锂离子二次电池正极材料LiVPO4F的制备及其电化学性能的研究

A new cathode material, LiVPO₄F, has been synthesized through two steps of solid-state reactions. In the first step, vanadium pentoxide, ammonium dihydrogen phosphate, and a high surface area carbon were pre-heated at 300 ℃ and reacted at 750 ℃ under an inert atmosphere to yield the trivalent vanadium phosphate VPO₄. In the second step, the product LiVPO₄F was synthesized by the reaction with VPO₄ and LiF. The LiVPO₄F was characterized by X-ray diffraction, scanning electron microscopy, cyclic voltammetry and charge/discharge testing measurements. The LiVPO₄F is triclinic crystalline system. At 0.1 C rate, the first charge/discharge capacities were 150.1 mAh·g^-1 and 132.6 mAh·g^-1; At 0.2 C rate, the first charge/discharge capacities were 142.9 mAh·g^-1 and 125.2 mAh·g^-1. The LiVPO₄F from this work has higher charge/discharge voltage 4.3 V and 4.1 V, respectively.     

掺镍型层状LixNiyMn1-yO2正极材料的合成与电性能研究

A kind of cathode material of layered Li_xNi_yMn_1-yO₂ characterized with the O2 type has been synthesized by a simple method. Its precursor Na_xNi_yMn_1-yO₂ has been prepared from manganese dioxide， nickel hydroxide and sodium carbonate at high temperature in air and quickly cooled in cold water， then it has been exchanged by the melted LiNO₃ at 300～400℃ in air. The effects of calcine-temperature for the precursors and its compositions (the content of Na and Ni) on the electrochemical properties of the material Li_xNi_yMn_1-yO₂ have been investingated by XRD and electrochemical tests. The results show that the sample Li_0.7Ni_0.3Mn_0.7O₂， has the best electrochemical properties which shows only one charge-discharge potential stage of 2.8～3.0V and has a high specific capacity over 180mAh·g^-1 cycled between 2.0～4.20V. A significant structure transformation to the spinal-type phase has not been found in the charge-discharge cycling and the discharge specific capacity around 165mAh·g^-1 has re-mained after the 20th cyclings for the material.     

碳包覆LiFePO4的一步固相法制备及高温电化学性能

Carbon coated LiFePO₄ cathode material was synthesized by one-step solid-state reaction and characterized by X-ray diffraction (XRD), field-emission-scanning electron microscope (FESEM). Electrochemical performances of the material as cathode in lithium-ion battery were investigated at medium and elevated temperature (30 and 55 ℃) by galvanostatic charge-discharge and A.C. impedance tests. The results show that carbon coated LiFePO₄ powder exhibits a well-crystallized olivine structure and spherical morphology with an average particle size of about 500 nm. Galvanostatic charge-discharge tests show that the reversible discharge capacity at 1 C and 1.5 C rates was improved from 121 and 105 mAh·g^-1 at 30 ℃ to 136 and 123 mAh·g^-1 at 55℃, respectively, while the enhancement of high temperature on electrochemical performance is less obvious at a rate lower than 0.5 C. Impedance spectra analyses indicate that the cathode material has a remarkably higher lithium-ion diffusivity at 55 ℃ than that at 30 ℃, which improves the electrochemical performance at high temperature.     

LiCoO2中锂离子固相扩散系数随循环次数的变化

The solid diffusion coefficient of lithium-ion in LiCoO₂ cathode material has been investigated by the capacity intermittent titration technique (CITT) at different voltages and at different charge/discharge cycles. By SEM, XRD and FTIR techniques, the structure of LiCoO₂ was studied before and after charge-discharge cycles, and the relationship between solid diffusion coefficient and crystal structure was further discussed. CITT results show that the value of Li⁺ solid diffusion coefficient of LiCoO₂ is about 10^-12 cm²·s^-1. During the whole charge-discharge cycles, the Li⁺ solid diffusion coefficient decreased within the voltage of 4.0～4.3 V, which is attributed to the change of the structure of LiCoO₂.     

流变相法制备LiNi0.5Mn1.5O4锂离子电池正极材料及其电化学性质

LiNi_0.5Mn_1.5O₄ was prepared by rheological method using CH₃COOLi, Ni(CH₃COO)₂ and Mn(CH₃COO)₂ as raw materials. XRD and SEM results show that LiNi_0.5Mn_1.5O₄ synthesized at 850 ℃ has cubic spinel structure with clearly defined shape and particle size of 0.2～0.4 μm. Electrochemical tests show that the LiNi_0.5Mn_1.5O₄ presents a plateau near 4.7 V and delivers the maximum discharge capacity of 140.5 mAh·g^-1. After 100 cycles, the capacity loss per cycle was only 0.015% discharged at 0.2C and the capacity retention was more than 76.3% discharged at 2.0C at room temperature and the capacity loss per cycle was only 0.32% discharged at 0.2C at 55 ℃.     

LiNi1-xMxVO4的红外光谱和拉曼光谱研究

The vanadates of LiNi_1-xM_xVO₄(M=Fe,Co,Ni) containing VO₄ tetrahedrons were synthesized by soft chemical method through a new mild liquid route. The samples sintered at 450℃ for 3h and at 650℃ for 3h are named for LT-LiNiVO₄ and for MT-LiNi_1-xM_xVO₄ respectively. All of the products were measured by X-ray diffraction, IR and Raman spectra respectively. In comparison with IR spectra of V₂O₅ and NiO, the LT-LiNiVO₄ has a strong and broad IR absorption band of VO₄ tetrahedrons located at 600～850cm^-1 with three small splitting peaks corresponding to the asymmetry stretching vibrations of V-O bonds. The results of IR and Raman spectra for MT-LiNi_1-xM_xVO₄ show that the cations of Ni²⁺, Co²⁺, Fe²⁺ have the influences on the frequency shifts of the V-O vibrations.     

纳米SrTiO3对高铁酸盐电化学性能影响研究

Two ferrates, K₂FeO₄ and BaFeO₄, had been prepared and characterized by XRD, IR and SEM. The electrochemical tests of the samples were carried out in the voltage range of 0.8～2.0 V and current density of 0.5～3.0 mA·cm^-2. The results indicated that performance of Zn-BaFeO₄ battery was superior to that of Zn-MnO₂ and Zn-K₂FeO₄ batteries. Nanometer SrTiO₃ prepared by Sol-gel methode with different ratio was added to the BaFeO₄ cathode in order to improve the discharge performance. The discharge capacity of the BaFeO₄ cathode was increased from 224 mAh·g^-1 to 246 mAh·g^-1 by addition of 5% nanometer SrTiO₃. The reason of enhancing BaFeO₄ electrochemical performance was discussed.     

球形La2O3∶Eu纳米晶的制备及其发光特性

The spheric La₂O₃∶Eu nanocrystals were prepared using NH₃·H₂O-NH₄HCO₃ mixture as precipitant. The material was characterized by FTIR, XRD and TEM techniques. The luminescence properties of Eu³⁺ in spheric La₂O₃ were measured by three dimension spectra, emission and excitation spectra. The results indicate that the La₂O₃∶Eu nanocrystals are in hexagonal phase by annealing at 800 ℃, the crystal size is about 30 nm. The maximum emission and excitation wavelength were determined by three dimensional spectroscopy to be at 591 nm and 394 nm, respectively. In emission spectrum the band at 591 nm and 612 nm are corresponding to ⁵D₀-⁷F₁ and ⁵D₀-⁷F₂ transition of Eu³⁺ ions. With increasing in annealing temperature the differences of intensity of the two transitions are increased. This phenomenon shows that the luminescence intensity of La₂O₃∶Eu nanocrystals can be tuned by changing annealing temperature.     

纳米Mn-Zn铁氧体的制备和研究

Nanosize manganese zinc ferrites were fabricated by hydrothermal precipitation route using Fe₂(SO₄)₃, ZnSO₄·7H₂O, MnSO₄·H₂O as material, then some calcinated at 500 ℃ and studied by XRD, TEM, IR and VSM. The results showed that the products were spinel crystal structure and uniformly sized nanoparticles (15～25 nm) with little aggregation. The analysis of IR showed that the superficial water can be eliminated, but that was embedded in crystal lattice can not be removed by calcinating. The effect Zn content x on the lattice (a) of nanosize Mn_1-xZn_xFe₂O₄ was also discussed. The lattice of nanosize Mn_1-xZn_xFe₂O₄ decreases with x increasing; and its value deviated the standard lattice (a₀) of normal size manganese zinc ferrites. A lot of water was absorbed during the hydrothermal process owing to the large surface of nanosize particles. The change of magnetic properties of Mn_xZn_1-xFe₂O₄ with x increasing was studied: nanosize Mn_xZn_1-xFe₂O₄ particles synthesized by us exhibited peculiar magnetic properties curve with Zn content (x) increasing, Superparamagnetic behaviors of the synthesized ZnFe₂O₄ samples were confirmed by magnetic characterization, which can be explained by the difference between the distribution of the metal ions (Mn²⁺, Zn²⁺ and Fe³⁺) among the tetrahedral (A) and the octahedral (B) sites of nanosize ferrite and that of bulk ferrite.     

LiV3O8的合成及其电化学性能研究

The layered trivanadate, LiV₃O₈, was prepared by sol-gel method with LiOH, V₂O₅ and H₂O₂ as initial reagents. The materials at different heat treatment conditions were characterized by XRD and TG-DTA. Their electrochemical behaviors were studied by galvanostatic charge-discharge and cyclic voltammetry. The results show that LiV₃O₈ prepared by sintering at 300 ℃ for 16 h has higher capacity, and its initial discharge capacity is 333.1 mAh·g^-1, and maintains a discharge capacity of 302.8 mAh·g^-1 after 10 cycles at 0.2 C and the voltage range of 1.8～4.0 V.     

Li_(1.3)Ti_(1.7)Al_(0.3)(PO_4)_3,Na_(1.3)Ti_(1.7)Al_(0.3)(PO_4)_3的离子交换研究

研究了在不同温度下的NaNO3和AgNO3水溶液中Li1.3Ti1.7Al0.3(PO4)3和Na1.3Ti1.7Al0.3(PO4)3离子交换行为.实验表明Li1.3Ti1.7Al0.3(PO4)3和Na1.3Ti1.7Al0.3(PO4)3均显示出了高选择性与Na+和Ag+进行离子交换的特征,且对Ag+的选择性高于Na+.升高温度可显著提高Ag/Li和Ag/Na的交换反应速度.     

Crystal growth, structure determination, and optical properties of new potassium-rare-earth silicates K3RESi2O7 (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu)

Single crystals of K₃RESi₂O₇ (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu) were grown from a potassium fluoride flux. Two different structure types were found for this series. Silicates containing the larger rare earths, RE=Gd, Tb, Dy, Ho, Er, Tm, Yb crystallize in a structure K₃RESi₂O₇ that contains the rare-earth cation in both a slightly distorted octahedral and an ideal trigonal prismatic coordination environment, while in K₃LuSi₂O₇, containing the smallest of the rare earths, lutetium is found solely in an octahedral coordination environment. The structure of K₃LuSi₂O₇ crystallizes in space group P6₃/mmc with a=5.71160(10) Å and c=13.8883(6) Å. The structures containing the remaining rare earths crystallize in the space group P6₃/mcm with the lattice parameters of a=9.9359(2) Å, c=14.4295(4) Å, (K₃GdSi₂O₇); a=9.88730(10) Å, c=14.3856(3) Å, (K₃TbSi₂O₇); a=9.8673(2) Å, c=14.3572(4) Å, (K₃DySi₂O₇); a=9.8408(3) Å, c=14.3206(6) Å, (K₃HoSi₂O₇); a=9.82120(10) Å, c=14.2986(2) Å, (K₃ErSi₂O₇); a=9.80200(10) Å, c=14.2863(4) Å, (K₃TmSi₂O₇); a=9.78190(10) Å, c=14.2401(3) Å, (K₃YbSi₂O₇). The optical properties of the silicates were investigated and K₃TbSi₂O₇ was found to fluoresce in the visible.     

Near infrared study of aqueous rare-earth ethylsulfates

The near infrared spectra of aqueous solutions of the ethylsulfates of La, Nd, Gd, Tb, Er, Yb, Lu, Y, and Na have been determined from about 0.2 mol-dm^–3 to nearly saturation. The extinction coefficients of water have been calculated taking into account the absorption of ethylslfate anions determined in separate experiments. Their values appeared to be nearly the same as that of pure water. The relative contents of free OH groups in 0.5 and 0.7M solutions have been estimated from the absorbances at 1160 nm. They were lower in solutions of the heavy rare-earth ethylsulfates (Tb, Er, Yb, Lu) than in equimolar solutions of the lighter ones (La, Nd), confirming our previous view that secondary hydration of the heavy trivalent rare-earth cations is distinctly stronger than that of the lighter ones. A comparison of the spectra of these aqueous ethylsulfates with those of perchlorates shows that the structure-breaking ability of the C₂H₅SO ₄ ^– ion is much smaller than that of perchlorate anion.     

Structural studies of five layer Aurivillius oxides: A2Bi4Ti5O18 (A=Ca, Sr, Ba and Pb)

The room temperature structures of the five layer Aurivillius phases A₂Bi₄Ti₅O₁₈ (A=Ca, Sr, Ba and Pb) have been refined from powder neutron diffraction data using the Rietveld method. The structures consist of [Bi₂O₂]²⁺ layers interleaved with perovskite-like [A₂Bi₂Ti₅O₁₆]²⁻ blocks. The structures were refined in the orthorhombic space group B2eb (SG. No. 41), Z=4, and the unit cell parameters of the oxides are a=5.4251(2), b=5.4034(1), c=48.486(1); a=5.4650(2), b=5.4625(3), c=48.852(1); a=5.4988(3), b=5.4980(4), c=50.352(1); a=5.4701(2), b=5.4577(2), c=49.643(1) for A=Ca, Sr, Ba and Pb, respectively. The structural features of the compounds were found similar to n=2-4 layers bismuth oxides. The strain caused by mismatch of cell parameter requirements for the [Bi₂O₂]²⁺ layers and perovskite-like [A₂Bi₂Ti₅O₁₆]²⁻ blocks were relieved by tilting of the TiO₆ octahedra. Variable temperature synchrotron X-ray studies for Ca and Pb compounds showed that the orthorhombic structure persisted up to 675 and 475 K, respectively. Raman spectra of the compounds are also presented.     

电感耦合等离子体光谱法(ICP-AES)测定银精矿中铜、铅、锌、砷、镉、钙、镁、锰含量

针对银精矿样品复杂,难消解的特点,研究了不同酸溶法和碱熔法对样品的消解情况,建立了硝酸,盐酸,氢氟酸,高氯酸消解银精矿的方法。根据元素灵敏度和抗干扰性,选定各元素的测定波长。通过酸溶样和碱熔样测定结果比对,验证了方法准确性。建立了四酸消解-电感耦合等离子体光谱法测定银精矿中铜、铅、锌、砷、镉、钙、镁、锰含量的方法,元素的线性相关系数均在0.9999以上。通过共存元素干扰实验,确定了银精矿中高含量元素(铜、铅、锌、铁、锑、铋等)对测定元素结果没有影响。方法检出限：Cu 0.0063 mg/L, Pb 0.0159 mg/L ,Zn 0.0090 mg/L,As 0.0192 mg/L, Cd 0.0093 mg/L ,Ca 0.0084 mg/L, Mg 0.0075 mg/L, Mn 0.0081 mg/L。测定下限：Cu 0.0105mg/L,Pb 0.0265 mg/L, Zn 0.0150 mg/L, As 0.0320 mg/L, Cd 0.0155 mg/L, Ca 0.0140 mg/L, Mg 0.0125 mg/L,Mn 0.0135 mg/L。3个样品的相对标准偏差在0.87%~3.56%之间,加标回收率在95.00%~103.56%之间。方法流程短,操作简单,快速,灵敏度和再现性高,结果准确可靠,可以满足银精矿中铜、铅、锌、砷、镉、钙、镁、锰含量的测定。     

The crystal chemistry of Bi6TP2O15+x, T=Fe, Ni, Zn: Isomorphism and polymorphism, structural relationship to Bi6TiP2O16

The crystal structures of compounds with nominal compositions Bi₆FeP₂O_15+x (I), Bi₆NiP₂O_15+x (II) and Bi₆ZnP₂O_15+x (III) were determined from single-crystal X-ray diffraction data. They are monoclinic, space group I2, Z=2. The lattice parameters for (I) are a=11.2644(7), b=5.4380(3), c=11.1440(5) Å, β=96.154(4)°; for (II) a=11.259(7), b=5.461(4), c=11.109(7) Å, β=96.65(1)°; for (III) a=19.7271(5), b=5.4376(2), c=16.9730(6) Å, β=131.932(1)°. Least squares refinements on F² converged for (I) to R1=0.0554, wR₂=0.1408; for (II) R₁=0.0647, wR₂=0.1697; for (III) R₁=0.0385, wR₂=0.1023. The crystals are complexly twinned by 2-fold rotation about , by inversion and by mirror reflection. The structures consist of edge-sharing articulations of OBi₄ tetrahedra forming layers in the a-c plane that then continue by edge-sharing parallel to the b-axis. The three-dimensional networks are bridged by Fe and Ni octahedra in (I) and (II) and by Zn trigonal bipyramids in (III) as well as by oxygen atoms of the PO₄ moieties. Bi also randomly occupies the octahedral sites. Oxygen vacancies exist in the structures of the three compounds due to required charge balances and they occur in the octahedral coordination polyhedron of the transition metal. In compound (III), no positional disorder in atomic sites is present. The Bi-O coordination polyhedra are trigonal prisms with one, two or three faces capped. Magnetic susceptibility data for compound (I) were obtained between 4.2 and 350 K. Between 4.2 and 250 K it is paramagnetic, μ_eff=6.1 μ_B; a magnetic transition occurs above 250 K.     

Preparation of ZrO2-TiO2-CeO2 and Its Application in the Selective Catalytic Reduction of NO with NH3

TiO₂,ZrO₂-TiO₂,andZrO₂-TiO₂-CeO₂ were prepared by co-precipitation method and characterized by X-ray diffraction (XRD), specific surface area measurements (BET), temperature programmed desorption (NH₃-TPD), oxygen storage capacity (OSC), and temperature programmed reduction (H₂-TPR). The results showed that ZrO₂-TiO₂-CeO₂ exhibited large number of surface strong acid, possessed some oxygen storage capacity, and strong redox property. The three materials were used as supports and the monolith catalysts were prepared with 1% (w) V₂O₅ and 9% (w)WO₃ for selective catalytic reduction (SCR) of NO with ammonia in the presence of excessive O₂, and the results of catalytic activity showed that the catalyst used ZrO₂-TiO₂-CeO₂ as support yielded nearly 100% NO conversion at 275 °C at a gas hourly space velocity (GHSV) of 10000 h⁻¹, and it had the best catalytic activity and showed great potential for practical application.     

B2O3-Bi2O3-ZnO-Al2O3玻璃助烧剂对BaTiO3陶瓷烧结条件、晶体结构和介电性能的影响

通过调节B₂O₃-Bi₂O₃-ZnO-Al₂O₃(BBZA)玻璃的添加量研究其对钛酸钡(BaTiO₃)陶瓷烧结条件、晶体结构和介电性能的影响。结果表明：添加适量的BBZA玻璃能够有效地将BaTiO₃陶瓷烧结温度由1 350℃降至950℃,并使其致密化。同时,添加BBZA玻璃后,BaTiO₃的晶体结构随着烧结温度的升高而发生转变(立方相→四方相)。另外,BBZA玻璃的引入使BaTiO₃陶瓷的居里峰得到了有效的抑制和拓宽。陶瓷微观形貌显示,玻璃相均匀分布在BaTiO₃晶粒表面。优化的BaTiO₃陶瓷制备条件如下：BBZA添加量(质量分数)为2.0%,烧结温度为950℃。在该条件下制备的BaTiO₃陶瓷介电常数达到1 364,介电损耗低至1.2%。     

The Phase Relations in the System In2O3–TiO2–MgO at 1100 and 1350°C

The phase relations in the system In₂O₃–TiO₂–MgO at 1100 and 1350°C are determined by a classical quenching method. In this system, there are four pseudobinary compounds, In₂TiO₅, MgTi₂O₅ (pseudobrookite type), MgTiO₃ (ilmenite type), and Mg₂TiO₄ (spinel type) at 1100°C. At 1350°C, in addition to these compounds there exist a spinel-type solid solution Mg_2−xIn_2xTi_1−xO₄ (0≤x≤1) and a compound In₆Ti₆MgO₂₂ with lattice constants a=5.9236(7) Å, b=3.3862(4) Å, c=6.3609(7) Å, β=108.15(1)°, and q=0.369, which is isostructural with the monoclinic In₃Ti₂FeO₁₀ in the system In₂O₃–TiO₂–MgO. The relation between the lattice constants of the spinel phase and the composition nearly satisfies Vegard's law. In₆Ti₆MgO₂₂ extends a solid solution range to In₂₀Ti₁₇Mg₃O₆₇ with lattice constants of a=5.9230(5) Å, b=3.3823(3) Å, c=6.3698(6) Å, β=108.10(5)°, and q=0.360. The distributions of constituent cations in the solid solutions are discussed in terms of their ionic radius and site preference effect.     

Microstructures of Some Bi-W-Nb-O Phases

Microstructures of three Bi-W-Nb-O phases have been examined by using high-resolution transmission electron microscopy. Bi₁₇W₂Nb₃O₃₉ and Bi₁₇WNb₃O₃₆ have incommensurate superstructures derived from the defect fluorite-type δ-Bi₂O₃ and can be regarded as intermediate phases between the type II solid solutions in the Bi-Nb-O and Bi-W-O systems. Bi₈W₂Nb₂O₂₃ has a Bi₂WO₆-like subunit cell with a stepped superstructure. Formation mechanisms of various superstructures are discussed.