Fe3O4@SiO2@mTiO2介孔多功能纳米复合颗粒的制备及载药能力

以溶剂热法制备氨基功能化的Fe_3O_4纳米颗粒为磁核,结合溶胶-凝胶法和模板法在其表面先后包覆上致密的SiO_2层和介孔TiO_2层,制备了磁性-发光-微波热转换性-介孔结构为一体的多功能核-壳结构纳米复合颗粒,并对其结构、性能及载药能力进行了研究。XRD分析表明:Fe_3O_4表面包覆上了无定形结构的SiO_2和TiO_2。TEM照片表明:所得的纳米复合颗粒具有明显的核壳结构和完美的球形,构成核的Fe_3O_4颗粒的尺寸在40~50 nm之间,Fe_3O_4@SiO_2@mTiO_2核壳结构纳米复合颗粒的尺寸为60~70 nm,壳层厚度约10 nm,并可观察到壳层中清晰的孔状结构。磁性、荧光光谱和微波热转换特性分析表明:该复合颗粒同时具有良好的发光性、磁性和微波热转换特性。N_2气吸附及药物负载率分析表明,该复合颗粒具有较高的比表面积(640 m~2·g~(-1))和介孔结构(孔径约2.8 nm)并且具有较高的药物负载率。     

Fe3O4@SiO2@polymer复合粒子的制备及在药物控制释放中的应用

本文通过多步反应制备了一种新型的、多层结构的、多功能的磁性纳米复合粒子, (Fe₃O₄@SiO₂@polymer). 纳米复合粒子内核是磁性Fe₃O₄纳米粒子, SiO₂包裹在Fe₃O₄上能够使其稳定分散和保护其不被腐蚀氧化; 中间层是生物相容的聚天冬氨酸(PAsp)载药层; 最外层是亲水的聚乙二醇(PEG)稳定层. 磁性纳米复合粒子各层都是生物相容的, 利用静电作用将抗癌药物阿霉素(DOX)负载在磁性纳米复合粒子中, 通过PAsp的pH响应调节了DOX的释放速率.     

核壳结构TiO2@SiO2催化碳酸二甲酯与苯酚酯交换合成碳酸二苯酯

以反相微乳液法和沉淀法相结合制备了核壳结构TiO₂@SiO₂,首次用于碳酸二甲酯与苯酚酯交换合成碳酸二苯酯反应,显示较好的催化活性. 采用200 ℃焙烧的TiO₂@SiO₂,用量0.20 g,反应9 h,苯酚转化率达41.8%,酯交换选择性为100%. 透射电镜显示TiO₂@SiO₂核厚壳薄,TiO₂核直径220-300 nm,SiO₂壳厚度40-60 nm,具有介孔结构. TiO₂@SiO₂对碳酸二甲酯与苯酚酯交换反应有好的重复使用性,使用4次苯酚转化率仍保持在40%以上. TiO₂与SiO₂发生相互作用,Ti进入骨架形成Ti-O-Si键,骨架Ti的形成提高了TiO₂@SiO₂的催化性能.     

中空Ta2O5/TiO2复合光催化剂的可控氧化制备及性能

以钛粉、钽粉为原料,炭黑作为反应性模板,通过熔盐法在炭黑表面原位生长了TaTiC₂纳米碳化物涂层,并以所得TaTiC₂/C复合物为碳化物前驱体,再经可控氧化制备出中空Ta₂O₅/TiO₂复合光催化剂。采用X射线粉末衍射（XRD）、扫描电子显微镜（SEM）、透射电子显微镜（TEM）、紫外-可见（UV-Vis）漫反射（DRS）及N₂物理吸附等手段对所制备的光催化剂进行形貌、显微结构及孔结构表征。以高压汞灯为紫外光源,以亚甲基蓝为目标降解物,通过光催化降解实验评价中空Ta₂O₅/TiO₂复合光催化剂的光催化活性。结果表明,熔盐法生长碳化物涂层厚度均匀（20~30 nm）,碳化物主要以TaTiC₂晶相存在且具有纳米级的颗粒尺寸。中空Ta₂O₅/TiO₂复合光催化剂同时具有200 nm左右的中空大孔结构及壳层10 nm左右的介孔结构。中空大孔和介孔的存在提高了所制备催化剂对亚甲基蓝的吸附能力。此外,TiO₂与Ta₂O₅通过电子能带结构的耦合,有效提高了光生电子和空穴的分离效率,从而显著提高了光催化活性。n_Ti∶n_Ta=2.5∶1.5时,相应的中空Ta₂O₅/TiO₂复合光催化剂表现出最佳的光催化活性,对亚甲基蓝的紫外光催化降解率高达97%。     

用于高效去除水中孔雀石绿的三层结构磁性复合材料Fe3O4@聚丙烯酸@ZiF-8的制备

设计并合成了一种以磁性纳米粒子为核，聚合物为中间层，金属有机骨架材料为外层的三层结构磁性复合材料(Fe₃O₄@PAA@ZIF 8)。首先利用溶剂热法制备Fe₃O₄纳米粒子，然后通过蒸馏沉淀聚合法在Fe₃O₄纳米粒子表面包覆聚丙烯酸(PAA)层，最后通过原位沉积法在PAA外部包覆ZIF 8。在对Fe₃O₄@PAA@ZIF 8的组成和结构进行表征的基础上，深入研究其对孔雀石绿(MG)的吸附性能。透射电子显微镜(TEM)显示 Fe₃O₄@PAA@ZIF 8 具有明显的三层结构，Fe₃O₄的平均粒径为 117nm，PAA 层厚度约为 17 nm，ZIF 8层的厚度约为 14 nm。Fe₃O₄@PAA@ZIF 8对 MG 的吸附量随着 pH 的升高而增大，吸附过程符合准二阶动力学模型和 Langmuir等温吸附模型。此外，Fe₃O₄@PAA@ZIF 8还表现出良好的重复利用性能，8次循环利用后对MG(500 mg·L^-1)的最大吸附量仍可达982 mg·g^-1。     

掺杂Fe2O3对吸附相反应技术制备TiO2的形貌和光催化性能的影响

利用吸附相反应技术制备得到了掺杂不同浓度的Fe₂O₃的TiO₂复合光催化剂。通过透射电子显微镜(TEM)、紫外可见光谱和X射线衍射(XRD)研究不同掺杂浓度对TiO₂形貌和结晶过程的影响,并利用3种波长光源下的甲基橙光降解实验考评了各个复合光催化剂的催化活性。结果表明,掺杂后复合光催化剂中Fe₂O₃分散性较好较均匀。在TiO₂紫外可见吸收光谱中由于Fe₂O₃的掺杂而出现了红移,而且随着掺杂浓度增加红移越来越明显,复合光催化剂的禁带宽度也越来越小。在焙烧过程中无定形Fe₂O₃或Fe³⁺进入了TiO₂的晶格结构,从而抑制了TiO₂的结晶过程。半导体禁带宽度的减少以及TiO₂结晶过程的抑制作用,都导致紫外光下复合光催化剂催化活性的降低。但Fe₂O₃的掺杂也使得复合光催化剂在可见光区出现了一定的光催化活性。     

核-隔层-壳结构Fe3O4@MoO3@mSiO2纳米载体的合成及其药物可控释放

利用加热均匀、迅速、热平稳性好和安全性高的微波热响应来实现药物的微波可控释放。引入具有微波热响应性质、热稳定性和化学稳定性好的MoO₃作为微波吸收物质,制备了核-隔层-壳结构Fe₃O₄@MoO₃@mSiO₂纳米药物载体。研究该纳米载体对药物布洛芬（IBU）的负载和微波响应可控释放过程。该纳米载体具有高的比表面积（222 cm²·g^-1）和较大的孔隙体积（0.14 cm³· g^-1）可用来负载药物。同时还具有较好的磁响应性,可实现药物的靶向给药,具有相对好的微波热响应性,可通过MoO₃中间层吸收微波辐射实现药物的可控释放。结果表明,在持续微波辐射360 min时IBU的释放率达到86%,远远高于仅搅拌时的释放率。     

SiO2/Co3O4核壳催化剂对AP热分解的催化性能研究

采用改良的Stöber法制备粒径约为200 nm的单分散球形SiO₂颗粒,以此为内核,分别通过液相沉淀法和尿素均匀沉淀法制备包覆形式不同的新型SiO₂/Co₃O₄核壳式纳米催化剂。采用X-射线衍射分析(XRD)、透射电子显微镜(TEM)、红外光谱分析(IR)、拉曼光谱分析(Raman)、BET比表面积测试等手段对产物进行表征,利用差式扫描量热仪(DSC)考察SiO₂/Co₃O₄复合物对高氯酸铵(AP)热分解反应的催化作用,探讨不同包覆形式对其催化活性的影响。结果表明,两种方法制备得到的SiO₂/Co₃O₄复合物分别为层包覆和粒子包覆,比表面积大,具有明显的核壳结构,且粒子包覆形式的SiO₂/Co₃O₄对AP热分解反应的催化效果最好,使AP的高温分解温度降低了110 ℃,放热量增加了662 J·g^-1。     

Ag@SiO2纳米颗粒的制备及其在H2O2检测上的应用

利用柠檬酸三钠还原硝酸银制备了银纳米颗粒(AgNPs), 然后通过氨水水解正硅酸乙酯(TEOS)的方法, 在AgNPs上沉积SiO₂, 制备出以Ag为核, SiO₂为壳的复合纳米颗粒(Ag@SiO₂). 调节TEOS用量, 可以控制SiO₂层的厚度. 根据AgNPs的局域表面等离激元共振(LSPR)效应, 将制得的Ag@SiO₂颗粒用于H₂O₂的检测, 检测下限为1 μmol/L, 并可以通过控制SiO₂层的厚度方便地调节Ag@SiO₂颗粒与H₂O₂反应的速率. 与传统方法相比, 具有简单、快速、成本低的优点. 分别运用TEM、紫外-可见分光光度计对反应前后Ag@SiO₂颗粒形貌及反应过程中其LSPR吸收的变化进行了表征.     

一锅法制备S型异质结光催化剂Fe2O3/Fe2TiO5及其高效降解有机污染物性能

首次采用简单的一锅法制备了Fe₂O₃/Fe₂TiO₅异质结纳米材料。构建S型异质结后,与纯的Fe₂O₃和Fe₂TiO₅相比,Fe₂O₃/Fe₂TiO₅复合材料表现出更高的光催化降解速率和效率。经过2.5 h的光照后,Fe₂O₃/Fe₂TiO₅可以降解接近100%的亚甲基蓝（MB）。在Fe₂O₃/Fe₂TiO₅复合材料中,Fe₂O₃和Fe₂TiO₅之间形成了内建电场,可以促进光生电子-空穴对的分离。因此,具有更高能量的Fe₂TiO₅导带中的电子和具有更高能量的Fe₂O₃价带中的空穴可以得到有效的保留,从而使它们更加有效地扩散到催化剂表面,并参加降解反应。此外,Fe₂O₃/Fe₂TiO₅复合材料具有很好的光催化稳定性。     

Li2O-TiO2-SiO2-P2O5和Li2O-TiO2-Al2O3-P2O5体系锂离子固体电解质的制备及性能研究

一些具有NASICON型网格结构的固体电解质具有高的电导率和好的稳定性,NASICON的意思是Na Super Ionic Conductor[1]。当NaZr2(PO4)3中P5 被Si4 部分取代时便可以得到具有NASICON结构的Na1 xZr2SixP3-xO12体系,其具有高的钠离子电导率。然而有相同结构的Li1 xZr2SixP3-xO12体系的离子电导率却很低,这是因为Li 半径太小,而NASICON三维网格结构的离子通道太大,两者不匹配而使电导率下降[2]。但当LiZr2(PO4)3中Zr4 被离子半径小些的Ti4 取代,所得LiTi2(PO4)3的通道就与Li 半径相匹配,适合于锂离子的迁移,从而使其电导率…     

Ion-beam irradiation of lanthanum compounds in the systems La2O3-Al2O3 and La2O3-TiO2

Thin crystals of La₂O₃, LaAlO₃, La_2/3TiO₃, La₂TiO₅, and La₂Ti₂O₇ have been irradiated in situ using 1 MeV Kr²⁺ ions at the Intermediate Voltage Electron Microscope-Tandem User Facility (IVEM-Tandem), Argonne National Laboratory (ANL). We observed that La₂O₃ remained crystalline to a fluence greater than 3.1×10¹⁶ ions cm⁻² at a temperature of 50 K. The four binary oxide compounds in the two systems were observed through the crystalline-amorphous transition as a function of ion fluence and temperature. Results from the ion irradiations give critical temperatures for amorphisation (T_c) of 647 K for LaAlO₃, 840 K for La₂Ti₂O₇, 865 K for La_2/3TiO₃, and 1027 K for La₂TiO₅. The T_c values observed in this study, together with previous data for Al₂O₃ and TiO₂, are discussed with reference to the melting points for the La₂O₃-Al₂O₃ and La₂O₃-TiO₂ systems and the different local environments within the four crystal structures. Results suggest that there is an observable inverse correlation between T_c and melting temperature (T_m) in the two systems. More complex relationships exist between T_c and crystal structure, with the stoichiometric perovskite LaAlO₃ being the most resistant to amorphisation.     

The reaction of MgCl2·4H2O with CCl2F2

A new reaction of MgCl₂·4H₂O with CCl₂F₂ is investigated by DTA and TG from room temperature to 350 °C. It is observed that MgF₂ was obtained between 252 and 350 °C, Below the temperature, MgCl₂·4H₂O dehydrates and hydrolyzes to MgCl₂ and Mg(OH)Cl, which are the real reactants of the reaction with CCl₂F₂. The formation of MgF₂ is ascribed to the reaction of MgCl₂ and Mg(OH)Cl with HF, which forms by decomposition of CCl₂F₂ with the taking part in of H₂O released from dehydration of hydrated magnesium chloride on the surface of MgCl₂ and Mg(OH)Cl, which catalyzes the decomposition of CCl₂F₂ in this case. Consequently, the reactions are tested in the fluid-bed condition. It is found that MgF₂ formed at temperatures down to 200 °C in a fluid-bed reactor. This reaction may be used as a method of disposing of the environmentally sensitive CCl₂F₂ (rather than release into the atmosphere). It is also a method for the preparation of MgF₂.     

Preparation of ZrO2-TiO2-CeO2 and Its Application in the Selective Catalytic Reduction of NO with NH3

TiO₂,ZrO₂-TiO₂,andZrO₂-TiO₂-CeO₂ were prepared by co-precipitation method and characterized by X-ray diffraction (XRD), specific surface area measurements (BET), temperature programmed desorption (NH₃-TPD), oxygen storage capacity (OSC), and temperature programmed reduction (H₂-TPR). The results showed that ZrO₂-TiO₂-CeO₂ exhibited large number of surface strong acid, possessed some oxygen storage capacity, and strong redox property. The three materials were used as supports and the monolith catalysts were prepared with 1% (w) V₂O₅ and 9% (w)WO₃ for selective catalytic reduction (SCR) of NO with ammonia in the presence of excessive O₂, and the results of catalytic activity showed that the catalyst used ZrO₂-TiO₂-CeO₂ as support yielded nearly 100% NO conversion at 275 °C at a gas hourly space velocity (GHSV) of 10000 h⁻¹, and it had the best catalytic activity and showed great potential for practical application.     

(Cl2AlNH2)n和(H2AlNH2)n(n=1～5)簇结构及其热力学性质

用HF自洽场理论和密度泛函理论(DFT)的B3LYP方法,在6 31G水平上研究了低聚物(Cl2AlNH2)n和(H2AlNH2)n(n=1～5)簇的几何构型、电子结构和聚合反应热力学性质,比较了两个系列化合物中化学键的强度.结果表明,Cl2AlNH2和H2AlNH2分子为C2 (EC)平面型结构,其中Al－N为由一个σ键和一个键组成的双键.(Cl2AlNH2)n和(H2AlNH2)n(n=1～5)分子为Dnh对称,Al－N是典型的σ单键 .低聚物(Cl2AlNH2)n和(H2AlNH2)n的稳定性顺序分别为: 3 > 2 > 4> 5 > 1和8 > 7 > 9 > 11 > 6.     

XRD and Si MAS-NMR spectroscopy across the β-Lu2Si2O7-β-Y2Si2O7 solid solution

Samples in the system Lu_2−xY_xSi₂O₇ (0?x?2) have been synthesized following the sol-gel method and calcined to 1300 °C, a temperature at which the β-polymorph is known to be the stable phase for the end-members Lu₂Si₂O₇ and Y₂Si₂O₇. The XRD patterns of all the compositions studied are compatible with the structure of the β-polymorph. Unit cell parameters are calculated as a function of composition from XRD patterns. They show a linear change with increasing Y content, which indicates a solid solubility of β-Y₂Si₂O₇ in β-Lu₂Si₂O₇ at 1300 °C. ²⁹Si MAS NMR spectra of the different members of the system agree with the XRD results, showing a linear decrease of the ²⁹Si chemical shift with increasing Y content. Finally, a correlation reported in the literature to predict ²⁹Si chemical shifts in silicates is applied here to obtain the theoretical variation in ²⁹Si chemical shift values in the system Lu₂Si₂O₇-Y₂Si₂O₇ and the results compare favorably with the values obtained experimentally.     

The crystal structure determinations and refinements of K2S2O7, KNaS2O7 and Na2S2O7 from X-ray powder and single crystal diffraction data

The crystal structures of K₂S₂O₇, KNaS₂O₇ and Na₂S₂O₇ have been solved and/or refined from X-ray synchrotron powder diffraction data and conventional single-crystal data. K₂S₂O₇: From powder diffraction data, monoclinic C2/c, Z=4, a=12.3653(2), b=7.3122(1), , β=93.0792(7)°, R_Bragg=0.096. KNaS₂O₇: From powder diffraction data; triclinic , Z=2, a=5.90476(9), b=7.2008(1), , α=101.7074(9), β=90.6960(7), γ=94.2403(9)°, R_Bragg=0.075. Na₂S₂O₇: From single-crystal data; triclinic , Z=2, a=6.7702(9), b=6.7975(10), , α=116.779(2), β=96.089(3), γ=84.000(3)°, R_F=0.033. The disulphate anions are essentially eclipsed. All three structures can be described as dichromate-like, where the alkali cations coordinate oxygens of the isolated disulphate groups in three-dimensional networks. The K-O and Na-O coordinations were determined from electron density topology and coordination geometry. The three structures have a cation-disulphate chain in common. In K₂S₂O₇ and Na₂S₂O₇ the neighbouring chains are antiparallel, while in KNaS₂O₇ the chains are parallel. The differences between the K₂S₂O₇ and Na₂S₂O₇ structures, with double-, respectively single-sided chain connections and straight, respectively, corrugated structural layers can be understood in terms of the differences in size and coordinating ability of the cations.     

EuZn2Si2 and EuZn2Ge2 Grown from Zn or Ga(ln)/Zn Flux

Single crystals of the novel ternary compounds EuZn₂Si₂ and EuZn₂Ge₂ were grown from pure gallium, indium, or zinc metal used as a flux solvent. Crystal properties were characterized using X-ray single-crystal analyses via Gandolfi and Weissenberg film techniques and by four-circle X-ray single-crystal diffractometry. The new compounds crystallize with ternary derivative structures of BaAl₄, i.e., EuZn₂Si₂ with ThCr₂Si₂-type (a=0.42607(2) nm, c=1.03956(5) nm, I4/mmm, R₁=0.038) and EuZn₂Ge₂ with CaBe₂Ge₂-type (a=0.43095(2) nm, c=1.07926(6) nm, P4/nmm, R₁=0.067). XAS and magnetic measurements on EuZn₂Si₂ and EuZn₂Ge₂ revealed in both compounds the presence of Eu²⁺ ions carrying large magnetic moments, which order magnetically at low temperatures. The magnetic phase transition occurs at T_N=16 and 7.5 K for the silicide and the germanide, respectively. In EuZn₂Si₂ there occurs a spin reorientation at 13 K and furthermore some canting of antiferromagnetically ordered moments below about 10 K. In EuZn₂Ge₂ a canted antiferromagnetic structure is formed just at T_N.     

Energetics of copper diphosphates – Cu2P2O7 and Cu3(P2O6OH)2

Differential scanning calorimetry and high temperature oxide melt solution calorimetry are used to study enthalpy of phase transition and enthalpies of formation of Cu₂P₂O₇ and Cu₃(P₂O₆OH)₂. α-Cu₂P₂O₇ is reversibly transformed to β-Cu₂P₂O₇ at 338–363 K with an enthalpy of phase transition of 0.15 ± 0.03 kJ mol⁻¹. Enthalpies of formation from oxides of α-Cu₂P₂O₇ and Cu₃(P₂O₆OH)₂ are −279.0 ± 1.4 kJ mol⁻¹ and −538.8 ± 2.7 kJ mol⁻¹, and their standard enthalpies of formation (enthalpy of formation from elements) are −2096.1 ± 4.3 kJ mol⁻¹ and −4302.7 ± 6.7 kJ mol⁻¹, respectively. The presence of hydrogen in diphosphate groups changes the geometry of Cu(II) and decreases acid–base interaction between oxide components in Cu₃(P₂O₆OH)₂, thus decreasing its thermodynamic stability.     

CeO2改性Ag-V2O5/TiO2催化剂的甲基吡啶氧化脱甲基性能

以锐钛矿TiO_2为载体,考察了CeO_2改性对Ag-CeO_2-V_2O_5/TiO_2催化3-甲基吡啶氧化脱甲基性能的影响,并优化了催化剂组成与制备条件.结果表明:Ce掺杂改性不仅能够与V物种作用形成Ce VO_4,而且促进V_2O_5分散,改善活性组分的氧化还原性能,从而提高3-甲基吡啶脱甲基转化率与选择性,改善Ag-V_2O_5/TiO_2催化性能.适宜的催化剂组成为V_2O_5负载量15%,Ce/V的摩尔比0.33,Ag质量分数1.0%.过高的焙烧温度将导致TiO_2载体向金红石型转变,Ag-CeO_2-V_2O_5/TiO_2适宜制备条件为450℃焙烧4 h.