不同衬底上Pb(Zr0.52Ti0.48)O3择优取向铁电薄膜的制备和研究

通过MOD法在Si(100)和Pt(111)/Ti/SiO₂/Si基片上制备出LaNiO₃ ( LNO)薄膜.再通过修 正的Sol-gel法，在Pt(111)/Ti/SiO₂/Si,LNO/Si(100)和LNO/Pt/Ti/SiO_{2< /sub>/Si三种衬底上 制备出具有择优取向的Pb(Zr0.52Ti0.48)O3铁电薄膜. 经XRD分析表明，L NO薄膜具有(100)择优取向的类钙钛矿结构；PZT薄膜均具有钙钛矿结构，且在Pt(111)/Ti/S iO2/Si衬底上的薄膜以(110)择优取向，在LNO/Pt/Ti/SiO2/Si和LN O/Si(100)衬底上的 薄膜以(100)择优取向.经场发射SEM分析和介电、铁电性能测试表明，在LNO/Si和LNO/Pt/Ti /SiO2/Si衬底上的PZT薄膜的平均粒径、介电常数以及剩余极化强度均比以Pt/T i/SiO2/Si为衬底的薄膜大. 关键词： 3}薄膜')" href="#">LaNiO₃薄膜 PZT铁电薄膜 择优取向 剩余极化强度     

Au/PZT/BIT/p-Si异质结的制备与性能研究

采用脉冲激光沉积(PLD)工艺,制备了以Bi₄Ti₃O₁₂(BIT)为过渡阻挡层的Au/PZT/BIT/p-Si异质结.研究了BIT铁电层对Pb(Zr_0.52Ti_0.48)O₃(PZT)薄膜晶相结构、铁电及介电性能的影响,对Au/PZT/BIT/p-Si异质结的导电机制进行了讨论.氧气氛530℃淀积的PZT为多晶铁电薄膜,与直接淀积在Si基片上相比,加入BIT铁电层后PZT铁 关键词： 铁电薄膜 异质结构 脉冲激光沉积(PLD)     

SrBi2Ta2O9铁电薄膜微结构及其抗疲劳等铁电特性的研究

在低温Pt/Ti/SiO₂/Si衬底上用脉冲准分子激光沉积技术结合氧气氛下700℃退火获得高质量的SBT薄膜，其择优取向为（008）和（115）．薄膜厚度约为200nm．铁电性能测试显示较饱和的、方形的电滞回线，其剩余极化和矫顽电场分别为10μC/cm²和57kV/cm，在10¹⁰次开关极化后没有显示任何疲劳，在5V直流电压下的漏电流密度约为4×10^-8A/cm²，直流击穿电场约为250kV/cm 关键词：     

溶胶-凝胶法制备(Ba0.7Sr0.3)TiO3/LaNiO3异质薄膜及其结构和介电性质研究

采用改进的溶胶-凝胶方法在单晶Si(100)衬底上制备了介电性能优异的(Ba_0.7Sr_0.3)TiO₃/LaNiO₃异质薄膜.实验发现，在750 ℃下 、O₂气氛中晶化的LaNiO₃薄膜的电阻率最小.C-V与I-V特性测量表明(Ba_0.7Sr_0.3)TiO₃薄膜具有优异的介电性能，在频率为50kHz、零偏压下的相对介电常数ε_r>300，偏压为6V时漏电流密度J_L<1.2×10^-6A/cm². 关键词： xSr_1-x)TiO_３铁电薄膜')" href="#">(Ba_xSr_1-x)TiO_３铁电薄膜 ３底电极')" href="#">LaNiO３底电极 溶胶-凝胶法     

(111)择优取向的Pb(Zr0.52Ti0.48)O3铁电薄膜的制备及研究

选用不同浓度的Pb(Zr_0.52Ti_0.48)O₃溶胶，用Sol-gel法在Pt/Ti/SiO₂/Si基片上沉积一层厚度不同的Pb(Zr_0.52Ti_0.48)O₃ (PZT52)过渡层，经400℃烘烤、550℃退火等程序后，再用Sol-gel法在PZT52过渡层上沉积Pb(Zr_0.52Ti_0.48)O _{关键词： PZT铁电薄膜 择优取向 过渡层 剩余极化强度}     

Sol-gel法制备Bi0.85Nd0.15FeO3多铁性薄膜

利用sol-gel法在Pt/Ti/SiO₂/Si衬底上制备出Bi_0.85Nd_0.15FeO₃薄膜.研究退火温度对其晶相形成的影响,发现在450 ℃退火时,Bi_0.85Nd_0.15FeO₃晶相开始形成,但是结晶较差,而且存在杂相;在500—600 ℃退火可以获得单相Bi_0.85Nd_0.15FeO₃薄膜,退火温度升高有利于其结晶.对600 ℃退火的Bi_0.85Nd_0.15FeO₃薄膜的介电、铁电和电磁性能进行了测试.在测试频率为1 MHz时,其介电常数和介电损耗分别为145,0.032;饱和磁化强度大约为44.8 emu/cm³;剩余极化值(2P_r)大约是16.6 μC/cm². 关键词： sol-gel法 0.85Nd_0.15FeO₃薄膜')" href="#">Bi_0.85Nd_0.15FeO₃薄膜 铁电性能 铁磁性能     

PbTiO3/PbZr0.3Ti0.7O3/PbTiO3夹心结构铁电薄膜子晶层的优化

用Sol-Gel法制备了Pb_(1+x)TiO₃/PbZr_03Ti_07O₃/Pb_(1+x)TiO₃(PT/PZT/PT)夹心结构及PZT铁电薄膜,为了获得高质量的PT/PZT/PT夹心结构铁电薄膜,使用不同过量Pb配比(x)的PbTiO₃ (PT)层进行制备,以获得优化的PT子晶层.X射线 关键词： PT/PZT/PT 夹心结构 子晶 铁电薄膜     

化学溶液法制备的Pb(Mg1/3Nb2/3)O3-PbTiO3薄膜的光学性能

用化学溶液方法在宝石衬底及有LaNiO₃缓冲层的Pt/TiO₂/SiO₂/Si衬底上制备了92%Pb(Mg_1/3Nb_2/3)O₃-8%PbTiO₃(PMNT)薄膜，X射线衍射测试结果表明：在有LaNiO₃缓冲层的Pt/TiO₂/SiO₂/Si衬底上制备的PMNT薄膜几乎是纯钙钛矿相，且薄膜 关键词： PMNT薄膜 光学性能 化学溶液法     

共溅射和离子注入制备的SiO2(Eu)薄膜中Eu3+到Eu2+的转变

采用共溅射方法和Eu离子注入热生长的SiO₂方法得到SiO₂(Eu)薄膜,Eu离子的浓度为4%和0.5%.对样品X射线吸收近边结构(XANES)的研究和分析表明,在高温氮气中发生了Eu³⁺向Eu²⁺的转变.SiO₂(Eu)薄膜高温氮气退火下蓝光的发射证明了这一结论 关键词： 2(Eu)薄膜')" href="#">SiO₂(Eu)薄膜 XANES     

La0.3Sr0.7TiO3模板层对Pb(Zr0.5Ti0.5)O3薄膜的铁电性能增强效应的研究

通过sol-gel法在Si (111) 基片上分别制备了LaNiO₃(LNO)底电极和LaNiO₃/La_0.3Sr_0.7TiO₃ (LNO/LSTO)底电极.然后采用sol-gel 方法，在两种衬底上分别制备了Pb (Zr_0.5Ti_0.5)O₃ (PZT)铁电薄膜.XRD分析表明，两种PZT薄膜均具有钙钛矿结构，且在LNO底电极上的PZT薄膜呈(100) 择优取向，而在LNO/LSTO底电极上的PZT薄膜呈随机取向.铁电性能测试表明，相对LNO衬底上制备的PZT薄膜，在LNO/LSTO底电极上制备的PZT薄膜的剩余极化强度得到了有效的增强，同时矫顽场也增大.介电常数和漏电流的测试表明，LNO/LSTO底电极上制备的PZT薄膜具有大的介电常数和漏电流. 关键词： PZT薄膜 铁电性 漏电流 0.3Sr_0.7TiO₃')" href="#">La_0.3Sr_0.7TiO₃     

利用高压拉曼散射研究Ge/SiO_2/Si纳米系统的压力/张力(英文)

pacc:7830,8100 WereportthepressuredependenceofGe nanocrystalsembeddedinSiO2filmmatrixonSi substrateusingRamanscatteringandfiniteele mentanalysis.DelaminationofSiO2filmfromthe Sisubstrateoccursat～23kbarduetothelarge differencebetweenthecompressibilityoft…     

The microstructure of SiO thin films: from nanoclusters to nanocrystals

The microstructure and electronic structure of silicon-rich oxide (SRO) films were investigated using transmission electron microscopy and electron energy loss spectroscopy as the main analytical techniques. The as-deposited SRO film was found to be a single phase SiO_1.0, as suggested by its electronic structure characteristics determined by the valence electron energy loss spectrum. This single phase undergoes a continuous but incomplete phase decomposition to Si and SiO₂ for films annealed between 300 and 1100°C. The resulting Si phase first appears as ～2?nm-diameter amorphous clusters which grow to larger sizes at higher annealing temperatures, but only crystallize at a critical temperature between 800 and 900°C. This cluster/matrix configuration of the SRO films is consistent with the appearance of the interface plasmon and its oscillator strength as a function of the nanoparticle size. Three separate stages were identified in the sequence of annealed films that were characterized by the presence of single-phase SiO, amorphous silicon nanoclusters, and silicon nanocrystals, respectively. The presence of amorphous silicon nanoclusters in the intermediate stage, the mean size of which can be controlled via annealing, may offer an alternative to silicon nanocrystal composites for optical applications.     

Formation of Nanodimensional SiO2 Films on the Surface of a Free Si/Cu Film System by $${\text{O}}_{2}^{ + }$$ Ion Implantation

Technical Physics - The composition and parameters of energy bands in thin SiO2 films grown on the surface of a free Si/Cu film system have been studied. It has been shown that unlike SiO2 films...     

掺杂Si/SiO_2界面电子结构与光学性质的第一性原理研究

采用基于密度泛函理论的第一性原理方法,在局域密度近似(LDA)下研究了B掺杂Si/SiO_2界面及其在压强作用下的电子结构和光学性质.能带的计算结果表明:掺杂前后Si/SiO_2界面均属于直隙半导体材料,但掺B后界面带隙由0. 74 eV减小为0. 57 eV,说明掺B使材料的金属性增强;对B掺杂Si/SiO_2界面施加正压强,发现随着压强不断增大,Si/SiO_2界面的带隙呈现了逐渐减小的趋势,并且由直隙逐渐转变为间隙.光学性质的计算结果表明:掺B对Si/SiO_2界面在低能区(即红外区)的介电函数虚部、吸收系数、折射率以及反射率等光学参数有显著影响,且在红外区出现新的吸收峰;对B掺杂Si/SiO_2界面施加正压强,随着压强增大,红外区的吸收峰逐渐消失,而在紫外区出现了吸收峰.上述结果表明,对Si/SiO_2界面掺B及施加正压强均可调控Si/SiO_2界面的电子结构与光学性质.本文的研究为基于Si/SiO_2界面的光电器件研究与设计提供一定的理论参考.     

SiO/SiO_2超晶格结构界面发光的研究

利用热蒸发技术在硅衬底上制备了层厚不同的SiO/SiO2超晶格样品.对其光致发光谱进行研究发现,随着SiO/SiO2超晶格中SiO层厚度的增加,发光峰在400～600 nm之间移动.研究表明,样品的发光中心来自于SiO/SiO2界面处的缺陷发光(界面态发光).即在样品沉积的过程中,在SiO/SiO2的界面处由于晶格的不连续性,会形成大量的Si-O悬挂键,这些悬挂键本身相互结合可以形成一定数量的缺陷,同时由于O原子容易脱离Si原子的束缚而产生扩散,因此,这些悬挂键可以与扩散的O原子结合,随着SiO层厚度的增加,在SiO/SiO2的界面处先后出现WOB(O3<≡Si-O-O·),NOV(O3≡Si-Si≡O3),E'中心(O≡Si·),NBOHC(O3≡Si-O·)等缺陷,这些缺陷在SiO层厚度增大的过程中对发光先后起到主导作用,从而使得发光峰产生红移.     

烧结过程中Ni-Al金属间化合物形成的内耗

Ni-Al金属间化合物是一类重要的高温结构材料,在多种领域具有明确的目标需求.粉末冶金技术是制备Ni-Al金属间化合物的一种重要选择.探索烧结过程中Ni-Al金属间化合物形成和转变过程,明确固相扩散反应发生温度和金属间化合物种类对调控烧结工艺和优化产品质量至关重要.本文采用内耗技术系统研究了Ni-Al粉末混合物压坯烧结过程的内耗行为.在内耗-温度谱上观察到一个显著内耗峰,随测量频率的增大而降低,但峰温无明显频率依赖性.同时,内耗峰随升温速率的增大向高温方向移动且峰值增加.分析认为,该峰与升温过程中金属间化合物NiAl3和Ni2Al3的形成有关,属于典型的相变内耗峰.此外,机械球磨可调控Ni-Al粉末混合物的微观结构,内耗峰随球磨时间增加向低温方向移动且峰值降低,表明固相扩散反应可在低温区域以较低速率进行.这与球磨过程中粉末颗粒的细化、粉末混合物的片层化、固溶度和表面能的提高以及缩短的原子扩散路径有关.同时也表明机械球磨可有效降低固相扩散反应起始温度进而降低烧结温度.     

非晶Si/SiO2超晶格结构的交流电致发光

设计并用磁控溅射方法制备了非晶Ｓｉ／ＳｉＯ２超晶格结构,以高纯多晶Ｓｉ为靶材,当以Ａｒ＋Ｏ２为溅射气氛时,得到ＳｉＯ２膜,仅以Ａｒ为气氛时,得到Ｓｉ膜。重复地开和关Ｏ２气,便交替地得到ＳｉＯ２和Ｓｉ膜。衬底在靶前往返平移,改变平移的速度或者改变溅射的功率,可以控制膜的厚度。通过透民镜的照片可以看出ＳｉＯ２和Ｓｉ膜具有均匀的周期结构,用低角Ｘ－射线反射谱表征了超晶格的周期结构和各层的厚度。透射光谱表     

Hydrogen Passivation Effect on Enhanced Luminescence from Nanocrystalline Si/SiO2 Multilayers

Nanocrystalline Si/SiO2 multilayers are prepared by thermally annealing amorphous Si/SiO2 stacked structures. The photoluminescence intensity is obviously enhanced after hydrogen passivation at various temperatures. It is suggested that the hydrogen trapping and detrapping processes at different temperatures strongly influence the passivation effect. Direct experimental evidence is given by electron spin resonance spectra that hydrogen effectively reduces the nonradiative defect states existing in the Si nanocrystas/SiO2 system which enhances the radiative recombination probability. The luminescence characteristic shows its stability after hydrogen passivation even after aging eight months.     

第一性原理研究厚度和空位缺陷对Si/SiO2界面电子结构与光学性质的影响

采用基于密度泛函理论的平面波超软赝势方法,在局域密度近似（LDA）下研究了Si纳米层厚度和O空位缺陷对Si/SiO2界面电子结构及光学性质的影响．电子结构计算结果表明：在0.815~2.580nm的Si层厚度范围内,Si/SiO2界面结构的能隙随着厚度减小而逐渐增大,表现出明显的量子尺寸效应,这与实验以及其他理论计算结果一致;三种不同的O空位缺陷的存在均使得Si/SiO2界面能隙中出现了缺陷态,费米能级向高能量方向移动,且带隙有微弱增加．光学性质计算结果表明：随着Si纳米层厚度的减小,Si/SiO2界面吸收系数产生了蓝移;O空位缺陷引入后,界面光学性质的变化主要集中在低能区,即低能区的吸收系数和光电导率显著增加．可见,改变厚度和引入缺陷能够有效地调控Si/SiO2界面体系的电子和光学性质,上述研究结果为Si/SiO2界面材料的设计与应用提供了一定的理论依据．     

第一性原理研究厚度和空位缺陷对Si/SiO2界面电子结构与光学性质的影响

采用基于密度泛函理论的平面波超软赝势方法,在局域密度近似（ LDA）下研究了Si纳米层厚度和O空位缺陷对Si／SiO2界面电子结构及光学性质的影响．电子结构计算结果表明：在0.815～2.580nm的Si层厚度范围内, Si／SiO2界面结构的能隙随着厚度减小而逐渐增大,表现出明显的量子尺寸效应,这与实验以及其他理论计算结果一致;三种不同的O空位缺陷的存在均使得Si／SiO2界面能隙中出现了缺陷态,费米能级向高能量方向移动,且带隙有微弱增加．光学性质计算结果表明：随着Si纳米层厚度的减小, Si／SiO2界面吸收系数产生了蓝移; O空位缺陷引入后,界面光学性质的变化主要集中在低能区,即低能区的吸收系数和光电导率显著增加．可见,改变厚度和引入缺陷能够有效地调控Si／SiO2界面体系的电子和光学性质,上述研究结果为Si／SiO2界面材料的设计与应用提供了一定的理论依据．