预氧化固气法合成LiNiO2的研究

LiNiO₂ was prepared by reaction of stoichiometric amounts of thoroughly-mixed LiOH·H₂O and preoxidation nanometer-scale Ni₃O₂(OH)₄ powders in O₂ at the temperature of 700℃ for 6h. The products were tested by XRD， XPS， SEM and electrochemistry methods. It was shown that product was LiNiO₂ single-phase， and the valence of nickel was +3; the average size of it was 40nm; its initial charge specific capacity is 168mAh·g^-1 and the coulomb efficiency is 90%; the second charge specific capacity is 160mAh·g^-1 and the coulomb efficiency is 96%.     

纳米SrTiO3对高铁酸盐电化学性能影响研究

Two ferrates, K₂FeO₄ and BaFeO₄, had been prepared and characterized by XRD, IR and SEM. The electrochemical tests of the samples were carried out in the voltage range of 0.8～2.0 V and current density of 0.5～3.0 mA·cm^-2. The results indicated that performance of Zn-BaFeO₄ battery was superior to that of Zn-MnO₂ and Zn-K₂FeO₄ batteries. Nanometer SrTiO₃ prepared by Sol-gel methode with different ratio was added to the BaFeO₄ cathode in order to improve the discharge performance. The discharge capacity of the BaFeO₄ cathode was increased from 224 mAh·g^-1 to 246 mAh·g^-1 by addition of 5% nanometer SrTiO₃. The reason of enhancing BaFeO₄ electrochemical performance was discussed.     

新型锂离子电池正极材料LiVOPO4的制备与表征

Novel lithium-ion battery cathode material LiVOPO₄ was synthesized by sol-gel method using lithium hydroxide, ammonium metavanadate, phosphoric acid and citric acid as raw materials. The microstructure, surface morphology and electrochemical properties were characterized by various electrochemical methods in combination with thermogravimertric (TG) analysis and differential thermal analysis (DTA), X-ray diffraction (XRD), infrared (IR) spectroscopy, scanning electron microscope (SEM). Results show that the sample obtained by calcinating at 650 ℃ for 6 h is made up of uniform particles with size of 2～3 μm. The first discharge, charge capacity and columbic efficiency of LiVOPO₄ is 137.1 mAh·g^-1, 146.1 mAh·g^-1 and 93.8%, respectively. After 80 cycles the discharge capacity is kept at 130.4 mAh·g^-1, which is 95.1% of the first discharge capacity, and the capacity loss per cycle was only 0.061%, suggesting the LiVOPO₄ derived by this method is a promising cathode material for lithium ion batteries.     

梯度材料LiNi0.8Co0.2O2的合成与表征

The gradient composite LiNi_0.8Co_0.2O₂ was synthesized using spherical Ni(OH)₂ particle coated by a sol-gel containing cobalt and lithium. The precursor was examined by DSC-TG. The gradient composite was characterized by SEM, EDS, XPS, XRD and ICP-AES. The XPS, EDS and ICP-AES results show that content of cobalt in the surface is higher than in the center of the spherical particle of the gradient composite. The first discharge specific capacity of the gradient composite sintered at 700 ℃ is 187.3 mAh·g^-1.     

锂离子电池用Li4Ti5O12-碳复合材料的制备与电化学性能

Li₄Ti₅O₁₂-C composite was prepared by sol-gel method using ethyl alcohol as solvent, lithium acetate and tetrabutyl titanate as raw materials, and graphite as carbon source. Li₄Ti₅O₁₂-C composites were characterized by thermogravimertric(TG) analysis and differential thermal analysis(DTA), X-ray diffraction(XRD), Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM) and electrochemical tests. Results show that Li₄Ti₅O₁₂-C composite with 5% carbon containing can be obtained by annealing the precursor at 600 ℃ for 6 h in N₂ atomsphere. The composites can deliver a specific capacity of 167.1 mAh·g^-1, 99.0% and 105.1% of the capacity can be retained after discharged for 80 times at 0.1C and 2.0C, respectively. Compared with pure Li₄Ti₅O₁₂, Li₄Ti₅O₁₂-C composite shares larger discharge capacity, better cyclability and rate performance.     

Li2CO3、NiO和电解MnO2合成高容量LiNi0.5Mn1.5O4及其表征

Well-developed crystalline LiNi_0.5Mn_1.5O₄ was prepared by solid-state reaction using Li₂CO₃, NiO and electrolytic MnO₂ at high heating and cooling rate. X-ray diffraction (XRD) patterns and scanning electron microscopic (SEM) images showed that LiNi_0.5Mn_1.5O₄ synthesized at 900 ℃ and 950 ℃ had cubic spinel structure with clearly defined shape. LiNi_0.5Mn_1.5O₄ spinel phase decomposed at 1 000 ℃ accompanying with structural and morphological degradation. TG measurement revealed that the weight loss during heating process could be mostly gained in cooling process, and the upward tendency of weight loss during heating process decreased, while that of irreversible weight loss rapidly increased with the increase of temperature. LiNi_0.5Mn_1.5O₄ powders prepared at 900 ℃ for 12 h delivered the maximum discharge capacity of 134 mAh·g^-1 with good cyclic performance at 2/7 C. In addition, by adjusting the calcination time at 900 ℃, the capacity and cycling performance of LiNi_0.5Mn_1.5O₄ were further enhanced.     

流变相法制备LiNi0.5Mn1.5O4锂离子电池正极材料及其电化学性质

LiNi_0.5Mn_1.5O₄ was prepared by rheological method using CH₃COOLi, Ni(CH₃COO)₂ and Mn(CH₃COO)₂ as raw materials. XRD and SEM results show that LiNi_0.5Mn_1.5O₄ synthesized at 850 ℃ has cubic spinel structure with clearly defined shape and particle size of 0.2～0.4 μm. Electrochemical tests show that the LiNi_0.5Mn_1.5O₄ presents a plateau near 4.7 V and delivers the maximum discharge capacity of 140.5 mAh·g^-1. After 100 cycles, the capacity loss per cycle was only 0.015% discharged at 0.2C and the capacity retention was more than 76.3% discharged at 2.0C at room temperature and the capacity loss per cycle was only 0.32% discharged at 0.2C at 55 ℃.     

掺镍型层状LixNiyMn1-yO2正极材料的合成与电性能研究

A kind of cathode material of layered Li_xNi_yMn_1-yO₂ characterized with the O2 type has been synthesized by a simple method. Its precursor Na_xNi_yMn_1-yO₂ has been prepared from manganese dioxide， nickel hydroxide and sodium carbonate at high temperature in air and quickly cooled in cold water， then it has been exchanged by the melted LiNO₃ at 300～400℃ in air. The effects of calcine-temperature for the precursors and its compositions (the content of Na and Ni) on the electrochemical properties of the material Li_xNi_yMn_1-yO₂ have been investingated by XRD and electrochemical tests. The results show that the sample Li_0.7Ni_0.3Mn_0.7O₂， has the best electrochemical properties which shows only one charge-discharge potential stage of 2.8～3.0V and has a high specific capacity over 180mAh·g^-1 cycled between 2.0～4.20V. A significant structure transformation to the spinal-type phase has not been found in the charge-discharge cycling and the discharge specific capacity around 165mAh·g^-1 has re-mained after the 20th cyclings for the material.     

碳包覆LiFePO4的一步固相法制备及高温电化学性能

Carbon coated LiFePO₄ cathode material was synthesized by one-step solid-state reaction and characterized by X-ray diffraction (XRD), field-emission-scanning electron microscope (FESEM). Electrochemical performances of the material as cathode in lithium-ion battery were investigated at medium and elevated temperature (30 and 55 ℃) by galvanostatic charge-discharge and A.C. impedance tests. The results show that carbon coated LiFePO₄ powder exhibits a well-crystallized olivine structure and spherical morphology with an average particle size of about 500 nm. Galvanostatic charge-discharge tests show that the reversible discharge capacity at 1 C and 1.5 C rates was improved from 121 and 105 mAh·g^-1 at 30 ℃ to 136 and 123 mAh·g^-1 at 55℃, respectively, while the enhancement of high temperature on electrochemical performance is less obvious at a rate lower than 0.5 C. Impedance spectra analyses indicate that the cathode material has a remarkably higher lithium-ion diffusivity at 55 ℃ than that at 30 ℃, which improves the electrochemical performance at high temperature.     

LiNi0.8Co0.2O2 / MWNTs复合物超级电容器电极材料的研究

Multiwalled carbon nanotubes (MWNTs) were used as the conductive additive in the electrode materials. The electrochemical properties of supercapacitors based on LiNi_0.8Co_0.2O₂ / MWNTs composite and LiNi_0.8Co_0.2O₂/acetylene black composite and MWNTs in 1.0 mol·L^-1 LiClO₄ / EC+DEC [V(EC)∶V(DEC)=1∶1] electrolyte were investigated by means of constant charge/discharge current tests, respectively. The experimental results show that the LiNi_0.8Co_0.2O₂ / MWNTs composite has better performance than that of others, and the maximum specific capacitance of the supercapacitor can reach 271.6 F·g^-1, while the energy density is up to 339.5 Wh·kg^-1. Furthermore, it is remarkable that the performance of MWNTs is better than that of acetylene black as the conductive additive.     

Sol-gel synthesis of K3InF6 and structural characterization of K2InC10O10H6F9, K3InC12O14H4F18 and K3InC12O12F18

K₃InF₆ is synthesized by a sol-gel route starting from indium and potassium acetates dissolved in isopropanol in the stoichiometry 1:3, with trifluoroacetic acid as fluorinating agent. The crystal structures of the organic precursors were solved by X-ray diffraction methods on single crystals. Three organic compounds were isolated and identified: K₂InC₁₀O₁₀H₆F₉, K₃InC₁₂O₁₄H₄F₁₈ and K₃InC₁₂O₁₂F₁₈. The first one, deficient in potassium in comparison with the initial stoichiometry, is unstable. In its crystal structure, acetate as well as trifluoroacetate anions are coordinated to the indium atom. The two other precursors are obtained, respectively, by quick and slow evaporation of the solution. They correspond to the final organic compounds, which give K₃InF₆ by decomposition at high temperature. The crystal structure of K₃InC₁₂O₁₄H₄F₁₈ is characterized by complex anions [In(CF₃COO)₄(OH_x)₂]^(5−2x)− and isolated [CF₃COOH_2−x]^(x−1)− molecules with x=2 or 1, surrounded by K⁺ cations. The crystal structure of K₃InC₁₂O₁₂F₁₈ is only constituted by complex anions [In(CF₃COO)₆]³⁻ and K⁺ cations. For all these compounds, potassium cations ensure only the electroneutrality of the structure. IR spectra of K₂InC₁₀O₁₀H₆F₉ and K₃InC₁₂O₁₂F₁₈ were also performed at room temperature on pulverized crystals.     

Li2O-TiO2-SiO2-P2O5和Li2O-TiO2-Al2O3-P2O5体系锂离子固体电解质的制备及性能研究

一些具有NASICON型网格结构的固体电解质具有高的电导率和好的稳定性,NASICON的意思是Na Super Ionic Conductor[1]。当NaZr2(PO4)3中P5 被Si4 部分取代时便可以得到具有NASICON结构的Na1 xZr2SixP3-xO12体系,其具有高的钠离子电导率。然而有相同结构的Li1 xZr2SixP3-xO12体系的离子电导率却很低,这是因为Li 半径太小,而NASICON三维网格结构的离子通道太大,两者不匹配而使电导率下降[2]。但当LiZr2(PO4)3中Zr4 被离子半径小些的Ti4 取代,所得LiTi2(PO4)3的通道就与Li 半径相匹配,适合于锂离子的迁移,从而使其电导率…     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

Synthesis, crystal structure, infrared and Raman spectra of Sr4Cu3(AsO4)2(AsO3OH)4·3H2O and Ba2Cu4(AsO4)2(AsO3OH)3

The two new compounds, Sr₄Cu₃(AsO₄)₂(AsO₃OH)₄·3H₂O (1) and Ba₂Cu₄(AsO₄)₂(AsO₃OH)₃(2), were synthesized under hydrothermal conditions. They represent previously unknown structure types and are the first compounds synthesized in the systems SrO/BaO-CuO-As₂O₅-H₂O. Their crystal structures were determined by single-crystal X-ray diffraction [space group C2/c, a=18.536(4) Å, b=5.179(1) Å, c=24.898(5) Å, β=93.67(3)°, V=2344.0(8) Å³, Z=4 for 1; space group P4₂/n, a=7.775(1) Å, c=13.698(3) Å, V=828.1(2) Å³, Z=2 for 2]. The crystal structure of 1 is related to a group of compounds formed by Cu²⁺-(XO₄)³⁻ layers (X=P⁵⁺, As⁵⁺) linked by M cations (M=alkali, alkaline earth, Pb²⁺, or Ag⁺) and partly by hydrogen bonds. In 1, worth mentioning is the very short hydrogen bond length, D···A=2.477(3) Å. It is one of the examples of extremely short hydrogen bonds, where the donor and acceptor are crystallographically different. Compound 2 represents a layered structure consisting of Cu₂O₈ centrosymmetric dimers crosslinked by As1φ₄ tetrahedra, where φ is O or OH, which are interconnected by Ba, As2 and hydrogen bonds to form a three-dimensional network. The layers are formed by Cu₂O₈ centrosymmetric dimers of CuO₅ edge-sharing polyhedra, crosslinked by As1O₄ tetrahedra. Vibrational spectra (FTIR and Raman) of both compounds are described. The spectroscopic manifestation of the very short hydrogen bond in 1, and ABC-like spectra in 2 were discussed.     

g-C_3N_4/CaTi_2O_5复合材料制备及其光催化性能

利用类石墨氮化碳(g-C_3N_4)和亚稳相钙钛氧化物(CaTi_2O_5)固相法制备C_3N_4/CaTi_2O_5复合材料。利用X射线衍射(XRD)、金相显微镜、扫描电子显微镜(SEM)及附带能谱分析仪(EDS)和N2吸附-脱附对样品的显微结构和比表面积进行检测分析,并用紫外-可见吸收光度计(UV-Vis)测试了样品的光吸收性能,研究C_3N_4与CaTi_2O_5物质的量之比(nC_3N_4/nCaTi_2O_5)对C_3N_4/CaTi_2O_5复合样品的物相结构和微观形貌的影响,同时考察C_3N_4/CaTi_2O_5复合样品在可见光照射下光催化降解罗丹明染料效果。实验结果表明:相比纯C_3N_4和CaTi_2O_5样品,C_3N_4/CaTi_2O_5复合样品在可见光下具有较高的光催化性能,随着nC_3N_4/nCaTi_2O_5增加,样品的光催化降解率随之增加而后降低,当nC_3N_4/nCaTi_2O_5=1∶1时,样品的光催化降解率达到最大值99.5%,并且循环重复利用5次后,样品的光催化剂降解率仍几乎保持不变。复合样品光催化性能提高主要归因于复合能级结构有效地抑制了电子和空穴复合所致。     

Magnetic diphase nanostructure of ZnFe2O4/γ-Fe2O3

Magnetic diphase nanostructures of ZnFe₂O₄/γ-Fe₂O₃ were synthesized by a solvothermal method. The formation reactions were optimized by tuning the initial molar ratios of Fe/Zn. All samples were characterized by X-ray diffraction, thermogravimetric analysis, infrared spectroscopy, and Raman spectra. It is found that when the initial molar ratio of Fe/Zn is larger than 2, a diphase magnetic nanostructure of ZnFe₂O₄/γ-Fe₂O₃ was formed, in which the presence of ZnFe₂O₄ enhanced the thermal stability of γ-Fe₂O₃. Further increasing the initial molar ratio of Fe/Zn larger than 6 destabilized the diphase nanostructure and yielded traces of secondary phase α-Fe₂O₃. The grain surfaces of diphase nanostructure exhibited a spin-glass-like structure. At room temperature, all diphase nanostructures are superparamagnetic with saturation magnetization being increased with γ-Fe₂O₃ content.     

Ion-beam irradiation of lanthanum compounds in the systems La2O3-Al2O3 and La2O3-TiO2

Thin crystals of La₂O₃, LaAlO₃, La_2/3TiO₃, La₂TiO₅, and La₂Ti₂O₇ have been irradiated in situ using 1 MeV Kr²⁺ ions at the Intermediate Voltage Electron Microscope-Tandem User Facility (IVEM-Tandem), Argonne National Laboratory (ANL). We observed that La₂O₃ remained crystalline to a fluence greater than 3.1×10¹⁶ ions cm⁻² at a temperature of 50 K. The four binary oxide compounds in the two systems were observed through the crystalline-amorphous transition as a function of ion fluence and temperature. Results from the ion irradiations give critical temperatures for amorphisation (T_c) of 647 K for LaAlO₃, 840 K for La₂Ti₂O₇, 865 K for La_2/3TiO₃, and 1027 K for La₂TiO₅. The T_c values observed in this study, together with previous data for Al₂O₃ and TiO₂, are discussed with reference to the melting points for the La₂O₃-Al₂O₃ and La₂O₃-TiO₂ systems and the different local environments within the four crystal structures. Results suggest that there is an observable inverse correlation between T_c and melting temperature (T_m) in the two systems. More complex relationships exist between T_c and crystal structure, with the stoichiometric perovskite LaAlO₃ being the most resistant to amorphisation.     

A new 2212-type stair like structure: Bi14Sr21Fe12O61, m=5 member of the generic [Bi2Sr3Fe2O9]m[Bi4Sr6Fe2O16] family

A new oxide, Bi₁₄Sr₂₁Fe₁₂O_61, with a layered structure derived from the 2212 modulated type structure Bi₂Sr₃Fe₂O₉, was isolated. It crystallizes in the I2 space group, with the following parameters: a=16.58(3) Å, b=5.496(1) Å, c=35.27(2) Å and β=90.62°. The single crystal X-ray structure determination, coupled with electron microscopy, shows that this ferrite is the m=5 member of the [Bi₂Sr₃Fe₂O₉]_m[Bi₄Sr₆Fe₂O₁₆] collapsed family. This new collapsed structure can be described as slices of 2212 structure of five bismuth polyhedra thick along , shifted with respect to each other and interconnected by means of [Bi₄Sr₆Fe₂O₁₆] slices. The latter are the place of numerous defects like iron or strontium for bismuth substitution; they can be correlated to intergrowth defects with other members of the family.     

Raman scattering investigations on lanthanum-doped Bi4Ti3O12-SrBi4Ti4O15 intergrowth ferroelectrics

The ferroelectric ceramics of Bi₄Ti₃O₁₂, SrBi₄Ti₄O₁₅, and lanthanum-doped Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅ were synthesized, and their Raman spectra were investigated. La-doping resulted in the enlargement of remnant polarization of Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅. The structure of the Bi₂O₂ layers and TiO₆ octahedra of the intergrowth was found to be different from those of Bi₄Ti₃O₁₂ and SrBi₄Ti₄O₁₅. La³⁺ ions exhibit pronounced selectivity for the occupation of A site as La content is lower than 0.50, and tend to be incorporated into Bi₂O₂ layers when the La content is higher than 0.50. Lanthanum substitution brings about the structural phase transition in Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅. The variation of ferroelectric property may be attributed to combined contribution from the decreasing of the oxygen vacancies, the relaxation of the lattice distortion, the destroying of the insulation and the space charge compensation effects of the Bi₂O₂ slabs.     

一维纳米Co_3O_4,Ag/Co_3O_4及CuO/Co_3O_4的合成与电催化性能(英文)

采用水热合成法制备了Co3O4及复合Ag/Co3O4、CuO/Co3O4一维纳米产品。用XRD,FE-SEM和TEM手段对产品进行了表征。采用循环伏安法研究了合成产品修饰的玻碳电极在碱性溶液中对对硝基苯酚的电催化还原性能。与裸玻碳电极相比,1mmol·L-1的对硝基苯酚在用Co3O4、特别是CuO/Co3O4修饰的玻碳电极上还原的峰电流明显增大,用Ag/Co3O4(Ag/Co原子比分别为1∶5和2∶5)修饰的玻碳电极催化还原对硝基苯酚时,尽管还原峰电流增大不是太大,但其峰电位明显降低(分别降低0.265和0.371V)。