采用空心阴极放电等离子体化学气相沉积方法制备a-CH薄膜

 研究了不同衬底-阴极距离、直流电压和H₂流量对a-CH薄膜沉积速率的影响。结果表明：衬底-阴极距离必须大于0.5cm，随着该距离的增加，薄膜的沉积速率减少；直流电压达550V时沉积速率最大；随着H2含量的增加，CH₄含量相对减少，沉积速率随之降低。用AFM观察了以该方法制得的448.4nm CH薄膜的表面形貌，表面粗糙度约为10nm。最后测出了不同条件下CH薄膜的UV-VIS谱，由此可以计算得到薄膜的禁带宽度及折射率。     

闪烁光纤在γ射线辐照下部分特性的蒙特卡罗模拟

 闪烁光纤在射线成像方面的应用越来越广泛。为了进一步了解闪烁光纤在射线辐照下的基本特性，基于蒙特卡罗方法，利用计算机模拟分析了γ射线在闪烁光纤中的好事例率与光纤长度及射线能量的关系，能量沉积效率与光纤长度及射线能量的关系。此项工作对于闪烁光纤阵列在射线成像，剂量场测量等方面的研究很有价值。     

Effects of Substrate Temperature on Helium Content and Microstructure of Nanocrystalline Titanium Films

Helium-charged nanocrystalline titanium films have been deposited by HeAr magnetron co-sputtering. The effects of substrate temperature on the helium content and microstructure of the nanocrystalline titanium films have been studied. The results indicate that helium atoms with a high concentration are evenly incorporated in the deposited titanium films. When the substrate temperature increases from 60℃ to 350℃ while the other deposition＇parameters are fixed, the helium content decreases gradually from 38.6 at.% to 9.2at.%, which proves that nanocrystalline Ti films have a great helium storage capacity. The 20 angle of the Bragg peak of （002） crystal planes of the He-charged Ti film shifts to a lower angle and that of （100） crystal plane is unchanged as compared with that of the pure Ti film, which indicates that the lattice parameter c increases and a keeps at the primitive value. The grain refining and helium damage result in the diffraction peak broadening.     

Monte Carlo方法研究低能电子束曝光沉积能分布规律

建立一个描述低能电子在多元多层介质中散射的物理模型,运用MonteCarlo方法模拟低能电子在靶体胶衬底中的复杂散射过程,在此基础上通过大量计算研究入射束能、胶层厚度、衬底材料等不同曝光条件对抗蚀剂沉积能密度分布的影响,获得沉积能分布规律:适量的低束能、薄胶层、低原子序数衬底可以使前散射电子对胶中沉积能密度分布的贡献增大、背散射电子的贡献减小,从而提高曝光分辨率. 关键词： 电子束曝光 MonteCarlo方法 低能电子散射 能量沉积     

Formation of Interfacial Layers in LaAlO3/Silicon during Film Deposition

We have studied the interracial reactions between amorphous LaAlO3 thin films and Si substrates, using high- resolution transmission electron microscopy and x-ray photoelectron spectroscopy. It has been shown that the interracial layer between LaAlO3 film and Si substrate chemical states show that the ratio of La 4d3/2 to Al 2p is SiLaxAlyOz. The depth distributions of La, Si and Al of the interfacial layer remains unchanged with the depth compared to that of the LaAlO3 film. Moreover, the Si content, in the interracial layer gradually decreases with increasing thickness of the interracial layer. These results strongly suggest that the Al element is not deficient in the interracial layer, as previously believed, and the formation of a SiLaxAlyOz interracial layer is mainly due to the diffusion of Si from the substrate during the LaAlO3 film deposition. With the understanding of the interracial layer formation, ones can control the interface characteristics to ensure the desired performances of devices using high-k oxides as gate dielectrics.     

CHBr薄膜制备的初步研究

碳氢（cH）及其掺杂材料常被用作ICF实验靶丸烧蚀层材料。制备CH薄膜及其掺杂材料的方法有很多，诸如：离子束辅助沉积、离子溅射沉积、低压等离子体化学气相沉积（LPPCVD）等。近年来，详细研究了LPPCVD法制备CH薄膜的制备方法与工艺，形成了比较成熟的技术路线与工艺路线，并为“神光”实验提供了一系列实验靶丸。     

热丝加热电流对CH薄膜沉积速率和表面形貌的影响

 热丝辅助裂解法是结合气相沉积制备聚对二甲苯薄膜和热丝化学气相沉积而形成的一种制-CH薄膜的新方法。热丝辅助裂解法的最大特点就是在保持低衬底温度情况下可以获得高沉积速率，而热丝加热电流对薄膜沉积速率和薄膜表面形貌具有重要影响。研究表明，热丝加热电流越大，薄膜沉积速率越高，在加热电流9A时，薄膜沉积速率可达0.002mm/min，同时薄膜表面粗糙度随之增加，薄膜表面也开始出现其它元素污染，因此，一般热丝加热电流选择为7A附近。     

电流计在交流电演示中的共振问题

主要讨论了磁电式电流计在输入低频交流电时发生的共振现象 ,分析影响磁电式电流计灵敏程度 (指针最大偏转角αm 大小 )的主要因素。     

沉积铁钝化膜的傅立叶变换表面增强拉曼光谱

利用恒电流沉积技术、傅立叶变换表面增强拉曼散射技术现场研究了0 1mol/LNaOH溶液中铁金属电极在不同电位下的表面氧化物的组成。结果表明,在电极预钝化区,表面首先生成的Fe(OH)2可由拉曼谱图中出现的550cm-1表征,证实了以往的研究结果。进入钝化区,表面二价氧化物逐步转化为高价氧化物Fe3O4及α 、δ 和γ FeOOH。在电位回扫的过程中,各氧化产物的还原以及铁表面SERS活性的逐渐消失导致谱峰强度降低。     

甚高频等离子体增强化学气相沉积法沉积μc-Si∶H薄膜中氧污染的初步研究

对不同的本底真空条件下,采用甚高频等离子体增强化学气相沉积技术沉积的氢化微晶硅（μc_Si∶H）薄膜中的氧污染问题进行了比较研究.对不同氧污染条件下制备的薄膜样品的x射线光电子能谱与傅里叶变换红外吸收光谱测量结果表明：μc_Si∶H薄膜中,氧以Si—O，O—O和O—H三种不同的键合模式存在,不同的键合模式源自不同的物理机理.μc_Si∶H薄膜的Raman光谱、电导率与激活能的测量结果进一步显示：沉积过程中氧污染程度的不同,对μc_Si∶H薄膜的结构特性与电学特性产生显著影响；而不同氧污染对μc_Si∶H薄膜电学特性的影响不同于氢化非晶硅（a_Si:H）薄膜. 关键词： 氢化微晶硅薄膜 甚高频等离子体增强化学气相沉积 氧污染