 为了研制低损耗、高性能的193 nm氟化物增透膜,研究了基底和不同氟化物材料组合对氟化物增透膜的影响。在熔石英基底上,将挡板法和预镀层技术相结合,采用热舟蒸发方式制备了不同氟化物材料组合增透膜,对增透膜的剩余反射率和光学损耗等光学特性,以及表面粗糙度和应力等特性进行了测量和比较。在分析比较和优化的基础上,设计制备的3层1/4波长规整膜系AlF3/LaF3增透膜在193 nm的剩余反射率低于0.14%,单面镀膜增透膜的透射率为93.85%,增透膜表面均方根粗糙度为0.979 nm,总的损耗约为6％。要得到高性能的193 nm增透膜,应选用超级抛光基底。     

Preparation of high performance thin-film polarizers

<正>The optical performance of thin film polarizers is highly sensitive to the layer thicknesses of thin film.The thicknesses of the sensitive layers are optimized in order to gain broader polarizing zone in such case when the total layer thickness does not increase.An automatic layer thickness control system is established,and errors caused by different monitoring methods are analyzed.With this thickness control system,thin-film polarizers with T_p higher than 98%and T_p/T_s higher than 200:1(T_p and T_s are transmissions for p- and s-polarizations,respectively) with the bandwidth of 11 nm are prepared.Using the system allows for optimum repeatability of three successive runs.     

溅射气压对X射线多层膜反射率的影响

本文在不同的溅射气压的情况下制备了具有相同结构参量的Mo/Si多层膜,测出了其对应的小角度X衍射曲线,在北京同步辐射实验室测量了多层膜的软X射线反射率.小角X射线衍射谱表明:随着溅射气压升高,多层膜的小角X射线衍射曲线的高次峰的峰高急剧变小,半峰宽变大.反射率测量结果也表明:多层膜的X射线反射率随溅射气压的升高而急剧降低.     

Wideband Antireflection Film Fabricated by Glancing Angle Deposition

Graded-index ZrO2 films has been fabricated on K9 glass by glancing angle deposition. Because the index mismatch at the interface has been reduced, the film results in wideband high-transmission antireflection. From 400nm to 1200nm, the film reflection is lower than 0.8% and the lowest value is 0.2% at 432nm.     

Interface roughness, surface roughness and soft X-ray reflectivity of Mo/Si multilayers with different layer number

A series of Mo/Si multilayers with the same periodic length and different periodic number were prepared by magnetron sputtering, whose top layers were respectively Mo layer and Si layer. Periodic length and interface roughness of Mo/Si multilayers were determined by small angle X-ray diffraction (SAXRD). Surface roughness change curve of Mo/Si multilayer with increasing layer number was studied by atomic force microscope (AFM). Soft X-ray reflectivity of Mo/Si multilayers was measured in National Synchrotron Radiation Laboratory (NSRL). Theoretical and experimental results show that the soft X-ray reflectivity of Mo/Si multilayer is mainly determined by periodic number and interface roughness, surface roughness has little effect on reflectivity.     

退火对电子束热蒸发193nm Al2O3/MgF2反射膜性能的影响

设计并镀制了193nm Al2O3/MgF2反射膜,对它们在空气中分别进行了250-400℃的高温退火,测量了样品的透射率光谱曲线和绝对反射率光谱曲线.发现样品在高反射区的总的光学损耗随退火温度的升高而下降,而后趋于饱和.采用总积分散射的方法对样品在不同退火温度下的散射损耗进行了分析,发现随着退火温度的升高散射损耗有所增加.因此,总的光学损耗的下降是由于吸收损耗而不是散射损耗起主导作用.对Al2O3材料的单层膜进行了同等条件的退火处理,由它们光学性能的变化推导出它们的折射率和消光系数的变化,从而解释了相应的多层膜光学性能变化的原因.反射膜的反射率在优化联系、镀膜工艺与退火工艺的基础上达98%以上.     

周期性梯度折射率多层膜的软X射线反射率

由于界面互扩散的存在，实际的超薄多层膜很难具有清晰的界面结构.假设超薄多层膜为具有周期性梯度折射率的多层膜结构，用直线模型和余弦模型模拟了周期性梯度折射率多层膜的软X射线反射率.结果证明，折射率余弦渐变的多层膜虽然不具有清晰的界面，但它同样具有很高的反射率.     

退火对电子束热蒸发Al2O3薄膜性能影响的实验研究

 用电子束热蒸发方法镀制了Al₂O₃材料的单层膜，对它们在空气中进行了250~400 ℃的高温退火。对样品的透射率光谱曲线进行了测量，计算了样品的消光系数、折射率和截止波长。通过X射线衍射仪（XRD）测量分析了薄膜的微观结构,采用表面轮廓仪测量了样品的表面均方根粗糙度。结果发现随着退火温度的提高光学损耗下降，薄膜结构在退火温度为400 ℃时仍然为无定形态，样品的表面粗糙度随退火温度的升高而增加。引起光学损耗下降起主导作用的是吸收而不是散射，吸收损耗的下降主要是由于退火使材料吸收空气中的氧而进一步氧化，从而使薄膜材料的非化学计量比趋于正常。     

不同类型蒸发源对平面夹具薄膜均匀性的影响

 分析了几种可能的实际蒸发源与薄膜均匀性的关系，其中包括扩展的平面蒸发源和曲面蒸发源。通过实验论证了薄膜均匀性对蒸发源尺寸和蒸发特性的依赖关系。得到的分析结果表明：当蒸发源半径和夹具高度的比值小于1/17时，蒸发源可以被视为一个点面源；大于 1/10时，应当把蒸发源视为面面源进行考虑。当挖坑深度和蒸发源半径的比值介于0和0.5之间时,挖坑对薄膜均匀性造成的影响基本可以忽略；大于0.6时，挖坑效应明显影响薄膜的均匀性。     

Moisture absorption characteristics of a SiO2 film from 2 to 3 μm

We prepare SiO2 coatings on different substrates by either electron-beam evaporation or dual ion-beam sputtering. The relative transmittances of the Si O2 coatings are measured during the heating process. The Si O2 coating microstructures are studied. Results indicate that the intensity and peak position of moisture absorption are closely related to the microstructures of the coatings. The formation of microstructures depends not only on the preparation process of the coatings but also on the substrate characteristics.