微乳法制备纳米TiO2 /SiO2的结构及光催化研究

Nanosized TiO₂ and TiO₂/SiO₂ particles were prepared by hydrolysis of tetrabutyl titanate (TBOT) and tetraethyl orthosilicate (TEOS) in the TX-100 reverse microemulsion. These particles were characterized by TG-DSC, XRD, FTIR, TEM，N₂ adsorption-desorption. Their photocatalytic activity was tested by degradation of methyl orange. The result shows that TiO₂/SiO₂ nanoparticles are with a monodispersed spherical phase and a uniform size distribution，and TiO₂ particles are dispersed on the surface of SiO₂. The band for Ti-O-Si vibration in FTIR was observed, the Ti-O-Si bond increased the stability of anatase TiO₂, suppressed the phase transformation of titania from anatase to rutile. And due to the addition of SiO₂, the average size of titania decreased from 38 nm in pure TiO₂ to 5 nm in TiO₂/SiO₂. It was found, under UV light irradiation, TiO₂/SiO₂ particles showed higher activity than pure TiO₂, and TiO₂/SiO₂(1/1) particles showed the highest photocatalytic activity on the photocatalytic decomposition of methyl orange, which was influenced by crystal structure, particle size, crystallinity and Surface area Characteristics.     

微乳法合成纳米SiO2/TiO2及其光催化性能

采用聚乙二醇辛基苯基醚(Triton X-100)/正己醇/环己烷/氨水微乳体系合成了纳米TiO2和SiO2/TiO2复合物,用X射线衍射、红外光谱和透射电镜对其结构进行了表征,并以甲基橙降解评价了其光催化性能,讨论了SiO2/TiO2摩尔比、晶相组成及粒径与光催化活性的关系.结果表明,SiO2/TiO2催化剂中形成了新的Ti-O-Si键和无定形SiO2;在纳米TiO2中复合SiO2能有效抑制锐钛矿向金红石的转变,增加锐钛矿的稳定性,并阻止TiO2晶粒的聚集生长.催化剂的光催化活性随金红石含量的增加而降低,加入适量SiO2能明显提高TiO2的光催化活性,其中摩尔比为1/7的SiO2/TiO2光催化活性最高.