(Bi,La)4Ti3O12-Sr(Bi,La)4Ti4O15共生结构铁电材料性能研究

采用固相烧结工艺，制备了不同La掺杂量(x=0.00，0.25，0.50，0.75，1.00，1.25和1.50) 的(Bi, La)₄Ti₃O₁₂-Sr(Bi, La)₄Ti4O₁₅ (SrBi_8-xLa_xT i₇O₂₇)共生结构铁电陶瓷样品.用x射线衍射对其进行微结构分析 ，并测量铁 关键词： 4Ti₃O₁₂-SrBi₄Ti₄O₁₅')" href="#">Bi₄Ti₃O₁₂-SrBi₄Ti_{4O15 La掺杂 铁电性能 居里温度 弛豫铁电}     

Mo掺杂SrBi4Ti4O15陶瓷的铁电介电性能

用传统的固相烧结工艺，制备了钼掺杂铁电陶瓷样品SrBi₄Ti₄O₁₅(SBTi)铁电陶瓷SrBi_4-2x/3Ti_4-xMo_xO₁₅(x=0.00，0.003，0.012，0.03，0.06，0.09).X射线衍射的结果表明，样品均为单一的层状钙钛矿结构相，Mo掺杂未改变SBTi的晶体结构.通过扫描电子显微镜观测发现，样品晶粒为片状，随掺杂量的增加，晶粒逐 关键词： 4Ti₄O₁₅')" href="#">SrBi₄Ti₄O₁₅ Mo掺杂 剩余极化 居里温度     

B位等价掺杂SrBi4Ti4O15铁电材料的性能研究

采用了传统的固相烧结工艺,制备了不同Zr和Hf掺杂量的SrBi₄Ti_4-xZr_xO₁₅（x=000,003, 006,010,020）和SrBi₄Ti_4－xHf_xO₁₅（x=000,0005, 0015,0030,0060）的陶瓷 关键词： 4Ti_4-xZr_xO₁₅')" href="#">SrBi₄Ti_4-xZr_xO₁₅ 4Ti_4－xHf_xO₁₅')" href="#">SrBi₄Ti_4－xHf_xO₁₅ 铁电性能 介电性能     

Dy掺杂对Sr2Bi4Ti5O18铁电陶瓷性能的影响

用传统固相烧结法制备了Sr₂Bi_4-xDy_xTi₅ O₁₈(SBDT-x, x=0—0.20)陶瓷样品. x射线衍射分析表明, 微量的Dy掺杂没有影 响Sr₂Bi₄Ti₅O₁₈(SBTi) 原有的层状钙钛 矿结构. 通过研究样品的介电特性, 发现Dy掺杂减小了材料的损耗因子, 降低了样品铁电- 顺电相转变的居里温度. 铁电性能测量结果表明, 随Dy含量的增加, SBDT-x系列样品的剩余 极化先增大, 后减小. 当Dy掺杂量为0.01时, 剩余极化达到最大值, 约为20.1 μC·cm^-2. 掺杂引起剩余极化的变化, 与材料中缺陷浓度、内应力以及晶格畸变程度等因 素有关, 是多种作用机理相互竞争的结果. (Bi₂O₂)²⁺ 层通常被看作是绝缘层和空间电荷库, 对材料的铁电性能起关键作用. 掺杂离子进入(Bi2O₂)²⁺层会导致铁电性能变差. 关键词： 2Bi₄Ti₅O₁₈陶瓷')" href="#">Sr₂Bi₄Ti₅O₁₈陶瓷 Dy掺 杂 铁电性能 居里温度     

La掺杂诱发层状钙钛矿型铁电体弛豫性相变的介电研究

制备了La掺杂层状钙钛矿铁电体材料SrBi₄Ti₄O₁₅, Sr₂Bi₄Ti₅O₁₈以及共生结构Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅，通过研究样品的变温介电特性发现，SrBi_4-xLa_{x 关键词： 弛豫性相变 微畴-宏畴 层状钙钛矿 介电性能}     

La掺杂对Bi4Ti3O12薄膜铁电性能的影响

利用Sol-Gel法在Pt/Ti/SiO₂/Si衬底上制备出Bi₄Ti₃O₁₂和Bi_3.25La_0.75Ti₃O₁₂薄膜，研究了La掺杂对Bi₄Ti₃O₁₂薄膜的晶体结构、铁电性能和疲劳特性的影响，发现La掺杂没有改变Bi₄Ti₃O₁₂薄膜的基本晶体结构，并且提高了Bi₄Ti₃O₁₂铁电薄膜的剩余极化值和抗疲劳性能，对La掺杂改善Bi₄Ti₃O₁₂铁电薄膜性能的机理进行了讨论. 关键词： 铁电性能 4Ti₃O₁₂薄膜')" href="#">Bi₄Ti₃O₁₂薄膜 3.25La_0.75Ti₃O₁₂薄膜')" href="#">Bi_3.25La_0.75Ti₃O₁₂薄膜 sol-gel法 La掺杂     

SrBi2Ta2O9/Bi4Ti3O12复合铁电薄膜的制备与特性研究

采用溶胶凝胶工艺在p-Si衬底上制备了SrBi₂Ta₂O₉/Bi₄Ti₃O₁₂复合铁电薄膜. 研究了SrBi₂Ta₂O₉/Bi₄Ti₃O₁₂复合薄膜的微观结构与生长行为、铁电性能和疲劳特性. 研究表明: Si衬底Bi₄Ti< 关键词： 2Ta₂O₉')" href="#">SrBi₂Ta₂O₉ 4Ti₃O₁₂')" href="#">Bi₄Ti₃O₁₂ 复合铁电薄膜 溶胶凝胶工艺     

SrBi4Ti4O15的化学键性质和铁电性研究

通过原子环境计算方法分析了正交相SrBi₄Ti₄O₁₅晶体内的键络结构、各原子的空间配位数及局域团簇结构. 在此基础上, 结合晶体分解理论将SrBi₄Ti₄O₁₅晶体分解为多个二元赝晶体, 根据化学键介电理论计算得到各赝晶体所对应化学键的有效价电子密度、离子性等化学键性质. 通过键偶极矩建立了铁电体自发极化强度与化学键性质之间的关系, 求得正交相SrBi₄Ti₄O₁₅沿a轴方向的自发极化强度为28.03 μC/cm², 与实验结果和其他理论计算值符合较好.     

Ag/Bi4Ti3O12栅n沟道铁电场效应晶体管制备及存储特性

在溶胶-凝胶工艺获得高质量Bi₄Ti₃O₁₂薄膜的基础上 ，制备了Ag/Bi₄Ti₃O₁₂栅n沟道铁电场效应晶体管. 研 究了Si基Bi₄Ti₃O₁₂薄膜的生长特性及其对铁电薄膜/ 硅的界面状态和铁电场效应晶体管存储特性的影响. 研究表明，在合理的工艺条件下可以获 得具有较高c-轴择优取向的纯钙钛矿相Si基Bi₄Ti₃O₁₂ 铁电薄膜并有利于改善Bi₄Ti₃O₁₂/Si之间的界面特性; 顺时针回滞的C-V特性曲线和C-T曲线表明Ag/Bi₄Ti₃O_{12栅n沟道铁电场效应晶体管具有极化存储效应和一定的极化电荷保持能力; 器件的转移(I< sub>sd}-V_G)特性曲线显示Ag/Bi₄Ti₃O_{12栅n沟道铁电场效应晶体管具有明显的栅极化调制效应. 关键词： 铁电场效应晶体管 4}Ti₃O₁₂')" href="#">Bi₄Ti₃O₁₂ 存储 特性 溶胶-凝胶工艺     

溶胶-凝胶法制备Sr2Bi4Ti5O18薄膜及其铁电性能研究

采用溶胶-凝胶法,在氧气氛中和层层晶化的工艺条件下,成功地制备了沉积在Pt/Ti/SiO₂/Si(100)衬底上的铁电性能优良的Sr₂Bi₄Ti₅O₁₈ (SBTi)薄膜,并研究了SBTi薄膜的微结构、表面形貌、铁电性能和疲劳特性.研究表明：薄膜具有单一的层状钙钛矿结构，且为随机取向；薄膜表面光滑，无裂纹，厚度约为725nm；铁电性能测试显示较饱和、方形的电滞回线，当外电场强度为275kV/cm时 关键词： 溶胶-凝胶法 铁电薄膜 2Bi₄Ti₅O₁₈')" href="#">Sr₂Bi₄Ti₅O₁₈     

Effects of vanadium doping on structure and electrical properties of SrBi4Ti4O15 thin films

The effects of vanadium(V) doping into SrBi₄Ti₄O₁₅ (SBTi) thin films on the structure, ferroelectric, leakage current, dielectric, and fatigue properties have been studied. X-ray diffraction result showed that the crystal structure of the SBTi thin films with and without vanadium is the same. Enhanced ferroelectricity was observed in the V-doped SrBi₄Ti₄O₁₅ (SrBi_4−x/3Ti_4−xV_xO₁₅, SBTiV-x (x = 0.03, 0.06, and 0.09)) thin films compared to the pure SrBi₄Ti₄O₁₅ thin film. The values of remnant polarization (2P_r) and coercive field (2E_c) of the SBTiV-0.09 thin film capacitor were 40.9 μC/cm² and 105.6 kV/cm at an applied electric field of 187.5 kV/cm, respectively. The 2P_r value is over five times larger than that of the pure SBTi thin film capacitor. At 100 kHz, the values of dielectric constant and dielectric loss were 449 and 0.04, and 214 and 0.06 for the SBTiV-0.09 and the pure SBTi thin film capacitors, respectively. The leakage current density of the SBTiV-0.09 thin film capacitor measured at 100 kV/cm was 6.8 × 10⁻⁹ A/cm², which is more than two and a half orders of magnitude lower than that of the pure SBTi thin film capacitor. Furthermore, the SBTiV-0.09 thin film exhibited good fatigue endurance up to 10¹⁰ switching cycles. The improved electrical properties may be related to the reduction of internal defects such as bismuth and oxygen vacancies with changes in the grain size by doping of vanadium into SBTi.     

Great enhancement in remnant polarization of SrBi4Ti4O15 thin films by A-site doping of Fe3+ ions

SrBi4-xFexTi4O15 (SBFT-x) thin films (x = 0.00, 0.05, 0.08, 0.15) have been synthesized on Pt/Ti/SiO2/Si (100) substrates by sol-gel method. This paper finds that Fe-doping does not change the crystal structure of SrBi4Ti4O15 (SBTi). The coercive filed (Ec) and remnant polarisation (Pr) increase at first, then decrease with the increase of Fe doping content. At a maximum applied field of 229 kV/cm, the 2Pr reaches a maximum value of 91.1 μC/cm2 at x = 0.05 and the corresponding Ec is 72 kV/cm. The 2Pr increases by about 260% and the Ec decreases by about 6%, respectively. Obviously, the ferroelectric property of SrBi4Ti4O15 is greatly enhanced by Fe doping. The fatigue-endurance characteristic of the SBFT-0.05 is not improved. After 1.1×109 read/write cycles at a frequency of 50 kHz, the nonvolatile polarisations (Pnv = P*-P∧) decreased about 48% of its initial value.     

Ferroelectric and dielectric properties of La/Mn co-doped Bi4Ti3O12 ceramics

La/Mn co-doped Bi4Ti3O12 ceramics,Bi3.25La0.75Ti3-xMnxO12(x=0.02,0.04,0.06,0.08),were prepared by the solid-state reaction method.The influence of manganese substitution for the titanium part in Bi 3.25 La 0.75 Ti 3 O 12 on the sintering behaviour,microstructure,Raman spectra and electrical properties was investigated.The experimental results show that the phase composition of all samples with and without manganese doping,sintered at 1000 ℃,consists of a single phase with a bismuth-layered structure belonging to the crystalline phase Bi4Ti3O12.There is no evidence of any impurity phase,but a small change in crystallographic orientation is observed.The Curie temperature of Bi3.25La0.75Ti3-xMnxO12 ceramics is steadily shifted to lower temperature with increasing Mn-doping content.Moreover,the remnant polarisation(Pr) of Bi3.25La0.75Ti2.92Mn0.08O12 samples increases with Mn-doping content,and the Bi3.25La0.75Ti2.92Mn0.08O12 sample exhibits the largest P r of 16.6 μC/cm 2.     

Si基Bi3.25La0.75Ti3O12铁电薄膜的制备与特性研究

采用Sol-Gel工艺低温制备了Si基Bi_3.25La_0.75Ti₃O₁₂铁电薄膜.研究了退火温度对薄膜微观结构、介电特性与铁电性能的影响.500℃退火处理的Bi_3.25La_0.75Ti₃O₁₂薄膜未能充分晶化，晶粒细小且有非晶团聚，介电与铁电性能均较差.高于550℃退火处理的Bi_3.25La_{0.75 关键词： 铁电薄膜 3.25}La_0.75Ti₃O₁₂')" href="#">Bi_3.25La_0.75Ti₃O₁₂ Sol-Gel工艺     

La substitution in four-layers Aurivillius phase SrBi4Ti4O15

Ceramics with the nominal composition of SrBi_4−xLa_xTi₄O₁₅ have been prepared within the range of 0≤x≤1.8, and the dielectric properties are investigated. Single phase SrBi_4−xLa_xTi₄O₁₅ solid solution exists until the secondary phase of La_2/3TiO₃ appears at x=1.6. The Curie temperature is 520 °C for pure SrBi₄Ti₄O₁₅, and it shifts to low temperature with increasing x, which is due to the smaller structural distortion caused by La³⁺ substitution. In addition, the dielectric constant anomaly is suppressed with the substitution. No dielectric relaxation behavior is observed. When x≥1.2, the paraelectric state is attained in the present ceramics. La³⁺ substitution effects on the SrBi₄Ti₄O₁₅ ceramics are also compared with the previous work on Bi_4−xLa_xTi₃O₁₂.