Magnetic and Crystalline Microstructures of Fe-Pt-B Nanocomposite Ribbons

We investigate magnetic and crystalline microstructures of melt-spun (Fe0.675Pt0.325)100-xBx (x=12, 14, 16, 18,20) nanocomposite ribbons after optimal thermal treatment using a magnetic force microscope. The magnetic microstructures are characterized by darker spots adjacent to brighter ones in a sub-micro scale and in random distribution. It is found that the strength of the exchange coupling interaction between the crystals in the 10-100 nm scale, implied by the maximum value (δM)max of the Henkel plot, could be roughly described by the ratio of the average width of the magnetic spots w^- to the average crystal size D^- for the ribbons. Moreover, we find that the intrinsic coercivity jHc of the ribbons is sensitive to their crystal sizes, and the smaller D^-, the higher jHc. Finally, by using roughness analysis, the curve of the root mean square values (δФ)rms of the phase shift of the magnetic force images versus the boron content x is obtained, which is qualitatively consistent with that of the magnetization σ12 kOe of the ribbons versus x.     

HDDR过程中三元和多元Nd-Fe-B合金磁畴结构的MFM研究

用磁力显微镜研究了三元Nd-Fe-B合金在HDDR过程的不同阶段(铸态、不充分吸氢歧化、充分吸氢歧化和脱氢再复合)的破畴结构。在铸态样品表面清楚地观察到了易磁化轴互相垂直的柱状晶表面的两类磁畴图型。当样品不充分吸氢歧化和充分吸氢歧化时，破畴结构明显发生变化，反映了Nd-Fe-B的分解产物NdH2，α-Fe和Fe2B及其微晶结构的变化。脱氢再复合后形成的微晶的磁畴结构则表明样品保留了铸态样品柱状晶的构型。此外，还对比研究了多元Nd-Fe-B合金在HDDR过程中的磁畴结构，并根据微磁结构分析，指出过量的Ga元素添加可抑制Nd2(Fe，M)14B相的吸氢歧化，从而导致相应HDDR粘结磁体性能降低。     

Magnetic domain structures of precipitation-hardened SmCo 2：17-type sintered magnets： Heat treatment effect

The typical magnetic domains of Sm（CObalFe0.25Cuo.07Zr0.02）7.4 magnets quenched through various heattreatment steps have been revealed by using magnetic force microscopy （MFM）. For the specimens in which the nominal c-axis is perpendicular to the imaging plane, the domain configurations change from plate-like for the as-sintered magnet to corrugation and spike-like for the homogenized one, and then to a coarse and finally to a finer domain structure when isothermally aged at 830℃ and then annealed at 400℃. However, only plate-like domains can be detected on the surfaces with the nominal c-axis parallel to the imaging plane. The finer domain （so-called interaction domain） is a characteristic magnetic domain pattern of the SmCo 2：IT-type magnets with high coercivities. Domain walls in a zigzag shape are revealed by means of MFM in final bulk SraCo 2：17-type sintered magnets.     

Organic quantum well and superlattice characteristics in quasi-one-dimensional multiblock copolymers

A tight-binding calculation was presented to describe multiblock copolymers, such as [...-(PA)x-(PPP)y-...] composed of PA (polyacetylene) and PPP (poly(p-phenylene). It is found that a copolymer has a quantum well and superlattice characteristics, and evident is the effect of the composite lengths, the interfacial couplings and the electron-phonon interactions on the electronic properties of a copolymer. The quantum tunneling, the Franz-Keldysh effect and the quantum confinement can be generated under an applied electric field. These results were compared to those of traditional inorganic quantum well and superlattice systems.     

系列脉冲偏磁场作用下硬磁泡的形成

实验研究了系列脉冲偏场作用下外延石榴石薄膜的硬磁泡(包括哑铃畴)的形成规律。发现系列脉冲对畴段的作用不是单次脉冲作用(软畴段硬化的物理过程)的简单迭加,而有其特有的规律性,存在着硬畴段进一步硬化及硬畴段软化的另两个物理过程。运用上述三个物理过程对实验结果作了解释。 关键词：     

石榴石磁泡薄膜各向异性常数K_u和K_l的转矩法测量

本文详细研究了GGG(Gd_3Ga_5O_(12))单晶基片的磁转矩与其几何参量及有关物理参量的关系,提出了由转矩曲线测量石榴石磁泡薄膜单轴各向异性常数K_u和立方磁晶各向异性常数K_l过程中扣除基片影响的一种方法。在此基础上利用二元回归法由实测的转矩曲线求出K_u和K_l,以及K_u和K_l的温度关系曲线。     

面内磁场对硬磁泡形成的影响

实验研究了面内磁场对一次脉冲偏磁场作用下外延石榴石薄膜中硬磁泡形成的影响,发现存在一个使硬磁泡不再形成的临界面内磁场H_in⁰,它与材料参量有关,通过实验,运用面内磁场对条状畴的作用和枝状畴的形成,定性解释了软硬磁泡形成的分界场H_[b]随面内磁场增大、快降以及缓降这三个物理过程。 关键词：     

聚合物基片对柔性有机发光器件性能的影响

以聚合物基片柔性ITO膜为透明电极，制备了ITO／TPD／Alq3／Al结构柔性有机发光器件，并与在相同条件下制备的玻璃基片相同结构器件作了比较。研究了不同基片对有机材料及器件性能的影响，指出选择不易吸湿、耐温高、热胀系数小的聚合物材料，提高柔性ITO膜的附着力和导电性，结合柔性ITO膜的具体特性。优化有机层的蒸镀条件，是提高柔性有机发光器件发光亮度和稳定性的重要途径。     

An investigation of phase separation by magnetic force microscopy in La0.45Sr0.55MnO3-δ(δ≈0.01)

We have found phase separation in La_0.45Sr_0.55MnO_3-δ (LSMO) by means of electron spin resonance, magnetic force microscopy (MFM) and magnetic measurements. Ferromagnetic and antiferromagnetic phases can coexist at low temperatures, and ferromagnetic and paramagnetic phases coexist when the temperature lies between the Néel and Curie temperatures. The size and shape of the ferromagnetic phases (the minority phases) was first observed directly from MFM images. It is suggested that the phase separation in LSMO is not the charge segregation type, but an electroneutral type due perhaps to the nonuniform distribution of oxygen vacancies.     

Magnetic Microstructures of PryFe90－yB10 （y = 8－11.76） Nanocrystalline Ribbons Using Magnetic Force Microscopy ＊

Magnetic microstructure of melt-spun PryFe90-yB10 (y = 8, 8.5, 9, 9.5, 10 and 11.76) nanocrystalline ribbons in an as-grown state has been studied using a magnetic force microscope. The magnetic domains are characterized by dark areas adjacent to bright areas in a sub-micron scale and in random distribution. By comparing with the size of the micro-crystals measured from the TEM image, the exchange coupling effect was confirmed to exist inall the ribbons. Using the roughness analysis, the variation of the root mean-square values of the phase shifts obtained from the magnetic force images versus the content y of Pr were measured, which is very consistent with the curve of the residual induction Bγ versus the content y.