Guest-assisted assembly strategy: boosting solvent-processed organic solar cells toward commercialization

Science China Chemistry -     

微流控纸芯片的加工及其分析应用的实验设计*

设计了一个使用喷墨打印法加工微流控纸芯片的实验,在经烷基烯酮二聚体(AKD)的正己烷溶液浸泡过的滤纸上,以三乙醇胺溶液为打印墨水,用喷墨打印机打印出设计好的芯片图案。滤纸加热后,打印区域呈现亲水性,非打印区域为疏水性,从而制备出纸芯片,用该纸芯片通过数字比色法实现了亚硝酸根离子的定量测定。该实验不使用昂贵仪器设备,易普及。通过实验,促使学生了解微流控芯片这一前沿科学技术,锻炼学生细致、灵巧的动手能力,激发学生科技创新活力。     

CdS/Si nanofilm heterojunctions based on amorphous silicon films:Fabrication,structures,and electrical properties

Shortening the distance between the depletion region and the electrodes to reduce the trapped probability of carriers is a useful approach for improving the performance of heterojunction.The CdS/Si nanofilm heterojunctions are fabricated by using the radio frequency magnetron sputtering method to deposit the amorphous silicon nanofilms and Cd S nanofilms on the ITO glass in turn.The relation of current density to applied voltage(I-V)shows the obvious rectification effect.From the analysis of the double logarithm I-V curve it follows that below~2.73 V the electron behaviors obey the Ohmic mechanism and above~2.73 V the electron behaviors conform to the space charge limited current(SCLC)mechanism.In the SCLC region part of the traps between the Fermi level and conduction band are occupied,and with the increase of voltage most of the traps are occupied.It is believed that Cd S/Si nanofilm heterojunction is a potential candidate in the field of nano electronic and optoelectronic devices by optimizing its fabricating procedure.     

白云石制备似立方体状方解石型碳酸钙晶体及其机理研究

以轻烧白云石粉、氯化铵和二氧化碳为原料,在未使用晶型控制剂的情况下,通过蒸氨-沉钙过程制备出了似立方体状碳酸钙。研究了反应温度、溶液中钙离子浓度、通气速率、搅拌速度以及陈化时间对碳酸钙中方解石相含量以及晶体形貌的影响,并探索了沉钙反应的晶型控制机理。结果表明,在反应温度40 ℃、钙离子浓度0.05 mol/L、通碳速率100 mL/min、搅拌速度400 r/min和陈化时间2 h的条件下,制备出形貌规整、粒径分布均匀的似立方体状碳酸钙,平均粒径为5~10 μm。该研究为提升白云石的使用价值、生产高附加价值的碳酸钙产品,以及提高白云石资源的利用率提供理论基础。     

Coupled Variational Inequalities: Existence,Stability and Optimal Control

Journal of Optimization Theory and Applications - In this paper, we introduce and investigate a new kind of coupled systems, called coupled variational inequalities, which consist of two elliptic...     

四方体MgO的制备及对有机染料的吸附

以六水氯化镁和六次甲基四胺为原料,采用水热法合成四方体MgO,考察其对有机染料甲基橙和亚甲基蓝的吸附行为.通过TGA-DTA、SEM、XRD、N2-sorption和FT-IR等手段表征样品.结果表明,原料浓度、温度和表面活性剂对四方体MgO结构的形成影响较小,而反应时间的延长有助于有序结构的组装.温度170℃、时间24h、MgCl2·6H2O与C6H12N4浓度比为1∶2和表面活性剂PVP是制备四方体MgO的最佳条件.在溶液浓度10mg · L-1的单一吸附实验过程中,四方体MgO对甲基橙和亚甲基蓝的去除率分别为91.3;和22.3;,吸附过程均为单层吸附且符合Langmuir等温吸附模型和伪二级吸附动力学方程.在溶液浓度40 mg·L-1、甲基橙和亚甲基蓝浓度比3∶1的混合溶液吸附过程中,四方体MgO对甲基橙和亚甲基蓝的去除率分别为80.1;和97.9;.     

不同波长条件KDP晶体的非线性光学性质研究

采用Z扫描方法系统的研究了KDP晶体在不同激光波长条件下的非线性光学性质.当λ=355 nm,功率密度为57.92 GW/cm2和λ=532 nm,功率密度为105.94 GW/cm2时,KDP晶体均呈现强烈的反饱和吸收和自聚焦效应,其非线性吸收系数和非线性折射率分别为6.50×10 -2cm/GW,1.17×10 -2cm/GW和8.02×10 -7cm2/GW,6. 14×10 -7cm2/GW;而在1064 nm波长,功率密度为347.95 GW/cm2时KDP晶体并未表现出明显的非线性性质.结果表明,在短波长的激光作用下,KDP晶体更容易产生非线性效应,双光子吸收是KDP晶体非线性吸收的主要机制.     

多层状碱式碳酸锌微晶的制备及其脱除Cu2+性能研究

以壳聚糖(CS)为生物模板,采用低温水热法成功制备出了多层状碱式碳酸锌(ZCHO)微晶.采用XRD、SEM和TG等手段对产物的结构、形态和热学性能进行了表征,结果表明,单个ZCHO微晶颗粒均是由许多ZCHO纳米片构成的.添加适量的CS对形成多层状ZCHO微晶起到了至关重要的作用.热重分析结果表明,CS辅助得到的碳酸锌微晶热稳定性较高.等温吸附实验表明,在室温下,多层状ZCHO微晶能有效脱除水体中的Cu2,去除量与浓度关系符合Freundlich模型.最后讨论了多层状ZCHO微晶大容量去除Cu2+的可能机理.     

QEPAS系统中石英音叉模态仿真计算与研究

对石英音叉增强型光声光谱(QEPAS)系统中常用的石英音叉进行了有限元模态计算，获得石英音叉前6阶振型与模态频率，认知了第4阶对称摆动振型为有效振动，利用单因素法分析了石英音叉的音臂长度l₁、音臂宽度w₁、音臂厚度t、音臂切角θ、音臂圆孔直径d及音臂圆孔高度h对低阶有效共振频率(Fre)的影响，敏感度依次为： l₁> w₁>d>θ>t>h，考虑实际设计情形，筛选出了l₁，w₁，d与h四个石英音叉设计变量，采用Box-Behnken实验设计方案与RSM(response surface methodology)方法，以Fre为函数目标，建立l₁，w₁，d与h的二次回归响应面模型，得到了参数之间的交互作用，利用Design-Expert软件对响应面模型进行设计参数反求，结果表明，在15 000 Hz≤Fre≤25 000 Hz计算区域内误差较小，基本满足QEPAS系统的计算需求，所提出的研究与设计方法具有一定通用性，可为QEPAS系统中石英音叉结构参数设计提供参考。