锡苯和铅苯二聚反应的理论研究

采用密度泛函理论B3LYP方法,研究了锡苯和铅苯的[2+2],[4+2]及[4+4]二聚反应的微观机理和势能剖面,考察了Sn(Pb)原子上的2,4,6-三甲基苯基(Mes)取代基对反应势能剖面的影响.研究结果表明,所有反应均为协同过程,且大多数情况下,2个C—Sn(Pb)键同步形成.[2+2]和[4+2]反应在热力学和动力学上均比相应的[4+4]反应容易进行,而[4+2]反应在动力学上比相应的[2+2]反应有利.Sn(Pb)原子上的Mes取代基在热力学和动力学上均不利于反应的进行.铅苯的动力学稳定性与锡苯相当,但其热力学稳定性高于锡苯.     

钙钛矿型Sr_（1－x）Bi_xFeO_（3－y）系列物的结构、电性及铁氧化态研究

在１１００℃制备了钙钛矿型非计量系列物Ｓｒ_（１－ｘ）Ｂｉ_ｘＦｅＯ_（３－ｙ），与文献相比，明显具有温度低、时间短、能耗少的特点。用化学分析方法测得其化学式及Ｆｅ离子的平均价态，用ＸＲＤ、交流阻抗、ＩＲ、Ｍｏｓｓｂａｕｅｒ谱等方法研究了其结构与性质，该类化合物具有Ｐｍ３ｍ对称性和半导体性质，铁离子会产生电荷歧化现象。     

催化动力学光度法测定水中痕量铁

本文研究了ｐｈ５．０的ＨＡｃ－ＮａＡｃ介质中，痕量铁催化过氧化氢氧化紫脲酸的褪色反应，建立了催化动力学光度法测定痕量铁的新方法，方法的线性范围０－０．４０，０．４０－２．０μｇ／２５ｍＬ，检出限为８×１０＾－１１ｇ／ｍＬ，用于水样中痕量铁的测定，结果满意。     

Comparative studies on the mechanism of uridine phosphorolysis

We have used quantum mechanical method to study the transition states(TSs) of uridine phosphorolysis reaction. Comparing the four different reaction pathways and the five transition states obtained, we conclude that enzymatic uridine phosphorolysis takes place mainly according to acid-catalyzed SN2 mechanism. The proposed reaction pathway is consistent with many experimental results.     

溶胶-凝胶制备技术与新型催化材料Ⅲ.溶胶粒子表面修饰方法制备催化膜

提出用溶胶粒子表面修饰方法，结合溶胶凝胶技术制备无机催化膜．该方法的基本原理是利用合适的金属配合物在胶粒表面的吸附作用，经溶胶凝胶过程，将活性组分结合到无机膜中．实验测定结果表明：（ＮｉＥＤＴＡ）２－，ＶＯ－３，ＭｏＯ２－４，（Ｐｄ（ＮＨ３）４）２＋，ＰｄＣｌ２－４，ＰｔＣｌ２－６和ＲｈＣｌ３－６可用来修饰ＡｌＯＯＨ溶胶．以Ｐｄ／γＡｌ２Ｏ３催化膜的制备为例，经三次溶胶凝胶过程，可制得无裂缺的厚度为９μｍ的Ｐｄ／γＡｌ２Ｏ３催化膜，膜材料的平均孔直径为６ｎｍ，Ｐｄ被均匀地分布在膜的顶层，其平均粒径为２３ｎｍ．     

Positive photosensitive polyimides with cyclobutane structure

A new family of positive photosensitive polyimide (PPI) systems composed of solvent soluble polyimides (Pls) with cyclobutane (CBDA) structures and diazonaphthoquinone compounds (DNQ) has been prepared. Heat and catalytic imidizations were carried out to obtain CBDA Pls; the former was better than the latter in controlling the molecular weight of the Pl. The ? OH groups in the Pls were easily acetylated during catalytic imidization, so ? COOH groups were selected as weak acidic groups in the Pls. The ? COOH groups were also effective in giving the Pls an alkaline solubility. Therefore, Pls having ? COOH groups were superior to those having ? OH groups for PPI systems. The photosensitive properties of various PPl systems containing ? COOH were found to vary with the fraction of ? COOH groups in the Pls, the content of DNQ in the systems, and the molecular weight of the Pls.     

Ti_(1-x)(Hf_(0·919)Zr_(0·08))_xNiSn的制备及热电性能

采用固相反应法合成了单相的Ti_(1-x)(Hf_(0·919)Zr_(0·08))_xNiSn(x=0·00—0·15),并用放电等离子烧结方法制备出密实块体材料.研究了Hf和Zr同时在Ti位上的等电子合金化对Ti基半Heusler化合物热电性能的影响规律.结果表明:少量的Hf和微量的Zr在Ti位上的等电子合金化,显著地降低了体系的热导率κ,同时显著地提高了体系的Seebeck系数α.组成为Ti_(1-x)(Hf_(0·919)Zr_(0·08))_(0.15)NiSn的试样室温热导率为3·72W·m-1K-1,在700K时ZT值达到最大为0·56.与三元TiNiSn相比,在相同温度下ZT值的提高率为190%—310%.     

Ni(111)表面一氧化碳和氢共吸附的密度泛函理论研究

本文用密度泛函理论(DFT)的总能计算研究了一氧化碳和氢原子在Ni(111)表面上p(2×2)共吸附系统的原子结构和电子态，结果表明CO和H原子分别被吸附于两个对角p(1×1)元胞的hcp和fcc位置.以氢分子和CO分子作为能量参考点，总吸附能为2.81 eV，相应的共吸附表面功函数φ为6.28 eV.计算得到的C—O，C—Ni和H—Ni的键长分别是1.19?, 1.96?和 1.71?，并且CO分子以C原子处于hcp的谷位与金属衬底原子结合.衬底Ni(111)的最外两层的晶面间距在吸附后的相对变化分别是 关键词： Fisher-Tropsch反应 催化作用 Ni(111) p(2×2)/(CO+H) 共吸附     

二氧化钒薄膜的低温制备及其性能研究

针对VO₂薄膜在微测辐射热计上的应用，采用射频反应溅射法，在室温下制备氧化钒薄膜；研究了氧分压对薄膜沉积速率、电学性质及成分的影响.通过调节氧分压，先获得成分接近VO₂的非晶化薄膜，再在400℃空气中氧化退火，便可制得高电阻温度系数，低电阻率的VO₂薄膜，电阻温度系数约为-4%/℃，薄膜方块电阻为R_□为100—300kΩ；薄膜在室温下沉积，400℃下退火的制备方法与微机电加工(micro electromechanic 关键词： 二氧化钒 电阻温度系数 氧分压 射频反应溅射法     

直接置换法制备包覆型纳米铜-银双金属粉末

 以AgNO₃为主盐，采用直接置换法初步制备了包覆型纳米铜-银双金属粉末，分析了工艺条件对包覆效果的影响，并用透射电子显微镜、X射线能量色散谱仪和X射线衍射仪进行了表征。实验结果表明：纳米铜-银双金属粉末为包覆型结构，平均粒径约70 nm，分散性较好，表面银的原子分数达到74.28%。在洗涤过程中加入一定量的保护剂，有效解决了纳米铜粉的氧化问题。