掺镍型层状LixNiyMn1-yO2正极材料的合成与电性能研究

A kind of cathode material of layered Li_xNi_yMn_1-yO₂ characterized with the O2 type has been synthesized by a simple method. Its precursor Na_xNi_yMn_1-yO₂ has been prepared from manganese dioxide， nickel hydroxide and sodium carbonate at high temperature in air and quickly cooled in cold water， then it has been exchanged by the melted LiNO₃ at 300～400℃ in air. The effects of calcine-temperature for the precursors and its compositions (the content of Na and Ni) on the electrochemical properties of the material Li_xNi_yMn_1-yO₂ have been investingated by XRD and electrochemical tests. The results show that the sample Li_0.7Ni_0.3Mn_0.7O₂， has the best electrochemical properties which shows only one charge-discharge potential stage of 2.8～3.0V and has a high specific capacity over 180mAh·g^-1 cycled between 2.0～4.20V. A significant structure transformation to the spinal-type phase has not been found in the charge-discharge cycling and the discharge specific capacity around 165mAh·g^-1 has re-mained after the 20th cyclings for the material.     

MgFe2O4-Fe2O3纳米粉体的软化学合成及电磁学特性

Nano-MgFe₂O₄-Fe₂O₃ magnetic powders were synthesized by citrate gel under microwave irradiation. The structure，particle size distribution，electromagnetic characteristics of nano-MgFe₂O₄-Fe₂O₃ were characterized by using TG-DTA, X-ray, electronic microscope, nano-size measurement and electromagnetism measurement apparatus。The results show that the product is a mixture of MgFe₂O₄ and Fe₂O₃ with average size of 44 nm, tanδ for the product is 0.265 and 0.610 at frequency of 1.0 GHz and 1.8 GHz respectively.     

Fe3O4/N-异丙烯酰胺(PNIPAM)纳米颗粒的合成

A magnetic and thermosensitive poly(N-isopropylacrylamide)(PNIPAM) nanoparticles were prepared by the following procedure. The core-shell composite microparticles were synthesized by precipitating polymerization with Fe₃O₄ being entrapped with SiO₂ as core and cross-linked PNIPAM as shell. Then， the SiO₂ core was etched by hydrofluoric acid and magnetic thermosensitive Fe₃O₄/PNIPAM particles were formed. It has also been shown that the Fe₃O₄/PNIPAM nanoparticles are featured by lower critical solution temperature (LCST) at 33.0 ℃ while the temperature varies from 28.0 ℃ to 36.0 ℃. The composite magnetic thermosensitive particles were characterized by XRD， SEM， TEM and FTIR. The synthetic mechanism is also discussed.     

阴极材料LaFe0.8-xCuxNi0.2O3的合成和烧结性能

LaFe_0.8-xCu_xNi_0.2O₃ (x=0.0~0.2) (LFCN), a new cathode material of solid oxide fuel cell (SOFC), was synthesized by Co-precipitation method using sodium bicarbonate. The lattice structures of samples with different x contents were characterized by XRD. Porosity and density of the porous LaFe_0.8-xCu_xNi_0.2O₃ (x=0.0~0.1) as a function of sintering temperature were investigated. It was found that the orthorhombic structure could be formed after calcination at 900 ℃ for 4 h. The particle size of LFCN was about 350 nm. The density of the porous LFCN increased with sintering temperature, but the opposite was true for the porosity. On the other hand, at the same sintering temperature, the porosity of LaFe_0.8-xCu_xNi_0.2O₃ (x=0.0~0.1) decreased with increasing x contents. It is indicated that the dopant of Cu on LaFe_0.8Ni_0.2O₃ can facilitate the sintering of the materials. After sintering at 1 100 ℃ for 4 h, the porous LaFe_0.7Cu_0.1Ni_0.2O₃ was still with appropriate structure, and its porosity was 29%.     

Li2CO3、NiO和电解MnO2合成高容量LiNi0.5Mn1.5O4及其表征

Well-developed crystalline LiNi_0.5Mn_1.5O₄ was prepared by solid-state reaction using Li₂CO₃, NiO and electrolytic MnO₂ at high heating and cooling rate. X-ray diffraction (XRD) patterns and scanning electron microscopic (SEM) images showed that LiNi_0.5Mn_1.5O₄ synthesized at 900 ℃ and 950 ℃ had cubic spinel structure with clearly defined shape. LiNi_0.5Mn_1.5O₄ spinel phase decomposed at 1 000 ℃ accompanying with structural and morphological degradation. TG measurement revealed that the weight loss during heating process could be mostly gained in cooling process, and the upward tendency of weight loss during heating process decreased, while that of irreversible weight loss rapidly increased with the increase of temperature. LiNi_0.5Mn_1.5O₄ powders prepared at 900 ℃ for 12 h delivered the maximum discharge capacity of 134 mAh·g^-1 with good cyclic performance at 2/7 C. In addition, by adjusting the calcination time at 900 ℃, the capacity and cycling performance of LiNi_0.5Mn_1.5O₄ were further enhanced.     

La2O2S∶Mn2+荧光粉的微波合成及其荧光特性

Using La₂(SO₄)3 and the active carbon powder as reactants, La₂O₂S∶Mn²⁺ red phosphor was synthesized by microwave radiation method. The phosphor was characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), laser-diffraction size analyzer and fluorospectrophotometer. The XRD analysis showed that the phosphor was pure phase La₂O₂S. The phosphor of La₂O₂S∶Mn²⁺ showed hexagonal crystal structure with diverse shapes, such as spherical and rod, with average particle size of 10.22 μm. The emission and excitation spectra of the phosphor were determined by fluorospectrophotometer and the results showed that the excitation spectrum of the phosphor under 600 nm emission wavelength was excitation bands between 250 nm and 350 nm with a peak value of 303 nm. Then ,when exicited under UV 303 nm, the phosphor showed broad band emission of 550~700 nm with a peak at 607 nm. In addition, the optimal effects were obtained for the phosphor preparation when the concentration of the activator Mn²⁺ was x_Mn=0.01, the ratio of C and O (n_C / n_O) in the reactants was 0.6∶1, and the time of reaction was about 1 h. La₂O₂S∶Mn²⁺ has strong absorption of UV spectrum and can emit bright red light.     

LiNi0.8Co0.2O2 / MWNTs复合物超级电容器电极材料的研究

Multiwalled carbon nanotubes (MWNTs) were used as the conductive additive in the electrode materials. The electrochemical properties of supercapacitors based on LiNi_0.8Co_0.2O₂ / MWNTs composite and LiNi_0.8Co_0.2O₂/acetylene black composite and MWNTs in 1.0 mol·L^-1 LiClO₄ / EC+DEC [V(EC)∶V(DEC)=1∶1] electrolyte were investigated by means of constant charge/discharge current tests, respectively. The experimental results show that the LiNi_0.8Co_0.2O₂ / MWNTs composite has better performance than that of others, and the maximum specific capacitance of the supercapacitor can reach 271.6 F·g^-1, while the energy density is up to 339.5 Wh·kg^-1. Furthermore, it is remarkable that the performance of MWNTs is better than that of acetylene black as the conductive additive.     

无氨湿法制备纳米晶In2O3及表征

Preparation of In₂O₃nano-scale powders by ultrasonic and homogeneous precipitation, using metal In and urea as raw materials, was reported for the first time, while the effects of reaction temperature, the ratio of the materials and the pH etc. on the preparation was dicussed. This method can be operated and industrialized easily with very low cost． The structural properties of precursor and In₂O₃were characterized by TG-DTA, XRD, ESCA and TEM. The results show that In₂O₃produced are very pure, monophase and spherical nano-scale powders with average size of 25 nm.     

LixNi0.8-yCo0.2ZnyOp的合成及电化学性能研究

A series of single-phase Li_xNi_0.8-yCo_0.2Zn_yO_p(0.96 ≤x≤ 1.10， 0 ≤y≤ 0.05， 2 ≤p≤ 2(1+y) ) (different in the y values) were synthesized by a two-step solid state reaction method， in which LiOH·H₂O， Zn-doped spherical Ni(OH)₂ and Co₂O₃ were used as the precursors. The ICP-AES analyses proved that the Zn-doped compounds synthesized had the nonstoichiometric form. The results of the XRD， SEM identified that the uniform particles of the as-prepared materials having a good layered structure were fine， narrowly distributed and well crystallized. The electrochemical performance test was carried out and the results showed that the as-prepared Zn-doped materials had not only a high capacity， but also a better cycling stability characterization than the un-doped one. The Li_1.06Ni_0.75Co_0.22Zn_0.03O_2.03 material has an initial reversible capacity as high as 160.5mAh·g^-1; and a first discharge efficiency 89.2%， and exhibits satisfactory cyclic stability with 90% retainable capacity after 50 cycles.     

多元掺杂尖晶石型Li1.02MxMn2-xQyO4-y正极材料的电化学特性

The effect of doping on the electrochemical performance was studied for spinel type Li_1.02M_xMn_2-xQ_yO_4-y used as cathode material in lithium-ion battery. TG/DTA curves of the precursor(the raw materials) doped with different elements were studied. The spinel materials Li_1.02Mn₂O₄, Li_1.02Co_0.02Cr_0.01La_0.01Mn_1.96F_0.02O_3.98, Li_1.02Co_0.02Cr_0.01 La_0.01Mn_1.96Cl_0.02O_3.98, Li_1.02Co_0.02La_1.02Mn_1.97Cl_0.02O_3.98, Li_1.02Co_0.02Cr_0.01Mn_1.97O₄, were prepared by solid-state reaction method after the pretreatment of conversion under low temperature and uniform mixing. X-ray diffraction patterns showed that all the samples had perfect spinel structure. SEM indicated that the particles of the samples had uniform size and were distributed evenly. The results of the charge/discharge curves showed that Li_1.02Co_0.02Cr_0.01La_0.01Mn_1.96F_0.02O_3.98 had better performance than other materials according to the inhibition of decline of reversible capacity of spinel Li_1.02M_xMn_2-xQ_yO_4-y. Therefore, cycle performance had been improved so obviously that 93.9% of the initial capacity were preserved after 100 cycles. Furthermore, electrochemical impedance tests were carried out with the spinel Li_1.02Co_0.02Cr_0.01La_0.01Mn_1.96F_0.02O_3.98 as working electrode, Lithium as counter electrode and reference electrode. Results showed that this material possessed good charge/discharge reversible capability and had the lowest impedance in 3.95～4.25 V range (on the stage of charge / discharge).     

Phase relations in the K2W2O7-K2WO4-KPO3-Bi2O3 system and structure of K6.5Bi2.5W4P6O34

The phase relations in the cross-section of the K₂W₂O₇-K₂WO₄-KPO₃ containing 15 mol% Bi₂O₃ were undertaken using flux method. Crystallization fields of K_6.5Bi_2.5W₄P₆O₃₄, K₂Bi(PO₄)(WO₄), Bi₂WO₆, KBi(WO₄)₂ and their cocrystallization areas were identified. Novel phase K_6.5Bi_2.5W₄P₆O₃₄ was characterized by single-crystal X-ray diffraction: sp. gr. P−1, a=9.4170(5), b=9.7166(4), c=17.6050(7) Å, α=90.052(5)°, β=103.880(5)° and γ=90.125(5)°. It has a layered structure, which contains {K₇Bi₅W₈P₁₂O₆₈}_∞ layers stacked parallel to ab plane and sheets composed by potassium atoms separating these layers. Sandwich-like {K₇Bi₅W₈P₁₂O₆₈}_∞ layers are assembled from [W₂P₂O₁₃]_∞ and [BiPO₄]_∞ building units, and are penetrated by tunnels with K/Bi atoms inside. FTIR-spectra of K₂Bi(PO₄)(WO₄) and K_6.5Bi_2.5W₄P₆O₃₄ were discussed on the basis of factor group theory.     

KCl-KBO2-K2CO3, K2MoO4-KBO2-K2CO3, and K2WO4-KBO2-K2CO3 ternary systems

phase diagrams of KCl-KBO₂-K₂CO₃, K₂MoO₄-KBO₂-K₂CO₃, and K₂WO₄-KBO₂-K₂CO₃ ternary systems were studied by a calculation-experimental method and differential thermal analysis (DTA). The coordinates of ternary eutectics were determined to be E ₁: 622°C, 8.5 mol % KBO₂, 56.5 mol % KCl, and 35 mol % K₂CO₃; E ₂: 710°C, 23 mol % KBO₂, 43 mol % K₂CO₃, and 34 mol % K₂MoO₄; E ₃: 710°C, 23 mol % KBO₂, 43 mol % K₂CO₃, and 34 mol % K₂WO₄. The specific heats of melting of the eutectics were determined.     

Sol-gel synthesis of K3InF6 and structural characterization of K2InC10O10H6F9, K3InC12O14H4F18 and K3InC12O12F18

K₃InF₆ is synthesized by a sol-gel route starting from indium and potassium acetates dissolved in isopropanol in the stoichiometry 1:3, with trifluoroacetic acid as fluorinating agent. The crystal structures of the organic precursors were solved by X-ray diffraction methods on single crystals. Three organic compounds were isolated and identified: K₂InC₁₀O₁₀H₆F₉, K₃InC₁₂O₁₄H₄F₁₈ and K₃InC₁₂O₁₂F₁₈. The first one, deficient in potassium in comparison with the initial stoichiometry, is unstable. In its crystal structure, acetate as well as trifluoroacetate anions are coordinated to the indium atom. The two other precursors are obtained, respectively, by quick and slow evaporation of the solution. They correspond to the final organic compounds, which give K₃InF₆ by decomposition at high temperature. The crystal structure of K₃InC₁₂O₁₄H₄F₁₈ is characterized by complex anions [In(CF₃COO)₄(OH_x)₂]^(5−2x)− and isolated [CF₃COOH_2−x]^(x−1)− molecules with x=2 or 1, surrounded by K⁺ cations. The crystal structure of K₃InC₁₂O₁₂F₁₈ is only constituted by complex anions [In(CF₃COO)₆]³⁻ and K⁺ cations. For all these compounds, potassium cations ensure only the electroneutrality of the structure. IR spectra of K₂InC₁₀O₁₀H₆F₉ and K₃InC₁₂O₁₂F₁₈ were also performed at room temperature on pulverized crystals.     

Solubility in the Na2Cr2O7-(NH4)2Cr2O7-K2Cr2O7-H2O system

Solubility in the Na₂Cr₂O₇-(NH₄)₂Cr₂O₇-K₂Cr₂O₇-H₂O four-component water-salt system at 25, 50, and 75°C was studied for the first time. Phase field boundaries for individual salts and potassium and ammonium dichromate solid solutions, monovariant lines, and invariant points were determined. Experimental data were used to optimize the looped isohydric process of potassium dichromate preparation involving additional salts.     

Li2SO4-Na2SO4-H2O和Li2SO4- K2SO4-H2O溶液的体积性质

本文用高精度数字式振荡管密度计测定了288K至318K温度范围内Li₂SO₄ + Na₂SO₄ + H₂O和 Li₂SO₄ + K₂SO₄ + H₂O三元体系的密度。混合溶液的离子强度范围从0.1到4.5 mol.kg_–1,混合溶液中Na₂SO₄和K₂SO₄的离子强度分数为0.2,0.4,0.6和0.8。用密度实验值拟合得到了不同温度下Pitzer离子相互作用模型混合参数θ_V和 ψ_V,模型的计算值与实验值的偏差在±0.002 g.cm_–3以内。用Pitzer模型计算了不同离子强度下三元体系的混合体积。     

NaBO2-NaCl-Na2CO3, NaBO2- Na2CO3-NaMoO4, NaBO2- Na2CO3-NaWO4, and NaBO2-NaCl-Na2WO4 ternary systems

The phase diagrams of the NaBO₂-NaCl-Na₂CO₃, NaBO₂-Na₂CO₃-Na₂MoO₄, NaBO₂- Na₂CO₃-Na₂WO₄, and NaBO₂-NaCl-Na₂WO₄ ternary systems were studied by a calculation-experimental method and differential thermal analysis. The coordinates of ternary eutectics were determined: E ₁: 612°C, 16 mol % NaBO₂, 42 mol % NaCl, and 42 mol % Na₂CO₃; E ₂: 568°C, 12 mol % NaBO₂, 28 mol % Na₂CO₃, and 60 mol % Na₂MoO₄; E ₃: 575°C, 12 mol % NaBO₂, 32 mol % Na₂CO₃, and 56 mol % Na₂WO₄; E ₄: 628°C, 8 mol % NaBO₂, 20 mol % NaCl, and 72 mol % Na₂WO₄; and E ₅: 655°C, 9 mol % NaBO₂, 53 mol % NaCl, and 38 mol % Na₂WO₄.     

Extension of the La7Mo7O30 structural type with La7Nb3W4O30 and La7Ta3W4O30 compounds

Two compounds of formula La₇A₃W₄O₃₀ (with A=Nb and Ta) were prepared by solid-state reaction at 1450 and 1490 °C. They crystallize in the rhombohedric space group R-3 (No. 148), with the hexagonal parameters: , and , . The structure of the materials was analyzed from X-ray, neutron and electronic diffraction. These oxides are isostructural of the reduced molybdenum compound La₇Mo₇O₃₀, which are formed of perovskite rod along [111]. An order between (Nb, Ta) and W is observed.     

Preparation and structure of NaSr0.5Al2B2O7 and NaCa0.5Al2B2O7

Two compounds NaSr_0.5Al₂B₂O₇ and NaCa_0.5Al₂B₂O₇, have been found to crystallize into a new structure type by Rietveld refinement from X-ray powder diffraction data. Their structure belongs to hexagonal space group P6₃/m, with lattice parameters of , for NaSr_0.5Al₂B₂O₇ and , for NaCa_0.5Al₂B₂O₇, respectively. The structure is built up by [Al₂B₂O₇]²⁻ double layer and Na⁺/Ca²⁺ or Na⁺/Sr²⁺ ions alternatively stacking along the c-axis. The sites in the inter-double layer are fully occupied jointly by Na and Ca or Sr, but the intra-double layer sites are only half occupied solely by Na. A mechanism of the transition of the structure from CaAl₂B₂O₇ to present structure type by replacing only 1% Ca by Na (2%) as observed by Chang and Keszler (Mater. Res. Bull. 33 (1998) 299) is also proposed.     

SnSbBiS4-SnS and SnSbBiS4-Sn2Sb6S11 sections of the SnS-Sb2S3-Bi2S3 ternary system

SnSbBiS₄-SnS and SnSbBiS₄-Sn₂Sb₆S₁₁ sections were studied by physicochemical methods (DTA, X-ray powder diffraction, microstructure observation, and microhardness measurements). These sections were found to be eutectic quasi-binary sections of the SnS-Sb₂S₃-Bi₂S₃ ternary system. Solid solution regions based on the initial components were found on either side of the sections. Alloys in the solid solution region are p-type semiconductors.     

Li2O-TiO2-SiO2-P2O5和Li2O-TiO2-Al2O3-P2O5体系锂离子固体电解质的制备及性能研究

一些具有NASICON型网格结构的固体电解质具有高的电导率和好的稳定性,NASICON的意思是Na Super Ionic Conductor[1]。当NaZr2(PO4)3中P5 被Si4 部分取代时便可以得到具有NASICON结构的Na1 xZr2SixP3-xO12体系,其具有高的钠离子电导率。然而有相同结构的Li1 xZr2SixP3-xO12体系的离子电导率却很低,这是因为Li 半径太小,而NASICON三维网格结构的离子通道太大,两者不匹配而使电导率下降[2]。但当LiZr2(PO4)3中Zr4 被离子半径小些的Ti4 取代,所得LiTi2(PO4)3的通道就与Li 半径相匹配,适合于锂离子的迁移,从而使其电导率…