锂离子电池正极材料LiMn2O4的合成与晶体结构（英）

Spinel LiMn₂O₄ powders were prepared using two-step synthesis method consisting of solid-state reaction method and citrate modified sol-gel method. The effects of the calcination temperature and the Li/Mn ratio of raw materials were studied on the physicochemical and electrochemical properties of the spinel LiMn₂O₄ powders, such as crystallinity, lattice constant and density. The title compound was characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Polycrystalline LiMn₂O₄ powers calcined at 750 ℃ were found to be composed of very uniformly-sized microcrystal with an average particle size of 300 nm. The improvement in electrochemical properties was mainly attributed to the process of re-grinding by absolute alcohol.     

铟锡氧化物纳米网的微波法制备及其光催化特性研究

By using ultrasonic and chemical liquid coprecipitation, the precursor was prepared with high purity In, SnCl₄·5H₂O and urea. The In₂O₃·SnO₂ nanonets were obtained from precursor by heating in microwave oven. The powders were characterized by XRD, TEM. The analyzed results show the sample is In₂O₃·SnO₂, and In₂O₃is rhombohedral system while SnO₂ is tetragonal system. The sample is in spherical grain shape, with average granularity of 35 nm, and the mesh diameter of 10～80 nm. The sample was with fluorescence and good photocatalytic performance for degradation of organic dyestuff.     

球形Gd2O3∶Eu纳米发光材料的制备

Spherical nanometer Gd₂O₃∶Eu luminescent materials were prepared by homogeneous precipitation method, and the properties were studied also. TG, FTIR and XRD analysis showed that the precursor was carbonate, the cubic Gd₂O₃was obtained after calcination. TEM photographs indicated that the samples were spherical and well dispersed with nanometer and submicrometer size of 200～300 nm which is the nanoparticles’ aggregate. The mechanics of agglomerating growth is also discussed. ED photograph showed that the particle was crystalline. The PL analysis exhibited that CTB band of nanometer Gd₂O₃∶Eu was of 17 nm red shift to bulk materials, and the emission peak was broadened due to the surface and interface effect of nanocrystals.     

Nd2O3添加量对BaTiO3陶瓷介电性能的影响

BaTiO₃ ceramics doped with Nd₂O₃(the additive content was respectively 0.001,0.002,0.003,0.005,0.01,0.03mol)were prepared by Sol-Gel method. Effects of Nd₂O₃ contents on the dielectric constant (ε), the dielectric loss (tanδ) ,the Curie-temperature (T_C) and the resistivity (ρ) of BaTiO₃ ceramic were studied. When Nd₂O₃ content was 0.001mol and 0.002mol, the dielectric constant was increased obviously, but the dielectric loss was also increased. When Nd₂O₃ content was 0.003mol, the dielectric constant was increased, and the dielectric loss was decreased, which was suitable for application in condenser. The resistivity was decreased obviously with the increasing of Nd₂O₃ contents, the resistivity was the smallest when Nd₂O₃ content was 0.001mol. The Curie-temperature was also decreased with the increasing of Nd₂O₃ contents.     

草酸盐共沉淀法制备Y1.84La0.16O3纳米粉体

Nanopowder of Y_1.84La_0.16O₃ was prepared by oxalate co-precipitation method. The powder was characterized by TG-DTA, XRD and TEM. The results show that the precursor is Re₂(NO₃)₂(C₂O₄)₂·2H₂O (Re=Y, La), and the Y_1.84La_0.16O₃ nanopowders produced by calcining the precursor at 1 000 ℃ for 4 h are 20～40 nm spherical particles and well dispersed. The powders were with high sintering activity and could be fabricated to transparent ceramic without additive at 1 450～1 550 ℃ in H₂ atmosphere for 3 hours. The total transmission of the transparent ceramic could reach 80%.     

In2O3八面体的碳还原法制备及其发光性能研究

In₂O₃ octahedrons were synthesized by carbothermal reduction using In₂O₃ nanoparticles as the source material. The as-synthesized products were characterized by X-ray powder diffraction (XRD), energy dispersive X-ray(EDX), scanning electron microscopy(SEM), transmission electron microscopy(TEM), high-resolution transmission electron microscopy (HRTEM), selected-area electron diffraction analysis(SAED) and Room-temperature photoluminescence(PL) spectroscopy. The results show that the products are single-crystalline In₂O₃ octahedrons, the length of the octahedrons is in the range of 400～3 000 nm; the PL patterns display two peaks located at 447nm and 555 nm upon excitation at 380 nm, and the other two peaks located at 444 nm and 550 nm upon excitation at 325 nm; the excitation pattern shows two peaks located at 274 nm and 371 nm, respectively. The growth mechanism of the In₂O₃ octahedrons is discussed, and the high supersaturation ratio is considered as the key factor.     

MgFe2O4-Fe2O3纳米粉体的软化学合成及电磁学特性

Nano-MgFe₂O₄-Fe₂O₃ magnetic powders were synthesized by citrate gel under microwave irradiation. The structure，particle size distribution，electromagnetic characteristics of nano-MgFe₂O₄-Fe₂O₃ were characterized by using TG-DTA, X-ray, electronic microscope, nano-size measurement and electromagnetism measurement apparatus。The results show that the product is a mixture of MgFe₂O₄ and Fe₂O₃ with average size of 44 nm, tanδ for the product is 0.265 and 0.610 at frequency of 1.0 GHz and 1.8 GHz respectively.     

Ceramic Filter Balls Loaded with α-Fe2O3 and Their Application to NH3-N Wastewater Treatment

Hydrolysis reaction of Fe(NO₃)₃ at a high temperature in the presence of urea as the homogeneous precipitant was studied. With the prepared ceramic filter balls loaded with α-Fe₂O₃ after high temperature calcination, the loading of α-Fe₂O₃ on the porous ceramic filter balls from Fe(NO₃)₃ solutions of different concentrations and mechanical stability of the loaded α-Fe₂O₃ were studied. The product was characterized using XRD and SEM. Adsorption experiments were conducted to evaluate the performance of the product in adsorbing NH₃-N. It turned out that the specific surface area of the ceramic filter balls loaded with α-Fe₂O₃ had increased to 36.5387 m²/g from original 4.6127 m²/g. When the concentration of Fe(NO₃)₃ was 0.40 mol/L, the loading of α-Fe₂O₃ on the ceramic filter balls accounted for 8.4% of the total mass of the adsorbent and α-Fe₂O₃ was adsorbed on the filter balls very well. The adsorption isotherm of NH₃-N on the ceramic filter ball adsorbent loaded with α-Fe₂O₃ was of Langmuir type. The saturated adsorption capacity was 3.33 mg/L, and the adsorption constant K was 0.1873. NH₃-N was adsorbed by α-Fe₂O₃ more easily, which was a kind of specific adsorption.     

磁性Fe3O4 /壳聚糖的化学修饰及包覆机理研究

Nano-sized Fe₃O₄ powder was prepared through an Oxygenation-Hydrothermal method. The chitosan magnetic complex was prepared by coating chitosan on the surface of Fe₃O₄ powders through Microlatex-Crosslinking Method. The product was characterized by IR， XRD， TEM， Vibrating Sample Magnetometer (VSM)， TG methods. Results show that the as-prepared powder is 25 nm in size and shows supermagnetism. The content of magnetite in microspheres is 37.8%. The mechanism for the coating reaction of chitosan to Fe₃O₄ nanoparticles is also suggested.     

硬脂酸法制备超细K2La2Ti3O10及其酸交换性质研究

A new stearic acid method(SAM) has been used to prepare ultrafine K₂La₂Ti₃O₁₀ nanocrystalline. Each state of synthesis process was followed by the use of FT-IR analysis. The resulting materials have been characterized by means of XRD， TEM， BET surface area analysis. The acid-exchanging property of the obtained product was also studied. The experimental results showed that comparing with the product of traditional solid-state reaction， the particle size of the K₂La₂Ti₃O₁₀ synthesized by SAM is greatly reduced， BET surface area is high(more than 11.83m²·g^-1) and has different acid-exchanging properties. It can be easily exfoliated in 2mol·L^-1 HNO₃ so-lution.     

溶剂热法合成In2S3/CuSe核壳结构粉体

本文以氯化铜、氯化铟、硫脲、亚硒酸以及硒粉为原料,乙二醇及乙二胺为溶剂,采用常压溶剂热法制备了硫化铟为核硒化铜为壳(In2S3/CuSe)的核壳结构复合粉体。主要探讨了反应温度、不同反应原料以及不同表面活性剂对产物物相以及形貌的影响。通过采用X射线衍射(XRD)、扫描电镜(SEM)对产物的物相、形貌以及组成进行了表征。实验结果表明:常压溶剂热条件下可以制备得In2S3/CuSe复合粉体,其最佳反应工艺参数是:于160℃下合成In2S3粉体为核,于100℃下合成包裹在In2S3表面的CuSe粉体从而获得In2S3/CuSe核壳结构复合粉。在该工艺参数下合成产物的形貌主要由圆球状颗粒组成,粉体的粒径分布在1~2μm。此外,本文也通过添加不同种类表面活性剂对产物的形貌进行了控制。     

熔盐法制备Ca0.9La0.2/3Cu3Ti4O12陶瓷粉体及其介电性能研究

以CaCO3,CuO,TiO2,La2O3为反应物,NaCl,KCl为熔盐,通过熔盐法分别在700、750、800、850℃条件下合成Ca0.9La0.2/3Cu3Ti4O12陶瓷粉体。利用XRD和SEM分别对陶瓷粉体的物相结构和微观形貌进行了分析,并对其介电性能进行了测试。实验结果表明,随着合成温度的升高,陶瓷粉体的钙钛矿相含量逐渐增大,与传统固相法相比,熔盐法制备的粉体无团聚现象,耗时少。Ca0.9La0.2/3Cu3Ti4O12粉体制备的陶瓷在1 000℃烧结、测试频率在100 Hz~10 kHz时,获得优良的介电性能:介电常数大大超过104,介电损耗在0.1~0.47之间。     

A sol-gel route for the development of rare-earth aluminum borate nanopowders and transparent thin films

A new sol-gel route was applied to obtain Y_0.9Er_0.1Al₃(BO₃)₄ crystalline powders and amorphous thin films by using Al(acac)₃, B(OPrⁱ)₃, Y(NO₃)₃·6H₂O, and Er(NO₃)₃·5H₂O as starting materials dissolved in propionic acid and ethyl alcohol mixtures. Our study shows that propionic acid acts as good chelant agent for yttrium and erbium ions while ethyl alcohol allows to dissolve Al(acac)₃. This process makes the resulting sols very stable to obtain homogeneous gels and transparent amorphous thin films. In addition, the propionic acid prevents the sol precipitation, making easy porous- and crack-free thin film depositions. Chemical reactions involved in the complexation were discussed. As-prepared powders and films are amorphous and present a good thermal stability due to their high glass transition (746 °C) and crystallization temperatures (830 °C). This new sol-gel route showed to be adequate to obtain dense and crack-free thin films free of organic and hydroxyl groups that can be considered as promising materials to be used in integrated optical systems.     

Synthesis and electrochemical properties of chemically substituted LiMn2O4 prepared by a solution-based gel method

Lithium manganese oxide, LiMn(2)O(4), and its substituted samples LiM(0.05)Mn(1.95)O(4) (M=Al, Co, and Zn) were first prepared by a cost-saving and effective new solution-based gel method using a mixture of acetate and ethanol as the chelating agent. The physical properties of the synthesized samples were investigated by thermogravimetry/differential thermal analysis, X-ray diffraction, and scanning electronic microscopy. The as-prepared powders were used as positive materials for a lithium-ion battery, whose charge/discharge properties and cycle performance were examined. The results revealed that all the substituted samples had better cycle performance than pure LiMn(2)O(4). Among these synthesized materials, the LiCo(0.05)Mn(1.95)O(4) sample had the best cycle performance. After 30 cycles, its capacity loss was only 3%. Therefore, cyclic voltammetry and electrochemical impedance spectroscopy were employed to characterize the reactions of Li ion insertion into and extraction from LiCo(0.05)Mn(1.95)O(4) electrodes.     

Mn2O3纳米结构的简易合成与电化学性质

用简易的室温或水热方法制备出不同形貌的MnCO₃微结构。经600 ℃热处理后,室温制备MnCO₃转变成Mn₂O₃胶体片,而水热制备MnCO₃样品则形成多孔Mn₂O₃纳米结构。然而,室温制备MnCO₃经120 ℃热处理后形成Mn₂O₃晶相。制备样品经过XRD和SEM表征表明,热处理MnCO₃前驱物形成Mn₂O₃过程导致产物形貌与结构变化。其形成机理又通过TEM和FTIR进一步研究。Mn₂O₃纳米结构的电容性质通过循环伏安法表征,结果表明Mn₂O₃形貌与结构对其电容有重要影响。     

纳米级PbCO3的制备与应用

PbCO3作为燃烧催化剂被广泛应用于推进剂中,但目前推进剂中使用的PbCO3颗粒尺寸大、粒度分布不均匀,严重地影响了固体推进剂的燃烧性能[1~3]。纳米粒子因其尺寸小,比表面积大,且随着粒径减小,比表面积急剧变大,活性中心数迅速增加,大大增强了纳米粒子的催化活性,使得各种纳米级     

Ti∶Al2O3纳米粉体的共沉淀法合成及表征

本文采用共沉淀法合成了Ti∶Al2O3纳米粉体。利用热重/差热(TG/DTA)/X射线衍射(XRD)/红外光谱(FTIR)/扫描电镜(SEM)以及能谱(EDS)等分析方法对合成的Ti∶Al2O3纳米粉体进行了表征。结果分析表明:前驱体在1200℃下,保温1 h可以得到纯的α-Al2O3晶相;粉体的粒径均匀、分散性好,平均粒径在25~50 nm之间。     

尖晶石型NiCr2O4的燃烧法合成及表征

通过溶胶-凝胶燃烧法制备了具有立方相的尖晶石型NiCr2O4颜料,并采用TG/DSC、XRD、FTIR和SEM等手段对其进行表征和研究。结果表明:将燃烧后的粉末于900℃下煅烧2 h可以得到单一相的NiCr2O4,温度达不到900℃时所得粉末(包括燃烧后粉末和500和700℃煅烧得到的粉末)为NiO和Cr2O3组成的混合物。利用紫外/可见/近红外分光光度计仔细研究了燃烧后粉末和煅烧后粉末的颜色参数。尽管具有相同的成分,500和700℃下煅烧得到的粉末与燃烧后粉末却具有明显不同的颜色,这可从一氧化镍为非整比化合物的角度加以解释。此外,900和1 000℃下煅烧得到的NiCr2O4粉末呈现出随温度变化的绿色。     

化学共沉淀法制备气敏材料Cd2+XSb2O6.8

采用化学共沉淀法,以可溶性的镉盐和三价锑盐为源物质、氢氧化物作共沉淀剂,在较宽的Cd/Sb摩尔配比范围内,制备出了具有缺陷烧绿石结构的镉锑复合氧化物Cd₂Sb₂O_6.8及其固溶体。研究了烧成条件对产物的影响,在较低温度(600℃)下得到了纯相Cd₂Sb₂O_6.8的超微粉,并对其高温反应机理进行了探讨。所得微粉产物制成的厚膜元件经气敏测试,发现n(Cd)/n(Sb)=1.10、 900 ℃、3 h烧成的间隙型固溶体Cd_2+XSb₂O_6.8,对乙炔气体具有非常优秀的气敏性能。