Crystal growth, structure determination, and optical properties of new potassium-rare-earth silicates K3RESi2O7 (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu)

Single crystals of K₃RESi₂O₇ (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu) were grown from a potassium fluoride flux. Two different structure types were found for this series. Silicates containing the larger rare earths, RE=Gd, Tb, Dy, Ho, Er, Tm, Yb crystallize in a structure K₃RESi₂O₇ that contains the rare-earth cation in both a slightly distorted octahedral and an ideal trigonal prismatic coordination environment, while in K₃LuSi₂O₇, containing the smallest of the rare earths, lutetium is found solely in an octahedral coordination environment. The structure of K₃LuSi₂O₇ crystallizes in space group P6₃/mmc with a=5.71160(10) Å and c=13.8883(6) Å. The structures containing the remaining rare earths crystallize in the space group P6₃/mcm with the lattice parameters of a=9.9359(2) Å, c=14.4295(4) Å, (K₃GdSi₂O₇); a=9.88730(10) Å, c=14.3856(3) Å, (K₃TbSi₂O₇); a=9.8673(2) Å, c=14.3572(4) Å, (K₃DySi₂O₇); a=9.8408(3) Å, c=14.3206(6) Å, (K₃HoSi₂O₇); a=9.82120(10) Å, c=14.2986(2) Å, (K₃ErSi₂O₇); a=9.80200(10) Å, c=14.2863(4) Å, (K₃TmSi₂O₇); a=9.78190(10) Å, c=14.2401(3) Å, (K₃YbSi₂O₇). The optical properties of the silicates were investigated and K₃TbSi₂O₇ was found to fluoresce in the visible.