碳纳米管的近边吸收谱研究

用X射线近边吸收谱研究了单壁, 双壁和多壁碳纳米管在超高真空系统中不同温度下退火处理后的行为.碳的K边吸收谱表明, 多壁管上吸附的杂质将在热处理过程中最先被去除, 其次是双壁管, 最后是单壁管.这种热处理下杂质去除的顺序说明了曲率越小杂质吸附得越牢靠, 即越容易吸附杂质.另外, 结果中显示, 经退火处理后3种碳纳米管在多重散射区域的峰结构呈现规律性的移动,由单壁管到多壁管, 谱峰向低能方向移动; 这是由于碳纳米管的层数不同造成的, 证明这部分谱峰结构直接受到碳纳米管层数的调制, 有利于鉴别3种碳纳米管.     

热处理对多元醇法制备的PtRu/C电催化剂的影响

采用热重、在线质谱、X射线衍射和透射电镜等技术研究了热处理对多元醇法制备的PtRu/C电催化剂催化活性的影响.结果表明,热处理前电催化剂表面吸附较多残余物种,在惰性气氛中200℃下热处理2h可以去除部分吸附物种.虽然热处理后电催化剂的平均粒径比热处理前稍有增大,但电催化剂颗粒的分散度仍较高.热处理后电催化剂催化甲醇电氧化反应的活性明显提高.     

Influences of SiO2 laser-induced protective layers and damage threshold of annealing on the Ta2O5 films

Ta2O5 films are prepared on BK7 substrates with conventional electron beam evaporation deposition. The effects of SiO2 protective layers and annealing on the laser-induced damage threshold （LIDT） of the films are investigated. The results show that SiO2 protective layers exert little influence on the electric field intensity （EFI） distribution, microstructure and microdefect density but increase the absorption slightly. Annealing is effective on decreasing the microdefect density and the absorption of the films. Both SiO2 protective layers and annealing are beneficial to the damage resistance of the films and the latter is more effective to improve the LIDT. Moreover, the maximal LIDT of Ta2O5 films is achieved by the combination of SiO2 protective layers and annealing.     

用直流矫顽力检验钢材热处理硬度的方法

一、引言至今,许多工厂还多应用破坏性的方法检验钢材热处理质量。例如,用洛氏、布氏硬度计等仪器检查硬度以及打开零件制成试样观察金相组织和表面硬化层深度。由于这些方法不宜用于大批成品和半成品检验,尤其对于形状复杂的零件更感困难。正因为这样,无损检查热处理质量的方法在不断地探索、研究和发展,并越来越多地应用到生产实践中。关于无损检测钢件热处理质量,一般来说包括检查零件热处理之后的硬度,表面硬化层深度(如渗碳层与高频淬火层深度),判别组织,以及分选混料几方面。     

Spectroscopic properties and mechanism of Tm^3＋/Er^3＋/Yb^3＋ co-doped oxyfluorogermanate glass ceramics containing BaF2 nanocrystals

Transparent Tm^3＋/Er^3＋/yb^3＋ co-doped oxyfluorogermanate glass ceramics containing BaF2 nanocrystals are prepared. Under excitation of a 980-nm laser diode （LD）, compared with the glass before heat treatment, the Tm^3＋/Er^3＋/yb^3＋ co-doped oxyfluorogermanate glass ceramics can emit intense blue, green and red up-conversion luminescence and Stark- split peaks; X-ray diffraction （XRD） and transmission electron microscope （TEM） results show that BaF2 nanocrystals with an average diameter of 20 nm are precipitated from the glass matrix. Stark splitting of the up-conversion luminescence peaks in the glass ceramics indicates that Tm^3＋, Er^3＋ and （or） Yb^3＋ ions are incorporated into the BaF2 nanocrystals. The up-conversion luminescence intensities of Tm^3＋, Er^3＋ and the splitting degree of luminescence peaks in the glass ceramics increase significantly with the increase of heat treat temperature and heat treat time extension. In addition, the possible energy transfer process between rare earth ions and the up-conversion luminescence mechanism are also proposed.     

Phase constitution and microstructure of Ce–Fe–B strip-casting alloy

The strip-casting technique plays an important role in fabricating high coercivity sintered magnet. In this paper, we investigate the phase constitution and the microstructure of rapidly solidified Ce-Fe-B alloy fabricated by strip-casting. We find that the Ce2FelgB phase coexists with Fe, Fe2B, and CeFe2 phases in the Ce-Fe-B strips. The eutectic stucture consisting of Fe and Fe2B is encased in Ce2Fe14B grains, which is blocked by the CeFe2 grains at triple junctions, indicating that the microstructure of Ce-Fe-B strip is characteristic of a peritectic solidification. Thermal analysis indicates that the large supercooling of Ce2Fe14B results in the residual Fe and Fe2B. The microstructural optimization in Ce-Fe-B strips without Fe and Fe2B could be achieved by a heat treatment of 1000 ℃.     

Sr_2ZnSi_2O_7∶Eu~(3+)的低温合成与发光性能

以介孔二氧化硅MCM-41为硅源,采用低温水热反应与后续煅烧相结合的方法合成Sr2-xZnSi2O7∶xEu3+红色荧光粉。实验结果表明,150℃水热处理16 h后的反应产物含Sr2ZnSi2O7相,经后续950℃煅烧3h得到Sr2ZnSi2O7纯相。在392 nm近紫外光的有效激发下,Sr2-xZnSi2O7∶xEu3+荧光粉显示Eu3+离子的特征跃迁发射,以615 nm的5D0→7F2跃迁发射峰为最强。适量Eu3+的掺杂对Sr2ZnSi2O7相结构几乎没有影响,当Eu3+离子的掺杂量x=0.10时,荧光粉发光强度最大。     

Effect of thermal treatment on structural change of anode electrocatalysts for direct methanol fuel cells

Commercially available carbon-supported Pt,PtCo and PtRu catalysts from E-TEK are heat-treated in turn at 600 ℃ and 800 ℃ each for an hour.The as-received and as-heated catalysts are used as anode catalysts for direct methanol fuel cells.Structural and surface composition changes induced by heating are analyzed by X-ray diffraction(XRD) and X-ray photoelectron spectroscopy(XPS),respectively.For the Pt catalyst,heating the catalysts caused only the mass activity decrease due to particle sintering,whereas the specific activity and CO tolerance remained unchanged.The performance of the PtCo and PtRu catalysts is affected differently by heating.Heating the PtRu catalyst adversely affects its catalytic activity and its CO tolerance due to Pt depletion at the surface.In contrast,although Pt depletion also takes place for the heated PtCo catalysts,these catalysts show an even higher specific activity and approximately the same CO tolerance.The observed difference is likely due to the optimum atomic ratio difference for Ru/Pt and Co/Pt;an increased atomic ratio on the surface for Co/Pt results in an activity enhancement,which is contrary to the effect of the increase of Ru/Pt atomic ratio.     

不同处理工艺对珍珠的紫外可见漫反射光谱的共性影响研究

主要基于紫外可见（UV-Vis）漫反射光谱首次对比研究了经过热处理、有机或无机染料改色或钴-60产生的γ射线辐照三种不同处理工艺对同为珍珠质的淡水与海水珍珠及贝壳珍珠层的漫反射光谱的影响机制。结果表明：（1）在不同颜色、淡海水属性的珍珠与贝壳珍珠层的UV-Vis反射光谱的紫外区皆存在约280 nm 处的吸收峰,上述吸收峰位归属于珍珠层中自身存在的有机质所致,而非珍珠的致色色素。（2）以上三种不同的处理工艺对上述280 nm处的吸收峰位存在一致的影响行为,即随着不同的处理工艺强度的增大,处理样品对应的反射谱图中约280 nm处吸收峰的强度逐渐降低直至消失。与此同时,珍珠的反射谱图中紫外区的反射主波长的反射强度也随之减弱,且反射主波长的峰位向可见光区发生显著红移。研究工作可为珍珠及珍珠的优化处理的鉴定筛选及其珍珠颜色的形成属性判定提供检测依据与理论支撑。     

15 T Nb3Sn磁体热处理传热分析及实验研究

大孔径高场磁体是开展超导材料性能研究的必要装置。依托聚变堆主机关键系统综合研究设施项目,中科院等离子体物理研究所将进行15 T高场复合超导磁体研制,磁体高场区由Nb₃Sn密绕线圈构成。热处理是Nb₃Sn线圈研制的关键工艺环节也是磁体研制的难点,要求磁体热处理温度均匀性优于±5℃。针对15 T Nb₃Sn密绕线圈热处理需求,研制了一套真空磁体热处理系统。利用该系统完成了线圈热处理实验,通过传热仿真与实验结果分析,线圈整体温度均匀性优于±3℃,最终各项指标均满足热处理技术要求。