Yb:Y2－2xLa2xO3激光透明陶瓷的光谱性能

对一种低温易烧结的Yb:Y_2-2xLa_2xO₃激光透明陶瓷的光谱性能进行了初步研究，Yb:Y_2-2xLa_2xO₃激光透明陶瓷具有宽的吸收带和大的吸收截面，在最强的吸收峰977nm处吸收截面达4.0×10^-20cm²；其荧光发射寿命为1.1ms，发射截面在1033nm处为1.0×10^-20cm²，在1077nm处为0.7×10^-20cm².Yb:Y_2-2xLa_2xO₃陶瓷的各项光学性能指标接近或达到单晶的指标. 关键词： 氧化镧钇 激光陶瓷 低温烧结 光谱性能     

Diode-Pumped Passively Q-Switched Yb：YAG Microchip Laser with a GaAs as Saturable Absorber

A passively Q-switched Yb: YAG microchip laser has been constructed by using a doped GaAs as the saturable absorber as well as the output coupler. At 13.5 W of pump power the device produces high-quality 3.4μJ 52ns pulses at 1030nm with a pulse repetition rate of 7.8 kHz in a TEM00-mode.     

超宽带THz雷达反隐身技术研究

超宽带THz雷达以其长距离分辨率、强穿透力、低截获率和强抗干扰性等特点在军事领域得到了日益关注。论述了超宽带THz雷达的应用原理和反隐身的独特优势,分析了超宽带THz雷达的部分技术难点,预测了超宽带THz雷达的发展趋势和应用前景。     

柱状ZnO阵列薄膜的生长及其发光特性

采用一种设备简单、原料低廉的新型方法，在镀有ZnO先驱薄膜的(0001)蓝宝石上利用水热 法制备出了柱状ZnO阵列薄膜.用扫描电镜(SEM)，X射线衍射(XRD)对样品的形貌和结构进行 了表征，结果显示ZnO薄膜为柱状阵列，基于蓝宝石衬底沿c轴择优生长，且(0004)摇摆曲线 半高宽度(FWHM)约为1.8°.此ZnO阵列薄膜具有很强的紫外发射光谱(PL). 关键词： 柱状ZnO阵列薄膜 水热法 (0001)蓝宝石 PL谱     

Ti:LiAlO2新型晶体的结构分析

通过研究提拉法生长的掺杂Ti浓度为0.2at%的LiAlO2晶体吸收光谱,荧光光谱和红外光谱,来分析此新型晶体的结构.分析发现光谱中仅出现了四价Ti离子的196nm的特征吸收峰,用235nm光激发得到384nm的特征发射峰;针对吸收光谱中660-820nm出现的四个弱小吸收峰提出了一个色心模型,从而解释了空气和富Li气氛处理后吸收峰消失的现象;对比纯LiAlO2晶体的红外光谱发现,Ti的掺入仅影响了[AlO4]键强,而[LiO4]及相关键强几乎不变;结合ICP测试估算出直径50mm,厚1mm的Ti:LiAlO2的Li空位为5.5×1020个.     

等离子体隐身技术

等离子体隐身技术的核心是电磁波与等离子体的相互作用。本论述了等离子体隐身技术的基本原理，发展现状与应用前景，并讨论了实现等离子体隐身的关键技术和目前存在的问题。     

750℃和850℃下MgB2纤维超导体的制备及性能研究

MgB2纤维超导体样品在750℃和850℃下被制备了出来,将它们与950℃下制备的MgB2纤维超导体样品相比较,具有了能弯曲的能力,不再像950℃下制备的样品那么脆而易断,不能弯曲.扫描电镜图像的观察表明750℃和850℃下制备的MgB2纤维超导体的结构是一层数百纳米厚的MgB2的薄膜生长在了硼纤维表面.由于硼纤维中绝大部分单质硼的存在,使750℃和850℃下制备出的MgB2纤维超导体样品具有了弯曲能力.     

共掺Na+的Yb3+∶CaF2晶体的荧光分析与低阈值激光运转

基于975nm激发的室温下荧光光谱测量，系统地研究了在新型钠、镱共掺的氟化钙晶体中钠离子的作用机理，分析了掺钠离子浓度与激光阈值的关系，获得了具有最低激光阈值的掺杂浓度优化配比. 激光实验表明对于2%Yb³⁺离子浓度的氟化钙，掺入3%的钠离子能够获得最低阈值的激光运转，这与理论和荧光分析完全一致. 关键词： 镱、钠共掺氟化钙 荧光光谱 激光阈值     

Surface Light Extraction Mapping from Photonic Quasicrystal on Current Two-Dimensional Array of 12-Fold Injected GaN-Based LEDs

A two-dimensional array of dodecagonal photonic quasicrystal （12PQC） is fabricated on the surface of current injected GaN-based LEDs to out-couple guided modes. The spatially-resolved surface light extraction mapping of 12PQC is observed and compared with that of triangular lattice photonic crystal （3PC） by microscopic electrical luminescence and scanning near-field microscopy. The higher enhancement factor of 12PQC is obtained to be larger than that of 3PC. It is shown that 12PQC is more favourable and efficient for light extraction of guided lights.     

Efficient Diode-Pumped Tm：YALO3 Laser with a Pump Recycling Scheme

By using a pump recycling configuration, the maximum power of 8.1 W in the wavelength range 1.935-1.938 μm is generated by a 5-ram long Tm：YAIOa （4 at.%） laser operating at 18℃ with a pump power of 24 W. The highest slope efficiency of 42% is attained, and the pump quantum efficiency is up to 100%. The Tm：YAlO3 laser is employed as a pumping source of singly-doped Ho（1%）：GdV04 laser operating at room temperature, in which continuous wave output power of greater than 0.2 W at 2.05/μm is achieved with a slope efficiency of 9%.