静电纺丝技术制备TiO2@SiO2亚微米同轴电缆与表征

用静电纺丝技术成功制备出大量的TiO₂＠SiO₂亚微米同轴电缆. 用TGA-DTA, XRD, SEM, TEM, EDS, FTIR分析技术对样品结构和组成进行了系统的表征. 结果表明, 得到的产物为TiO₂＠SiO₂亚微米级同轴电缆, 以无定型SiO₂为壳层, 晶态TiO₂为芯层, 电缆平均直径450 nm, 壳层厚度90 nm, 电缆长度＞300 μm, 同时在样品中发现个别纤维呈现管状结构, 对其形成机理进行了讨论.     

核壳结构TiO2@SiO2催化碳酸二甲酯与苯酚酯交换合成碳酸二苯酯

以反相微乳液法和沉淀法相结合制备了核壳结构TiO₂@SiO₂,首次用于碳酸二甲酯与苯酚酯交换合成碳酸二苯酯反应,显示较好的催化活性. 采用200 ℃焙烧的TiO₂@SiO₂,用量0.20 g,反应9 h,苯酚转化率达41.8%,酯交换选择性为100%. 透射电镜显示TiO₂@SiO₂核厚壳薄,TiO₂核直径220-300 nm,SiO₂壳厚度40-60 nm,具有介孔结构. TiO₂@SiO₂对碳酸二甲酯与苯酚酯交换反应有好的重复使用性,使用4次苯酚转化率仍保持在40%以上. TiO₂与SiO₂发生相互作用,Ti进入骨架形成Ti-O-Si键,骨架Ti的形成提高了TiO₂@SiO₂的催化性能.     

同轴静电纺丝技术制备Y2O3:Eu3＋@SiO2豆角状纳米电缆与表征

采用同轴静电纺丝技术, 以氧化钇、氧化铕、正硅酸乙酯(C₈H₂₀O₄Si)、无水乙醇、PVP和DMF为原料, 成功制备出大量的Y₂O₃:Eu^3＋@SiO₂豆角状纳米电缆. 用TG-DTA, XRD, SEM, TEM和荧光光谱等分析技术对样品进行了系统地表征． 结果表明, 得到的产物为Y₂O₃:Eu^3＋@SiO₂豆角状纳米电缆, 以无定型SiO₂为壳层, 晶态Y₂O₃:Eu^3＋球为芯, 电缆直径约为200 nm, 内部球平均直径约150 nm, 壳层厚度约为25 nm, 电缆长度＞300 μm. 纳米电缆内部为球状结构, 沿着纤维长度方向有序排列, 形貌均一. Y₂O₃:Eu^3＋@SiO₂豆角状纳米电缆在246 nm紫外光激发下, 发射出Eu^3＋离子特征的波长为614 nm的明亮红光. 对其形成机理进行了初步讨论.     

Fe3O4@SiO2@mTiO2介孔多功能纳米复合颗粒的制备及载药能力

以溶剂热法制备氨基功能化的Fe₃O₄纳米颗粒为磁核,结合溶胶-凝胶法和模板法在其表面先后包覆上致密的SiO₂层和介孔TiO₂层,制备了磁性-发光-微波热转换性-介孔结构为一体的多功能核-壳结构纳米复合颗粒,并对其结构、性能及载药能力进行了研究。XRD分析表明:Fe₃O₄表面包覆上了无定形结构的SiO₂和TiO₂。TEM照片表明:所得的纳米复合颗粒具有明显的核壳结构和完美的球形,构成核的Fe₃O₄颗粒的尺寸在40~50 nm之间,Fe₃O₄@SiO₂@mTiO₂核壳结构纳米复合颗粒的尺寸为60~70 nm,壳层厚度约10 nm,并可观察到壳层中清晰的孔状结构。磁性、荧光光谱和微波热转换特性分析表明:该复合颗粒同时具有良好的发光性、磁性和微波热转换特性。N₂气吸附及药物负载率分析表明,该复合颗粒具有较高的比表面积(640 m²·g^-1)和介孔结构(孔径约2.8 nm)并且具有较高的药物负载率。     

微乳法制备纳米TiO2 /SiO2的结构及光催化研究

Nanosized TiO₂ and TiO₂/SiO₂ particles were prepared by hydrolysis of tetrabutyl titanate (TBOT) and tetraethyl orthosilicate (TEOS) in the TX-100 reverse microemulsion. These particles were characterized by TG-DSC, XRD, FTIR, TEM，N₂ adsorption-desorption. Their photocatalytic activity was tested by degradation of methyl orange. The result shows that TiO₂/SiO₂ nanoparticles are with a monodispersed spherical phase and a uniform size distribution，and TiO₂ particles are dispersed on the surface of SiO₂. The band for Ti-O-Si vibration in FTIR was observed, the Ti-O-Si bond increased the stability of anatase TiO₂, suppressed the phase transformation of titania from anatase to rutile. And due to the addition of SiO₂, the average size of titania decreased from 38 nm in pure TiO₂ to 5 nm in TiO₂/SiO₂. It was found, under UV light irradiation, TiO₂/SiO₂ particles showed higher activity than pure TiO₂, and TiO₂/SiO₂(1/1) particles showed the highest photocatalytic activity on the photocatalytic decomposition of methyl orange, which was influenced by crystal structure, particle size, crystallinity and Surface area Characteristics.     

TiO2 / SiO2核 / 壳结构复合粒子的组装及其电化学性能

TiO₂ coated SiO₂ materials as anode for lithium-ion batteries were synthesized via an in situ hydrolysis of tetraethyl orthosilicate under ultrasonic irradiation using nanometer-sized TiO₂ colloids as precursors. The XRD patterns indicate that the as-prepared core/shell particles remain anatase after calcining below 800 ℃. TEM observation shows that the particle size of TiO₂ / SiO₂ composites is ca. 200 nm, and a homogeneous SiO₂ layer is coated on the surfaces of TiO₂ particles. FTIR spectra demonstrate that SiO₂ could have been coated on the surfaces of TiO₂ particles via a chemical bonding. In addition, the first specific charge and discharge capacities of the coated particle electrode were 66.4 mAh·g^-1 and 90.7 mAh·g^-1, respectively, which indicates that the TiO₂ / SiO₂ particles are more stable than the monodispersed TiO₂. Meanwhile, the new material has good lithium intercalation-deintercalation performances.     

磁载光催化剂TiO2/SiO2/Ni0.5Fe2.5O4的制备及其催化氧化性能

采用固相反应法制备磁载体(SiO₂/Ni_0.5Fe_2.5O₄),溶胶-凝胶法得到易于磁分离回收的磁载光催化剂TiO₂/SiO₂/Ni_0.5Fe_2.5O₄。用XRD、SEM、IR和UV-Vis等进行表征。研究了太阳光下催化剂对亚甲基蓝溶液的脱色性能。结果表明,在太阳光下,磁载光催化剂TiO₂/SiO₂/Ni_0.5Fe_2.5O₄可使亚甲基蓝溶液迅速脱色；3次循环使用后脱色率仍为95%以上,回收率为98.8%。     

多重射流燃烧反应制备的TiO2/ SiO2纳米复合颗粒的形态和结构

TiO₂-SiO₂ nanocomposite particles were prepared in premixed H₂ / Air flame, and the morphology and structure of these nanocomposites were characterized by FTIR, XRD, TEM and HRTEM. The morphology of SiO₂ / TiO₂ nanocomposites was different from that of pure TiO₂ or SiO₂ nanoparticles, and the chemical bond of Ti-O-Si was found in the nanocomposites indicating that the TiO₂ / SiO₂ nanocomposites were not merely a physical mixture of TiO₂ and SiO₂. TiO₂ nanocrystalline grains with sizes of 1～2 nm were homogeneously dispersed in the amorphous SiO₂ matrix when TiCl₄ and SiCl₄ were mixed at molecular level in the flame. The particle size and rutile content decreased with increasing of SiO₂ molar ratio.     

具有光催化性能的TiO2-SiO2/TiO2两层增透膜的设计与制备

采用膜层设计理论设计了以TiO₂为内层膜,TiO₂-SiO₂复合膜为外层膜的两层增透膜,以钛酸丁酯（TBOT）和正硅酸乙酯（TEOS）作为前驱体,采用溶胶-凝胶法制备了TiO₂溶胶以及SiO₂溶胶,将两种溶胶按比例混合得到了TiO₂-SiO₂复合溶胶,在高硼硅玻璃上镀膜测试。透过率测试结果表明,在波长为550nm处的透过率最高能达到99.4%。在光催化实验中,采用罗丹明B模拟有机污染物,考察了TiO₂对光催化反应的影响。结果表明,在TiO₂存在的情况下,罗丹明B的降解速度大大提高,光催化效率显著增加。     

SiO2/PE/ Bi2S3核壳结构纳米颗粒的合成与性能(英)

以多层电解质作为微型反应器，制备了SiO₂/ Polyelectrolyte(PE) / Bi₂S₃核壳纳米粒子。XRD结果表明Bi₂S₃颗粒属于正交晶系。由透射电镜和场发射扫描电镜照片可知，在直径为640 nm左右的SiO₂表面覆盖了厚度35 nm的Bi₂S₃壳层。红外光谱分析结果表明硅烷网络在结构上发生了变化(SiO₂表面的硅烷醇键沉积在Bi₂S₃的表面)。SiO₂核和SiO₂ / PE / Bi₂S₃的紫外-可见吸收光谱显示在900 nm存在典型吸收边。     

Fabrication and characterization of TiO<Subscript>2</Subscript>–SiO<Subscript>2</Subscript> composite nanoparticles and polyurethane/(TiO<Subscript>2</Subscript>–SiO<Subscript>2</Subscript>) nanocomposite films

TiO₂–SiO₂ composite nanoparticles were prepared by a sol–gel process. To obtain the assembly of TiO₂–SiO₂ composite nanoparticles, different molar ratios of Ti/Si were investigated. Polyurethane (PU)/(TiO₂–SiO₂) hybrid films were synthesized using the “grafting from” technique by incorporation of modified TiO₂–SiO₂ composite nanoparticles building blocks into PU matrix. Firstly, 3-aminopropyltriethysilane was employed to encapsulate TiO₂–SiO₂ composite nanoparticles’ surface. Secondly, the PU shell was tethered to the TiO₂–SiO₂ core surface via surface functionalized reaction. The particle size of TiO₂–SiO₂ composite sol was performed on dynamic light scattering, and the microstructure was characterized by X-ray diffraction and Fourier transform infrared. Thermogravimetric analysis and transmission electron microscopy (TEM) employed to study the hybrid films. The average particle size of the TiO₂–SiO₂ composite particles is about 38 nm when the molar ratio of Ti/Si reaches to1:1. The TEM image indicates that TiO₂–SiO₂ composite nanoparticles are well dispersed in the PU matrix.     

Preparation, characterization, and infrared emissivity property of optically active polyurethane/TiO2/SiO2 multilayered microspheres

Optically active polyurethane/titania/silica (LPU/TiO₂/SiO₂) multilayered core–shell composite microspheres were prepared by the combination of titania deposition on the surface of silica spheres and subsequent polymer grafting. LPU/TiO₂/SiO₂ was characterized by FT-IR, UV–vis spectroscopy, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), SEM and TEM, and the infrared emissivity value (8–14 μm) was investigated in addition. The results indicated that titania and polyurethane had been successfully coated onto the surfaces of silica microspheres. LPU/TiO₂/SiO₂ exhibited clearly multilayered core–shell construction. The infrared emissivity values reduced along with the increase of covering layers thus proved that the interfacial interactions had direct influence on the infrared emissivity. Besides, LPU/TiO₂/SiO₂ multilayered microspheres based on the optically active polyurethane took advantages of the orderly secondary structure and strengthened interfacial synergistic actions. Consequently, it possessed the lowest infrared emissivity value.     

Two‐Dimensional Hollow TiO2 Nanoplates with Enhanced Photocatalytic Activity

Two‐dimensional anatase TiO₂ hollow nanoplates were firstly synthesized through a facile synthesis route by using α‐Fe₂O₃ nanoplates as removable templates. Two‐dimensional hollow TiO₂ nanoplates with different ratios of anatase and rutile phases were obtained by adjusting the calcining temperature. The average diameters were around 600 nm, and the shell thickness was approximately 30 nm. The photocatalytic performance of TiO₂ was investigated by decomposing rhodamine B under simulated sunlight. Among the TiO₂ samples, the anatase TiO₂ hollow nanoplates manifested a significant enhancement in the photocatalytic performances. The excellent catalytic performance can be attributed to the unique structure of the two‐dimensional anatase TiO₂ hollow nanoplates, including a large surface area and increased dye–photocatalyst contact areas as well as more active sites for photodegradation.     

超临界流体干燥法制备纳米TiO2-SnO2-SiO2复合光催化剂及其光催化性能研究

半导体多相光催化法作为一种污染治理新技术越来越受到人们的重视,在所使用的半导体光催化剂中,TiO2以无毒,催化活性高,价廉,无污染等特点,成为最具有前途的绿色环保型催化剂之一[1],但其自身具有局限性,如禁带宽度大,需在近紫外光下才能激发产生电子空穴对,对太阳光的利用率仅     

可磁分离二氧化钛光催化剂的制备及其光催化性能

通过液相催化相转化的方法制备了一种可磁分离的光催化剂TiO₂/SiO₂/NiFe₂O₄(TSN),这种光催化剂显示出了超顺磁性,能够通过外加磁场方便的实现催化剂在水中的分离与回收。该光催化剂的X-射线衍射和TEM结果表明：纳米TiO₂颗粒包裹在磁性颗粒-SiO₂/NiFe₂O₄(SN)的周围形成TiO₂层。利用光催化降解甲基橙的效果来考察了这种光催化剂的活性,结果表明：在NiFe₂O₄和TiO₂之间包覆一层无定型的SiO₂,可以显著的提高催化剂的脱色效果,3次循环后,仍能保持良好的催化活性。     

锌离子掺杂的二氧化钛介孔空心微球的制备及光催化性能

以二氧化硅为模板,钛酸四丁酯(TBOT)为钛源,硝酸锌为锌源,采用溶胶凝胶法制备了锌离子掺杂的介孔二氧化钛空心微球。采用X射线衍射(XRD)、比表面积(BET)、透射电镜(TEM)、扫描电镜(SEM)和X射线光电子能谱(XPS)等技术对样品进行表征,以亚甲基蓝(MB)的光催化降解为目标反应评价其光催化活性。结果表明,去核之后的复合微球为空心微球,壁厚为20 nm左右。钛酸四丁酯溶液的滴加时间对微球的形貌影响较大,当滴加时间大于15 min时,可以得到结构清晰的空心微球。用氢氧化钠溶液去除二氧化硅核,反应90 min,二氧化硅可以被完全去除。X射线衍射表明,实验得到的掺杂锌离子的空心微球和没有掺杂锌离子的空心微球都是锐钛矿。当锌离子的摩尔分数为0.3%时,二氧化钛空心微球的晶粒尺寸最小,比表面积最大,催化亚甲基蓝降解的效率最高。     

Preparation and Characterization of Polypyrrole/TiO2 Coaxial Nanocables

Summary: We demonstrate in this communication that large‐scale coaxial nanocables of polypyrrole (PPy)/TiO₂ can be obtained via three steps: (1) synthesis of TiO₂ nanofibers by electrospinning; (2) physical adsorption Fe³⁺ oxidant on the surface of TiO₂ nanofibers; (3) followed by polymerization of pyrrole (from vapor) on the surface of TiO₂ nanofibers. During the synthesis, the PPy formed on TiO₂ nanofibers as a template and formed PPy/TiO₂ coaxial nanocables. TEM image proved that PPy (20 nm thickness) covered the surface of TiO₂ nanofibers. Fourier‐transform infrared (FTIR), X‐ray photoelectron spectra (XPS), and X‐ray diffraction patterns (XRD) characterized the chemical structure of the coaxial nanocables. Surface photovoltage spectroscopy (SPS) revealed the surface properties of the PPy/TiO₂ coaxial nanocables.

TEM image of individual PPy/TiO₂ coaxial nanocable.     

Nanoscale composite materials in the system SiO2–TiO2

Nanoscale composite materials based on the SiO₂–TiO₂ system were prepared in the form of co-precipitated composites and core SiO₂–shell TiO₂ composites, with specific surface area 150–650 m²/g and sorption volumes 0.1–1.0 cm³/g. It is shown that variation of phase composition and morphology permits to change their structural-adsorption properties and nanocrystallites size after thermal treatment. It is discovered that co-precipitated composite materials differ from core SiO₂–shell TiO₂ composites by a component interaction degree. It determines the difference of the titan-containing component crystallization process and alteration of their structural-absorption properties after thermal treatment. The results of the tests of composites as photocatalysts for Rhodamine B decomposition reaction, as catalysts of Hantzsch and Biginelli reaction, and as fillers in electrorheological fluids are shown.     

静电自组装制备纳米TiO2/SiO2光催化材料

采用静电自组装方法制备了纳米TiO2/SiO2光催化材料。采用巯丙基三甲氧基硅烷偶联剂对SiO2进行干法改性,采用双氧水/冰醋酸将偶联剂巯基基团氧化为磺酸基基团。在正负电荷的吸引下,带负电荷的SiO2与带正电荷的钛聚合阳离子自发地组装在一起,经一定温度热处理得到纳米TiO2/SiO2光催化材料。采用XRD、FTIR、PL、UV-Vis DRS、SEM和ICP等对材料进行了分析和表征。采用甲基橙溶液评价材料的光催化性能。结果表明:SiO2促使锐钛矿的形成,抑制锐钛矿向金红石的转变,减小TiO2的晶粒尺寸,使得TiO2光吸收波长发生蓝移。TiO2与SiO2通过Si-O-Ti键发生结合。采用静电自组装方法制备的材料中TiO2的含量高于传统方法,导致材料的光催化性能有所提高。