron-sputtering technique. Film morphologies and nanorod microstructure are investigated by using scanning electron microscopy, high-resolution transmission electron microscopy （HRTEM）, and x-ray diffraction. It is found that the mean diameter of the nanorods ranges from 30nm to 100nm and the height ranges from 30nm to 200nm. The HRTEM investigations show that the indium nanorods are single crystals and grow along the [100] axis. The nanorods grow from the facets near the surface undulation that is caused by compressive stress in the indium grains generated during grain coalescence process. For low melting point and high diffusivity metal, such as bismuth and indium, this spontaneous nanorod growth mechanism can be used to fabricate nanostructures.     

反应离子镀光学薄膜的微观结构分析

用反应离子镀方法制备了ＴｉＯ２单层膜及ＴｉＯ２／ＳｉＯ２多层膜，用透射电子显微镜分别观察了由反应离子镀方法及传统蒸镀法二种不同工艺制得的ＴｉＯ２单层膜及ＴｉＯ２／ＳｉＯ２多层膜的断面结构，并对ＴｉＯ２单层膜进行了喇曼分析和卢瑟福背散射分析。     

模压条件对聚乙烯/碳黑PTC复合材料电阻特性的影响

聚合物基PIE(Positive Temperature Coefficient)复合材料的主要组成为聚合物基体及导电填料，具有室温电阻率低、质软、易加工成形、价格低廉等优点，在医疗、计算机、程控电话交换机、手机电池、汽车配件、家电产品、工业仪表、运载火箭、火灾报警等领域得到了广泛的应用。我们     

A fibrous hypercrosslinked sorbent prepared on PP-ST-DVB matrix via post-crosslinking reaction

A fibrous sorbent possessing abundant micropore structure was firstly prepared via post-crosslinking reaction on the PP-ST-DVB original fiber. Its micromorphology and sorptive properties were investigated, and the results demonstrated that the novel fibrous hypererosslinked sorbent has narrow pore-size distribution, small average porous radius （1.90 nm）, high specific surface area （362.31 m^2/g）, and fine sorptive properties for small organic molecules.     

Effects of Substrate Temperature on Helium Content and Microstructure of Nanocrystalline Titanium Films

Helium-charged nanocrystalline titanium films have been deposited by HeAr magnetron co-sputtering. The effects of substrate temperature on the helium content and microstructure of the nanocrystalline titanium films have been studied. The results indicate that helium atoms with a high concentration are evenly incorporated in the deposited titanium films. When the substrate temperature increases from 60℃ to 350℃ while the other deposition＇parameters are fixed, the helium content decreases gradually from 38.6 at.% to 9.2at.%, which proves that nanocrystalline Ti films have a great helium storage capacity. The 20 angle of the Bragg peak of （002） crystal planes of the He-charged Ti film shifts to a lower angle and that of （100） crystal plane is unchanged as compared with that of the pure Ti film, which indicates that the lattice parameter c increases and a keeps at the primitive value. The grain refining and helium damage result in the diffraction peak broadening.     

Effects of Processing Parameters on Microstructure and Properties of Nanoscale ZrC/ZrB2 Multilayered Coatings

ZrC/ZrB2 multilayered coatings with bilayer periods of 3.5-40nm are synthesized by rf magnetron sputtering. Analyses of x-ray diffraction, scanning electron microscopy and nanoindentation indicate that multilayered coatings possess much higher hardness and greater fracture resistance than monolithic ZrC and ZrB2 coatings. A maximum hardness （41.TCPa） and a critical fracture load （73.7mN） are observed in the multilayer with A = 32 nm deposited at the substrate bias -40 V. Higher residual stress built in the ZrC layer can be released by periodic insertion of ZrB2 into the ZrC layer. A clear multilayered structure with mixed ZrB2（001）, ZrB2 （002） and ZrC （111） orientations should be responsible for the enhanced mechanical properties.     

Morphology of Platinum Nanowire Array Electrodepostied Within Anodic Aluminium Oxide Template Characterized by Atomic Force Microscopy

Unifrom platinum nanowires were synthesized by electrodepositing the platinum under a very low altering current frequency(20Hz) and increasing voltage(5-15V）in the proes of anodic aluminium oxide(AAO) template. Atomic force microscopy observation indicates that the template membranes we obtained have hexagonally clse-packed nanochannels.The platinum nanowires have highly ordered arrays after partially dissolving the aluminium oxide membrane.With the increasing dissolvoing time,the platinum nanowire array collapsed.A concave topography of the aluminium substrate was observed after the aluminium oxide membrane was dissolved completely and the platinum nanowires were released from the template.Platinum nanowires were also characterized by transmission electron microscopy and the phase structure of the Al/AAO/Pt composite was proven by x-ray diffraction.     

Mg粉粒度对MgB_2超导体宏观特征和显微结构的影响

研究了Mg粉粒度对MgB2超导体宏观特征和显微结构的影响规律。将不同粒度的Mg粉和B粉分别按1.03∶2的比例混合、压制成型后,在流通高纯氩气的条件下于800℃烧结1h,制备出MgB2块材。利用阿基米德方法、X射线衍射仪和扫描电子显微镜等分别测试样品的密度、物相组成和显微结构等。结果表明,Mg粉粒度对MgB2超导体的物相组成没有影响;随着Mg粉粒度的增加,MgB2超导体的最大气孔尺寸、质量损失率、体积膨胀系数都逐渐增大,但其密度逐渐降低。     

Higher-order effects on self-similar parabolic pulse in the microstructured fibre amplifier

By considering higher-order effects, the properties of self-similar parabolic pulses propagating in the microstructured fibre amplifier with a normal group-velocity dispersion have been investigated. The numerical results indicate that the higher-order effects can badly distort self-similar parabolic pulse shape and optical spectrum, and at the same time the peak shift and oscillation appear, while the pulse still reveals highly linear chirp but grows into asymmetry. The influence of different higher-order effects on self-similar parabolic pulse propagation has been analysed. It shows that the self-steepening plays a more important role. We can manipulate the geometrical parameters of the microstructured fibre amplifier to gain a suitable dispersion and nonlinearity coefficient which will keep high-quality self-similar parabolic pulse propagation. These results are significant for the further study of self-similar parabolic pulse propagation.