球形La2O3∶Eu纳米晶的制备及其发光特性

The spheric La₂O₃∶Eu nanocrystals were prepared using NH₃·H₂O-NH₄HCO₃ mixture as precipitant. The material was characterized by FTIR, XRD and TEM techniques. The luminescence properties of Eu³⁺ in spheric La₂O₃ were measured by three dimension spectra, emission and excitation spectra. The results indicate that the La₂O₃∶Eu nanocrystals are in hexagonal phase by annealing at 800 ℃, the crystal size is about 30 nm. The maximum emission and excitation wavelength were determined by three dimensional spectroscopy to be at 591 nm and 394 nm, respectively. In emission spectrum the band at 591 nm and 612 nm are corresponding to ⁵D₀-⁷F₁ and ⁵D₀-⁷F₂ transition of Eu³⁺ ions. With increasing in annealing temperature the differences of intensity of the two transitions are increased. This phenomenon shows that the luminescence intensity of La₂O₃∶Eu nanocrystals can be tuned by changing annealing temperature.

Preparation and Luminescence Properties of Spheric La2O3:Eu Nanocrystals