锐钛矿型TiO2水溶胶的低温制备及其表征

Anatase titanium dioxide hydrosol was prepared at low temperature by a simple method. The title material was characterized by TEM, XRD, FTIR and BET, respectively. The photocatalytic activity of the as-prepared TiO₂ was evaluated by the degradation of methyl orange solution under sunlight and the photocatalytic oxidation of acetone in air. The results showed that the titanium dioxide hydrosol was composed of anatase phase with average grain size of about 7 nm, and the crystallinity became more perfect with the increase of temperature. The BET surface areas were more than 220 m²·g^-1 for these samples. It is found that the photocatalytic activity was much better for the higher heat processing temperature. Especially, the photocatalytic activity of the sample with a heat treatment of 110 ℃ was better than that of P25. In addition, TiO₂ hydrosol also possessed good photocatalytic activity under the sunlight illumination.     

掺钇锆酸锶-TiO2复合光催化剂的制备及性能研究

SrZrO₃ particles were prepared by a co-precipitation method and Sr(Zr_1-xY_x)O_3-δ -TiO₂ composite particles were then synthesized by Sr(Zr_1-xY_x)O_3-δ and titanium dioxide. The composite particles were characterized by XRD, SEM, FTIR and TG-DTA techniques. The photocatalytic degradation of methylene blue (MB) in aqueous solution was used as a probe reaction to evaluate the photocatalytic activity of the composite particles. The effect of the preparation method for SrZrO₃, doping content of yttrium and TiO₂ amount in the composite particles on the photocatalytic activity of composite particles was also discussed. The results show that the methylene blue solution could be completely degraded by Sr(Zr_1-xY_x)O_3-δ -TiO₂ composite particles under UV-light or visible light irradiation. The photocatalytic activity of composite particles was higher than that of pure TiO₂. The fast recombination of photogenerated electrons and holes were restrained by the heterojunction formed in composite particles. The particle of SrZrO₃ prepared by co-precipitation was small, and the photocatalytic activity of composite particles prepared from this kind of SrZrO₃ was higher than that of particles prepared by solid sintering method. The best doping content of yttrium is 5%. The optimal content of TiO₂ in composite particles is 90wt%, 70wt%, respectively under UV-light and visible light irradiation, the degradation rates of MB are 98.8% and 93.5% , respectively after 50 min irradiation.     

TiO2胶粒在铝合金表面的电泳沉积及所制薄膜的光催化性能研究

TiO₂ membranes were prepared on aluminum-alloy thin plates by electrophoretic deposition and dip coating in a colloid solution of TiO₂, respectively. The photocatalytic activity of TiO₂ membrane was compared using ethylene as reactant, and the crystal and morphological structure of the membrane were characterized by XRD and SEM. The results showed that a more compact membrane with high loading of TiO₂ but lower photocatalytic activity of unit TiO₂ mass was obtained by electrophoresis compared with dip coating method. The addition of polyethylene glycol (PEG) to the sol of TiO₂ could improve the specific photocatalytic activity (ethylene conversion per unit mass TiO₂ and unit area of membrane piece) of the electrophoresis-membrane prepared from the sol, but could not change the specific photocatalytic activity of the dip-coating membrane from the sol. The ethylene conversion on the electrophoresis membrane prepared from the sol containing PEG (50 g·L^-1) was 9 times of that on the dip coating membrane. The effect of PEG on the properties of electrophoresis-membrane of TiO₂ was attributed to the change of electrokinetic properties of sol. Addition of PEG decreased ζ potential value of the sol and the mobility of the sol particle, increased viscidity of the colloid, thus decreasing both the electrophoresis deposition velocity of colloid particles and the electroosmosis velocity of diffuse layer of colloid particles. These favored the formation of a low compact and porous membrane on the electrode in electric field, and thus increasing the availability of TiO₂ in photocatalytic process.     

TiO2 / SiO2核 / 壳结构复合粒子的组装及其电化学性能

TiO₂ coated SiO₂ materials as anode for lithium-ion batteries were synthesized via an in situ hydrolysis of tetraethyl orthosilicate under ultrasonic irradiation using nanometer-sized TiO₂ colloids as precursors. The XRD patterns indicate that the as-prepared core/shell particles remain anatase after calcining below 800 ℃. TEM observation shows that the particle size of TiO₂ / SiO₂ composites is ca. 200 nm, and a homogeneous SiO₂ layer is coated on the surfaces of TiO₂ particles. FTIR spectra demonstrate that SiO₂ could have been coated on the surfaces of TiO₂ particles via a chemical bonding. In addition, the first specific charge and discharge capacities of the coated particle electrode were 66.4 mAh·g^-1 and 90.7 mAh·g^-1, respectively, which indicates that the TiO₂ / SiO₂ particles are more stable than the monodispersed TiO₂. Meanwhile, the new material has good lithium intercalation-deintercalation performances.     

N 掺杂TiO2光催化剂的制备及其可见光活性研究

A visible-light-active photocatalyst was prepared by calcination of the hydrolysis product of tetrabutyl titanate with ammonia as precipitant. The photocatalyst was characterized by X-ray diffraction (XRD), UV-Vis diffuse reflection spectra (DRS), thermal gravimetric-differential thermal analysis (TG-DTA), X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM). The color of the photocatalyst was yellow and could absorb light wavelength under 550 nm as measured by DRS. The catalyst calcined at higher temperature will give lower absorbance for visible light. Structures of the sample were characterized mainly to be anatase by XRD except for the sample calcined at 700 ℃ which gave mixtures of anatase and rutile. TG-DTA results showed that temperature for anatase formation was 415 ℃. XPS results showed that doped-nitrogen was presented in the sample, they are important to show visible-light absorbency. The photocatalytic activities were evaluated using methyl orange and phenol as model pollutants, the results showed that over 90% of phenol could be degraded under visible light using N/TiO₂ as the catalyst after 4 hours reaction. Almost the same activity was found for the TiO₂ photocatalyst calcined at different temperature under sunlight but activities were different when the treatment was under UV light.     

碱土金属掺杂纳米TiO2催化剂的制备与光催化活性的评价

The nanometer TiO₂ were prepared by the hydrolyze-gel method and fellowed by doping alkaline-earth metals (Mg, Ca, Sr, Ba). XRD, SEM, diffuse reflection spectra were used to investigate their characteristices. The result indicates that the average particles size of the TiO₂ is about 80 nm and keep uniformity in distributing. The product was mainly anatase in 300～400 ℃ calcinations, the einstein shift of absorption spectrum was observed after doping the alkaline-earth metals. The best mole percentages of Mg, Ca, Sr and Ba are 0.5%, 1.0%, 1.5%, 1.5% respectively. Under the same reaction conditions, it is more effective to the UV-catalyed degradation reaction that the catalysts containing Mg and Ca were calcined at 300 ℃ for 1h or containing Sr and Ba were calcined at 400 ℃ for 1 h. The photocatalystic activity is considerably depondent on pH and the concentration of the oxidant. Using the sunlight to do the degradation experimental, the result also show that the doping catalysts has higher degradation efficiency than that of pure TiO₂.     

乙烯在纳米催化剂InVO4-TiO2上的可见光降解

The InVO₄-TiO₂ nano-crystalline photocatalyst was prepared by sol-gel method and characterized by DRS, FTIR, Raman and XRD. The photocatalytic activities of the prepared sample were investigated by photocatalytic degradation of ethylene in the gaseous phase under visible light irradiation (λ>450 nm). The results indicate that both of pure TiO₂ and InVO₄ or their simple mixture show no photocatalytic activities for degradation of ethylene under visible light irradiation. However, as-synthesized InVO₄-TiO₂ catalyzes the degradation of ethylene into CO₂ under visible light irradiation. In addition, the interaction between InVO₄ and TiO₂ results in some structural distortion to all the crystal forms of TiO₂ in as-synthesized catalyst InVO₄-TiO₂.     

多重射流燃烧反应制备的TiO2/ SiO2纳米复合颗粒的形态和结构

TiO₂-SiO₂ nanocomposite particles were prepared in premixed H₂ / Air flame, and the morphology and structure of these nanocomposites were characterized by FTIR, XRD, TEM and HRTEM. The morphology of SiO₂ / TiO₂ nanocomposites was different from that of pure TiO₂ or SiO₂ nanoparticles, and the chemical bond of Ti-O-Si was found in the nanocomposites indicating that the TiO₂ / SiO₂ nanocomposites were not merely a physical mixture of TiO₂ and SiO₂. TiO₂ nanocrystalline grains with sizes of 1～2 nm were homogeneously dispersed in the amorphous SiO₂ matrix when TiCl₄ and SiCl₄ were mixed at molecular level in the flame. The particle size and rutile content decreased with increasing of SiO₂ molar ratio.     

可见光催化剂S/TiO2的制备与表征

The sulfur-doped titanium dioxide (S/TiO₂) was prepared by calcinations. The photocatalytic decomposition of benzoic acid solution was carried out under simulated sun light; the photocatalytic activity is 2.7 times of TiO₂. The results of XRD show that the sulfur can restrain the crystallization transformation of TiO₂ from anatase to rutile, although the calcinations temperature has attained 500 ℃, the crystallization still is anatase entirely. The responsive wavelength range of S/TiO₂ was shifted; it has obvious absorption in the region from 320 to 550 nm. The S (S⁶⁺) substituted for some of the lattice titanium atoms in S/TiO₂. At the same time the XRF also prove the formation of S⁶⁺ and the atomic content is 2.13%.     

湿法水解制备可见光催化剂N/TiO2

The N/TiO₂ was prepared by wet hydrolyzation method. The photocatalytic decomposition of benzoic acid solution was carried out under simulated sun light; the photocatalytic activity was 2.47 times of TiO₂. The products were characterized by XRD, SPS, EFISPS and XPS, respectively. The results of XRD showed that the N could restrain the crystallization transformation of TiO₂ from anatase to rutile. The N/TiO₂ was still n-type semiconductor, and the absorbance wavelength appeared red-shifted by N-doping. The band gap of N/TiO₂ was decreased to 2.7 eV. The amount of doped-N is about 0.94at.%. The binding energy of N1s are 396.62 eV (Ti-N bonds, β-N) and 400.87 eV (N-N bonds, γ-N₂), respectively, and the photocatalytic activity of N/TiO₂ under visible light is related to the β-N. The N atoms replace the O of the TiO₂ and form the Ti-N bonding.     

微乳法合成纳米SiO2/TiO2及其光催化性能

采用聚乙二醇辛基苯基醚(Triton X-100)/正己醇/环己烷/氨水微乳体系合成了纳米TiO2和SiO2/TiO2复合物,用X射线衍射、红外光谱和透射电镜对其结构进行了表征,并以甲基橙降解评价了其光催化性能,讨论了SiO2/TiO2摩尔比、晶相组成及粒径与光催化活性的关系.结果表明,SiO2/TiO2催化剂中形成了新的Ti-O-Si键和无定形SiO2;在纳米TiO2中复合SiO2能有效抑制锐钛矿向金红石的转变,增加锐钛矿的稳定性,并阻止TiO2晶粒的聚集生长.催化剂的光催化活性随金红石含量的增加而降低,加入适量SiO2能明显提高TiO2的光催化活性,其中摩尔比为1/7的SiO2/TiO2光催化活性最高.     

Synthesis of nanosized TiO2/SiO2 particles using microwave processes and their photocatalytic activity on the decomposition of orange II

The nanosized titania and TiO₂/SiO₂ particles were prepared by the microwave-hydrothermal method. The effect of physical properties TTIP/TEOS ratio and calcination temperature has been investigated. The major phase of the pure TiO₂ particle is of the anatase structure, and a rutile peak was observed above 800°C. In TiO₂/SiO₂ particles, however, no significant rutile phase was observed, although the calcination temperature was 900°C. No peaks for the silica crystal phase were observed at either silica/titania ratio. The crystallite size of TiO₂/SiO₂ particles decreases as compared to pure TiO₂ at high calcination temperatures. The TiO₂/SiO₂ particles show higher activity on the photocatalytic decomposition of orange II as compared to pure TiO₂ particles.     

TiO2-CoFe2O4磁性复合材料制备及太阳光催化性能

以四氯化钛、三价铁盐和二价钴盐为前驱体,采用超声波技术一步合成了TiO2-CoFe2O4新型复合光催化剂,运用VSM、XRD、TEM和UV-Vis技术进行了表征,以甲基橙为模拟污染物在太阳光照射下研究其光催化活性。结果表明:所制得的样品具有良好的顺磁性,其饱和磁化强度为212 Gs;样品中TiO2和CoFe2O4分别以锐钛矿相和尖晶石结构存在,粒径尺寸在40～50 nm之间;样品在紫外-可见区有很强的吸收。光催化结果表明复合催化剂具有较高的太阳光催化活性,循环使用3次,仍能保持良好的催化活性。     

溶胶-凝胶法制备复合MxOy-TiO2光催化剂

以无机盐TiCl4为原料制备TiO2溶胶,并利用溶胶胶粒修饰法制备SiO2 TiO2、ZrO2 TiO2、WO3 TiO3、MoO3 TiO2及Pt/TiO2光催化剂,用于光催化氧化甲醛反应,考察添加物对 催化剂光催化性能的影响.其中,SiO2 TiO2催化剂的光催化氧化降解甲醛性能最好,而MoO3 TiO2的催化性能最差.SiO2 TiO2催化剂优良的光催化性能可归于SiO2 TiO2催化剂的高 比表面积,高空隙率,小晶粒粒径和强吸光性能等性质的综合影响.     

钛酸纳米管前驱体水热制备TiO2：水热媒介对结晶度及光催化活性的影响

以钛酸纳米管为先驱体,180℃24 h同一水热条件下,利用H2O、HNO3、KBF4以及HNO3+KBF4的4种水热媒介溶液,制备了高结晶度高光催化活性的TiO2,并研究了水热媒介对TiO2结晶度、表面羟基和光催化活性的影响。通过扫描电镜(SEM)、X射线衍射(XRD)、红外测试(FTIR)、X射线光电子能谱(XPS)、紫外可见漫反射吸收光谱(UV-Vis)进行了结构表征。光催化活性通过降解甲基橙溶液进行了评价。结果表明,与其他3种媒介相比,HNO3+KBF4溶液为水热媒介制备的锐钛矿晶型TiO2,结晶度高,表面羟基含量高,因此,呈现高的光催化活性。     

Bi2O3 /TiO2复合纳米颗粒的可见光光催化性能

采用溶胶与水热相结合的方法合成了具有可见光光催化活性的复合纳米颗粒Bi2O3/TiO2,并对其进行了X射线衍射、透射电镜、X射线光电子能谱、紫外-可见漫反射谱、红外光谱、低温N2吸附脱附及电子顺磁共振分析。结果表明,复合少量的氧化铋可显著抑制TiO2由锐钛矿到金红石的相转移过程,并将光吸收范围扩展到可见光区。可见光照射下(λ>420 nm),利用电子顺磁共振技术检测到明显的羟基自由基(.OH)信号。铋的最佳掺杂量为Bi/Ti质量比2.0%,适量铋的掺入能显著改善锐钛矿TiO2的结晶度,抑制光生电子-空穴对的复合,提高光催化量子效率。通过可见光照射下,4-氯酚的降解实验测试Bi2O3/TiO2复合纳米颗粒的可见光光催化活性。同时,利用气-质联用仪对4-氯酚降解过程的中间产物进行了测定,并提出可见光照射下的Bi2O3光敏化机理。     

MCM-41分子筛担载纳米TiO2复合材料光催化降解罗丹明B

采用溶胶-凝胶法将TiO2担载在介孔MCM-41分子筛上, 制备了不同TiO2含量的系列TiO2/MCM-41复合材料, 利用X射线衍射、N2吸附、紫外-可见光谱和透射电镜等方法对其进行表征. TiO2的晶型为锐钛矿相, 复合材料的比表面积和孔体积随其中TiO2担载量(复合材料中TiO2与MCM-41的质量比)的增加而减小, TiO2的平均粒径随其担载量的增加而增大. 以罗丹明B的光催化降解为探针反应, 评价了TiO2/MCM-41复合材料的光催化降解活性. 结果表明, 在紫外光照射下, 罗丹明B在该复合材料上的光催化降解反应遵循一级反应动力学, 复合材料对罗丹明B的光催化降解活性明显高于商用TiO2 (P-25), 复合材料的光催化降解活性由复合材料的吸附能力和所含TiO2的光催化活性共同决定.     

低温下溶胶凝胶法制备TiO2纳米晶

从含过量水的溶胶出发,在室温下得到了TiO₂纳米晶。通过红外光谱,透射电子显微镜法和X射线粉末衍射法对含有过量水的溶胶体系中TiO₂纳米晶的室温形成机理进行了研究。与传统的溶胶凝胶法相比,在改良的溶胶凝胶体系中,在缩聚反应之前由于水过量使得钛的先驱体快速且充分的水解,从而生成[TiO₆]基团,随之形成TiO₂纳米晶。晶粒的尺寸为约3.5 nm,该法得到的TiO₂纳米晶比传统溶胶凝胶法得到的TiO₂纳米晶和商用光催化剂德固赛P25具有更好的光催化活性。     

Synthesis of bimodal porous structured TiO2 microsphere with high photocatalytic activity for water treatment

In this work bimodal structured titanium dioxide (TiO₂) microsphere has been prepared from commercial TiO₂ powder and nano-sized titania gel via sol–gel spray-coating technique. Crystallization and transformation behavior of titania gel were investigated. The results revealed that the crystallization and transformation of anatase particles were substantially affected by the concentration of solvent and calcination temperature. Anatase crystallite size of 10 nm was obtained at mole ratio of solvent/precursor 50/1 and calcination temperature of 450 °C. The prepared nano-sized titania gel was embedded within the core (commercial TiO₂, P25) during the spraying process. The prepared TiO₂ microsphere was characterized using X-ray diffractometer (XRD), scanning electron microscope (SEM), field emission electron microscope (FESEM) and micropore analysis. The photocatalytic activity was monitored by following the degradation of phenol with activity benchmarked against commercial P25 (Degussa). The increase of photocatalytic activity of TiO₂ microsphere was attributed to the nano-sized anatase crystallite which has been incorporated into the TiO₂ microsphere.