低温CVD法在玻璃衬底上制备ZnO纳米线阵列

采用化学气相沉积(CVD)法在镀Cr(20nm)的玻璃衬底上,低温制备了ZnO纳米线阵列。利用扫描电子显微镜(SEM)和X射线衍射(XRD)对样品的表面形貌和微结构进行了分析表征。结果表明:源分解温度1350℃,衬底温度450～500℃,氩气流量为35sccm时,ZnO纳米线在玻璃衬底上呈现有序生长;XRD谱图中只观测到ZnO(002)衍射峰。表明制备的纳米线阵列具有高度c轴择优取向生长特性和较高的结晶质量。     

ZnO薄膜的制备和结构特性及应变

在SiO₂/Si衬底上面,利用射频磁控溅射方法,在不同的工艺条件下生长ZnO薄膜,然后进行热处理(600～1000℃退火).研究了氩氧比和退火温度对薄膜结晶性能的影响.薄膜的表面结构和晶体特性通过扫描电子显微镜(SEM)、X射线衍射(XRD)来进行表征.结果表明:所制备的薄膜为多晶纤锌矿结构,具有垂直于衬底的c轴(002)方向的择优取向性.热处理可使ZnO(002)衍射峰相对强度增强,半峰全宽(FWHM)变小,即退火使c轴生长的薄膜取向性增强.未经退火的ZnO薄膜存在张应力,经过热处理后应力发生改变,最后变成压应力,并且随着退火温度的升高,压应力逐渐增大.     

MOCVD方法生长ZnO微米柱的结构与光学性质

通过X射线衍射、扫描电子显微镜和变温光致发光光谱对MOCVD方法生长在蓝宝石衬底上的ZnO微米柱材料的结构及发光特性进行了表征.X射线衍射结果表明,ZnO具有良好的c轴择优取向,扫描电子显微镜图中可观察出ZnO微米在呈六角结构生长,半径约为0.5～1.5μm.样品的发光光谱通过He-Cd激光器的325nm线激发,从光谱中发现低温(81K)下出现极强的与激子相关的带边发光峰,温度升高到360K时与自由激子相关的紫外发射峰仍然是清晰可见.     

退火对ZnO薄膜光学特性的影响

用射频磁控溅射法在蓝宝石衬底上制备出ZnO薄膜,通过X射线衍射(XRD)、扫描电镜(SEM)和光致发光(PL)谱等研究了退火温度对ZnO薄膜结构和光学性质的影响。测量结果显示,所制备的ZnO薄膜为六角纤锌矿结构,具有沿c轴的择优取向;随着退火温度的升高,(002)XRD峰强度和平均晶粒尺寸增大,(002)XRD峰半高宽(FWHM)减小,光致发光紫外峰强度增强。结果证明,用射频磁控溅射法通过适当控制退火温度可得到高质量ZnO薄膜。     

利用P-MBE方法在(400)Si衬底上生长ZnO薄膜

利用等离子体辅助分子束外延(P-MBE)方法在(400)Si衬底上生长ZnO薄膜。为改善生长后样品的质量,把样品解理成三块后,在不同温度下氧气气氛中退火。通过X射线衍射(XRD)谱和光致发光(PL)谱进行表征,讨论了用P-MBE方法在Si基上生长的ZnO的室温光致发光发光峰的可能原因。     

气相输运法制备ZnO薄膜(英文)

运用气相输运技术在不同的衬底上制备ZnO薄膜,同时对这些ZnO薄膜的表面形貌、晶体结构和光学特性进行表征。在扫描电子显微镜图像上可以看到,相比没有镀金的Si衬底,ZnO纳米颗粒在镀金的Si衬底上的生长尺寸较大。X射线衍射测试结果表明,在Si(111)和Si(100)衬底上生长的ZnO薄膜显示出不同的六角纤锌矿结构的衍射峰,但没有出现立方闪锌矿ZnO结构的衍射峰。在镀金的Si衬底上,ZnO薄膜生长取向主要为c轴方向。此外,所有ZnO样品的光致发光谱上均只出现一个狭窄且强的紫外峰,约在389 nm(3.19 eV)波长处。     

PLD方法制备的ZnO纳米柱结构及光学特性

采用无催化脉冲激光沉积(PLD)方法,在InP(100)衬底上生长纳米ZnO柱状结构。采用扫描电子显微镜(SEM)、X射线衍射(XRD)以及光致发光(PL)谱等表征手段对ZnO纳米柱的形貌、晶体结构和光学特性进行了观察。SEM图像观察到ZnO纳米柱状结构具有一定的取向性;XRD测试在2θ=34.10°处观测到强的ZnO(002)衍射峰,证实ZnO纳米柱具有较好的c轴择优取向;室温PL谱在379nm处观察到了强的自由激子发射峰(半峰全宽为19nm),未探测到深能级跃迁发射峰,表明生长的纳米ZnO结构具有很高的光学质量。     

低温缓冲层对氧化锌薄膜质量的影响

利用金属有机化学气相沉积(MOCVD)法,在Si衬底上外延生长ZnO薄膜。为了改善氧化锌薄膜的质量,首先在Si衬底上生长低温ZnO缓冲层,然后再生长高质量的ZnO薄膜。通过XRD、SEM、光致发光(PL)光谱的实验研究,发现低温ZnO缓冲层可有效降低ZnO薄膜和Si衬底之间的晶格失配以及因热膨胀系数不同引起的晶格畸变。利用低温缓冲层生长的ZnO薄膜的(002)面衍射峰的强度要比直接在Si上生长的ZnO薄膜样品的高,并且衍射峰的半高宽也由0.21°减小到0.18°,同时有低温缓冲层的样品室温下的光致发光峰也有了明显的增高。这说明利用低温缓冲层生长的ZnO薄膜的结晶质量和光学性质都得到了明显改善。     

联合体驱使生长法制备ZnO纳米棒及其表征

在常压环境下采用联合体驱使生长(Aggregation-driven growth)法在镀有ZnO纳米薄膜的医用盖玻片衬底和锌箔上制备了不同直径、高取向、密集生长的ZnO纳米棒阵列结构,发现平均直径与生长时间呈线性关系。X射线衍射(XRD)谱图中出现了较强的(002)峰,表明制备的纳米棒阵列具有高度c轴择优生长取向;高分辨透射电子显微镜(HRTEM)和选区电子花样衍射图谱(SAED)结果表明我们得到的单根纳米棒为沿(002)生长的单晶结构。分析确定盖玻片上的纳米棒阵列是以ZnO纳米薄膜缓冲层上的ZnO种子颗粒为成核点生长形成的。     

ZnO薄膜的分子束外延生长及性能

利用分子束外延(MBE)和氧等离子体源辅助MBE方法分别在Si(100)、GaAs(100)和蓝宝石Al2O3(0001)衬底上用Zn、ZnS或以一定Zn-O化学计量比作缓冲层,改变衬底生长温度和氧压,并在氧气氛下,进行原位退火处理,得到ZnO薄膜。依据X射线衍射(XRD)图,表明样品的结晶性能尚好,且呈c轴择优取向;实验结果表明在不同衬底上生长的ZnO薄膜,由于晶格失配度不同,其衍射峰也有区别。用原子力显微镜(AFM)观测薄膜的表面形貌,为晶粒尺寸约几十纳米的ZnO纳米晶,且ZnO晶粒呈六边形柱状垂直于衬底的表面。采用掠入射X射线反射率法测膜厚。在360nm激发下,样品的发光光谱是峰值为410,510nm的双峰谱,是与样品表面氧缺陷有关的深能级发光。     

利用MOCVD技术生长As掺杂的p-ZnMgO薄膜

利用GaAs夹层掺杂的新方法,采用金属有机化学气相沉积(MOVCD)技术,通过控制生长温度,在蓝宝石衬底上成功制备出As掺杂的p型ZnMgO薄膜.利用X射线衍射分析(XRD)、霍尔效应测试和光致发光(PL)谱等表征方法对薄膜的晶体结构、电学性能和光学特性进行分析.结果表明:高温生长的ZnMgO薄膜具有良好的c轴取向性;...     

基于旋涂法和电子束蒸发法制备的V2O5/Ag/V2O5叠层透明导电薄膜

利用溶胶-凝胶技术与电子束蒸镀相结合的方法在常温下制备了叠层V₂O₅/Ag/V₂O₅（VAV）透明导电薄膜,研究了各层薄膜厚度对叠层结构光电特性的影响。用原子力显微镜、紫外-可见光分光光度计、四探针电阻仪及开尔文探针对样品的表面形貌、光电性能及功函数等性质进行了表征。实验结果表明,该薄膜具有良好的光学和电学性质,可见光（380~780 nm）平均透过率达75%,迁移率为16.89 cm²/（V·s）,载流子浓度为－1.043×10²² cm^-3,方块电阻值为15.1 Ω/□,功函数为5.17 eV。该制备方法降低了V₂O₅薄膜的工艺制备难度,为该材料在太阳能电池中的应用创造了良好的前期基础。     

Superior material qualities and transport properties of InGaN channel heterostructure grown by pulsed metal organic chemical vapor deposition

Pulsed metal organic chemical vapor deposition is introduced into the growth of In Ga N channel heterostructure for improving material qualities and transport properties. High-resolution transmission electron microscopy imaging shows the phase separation free In Ga N channel with smooth and abrupt interface. A very high two-dimensional electron gas density of approximately 1.85 × 1013cm-2is obtained due to the superior carrier confinement. In addition, the Hall mobility reaches 967 cm2/V·s, owing to the suppression of interface roughness scattering. Furthermore, temperature-dependent Hall measurement results show that In Ga N channel heterostructure possesses a steady two-dimensional electron gas density over the tested temperature range, and has superior transport properties at elevated temperatures compared with the traditional Ga N channel heterostructure. The gratifying results imply that In Ga N channel heterostructure grown by pulsed metal organic chemical vapor deposition is a promising candidate for microwave power devices.     

铟锡氧化物薄膜表面等离子体损耗降低的研究

本文采用直流磁控溅射方法在普通浮法玻璃基底上制备了立方多晶铁锰矿结构的铟锡氧化物(indium tin oxide, ITO)薄膜,并对其进行了结晶性、表面粗糙度、紫外-可见吸收光谱、折射率、介电常数及霍尔效应的测试.研究了溅射时基底温度的改变对于ITO薄膜的光电、表面等离子体性质的影响.随着基底温度由100?C升高至500?C,其光学带隙(3.64—3.97eV)展宽,减少了电子带间跃迁的概率,有效降低了ITO薄膜的光学损耗.与此同时,对应ITO薄膜的载流子浓度(4.1×10~(20)-—2.48×10~(21)cm~(-3))与迁移率(24.6—32.2 cm~2·V~(-1)·s~(-1))得到提高,电学损耗明显降低.     

旋涂法制备氧化锆介质层及其在薄膜晶体管中的应用

采用旋涂法制备了氧化锆介质层薄膜,重点讨论了退火温度以及旋涂转速对薄膜性能的影响及作用机制。研究发现高温后退火一方面使得氧化锆水合物脱水形成氧化锆,另一方面促使氧化锆薄膜结晶。此外,转速较高时,其变化对薄膜厚度及粗糙度无显著影响。当转速为5 000 r/min、退火温度为300℃时,制备的绝缘层厚度具有良好的厚度均匀性,粗糙度为0.7 nm,漏电流为3.13×10^-5 A/cm²（电场强度1 MV/cm）。最终,利用ZrO₂薄膜作为栅极绝缘层,在玻璃基板上制备了铟镓锌氧化物-薄膜晶体管（IGZO-TFT）,其迁移率为6.5 cm²/（V·s）,开关比为2×10⁴。     

Al组分对MOCVD制备的AlxGa1-xN/AlN/GaN HEMT电学和结构性质的影响

采用金属有机化合物化学气相沉积（MOCVD）方法制备了不同Al组分（x=0.19,0.22,0.25,0.32）的Al_xGa_1-xN/AlN/GaN 结构的高电子迁移率晶体管（HEMT）材料。研究了Al_xGa_1-xN势垒层中Al组分对HEMT材料电学性质和结构性质的影响。研究结果表明,在一定的Al组分范围内,二维电子气（2DEG）浓度和迁移率随着Al组分的升高而增大。然而,过高的Al组分导致HEMT材料表面粗糙度增大,2DEG迁移率降低,该实验现象在另一方面得到了原子力显微镜测试结果的验证。在最佳Al组分（25%）范围内,获得的 HEMT材料的2DEG浓度和室温迁移率分别达到1.2×10¹³ cm^-2和1 680 cm²/（V·s）,方块电阻低至310 Ω/□。     

高阻GaN的MOCVD外延生长

利用金属有机化合物气相沉积(MOCVD)在蓝宝石衬底上生长了高阻GaN薄膜。对GaN成核层生长的反应室压力、生长时间和载气类型对GaN缓冲层电学特性的影响进行了分析。实验结果表明,延长GaN成核层的生长时间,降低成核层生长时的反应室压力,载气由H₂换为N₂都会得到高阻的GaN缓冲层。样品的方块电阻R_s最高为2.49×10¹¹ Ω/□。以高阻GaN样品为衬底制备了AlGaN/AlN/GaN结构HEMT器件,迁移率最高达1 230 cm²/(V·s)。     

不同织构CVD金刚石膜的Hall效应特性

采用热丝化学气相沉积法在p型硅衬底上制备了不同织构的多晶金刚石膜,使用XRD表征了CVD金刚石膜的结构特征, 研究了退火后不同织构金刚石膜的电流特性, 使用Hall效应检测仪研究了金刚石膜的霍尔效应特性及随温度变化的规律, 结果表明所制备的金刚石膜是p型材料, 载流子浓度随着温度的降低而增加, 迁移率随着温度的降低而减小. 室温下[100]织构金刚石薄膜的载流子浓度和迁移率分别为4.3×10⁴ cm^-3和76.5 cm²/V·s.     

生长温度对MOCVD外延ZnO纳米结构的影响

为了探究生长温度对外延ZnO纳米结构的影响,得到ZnO纳米结构可控生长的生长温度条件。利用金属有机化学气相沉积（MOCVD）方法,设计并获得了不同生长温度的ZnO外延样品,并对所有样品进行了表面形貌、光学特性、电学特性表征和结晶质量表征。实验结果表明:600℃生长的ZnO纳米柱横向尺寸最小,为65 nm左右,其光学特性也相对较好,晶体衍射峰的半峰宽最小,为0.165°,晶粒尺寸最大,为47.6 nm;电学性质相对最优的为640℃生长的ZnO样品,霍尔迁移率高达23.5 cm²/（V·s）。通过结果分析发现,生长温度能影响外延ZnO的生长模式,从而影响ZnO的形貌、光学、电学和晶体质量等特性。     

α-四噻吩薄膜的生长及性能研究

利用原子力显微镜(AFM)、X射线衍射仪(XRD)研究了在氧化硅衬底上生长的α-四噻吩(α-4T)薄膜的表面形貌及分子取向。在低温下,获得了大尺寸、高有序的α-4T薄膜,为横向生长模式。衬底温度35 ℃以上转为纵向生长模式。晶体结构分析发现,α-4T薄膜属于单斜晶系,分子c-轴垂直基板排列。强的衍射峰和高有序的衍射峰意味着α-4T薄膜具有高的有序性和结晶性。电性能研究发现,提高衬底温度有利于提高薄膜的迁移率,衬底温度为35 ℃时器件迁移率为3.53×10^-2 cm²·V^-1·s^-1。但衬底温度进一步增加,迁移率反而下降,与原子力分析结果一致。低温退火可以降低器件的亚阈值陡度,从13.27 V·dec^-1降低到3.83 V·dec^-1,使器件的界面缺陷降低,电性能提高。