不同铈添加量对CeO2-ZrO2-Al2O3材料性能的影响

采用共沉淀法制备了一系列不同铈添加量的CeO2-ZrO2-Al2O3(CZA)储氧材料,并通过XRD、低温N2吸附-脱附、氧脉冲吸附(OSC)和H2-TPR等手段进行了表征。XRD结果表明,在1 000和1 100℃高温焙烧后,当CeO2添加量为8%时样品具有最好的结构稳定性能。N2吸附-脱附结果表明,CeO2添加量为8%时样品具有最好的织构性能,1 000℃时,比表面积和孔容分别为:136.6 m2.g-1和0.38 mL.g-1;1 100℃时,比表面积和孔容分别为:83.7 m2.g-1和0.23 mL.g-1。OSC结果显示,CeO2添加量为8%时样品具有最大的储氧量,1 000℃和1 100℃分别为70μmol.g-1和31μmol.g-1。H2-TPR结果表明,CeO2添加量为8%时样品具有最佳的还原性能。     

掺杂Mn对CeO2-ZrO2-Al2O3材料性质的影响

采用共沉淀法制备了一系列Mn掺杂摩尔分数为0～5%的CeO2-ZrO2-Al2O3(CZA)复合氧化物, 并采用BET, OSC, XRD, XPS, H2-TPR等方法对所制备的材料进行了表征. 结果表明, 所制备的材料均形成了稳定的CZA固溶体, 尤其是Mn掺杂0.5%的材料在600和1000 ℃焙烧后均表现出最好的织构性能. OSC和H2-TPR的结果表明, Mn掺杂量≤1%时, 氧在材料中的体相移动是材料储氧和被还原的速控步骤, 并且Mn的掺杂量为0.2%时, 储氧量最大, 材料的还原温度也最低; Mn掺杂量>1%时, Mn物种对材料储氧和被还原的作用显著. XPS结果表明, Mn在焙烧过程中会迁移向表面, 结合H2-TPR结果可知, 新鲜样品表面的MnOx物种主要为Mn2O3, 而老化样品主要为Mn3O4.     

镧、锰掺杂改性CeO2-ZrO2-Al2O3固溶体的性能

采用共沉淀法制备了一系列La, Mn共掺杂的CeO2-ZrO2-A12O3(CZA)复合氧化物, 采用BET, XRD, H2-TPR, XPS和XRF等方法对样品进行表征. 结果表明, 全部样品均形成了稳定的CZA固溶体, 经600 ℃焙烧后表现出良好的织构性能, 1000 ℃老化后, La, Mn共掺杂样品具有最佳的高温稳定性; H2-TPR测试表明, La, Mn之间存在正协同效应, 共掺杂的样品具有最佳的低温还原性能和高温稳定性; XPS结果表明, 掺杂La可有效抑制在焙烧过程中Mn向表面的迁移, 从而保持较高的表面吸附氧浓度.     

不同沉淀剂对Ce0.65Zr0.35O2复合氧化物性能的影响

本文选用不同沉淀剂,用共沉淀法制备了稀土储氧材料Ce0.65Zr0.35O2复合氧化物,对用不同沉淀剂制备出的氧化物样品进行了XRD,BET,OSC和H2-TPR的测试和分析。结果表明,用不同沉淀剂制备出的氧化物,均为立方相的铈锆固溶体,经1000℃5小时老化后也无相的分离;以(NH4)2CO3和NH3.H2O的混合物为沉淀剂制备出的氧化物有最大的比表面积,经600℃焙烧后高达120m2/g以上;并且样品具有良好的储氧性能及低温还原能力。     

CeO2-ZrO2-Al2O3 的制备及其负载钯三效催化剂的催化性能

 采用共沉淀法制备了一系列不同 Al2O3 含量的 CeO2-ZrO2-Al2O3(CZA) 氧化物,并用 X 射线衍射、激光拉曼光谱和 N2 吸附-脱附等手段进行了表征. 以 CZA 为载体, 采用浸渍法制得钯基催化剂. 结果表明, 当 Al2O3 含量为 80%时, 新鲜 CZA 样品中出现γ-Al2O3 相. 经 600 ºC 焙烧后, Al2O3 在 CZA 样品中的溶域值略小于 80%. 经 1 000 ºC 老化后, CZA 样品中 Al2O3 含量为 60%时, 才开始出现微弱 γ-Al2O3 相, 而其他氧化物物相结构稳定. 添加 Al2O3 后材料比表面积和储氧量明显增大. 随着 Al2O3 含量的增加, CZA 样品的储氧量由 336.2 增至 486.2 μmol/g, 表现出良好的抗高温老化性能. 当 Al2O3 含量为 40% 时, 新鲜催化剂对 C3H8 的起燃温度和完全转化温度分别为 238 和 292 ºC, 同时具有良好的温度特性和较宽的空燃比窗口.     

CeO_2-ZrO_2-Al_2O_3稀土储氧材料制备工艺的研究

采用化学沉淀法制备了系列CeO2-ZrO2-Al2O3稀土储氧材料,并用BET,XRD和储氧性能测定等表征手段考察了陈化时间、La2O3含量、反应pH和沉淀方式等工艺因素对CeO2-ZrO2-Al2O3比表面积、储氧性能和结构的影响。结果表明:当陈化时间为12 h,反应pH=10时,掺杂2%(质量分数)La2O3的CeO2-ZrO2-Al2O3样品在老化前后均具有很高比表面积和良好的储氧性能,并且pH为影响样品比表面积及热稳定性能的主要因素。与一步法沉淀相比,二步法制得的CeO2-ZrO2-Al2O3样品具有很高的热稳定性能,1050℃老化5 h后的样品比表面积高达46.4 m2.g-1,但储氧性能略差,这与Al2O3对CeO2-ZrO2的结构影响程度有关。     

不同铝源与铈锆复合的性能及机制

制备了CZ及CZ/AL,CZ/AS与CZ/AM(铈锆固溶体与氧化铝的复合氧化物),通过X射线衍射(XRD)、比表面(BET)、储放氧(OSC)和透射电镜(TEM)等手段对样品的晶相结构、比表面、储氧性能及微观结构等进行表征。结果表明:CZ/AL及CZ/AS都可形成单一稳定的立方晶型结构,氧化铝的掺杂可提高铈锆固溶体的比表面及耐高温稳定性,其中CZ/AS的比表面最高,CZ/AL储氧性能最大。此外,其复合机理表明,Al2O3与铈锆固溶体在纳米级别上的化学复合与纯粹的机械混合相比,前者具有更加稳定的晶型结构、更大的比表面和更好的储氧性能。     

钙改性的Pd/CeO2-ZrO2-Al2O3催化剂催化甲醇裂解反应

采用共沉淀法制备了未改性的和Ca掺杂的CeO2-ZrO2-Al2O3样品,进一步用浸渍法制备了Pd/CeO2-ZrO2-Al2O3(Pd/CZA)和Pd/CeO2-ZrO2-Al2O3-CaO (Pd/CZACa)催化剂.运用X射线衍射、N2吸附-脱附、储氧量测定、CO化学吸附、NH3程序升温脱附、CO2程序升温脱附、...     

合成方法对Rh/CeO2-ZrO2-La2O3催化剂的结构、表面性能及DeNOx活性的影响

用沉积沉淀法合成两种不同系列的CeO2-ZrO2-La2O3混合氧化物(ZrO2和La2O3沉积CeO2粒子(标记为A-x)以及CeO2和La2O3沉积ZrO2粒子(标记为B-x)),并用作Rh催化剂的载体。XRD、拉曼、TPR、XPS和O2脉冲等表征结果显示出不同的沉积顺序将导致不同的结构和氧化还原性能,且B-x具有更高的氧迁移性、储氧能力和表面Ce浓度。当其负载Rh后,Rh/B-x催化剂具有更高的NO和CO转化率及N2选择性,且Ce的最佳含量为50at%。这可能归因于Rh负载于富铈表面形成更多有利于NO分解的表面Ce3+活性位。     

Pr-Ce-Zr复合氧化物的结构与储氧性能研究

采用氨水共沉淀方法制备了PrxCe0.3－xZr0.7O2（x=0,0．1,0．2,0．3）复合氧化物,对样品进行了X光衍射、比表面积等表征及动态和静态储氧性能测试。结果表明,Pr进入铈锆的晶格,形成了良好的固溶体,并有效地阻止了水热老化处理造成铈锆的分相。在富锆复合氧化物中,Pr本身的氧化还原能力较弱,对固溶体的总储氧能力贡献不大;而适量Pr掺杂（10％,原子分数）可以对铈锆样品的表面改性,提高动态储放氧能力。     

CeO2-ZrO2-La2O3-Al2O3 composite oxide and its supported palladium catalyst for the treatment of exhaust of natural gas engined vehicles

Composite supports CeO2-ZrO2-Al2O3 (CZA) and CeO2-ZrO2-Al2O3-La2O3 (CZALa) were prepared by co-precipitation method. Palladium catalysts were prepared by impregnation and their purification ability for CH4, CO and NOx in the mixture gas simulated the exhaust from natural gas vehicles (NGVs) operated under stoichiometric condition was investigated. The effect of La2O3 on the physicochemical properties of supports and catalysts was characterized by various techniques. The characterizations with X-ray diffraction (XRD) and Raman spectroscopy revealed that the doping of La2O3 restrained effectively the sintering of crystallite particles, maintained the crystallite particles in nanoscale and stabilized the crystal phase after calcination at 1000 ℃. The results of N2-adsorption, H2-temperature-programmed reduction (H2-TPR) and oxygen storage capacity (OSC) measurements indicated that La2O3 improved the textural properties, reducibility and OSC of composite supports. Activity testing results showed that the catalysts exhibit excellent activities for the simultaneous removal of methane, CO and NOx in the simulated exhaust gas. The catalysts supported on CZALa showed remarkable thermal stability and catalytic activity for the three pollutants, especially for NOx. The prepared palladium catalysts have high ability to remove NOx, CH4 and CO, and they can be used as excellent catalysts for the purification of exhaust from NGVs operated under stoichiometric condition. The catalysts reported in this work also have significant potential in industrial application because of their high performance and low cost.     

共沉淀法制备的CeO2-ZrO2-Al2O3材料及性能

采用简单易操作的共沉淀法制备了性能优异的CZA材料, 并通过对其晶体结构的表征, 初步探讨了ZrO2和Al2O3在CZA中的存在方式.     

超声波振动在Ce-Zr-La／Al2O3及负载型Pd三效催化剂制备中的应用

制备了CeO2-ZrO2-La2O3/Al2O3材料,在制备过程中使用超声波振动对材料进行处理,并以此材料为载体制备了单Pd三效催化剂.对所制备的载体进行了织构性能分析(BET)和X射线衍射(XRD)表征.对催化剂进行了NO程序升温脱附(NO-TPD)及H2程序升温还原(H2-TPR)表征,并对催化剂进行了活性测试.BET结果表明,900 ℃焙烧后,超声波振动处理的载体比表面积为130 m2·g-1,而没有进行处理的载体比表面积为117 m2·g-1.超声波处理的CeO2-ZrO2-La2O3/Al2O3材料介孔直径为11.4 nm,相对较大,载体更加稳定.XRD测试结果表明,超声波处理的载体在1150 ℃焙烧5 h后仍然只有Ce0.5Zr0.5O2一个单一物相,而未经过超声波处理的载体此时出现相分离,体相中有θ-Al2O3出现.以超声波处理材料为载体的Pd催化剂新鲜和老化后NO-TPD测试结果变化很小.H2-TPR测试中,超声波振动处理的材料制备的催化剂中活性组分和载体的还原峰温较未超声处理材料制备的催化剂稍高,而峰面积远大于未超声处理材料制备的催化剂.活性测试结果说明,由超声波振动处理过的载体制备的三效催化剂对汽车尾气中的三种污染物的起燃温度更低,有更好的活性以及温度特性.     

沉淀方法对CeO2-ZrO2系储氧材料性能的影响

利用不同沉淀方法制备了一系列CeO2-ZrO2系储氧材料,并应用BET、XRD、TPR及其储氧性能测定等方法对储氧材料进行了研究.结果表明,不同的沉淀方法对样品的结构和性能有重要的影响.并流法可得到耐高温,储氧性能好,比表面积高的储氧材料;正滴法所得样品储氧量低但稳定,其比表面积抗老化性能差;反滴法所制备的样品储氧性能好,老化后比表面积较低.三种沉淀方法均可形成CeO2-ZrO2固溶体,材料的还原性能取决于比表面积,但与储氧性能无直接关系.     

超声波振动在Ce-Zr-La/Al2O3及负载型Pd三效催化剂制备中的应用

制备了CeO2-ZrO2-La2O3/Al2O3材料, 在制备过程中使用超声波振动对材料进行处理, 并以此材料为载体制备了单Pd三效催化剂. 对所制备的载体进行了织构性能分析(BET)和X射线衍射(XRD)表征. 对催化剂进行了NO程序升温脱附(NO-TPD)及H2程序升温还原(H2-TPR)表征, 并对催化剂进行了活性测试. BET结果表明, 900 ℃焙烧后, 超声波振动处理的载体比表面积为130 m2·g-1, 而没有进行处理的载体比表面积为117 m2·g-1. 超声波处理的CeO2-ZrO2-La2O3/Al2O3材料介孔直径为11.4 nm, 相对较大, 载体更加稳定. XRD测试结果表明, 超声波处理的载体在1150 ℃焙烧5 h后仍然只有Ce0.5Zr0.5O2一个单一物相, 而未经过超声波处理的载体此时出现相分离, 体相中有θ-Al2O3出现. 以超声波处理材料为载体的Pd催化剂新鲜和老化后NO-TPD测试结果变化很小. H2-TPR测试中, 超声波振动处理的材料制备的催化剂中活性组分和载体的还原峰温较未超声处理材料制备的催化剂稍高, 而峰面积远大于未超声处理材料制备的催化剂. 活性测试结果说明, 由超声波振动处理过的载体制备的三效催化剂对汽车尾气中的三种污染物的起燃温度更低, 有更好的活性以及温度特性.