棒状CuFe4Ox的可控合成及其异戊醇脱氢反应的催化性能

利用液相沉淀法可控合成了均匀的棒状CuFe₄O_x催化剂。通过原位X射线粉末衍射（XRD）、高分辨透射电子显微镜（TEM）及程序升温还原（TPR）等手段表征其晶相结构、形貌和还原性能。通过还原棒状CuFe₄O_x获得Cu⁰/Fe₃O₄ 纳米棒,原位X射线光电子能谱（XPS）用于确定Cu⁰/Fe₃O₄ 表面的相组成。通过液相沉淀法制备棒状CuFe₄O_x,在120℃保持3 h后加入Na₂CO₃溶液至pH等于9时所得棒状形貌最为规整。以异戊醇脱氢反应作为探针反应,比较了Cu⁰/Fe₃O₄ 纳米棒和Cu⁰/Fe₃O₄ 纳米颗粒的催化反应性能,发现Cu⁰/Fe₃O₄ 纳米棒比Cu⁰/Fe₃O₄ 纳米粒子具有更好的活性和稳定性,表明棒状Fe₃O₄ 担载的Cu纳米粒子具有更好的结构稳定性。     

纳米Mn-Zn铁氧体的制备和研究

Nanosize manganese zinc ferrites were fabricated by hydrothermal precipitation route using Fe₂(SO₄)₃, ZnSO₄·7H₂O, MnSO₄·H₂O as material, then some calcinated at 500 ℃ and studied by XRD, TEM, IR and VSM. The results showed that the products were spinel crystal structure and uniformly sized nanoparticles (15～25 nm) with little aggregation. The analysis of IR showed that the superficial water can be eliminated, but that was embedded in crystal lattice can not be removed by calcinating. The effect Zn content x on the lattice (a) of nanosize Mn_1-xZn_xFe₂O₄ was also discussed. The lattice of nanosize Mn_1-xZn_xFe₂O₄ decreases with x increasing; and its value deviated the standard lattice (a₀) of normal size manganese zinc ferrites. A lot of water was absorbed during the hydrothermal process owing to the large surface of nanosize particles. The change of magnetic properties of Mn_xZn_1-xFe₂O₄ with x increasing was studied: nanosize Mn_xZn_1-xFe₂O₄ particles synthesized by us exhibited peculiar magnetic properties curve with Zn content (x) increasing, Superparamagnetic behaviors of the synthesized ZnFe₂O₄ samples were confirmed by magnetic characterization, which can be explained by the difference between the distribution of the metal ions (Mn²⁺, Zn²⁺ and Fe³⁺) among the tetrahedral (A) and the octahedral (B) sites of nanosize ferrite and that of bulk ferrite.     

纳米钙钛矿LaxSr1-xFe1-yCoyO3复合氧化物的制备和表征

用甘氨酸-硝酸盐燃烧合成法，制备La_xSr_1-xFe_1-yCo_yO₃复合氧化物的陶瓷粉末，对该钙钛矿型氧化物进行了XRD、IR、紫外漫反射光谱及循环伏安曲线分析。结果表明：该复合氧化物粉体平均晶粒为15.3～29.8 nm,为立方和正交晶系。该氧电极具有双功能催化特性，但不完全可逆。对水溶液染料进行光解实验，利用紫外-可见、人工神经网络光度法研究La_xSr_1-xFe_1-yCo_yO₃的催化性能。结果表明：CO²⁺的加入可使La_xSr_1-xFeO₃的光催化活性有所提高，B位离子(Fe³⁺，CO²⁺)改变与加入，使La_xSr_1-xFe_1-yCo_yO₃(x=0.7，0.3；y=0.3，0.9，1)光催化活性高于La_xSr_1-xFeO₃。同时，对5种染料进行紫外光解，在0.75 h，脱色率大于91%，并为动力学一级反应。     

纳米Fe3O4及Ni2+掺杂Fe3O4的制备、表征及吸附Pb(Ⅱ)的特性

采用一种改进的共沉淀法制备了纳米磁铁矿(Fe₃O₄)及Ni²⁺掺杂磁铁矿(Ni_xFe_3-xO₄,x=0.1,0.3,0.6),用X-射线衍射(XRD)、扫描电镜(SEM)、氮气物理性吸附、酸碱滴定等手段对产物进行了表征,用平衡吸附法研究了4种样品对Pb(Ⅱ)离子的吸附容量及吸附模型。结果表明,Fe₃O₄和3种Ni_xFe_3-xO₄均为近似球形的单相晶质纳米颗粒;与Fe₃O₄比较,Ni_xFe_3-xO₄的颗粒尺寸变小、表面电荷零点和pH＝5.0时的表面正电荷量降低;样品的孔体积、比表面积和表面分形度以及表面羟基含量都随产物中Ni²⁺掺杂量的增加而升高。4种样品对Pb(Ⅱ)的等温吸附数据均适合用Langmuir模型拟合(R₂=0.9942~0.9858),其相关系数的大小表现为:Fe₃O₄>Ni_0.1Fe_2.9O₄>Ni_0.3Fe_2.7O₄=Ni_0.6Fe_2.4O₄;Freundlich模型对样品等温吸附Pb(Ⅱ)的实验数据拟合度较低(R²=0.9813~0.9477),4种样品的Freundlich相关系数的大小关系与Langmuir相关系数相反。初始pH=5.0时,Fe₃O₄,Ni_0.1Fe_2.9O₄,Ni_0.3Fe_2.7O₄和Ni_0.6Fe_2.4O₄对Pb(Ⅱ)的最大吸附容量分别为6.02,6.68,7.29和8.34mg·g^-1。可见,Ni_xFe_3-xO₄(尤其是Ni²⁺掺杂量较高的产物)对水环境中重金属Pb(Ⅱ)的去除能力明显高于Fe₃O₄。     

纳米Fe3O4及Ni2 掺杂Fe3O4的制备、表征及吸附Pb(Ⅱ)的特性

采用一种改进的共沉淀法制备了纳米磁铁矿(Fe₃O₄)及Ni²⁺掺杂磁铁矿(Ni_xFe_3-xO₄,x=0.1,0.3,0.6),用X-射线衍射(XRD)、扫描电镜(SEM)、氮气物理性吸附、酸碱滴定等手段对产物进行了表征,用平衡吸附法研究了4种样品对Pb(Ⅱ)离子的吸附容量及吸附模型。结果表明,Fe₃O₄和3种Ni_xFe_3-xO₄均为近似球形的单相晶质纳米颗粒;与Fe₃O₄比较,Ni_xFe_3-xO₄的颗粒尺寸变小、表面电荷零点和pH＝5.0时的表面正电荷量降低;样品的孔体积、比表面积和表面分形度以及表面羟基含量都随产物中Ni²⁺掺杂量的增加而升高。4种样品对Pb(Ⅱ)的等温吸附数据均适合用Langmuir模型拟合(R²=0.9942~0.9858),其相关系数的大小表现为：Fe₃O₄>Ni_0.1Fe_2.9O₄>Ni_0.3Fe_2.7O₄=Ni_0.6Fe_2.4O₄;Freundlich模型对样品等温吸附Pb(Ⅱ)的实验数据拟合度较低(R²=0.981 3~0.947 7),4种样品的Freundlich相关系数的大小关系与Langmuir相关系数相反。初始pH=5.0时,Fe₃O₄,Ni_0.1Fe_2.9O₄,Ni_0.3Fe_2.7O₄和Ni_0.6Fe_2.4O₄对Pb(Ⅱ)的最大吸附容量分别为6.02,6.68,7.29和8.34 mg·g^-1。可见,Ni_xFe_3-xO₄(尤其是Ni²⁺掺杂量较高的产物)对水环境中重金属Pb(Ⅱ)的去除能力明显高于Fe₃O₄。     

Ba0.98Bi0.02(Ti0.9Zr0.1)1-xCuxO3陶瓷的介电性能、弛豫行为与结晶化学特性

采用固相合成法, Bi3+作施主掺杂A位, Cu₂₊作受主掺杂B位, 制备了Ba_0.98Bi_0.02(Ti_0.9Zr_0.1)_1-xCu_xO₃(x=0, 0.01, 0.02, 0.03)陶瓷样品。借助XRD、LCR等研究了该陶瓷的结构与介电性能。结果表明:当x=0.03时, 陶瓷样品出现第二相。通过GULP模拟, 缺陷偶极子的稳定性从低到高依次为:[2Bi_Ba^·+V_Ba"]、[2Bi_Ba^·+Cu_Ti/Zr"]、[Cu_Ti/Zr"+V_O^··], 结合实验可知:介电弛豫程度与晶体中缺陷偶极子的存在形式相关, 其中x=0.01时, 晶体中以[2Bi_Ba^·+Cu_Ti/Zr"]为主。随Cu₂₊掺杂量的增加, 介电常数增加, 介电常数与B位键价和呈反比变化、与八面体BO₆的体积呈正比变化。     

纳米CuFe2O4-rGO复合材料的制备及电化学性能

采用溶剂热法成功制备了纳米CuFe₂O₄-rGO复合材料。通过X射线衍射（XRD）,扫描电子显微镜（SEM）、透射电子显微镜（TEM）和电化学工作站对样品的结构、形貌及电容特性进行表征。结果表明,CuFe₂O₄纳米粒子均匀地分散在石墨烯片层间,其中CuFe₂O₄-20% rGO复合材料具有最优的电化学性能,当电流密度1 A·g^-1时,其比电容为1 952.5 F·g^-1,当电流密度为1 A·g^-1时,CuFe₂O₄-20% rGO复合材料经1 000次充放电后的比电容保持率为86.17%。     

不同形貌Fe3O4纳米粒子的氧化沉淀法制备与表征

用一种方法成功合成出了球体、四方体、八面体、不规则多面体、三角形和不规则颗粒等六种具有不同形貌的Fe₃O₄纳米粒子，通过扫描电子显微镜(SEM)表征了粒子形貌。试样经过X-射线衍射(XRD)表征具有尖晶石结构，且结晶良好。经震动样品磁强计(VSM)测定，各种形貌的Fe₃O₄纳米粒子都具有良好的磁性，其中八面体形貌的Fe₃O₄纳米粒子的饱和磁化强度达到86.56 emu·g^-1，剩磁为10.64 emu·g^-1，矫顽力为138 Oe。讨论了不同形貌的Fe₃O₄纳米粒子的形成机制，得出了晶核的生长环境对纳米粒子的形貌有重要影响的结论。     

Ce1－xNdxO2－δ固溶体的电子顺磁共振谱和阻抗谱的研究

利用溶胶-凝胶方法在800 ℃焙烧10 h后, 合成了固溶体Ce_1－xNd_xO_2－δ (x＝0.05～0.55), X射线衍射(XRD)测试表明固溶体已经形成立方萤石结构; 电子顺磁共振谱(EPR)研究表明在固溶体Ce_1－xNd_xO_2－δ中随着掺杂量x的增大, Ce^3＋离子含量减少, 说明掺杂Nd^3＋离子可以抑制Ce^4＋的还原; 交流阻抗谱的测量表明固溶体Ce_0.9Nd_0.1O_2－d 具有离子导电特性, 600和700 ℃时的电导率分别为4.25×10^－3和1.12×10^－2 S•cm^－1, 活化能为0.68 eV.     

Ba0.4Sr0.6Co1-xFexO3-δ系阴极材料的制备和表征

采用甘氨酸-硝酸盐(GNP)法合成了中温固体氧化物燃料电池阴极材料Ba_0.4Sr_0.6Co_1-xFe_xO_3-δ(x=0.0～0.8)系列粉体。利用XRD和SEM对材料的结构和微观形貌进行分析,用直流四端子法测量了烧结陶瓷体在中温(450～800 ℃)范围内的电导率。结果表明,制备的样品为单一钙钛矿相,随着Fe含量增加,XRD衍射峰值向高角度方向稍有偏移。电导率随着温度及Fe含量的变化出现极大值,在x＜0.2时,Ba_0.4Sr_0.6Co_1-xFe_xO_3-δ系列烧结体在中温(450～800 ℃)区的电导率,随Fe掺入量的增大而增大,x=0.2样品的电导率最高,800 ℃时达244.7 S·cm^-1,远超过文献报道值,进一步增大Fe含量导电性能变差。     

LixNi0.8-yCo0.2ZnyOp的合成及电化学性能研究

A series of single-phase Li_xNi_0.8-yCo_0.2Zn_yO_p(0.96 ≤x≤ 1.10， 0 ≤y≤ 0.05， 2 ≤p≤ 2(1+y) ) (different in the y values) were synthesized by a two-step solid state reaction method， in which LiOH·H₂O， Zn-doped spherical Ni(OH)₂ and Co₂O₃ were used as the precursors. The ICP-AES analyses proved that the Zn-doped compounds synthesized had the nonstoichiometric form. The results of the XRD， SEM identified that the uniform particles of the as-prepared materials having a good layered structure were fine， narrowly distributed and well crystallized. The electrochemical performance test was carried out and the results showed that the as-prepared Zn-doped materials had not only a high capacity， but also a better cycling stability characterization than the un-doped one. The Li_1.06Ni_0.75Co_0.22Zn_0.03O_2.03 material has an initial reversible capacity as high as 160.5mAh·g^-1; and a first discharge efficiency 89.2%， and exhibits satisfactory cyclic stability with 90% retainable capacity after 50 cycles.     

直接Z型Zn2SnO4-xNx/ZnO1-yNy异质结光催化剂的制备及机理

采用微波溶剂热法成功制备直接Z型Zn_2SnO_(4-x)N_x/ZnO_(1-y)N_y核壳结构异质结光催化剂。2种物质不同的功函数改变了其表面电荷密度,并在界面处形成内建电场,导致其从传统的Ⅰ型镶嵌异质结转变为Ⅱ型异质结,再转变为Z型异质结构。N杂质原子替代O原子进入Zn_2SnO_4和ZnO的晶格,在两者的价带(VB)顶部形成双杂质能级。核壳结构的Z型异质结光催化剂对罗丹明B的降解速率为纯相Zn_2SnO_(4-x)N_x的1.40～1.43倍,同时具有良好的循环稳定性,且可以降解亚甲基蓝、甲基橙、水杨酸等污染物。Z型异质结的形成使其光生电子-空穴对具有较强的氧化还原能力,而双杂质能级的存在可以拓宽其光响应范围并提高载流子的分离效率。因此,Zn_2SnO_(4-x)N_x/ZnO_(1-y)N_y异质结光催化剂高的光催化活性归因于Z型异质结和双杂质能级的协同作用。     

层状O2结构锂锰氧化物Li0.60[MgxCoyMn1-x-y]O2的制备及结构表征

本文采用离子交换法分别制备了双复合锂锰氧化物Li_0.60[Mg_xMn_1-x]O₂(0.05 ≤ x ≤ 0.15)和三复合锂锰氧化物Li_0.60[Mg_xCo_yMn_1-x-y]O₂(x=0.05，0.05 ≤      

用于NO_x低温下吸附还原的CoO_x/CeO_2二元氧化物的制备

研究了以多孔二氧化硅微球和活性炭为载体制备NOx吸附/还原催化剂的方法,摸索了最佳Ce/Co物质的量的比例。采用低温氮吸附方法测定了样品的BET比表面和孔容,利用XRD方法表征了样品中所掺杂的金属元素的晶型。研究发现:当nCe/nCo=75/25时,材料获得最佳NOx吸附能力,当以多孔二氧化硅微球作载体时,材料对于NOx的吸附主要来自CoOx和CeO2的二元氧化物;当以活性炭作为载体时,活性炭参与了NOx的吸附,因此其吸附容量大大提高。对NOx的吸附机理进行了探讨,并研究了样品的NH3还原性质。     

Chromium(III) Hydroxide Solubility in The Aqueous Na+-OH?-H2PO?4-HPO2?4-PO3?4-H2O System: A Thermodynamic Model

Chromium(III)-phosphate reactions are expected to be important in managing high-level radioactive wastes stored in tanks at many DOE sites. Extensive studies on the solubility of amorphous Cr(III) solids in a wide range of pH (2.8–14) and phosphate concentrations (10^–4 to 1.0 m) at room temperature (22±2)°C were carried out to obtain reliable thermodynamic data for important Cr(III)-phosphate reactions. A combination of techniques (XRD, XANES, EXAFS, Raman spectroscopy, total chemical composition, and thermodynamic analyses of solubility data) was used to characterize solid and aqueous species. Contrary to the data recently reported in the literature,⁽¹⁾ only a limited number of aqueous species [Cr(OH)₃H₂PO^–₄, Cr(OH)₃(H₂PO₄)^2–₂), and Cr(OH)₃HPO^2–₄] with up to about four orders of magnitude lower values for the formation constants of these species are required to explain Cr(III)-phosphate reactions in a wide range of pH and phosphate concentrations. The log K^o values of reactions involving these species [Cr(OH)₃(aq)+H₂PO^–₄⇌Cr(OH)₃H₂PO^–₄; Cr(OH)₃(aq)+2H₂PO^–₄⇌Cr(OH)₃(H₂PO₄)^2–₂; Cr(OH)₃(aq)+HPO^2–₄⇌Cr(OH)₃HPO^2–₄] were found to be 2.78±0.3, 3.48±0.3, and 1.97±0.3, respectively.     

CCl2自由基被无机小分子猝灭的速率常数

对CCl4/Ar混合气体脉冲直流高压放电产生CCl2自由基,用541.52 nm激光将电子基态CCl2激励到A 1B1(0,4,0)振动能级上. 通过检测激发态CCl2时间分辨荧光信号,测得室温下CCl2(A 1B1和a 3B1)被O2、N2、NO、 CO2、 CS2、H2O、SO2,和SF6分子猝灭的实验结果.用我们提出的三能级模型分析处理实验数据,获得了CCl2(A 1B1)态和CCl2(a 3B1)态的碰撞猝灭速率常数kA和ka值.     

SiO2/TiO2-xCx/C的制备、表征及其吸附和可见光催化性能

以SiO2为成核中心,钛酸四丁酯为钛源,分别以多羟基化合物乙二醇、丙三醇、葡萄糖和聚乙烯醇为联接剂,采用水解沉淀法制备了碳掺杂和包覆的多孔SiO2/TiO2-xCx/C可见光响应型光催化剂。采用X-射线衍射(XRD)、透射电子显微镜(TEM)、X-射线光电子能谱(XPS)、傅里叶变换-红外光谱(FTIR)、比表面积(BET)和紫外-可见(UV-Vis)漫反射光谱对样品进行表征。对不同结构样品的形成机理进行了分析。以次甲基蓝(MB)溶液为模拟废水,对样品的吸附性能和可见光催化性能进行了评价。结果表明,多羟基化合物对材料的结构和性能有重要影响。碳的掺杂和包覆使材料的吸收光谱包含了整个可见光区,而多孔结构使材料的吸附性能得到提高。以聚乙烯醇为原料所得样品吸附性能最好,30 min内吸附率达到70%;而以丙三醇为原料所得样品具有最好的可见光催化性能,40 min内次甲基蓝的降解率达到95%。     

CrOx-CeO2二元氧化物表面NO的NH3催化还原反应机理

利用原位漫反射红外光谱法研究了473 K下在CrOx-CeO₂二元氧化物表面NO的NH₃催化还原反应的机理。研究了CrO-CeO₂二元氧化物表面在反应过程中的表面吸附物种。为了更加清晰的了解反应过程, 在SCR反应过程中分别切断NH₃和NO的气流, 并采集了所生成的原位漫反射红外光谱图, 通过研究以上结果得出结论:当前状态下的SCR反应过程可能服从E-R机理。     

CCl2(A 1B 1,a3B1)自由基被烷烃类分子猝灭动力学

用放电 LIF实验装置,对CCl4/Ar混合气体放电产生CCl2自由基,再用541.52 nm激光将电子基态CCl2激励到激发态A 1B1(0,4,0)振动能级上,通过检测激发态CCl2时间分辨荧光信号,测得室温下CCl2(A 1B1)被烷烃类分子猝灭的实验结果,用我们提出的三能级模型分析处理实验数据,获得CCl2(A 1B1)态和CCl2(a 3B1)态的碰撞猝灭速率常数kA和ka值.