铜溶胶的制备

本文探讨了铜溶胶的制备条件如保护剂、还原剂、铜盐的种类及用量、反庆温度对铅溶胶稳定性的影响。实验结果表明，在适当的条件下，在空气中可以制得稳定存在的铜溶胶，其在条件下可保存１８个月不被氧化，溶胶中铜粒子的平均粒径在４３－１７４ｎｍ的范围。     

镁铝氢氧化物正电溶胶的制备

对镁铝氢氧化物制备的反应条件进行了研究，结果表明：溶胶中镁铝比随混合溶液中镁铝比的增加而增加到一极限值(Mg/Al=2)。随着制备时的镁铝比的增加，溶胶的固含量增加，其产率下降，但ζ电位先上升而后下降。在溶液中镁铝比大于2∶1时，溶胶中只有镁铝氢氧化物。随温度的升高，在胶溶过程中颗粒增大，为六角片状微晶。     

树脂交换法制备白炭黑溶胶

用白炭黑溶胶作造纸工业的添加剂,可以改进纸的滞留性和脱水性,将带有阴离子的白炭黑溶胶与一些阳离子聚合物一起使用,效果更佳。在造纸工业中添加的白炭黑溶胶粒径应在4～7nm,比表面为700～300m^2／g,稳定性好,传统方法制备的白炭黑溶胶难于达到此要求。本文对用树脂交换法制备白炭黑溶胶的条件、影响因素、最佳工艺进行了探讨。     

氢氧化铁溶胶制备条件对其电泳等性能的影响

In order to explore the optimum preparation conditions, effects of FeCl₃ dosage, hydrolysis temperature and dialysis time on the particle size, conductivity, pH and double layer potential (ζ) of Fe(OH)₃ sol were systematically studied. The ultraviolet-visible reflection spectrophotometry was used to track the particle size of Fe(OH)₃ sol. With the increase of FeCl₃ dosage, the particle size of the colloid increased, the reflectivity decreased and the reflection wavelength shifted to longer wavelength, which is in accordance with the quantum confinement effect theory. The excessive Cl^- would inhibit the conductivity, and the stability of Fe(OH)₃ sol with larger particle size would be worse. Because of the better synergistic effect of q/m and V/l under the action of electric field of 80 V with electrophoresis, the ζ of the Fe(OH)₃ sol prepared under the optimum conditions (c_FeCl3, 0.01 mol·L^-1; 100℃; dialysis time, 1 d) was 43.67 mV which was most close to the theoretical value of 44.00 mV.     

均分散氧化亚铜溶胶的制备

均分散体系是指分散相粒子形状大小均相同的体系,我们曾研究过尿素水解法和强制水解法制备均分散氧化铜微粒.手续上大大简化.因为均分散制备不同于机械粉碎、气相沉积等方法,体系是在液相中生成晶核后,各个晶核同步生长形成的.因此,溶液中的pH、阴离子、络合剂、反应物浓度以及温度都会影响粒子生长.McFadyen 等人曾研究过酒石酸铜用葡萄糖还原氧化亚铜微粒,由于条件不同可得不同形状大小微粒.     

氢氧化铝镁正电溶胶制备及性能研究

氢氧化铝镁正电溶胶制备及性能研究侯万国，张春光，孙德军，梁晓丽，王果庭（山东大学胶体与界面化学研究所，济南，２５０１００）关键词混合金属氢氧化物，溶胶，超细颗粒混合金属氢氧化物的合成、组成及结构等已得到广泛研究［１，２］．我们也曾用插入法合成了混合金...     

溶胶—凝胶法制备超细SiO2

ＳｉＯ２气凝胶超细粉由ＴＥＯＳ（正硅酸乙酯）在乙醇溶液中水解聚合后经超临界流体干燥（ＳＣＦＤ）制得。本文考察了ＴＥＯＳ的浓度、水和ＴＥＯＳ护林经以及焙烧温度对超细分织构性能的影响。结果表明，超细ＳｉＯ２的比表面积、总孔容、孔分布、最可几孔径及表观堆密度均随制备参数而改变。而以ＳｉＯ２气凝胶超细粉估为基本载体材料的Ｃｏ／ＺｒＯ２－ＳｉＯ２催化剂显示出高的ＣＯ＋Ｈ２合成重质烃的活性和选择性。     

NMP中制备TiO2溶胶及其凝胶化

溶胶-凝胶过程;NMP中制备TiO2溶胶及其凝胶化     

溶胶-凝胶法制备氧化铝光学薄膜

氧化铝薄膜性能优异,具有较高的介电常数、高热导率、抗辐照能力强、抗碱离子渗透能力强以及在很宽的波长范围内透明等性能。因此,氧化铝薄膜广泛地应用于微电子器件、电致发光器件、光波导器件以及抗腐蚀涂层等众多领域[1]。特别是氧化铝光学薄膜具有高的抗激光损伤阈值[2],用     

新颖的玻璃制备方法—溶胶—凝胶法

长期以来,玻璃和光学纤维玻璃的制备几乎都是使用熔融—冷却法。这种方法不仅需要昂贵的生产设备,而且难以得到高纯度和高均匀度的材料。尤其是对于一些具有特殊结构和高熔点的玻璃材料,熔融—冷却法往往无能为力。     

溶胶凝胶法制备取向性氧化铝超滤陶瓷膜

用金属醇盐的溶胶-凝胶法在多孔α-Al_2O_3衬底上制备了孔径均一的γ-Al_2O_3超滤膜.经X射线衍射仪、扫描与透射电子显微镜以及静态氮吸附等手段对膜的结构、形貌与孔径大小分布等进行了表征.实验发现顶层膜取向生长,膜厚受浸取时间、溶胶浓度、粘度和实验温度等因素影响.典型条件下可在20mm×20mm衬底上制备孔径均一、大小为3.8～4.8nm和厚度2μm左右的无裂纹、无孔洞等表面缺陷的多孔γ-Al_2O_3陶瓷膜.     

溶胶-凝胶方法制备ZnO:Al薄膜及其制备工艺条件研究

采用Sol-Gel工艺在玻璃基片上制备出C轴择优取向性、高可见光透过率以及高电导率的Al³⁺离子掺杂的ZnO透明导电薄膜ZnO:Al(ZAO薄膜).并研究了退火温度、Al掺杂量等对其光电性能的影响.结果表明,溶胶-凝胶法制备ZAO薄膜的最佳工艺条件为:溶胶浓度0.75 mol/L、掺杂量1.5 atm%,镀膜层数10层(厚度约为136 nm)、退火温度600℃.     

针状TiO2锐钛矿晶粒溶胶的制备、结构及形成机理研究

The PTA sol was prepared using titanyl sulfate(TiOSO₄), peroxide (H₂O₂) and ammonia (NH₃·H₂O) as raw materials. The semitransparent, light yellow AS(autoclaved sol) with ultra-fine needle-like anatase crystals was synthesized by autoclaving the PTA sol at 80～100 ℃ for different times. The anatase crystals were needle-like and 80 nm in length, 20～30 nm in diameter. The FTIR, XRD, SEM were used to analyse the chemical structure, properties of the AS and influencing factors during the sol preparation. The mechanism model of the AS formation was established based on the inorganic and crystal structural chemistry. The PTA molecules were decomposed to form Ti⁴⁺ under hydrothermal conditions and the Ti⁴⁺ were hydrated with water to get [Ti(OH)₄(OH₂)₂]⁰, a growing units of the anatase crystals. The appearance of the needle-like anatase crystals and the anatase precipitate are also explained in this paper.     

硅胶整体柱的制备及制备条件对整体柱的影响

研究了硅胶整体柱的制备工艺及温度、pH对凝胶化过程的影响,探讨了不同的四甲氧基硅烷／聚乙二醇比例、不同制也剂浓度对柱结构的影响,以及不同焙烧温度和酸活化处理方法对柱体Si0H含量和线性收缩率的影响,由此确定最佳制备条件。结果表明,采用改进的溶胶-凝胶工艺制备的硅胶整体柱,无开裂变形现象;不同制备条件,可以产生具有不同微米级鞍形骨架、微米级大孔和纳米级中孔的整体柱,可适合不同物质的分离和分析。     

纳米氧化铁制备中的团聚问题

纳米材料是近年来的研究热点。通常的纳米Fe2O3粒子制备过程中处理温度高,粒子易团聚,难于分离[1～4]。本文用溶胶 凝胶 相转移法制得粒径为20-50nm的Fe2O3,胶溶过程控制pH在2左右,煅烧温度降至420℃,用无水氯化钙、无水硫酸钠两级脱水干燥,减小了团聚,使其更具实用性。1　实验取23 8gFeCl3·6H2O溶于500ml蒸馏水,取200ml此三氯化铁溶液,搅拌下逐滴加入10ml氨水与40ml蒸馏水的混合液中直至其显弱碱性。将沉淀过滤,洗涤,在滤液中加硝酸银溶液至无白色沉淀。胶溶剂为0 7～1 5mol/LFeCl3溶液,用量40ml,胶溶温度70℃左右,pH值控制在2…     

拟薄水铝石溶胶法制备改性氧化铝的研究

通过BET表征和微反活性评价,对溶胶法制备的氧化铝样品的物理性能和反应性能进行了初步的研究.实验结果表明固含量、酸种类以及添加物稀土的种类均会对氧化铝的性能产生一定的影响.     

溶胶凝胶法制备Y_2O_3∶Eu发光薄膜

以无机盐为水解原料,用溶胶 凝胶法制备了透明、稳定的前驱液,加入适量的成膜物质聚乙烯醇后,用浸渍拉提法在石英玻璃表面得到均匀的溶胶膜,经过室温干燥和低温处理的薄膜再于一定的温度下烧结,得到了红光发射掺铕的氧化钇薄膜.通过X射线衍射对膜的结构进行表征,表明在600℃时就开始了晶化,在900℃时形成单相Y2O3晶体.激发光谱和发射光谱显示,在220nm和260nm之间有很宽的激发峰,最强峰在236nm处,而发射主峰在614nm处,是一种很好的红光发射薄膜材料.     

改性SrTiO3陶瓷电容器材料的化学制备及电性研究

本文采用（Ｃ４Ｈ９Ｏ）４Ｔｉ，Ｓｒ（ＮＯ３）２和Ｎｉ（ＮＯ３）３为原料制成柠檬酸多元配合物溶液，经过形成溶胶凝胶过程，在一定条件下进行热分解，获得组成为：０．９１ＳｒＴｉＯ３＋０．０９（Ｂｉ２Ｏ３．３ＴｉＯ２）的陶瓷粉料，上述粉料掺入３ｍｏｌ％ＰｂＯ，３Ｍｏｌ％Ｌｉ２Ｏ和０．４ｍｏｌ％Ｒｂ２Ｏ后经混全，压片、干燥和烧结等步骤制成改性ＳｒＴｉＯ３电容器材料，电性研究表明，用这种材料制成的电容器其介电     

PMMA/TiO_2-SnO_2有机无机杂化材料的制备及表征

以乙酰丙酮为偶联剂,应用溶胶-凝胶法制备了聚甲基丙烯酸甲酯(PMMA)/TiO2-SnO2有机无机杂化材料。采用红外光谱(FT-IR)、紫外光谱(UV)对PMMA/TiO2-SnO2进行表征,并测定其TG性质。结果表明:在聚合反应过程中,有机聚合物和无机组分之间通过共价键相连,并且该杂化材料具有良好的抗紫外光辐射性能和热稳定性能。     

溶胶—凝胶法制备Na5YSi4O12及其离子导电性质

用溶胶－凝胶方法制备了钠快离子导体Ｎａ５ＹＳｉ４Ｏ１２（简称ＮＹＳ）的纯相，应用交流阻抗谱技术测定了样品的离子导电活化能，用扫描电子显微镜对用不同制备的样品烧结体表面进行了观察，与传统固相反应法制备的ＮＹＳ离子导体相比，用溶胶－凝胶方法制备的ＮＹＳ烧结体具有较好的界面效应。