TiO2/BixTiyOz气相光催化降解苯的动力学模型及反应机理

在密闭不锈钢反应器内考察了TiO2/BixTjyOz催化剂气相光催化降解苯的性能.结果表明,TiO2负载于Bi12TiO20,Bi2Ti2O7和Bi4Ti3O12上制成的催化剂,光催化活性得到很人的提高,TiO2最佳负载量为2.0%;其中,TiO2/Bi12TiO20的光催化活性最高,苯最高转化率是纯TiO2的2倍,催化剂使用寿命也延长了1倍.在本文实验条件下,TiO2/Bi12TiO20上苯气相光催化降解符合Lang-muir-Hinshelwood动力学模型,光催化反应速率常数k和Langmuir吸附常数K分别为0.006 4mg/(L·min)和9.670 2L/mg.采用红外光谱对失活的催化剂进行表征,结果表明催化剂表面出现了羰基与羟基等的振动峰,同时检测到主要的中间产物是2,6-二叔丁基-4-甲基苯酚,它吸附在催化剂表面活性化上而导致催化剂失活.最后推测了苯在催化剂表面气相光催化降解的反应机理.     

SnO2/TiO2纳米管复合光催化剂的性能及失活再生

基于微波水热法和微乳液法合成SnO₂/TiO₂纳米管复合光催化剂. 通过X射线衍射（XRD）、配有能量色散X射线光谱仪（EDX）的透射电镜（TEM）和电化学手段对光催化剂进行表征. 以甲苯为模型污染物,考察光催化剂在紫外光（UV）和真空远紫外光（VUV）下的性能及失活再生. 结果表明,SnO₂/TiO₂纳米管复合光催化剂形成三元异质结（锐钛矿相TiO₂（A-TiO₂）/金红石相TiO₂（R-TiO₂）、A-TiO₂/SnO₂和R-TiO₂/SnO₂异质结）,促使光生电子-空穴对的有效分离,提高光催化活性. SnO₂/TiO₂表现出最佳的光催化性能,UV和VUV条件下的甲苯降解率均达100%,CO₂生成速率（k₂）均为P25的3倍左右. 但由于UV光照矿化能力不足,中间产物易在催化剂表面累积. 随着UV光照时间的增加,SnO₂/TiO₂逐渐失活,20 h 后k₂由138.5 mg·m^-3·h^-1下降到76.1 mg·m^-3·h^-1. 利用VUV再生失活的SnO₂/TiO₂,过程中产生的·OH、O₂^-·、O（¹D）、O（³P）、O₃等活性物质可氧化吸附于催化剂活性位的难降解中间产物,使催化剂得以再生,12 h后k₂恢复到143.6 mg·m^-3·h^-1. UV和VUV的协同效应使UV降解耦合VUV再生成为一种可持续的光催化降解污染物模式.     

核-壳式纳米SnO2/TiO2光催化剂的制备和性能

 以纳米SnO2·nH2O胶体粒子为基质,采用活性层包覆法制备了纳米SnO2/TiO2复合光催化剂,并用R,TEM,XPS和XRD等手段进行了表征. 采用敌敌畏的光催化降解反应对所制催化剂的活性进行了评价. 结果表明,SnO2/TiO2为核-壳结构,粒径约为12 nm. SnO2/TiO2的光催化活性受TiO2含量及SnO2·nH2O乙醇溶液含水量的影响. 最佳条件为SnO2/TiO2中TiO2含量为56.45%,SnO2·nH2O乙醇溶液含水量为20%. 所制SnO2/TiO2光催化活性比纯TiO2显著提高,且光催化活性稳定,可重复使用.     

气相苯在TiO2光催化剂上吸附常数和光催化反应常数测定

采用溶胶-凝胶法制备TiO2光催化剂以及掺杂Fe3 和Ce3 的TiO2光催化剂,进行间歇式光催化降解气相苯动力学实验,基于光催化Langmuir-Hinshelwood反应动力学模型(L-H模型),测定气相苯在3种光催化剂上的降解动力学常数和吸附平衡常数.根据光催化降解气相苯实验动力学曲线和L-H模型,估算出TiO2、Fe3 /TiO2和Ce3 /TiO2光催化剂光催化降解苯的反应速率常数k和Langmuir吸附常数K分别为0.5247g/m3·min、1.523g/m3·min、1.010g/m3·min和8.605×10-2m3/g、2.390×10-2m3/g、3.928×10-2m3/g.掺杂Fe3 和Ce3 可明显提高光催化剂光催化降解苯的反应速率常数k,其中Fe3 /TiO2,的反应速率常数k最大.     

X射线光电子能谱法研究UV_(254nm)光催化、O_3强化UV_(254nm)光催化和真空紫外光催化降解甲醛中Pt-TiO_2薄膜的表面性质(英文)

以Pt-TiO2为光催化剂,研究了气相甲醛分别在35 h连续UV254 nm光催化、O3强化UV254 nm(O3+UV254 nm)光催化和真空紫外(UV254+185 nm)光催化中的降解效率,考察了副产物O3的去除率,采用X射线光电子能谱(XPS)法分析Pt-TiO2在不同光催化前后Pt的电子态和累积有机产物,研究纳米Pt对甲醛降解和O3去除的强化机理.连续光催化降解实验表明,以纳米Pt改性TiO2可以同时增强甲醛和O3的去除率,特别是O3的去除率可提高3.1–3.4倍.对催化剂C 1s和O 1s峰分别经分峰拟合处理后,发现Pt-TiO2上累积的含羰基和羟基的有机物含量按以下顺序减少:UV254 nm光催化O3强化UV254 nm光催化真空紫外光催化,而在连续35 h光催化降解过程中,催化剂的失活现象却按相反的方向变得越来越不明显.负载的金属Pt在O3+UV254 nm和UV254+185nm光催化过程中被氧化成PtOads和Pt4+物种,而在UV254 nm光催化过程中金属Pt未被氧化,所以推测是气相中的O3和羟基自由基参与金属Pt的氧化过程.Pt-TiO2表面高价态的Pt氧化物种可作为光生电子捕获中心,强化光生载流子的分离过程,增强Pt-TiO2的光催化活性.Pt氧化物种可作为O3分解的活化中心,使Pt-TiO2对O3的分解效率远高于纯TiO2.以XPS对比研究在三种不同光催化环境中Pt-TiO2表面性质,可以解释在UV254+185 nm光催化过程中纳米Pt对甲醛和O3同时去除的强化机理,并说明了催化剂不失活的内在原因.     

TiO2/SnO2复合光催化剂的制备及光催化降解敌敌畏

包覆型催化剂;TiO2/SnO2复合光催化剂的制备及光催化降解敌敌畏     

ZnO和TiO2粒子的光催化活性及其失活与再生

 利用XRD，TEM，BET和UV－Vis等测试技术对商品的ZnO及TiO2和纳米ZnO及TiO2粒子进行了表征．无论是商品的还是纳米的，在光催化氧化降解气相n－C7H16和SO2及液相苯酚的反应中，TiO2均表现出比ZnO高的光催化活性，并从光腐蚀性和表面电荷两方面分析了其原因．在光催化氧化降解n－C7H16的反应中，ZnO粒子易失活，而TiO2粒子不易失活．但是，在光催化氧化降解SO2的反应中，ZnO和TiO2粒子均易失活．SPS和XPS测试结果表明，光催化剂表面的导电类型由反应前的n型变成了失活后的p型．这主要是由于反应产物发生吸附所致．失活后的光催化剂可以通过浸洗和干燥再生．     

Fe3+掺杂TiO2光催化降解聚乙烯薄膜的研究

以快速溶胶-凝胶法制备了纳米TiO2光催化剂,并用Fe3 对其掺杂改性,在室温条件下,用于固相光催化降解聚乙烯(PE)包装薄膜的研究.对催化剂和薄膜进行了X衍射分析(XRD)、傅立叶红外光谱分析(FT-IR)、扫描电子显微镜(SEM)形貌观察.结果表明,60W紫外光辐射240h后,PE失重为8.43%,锐钛矿型纳米TiO2光催化剂使PE失重30.66%;用Fe3 掺杂后,0.5?2O3/TiO2、1.0?2O3/TiO2和2.0?2O3/TiO2分别使PE失重35.91%、20.72%和13.30%.光催化剂加速了PE的失重,碳链的断裂和光氧化腐蚀,在薄膜表面形成大量的坑洞,降解产物中的小分子量的石蜡含量明显增高.Fe3 掺杂有一个最佳量,0.5?2O3/TiO2光催化降解PE的活性最高.     

TiO_2/活性炭纤维复合材料去除室内挥发性有机物的研究进展

多孔材料与纳米TiO2复合是目前光催化领域的研究热点。多孔材料作为吸附中心可为TiO2光催化剂提供高浓度反应环境,加快催化剂传质速率,提高催化剂矿化效率,抑制催化剂失活,解决催化剂分离难题;TiO2作为降解中心可实现多孔材料的原位再生,增加其平衡吸附量,从而实现对室内挥发性有机物(VOCs)污染的高效深度净化。本文就TiO2/活性炭纤维(ACF)复合材料的制备方法、TiO2/ACF去除VOCs的环境影响因素及协同作用机制进行了综述,并对今后的研究提出了展望。     

不同紫外光源下MnO2对TiO2光催化活性的影响

采用动力学方法研究了3种紫外光源下MnO2颗粒物对TiO2光催化活性的影响, 使用的光源包括UV365/28 W, UV302/16 W和UV254/25 W, 实验用的MnO2包括α-MnO2, β-MnO2和δ-MnO2. 实验结果表明, 当水悬浮液中有MnO2颗粒物存在时, 在UV365/28W和UV302/16W两种紫外光源下TiO2光催化剂会失活, 而在UV254/25W紫外光源下TiO2光催化剂能基本保持稳定. TiO2光催化剂的稳定性与使用的紫外光源的波长有关.     

Au/TiO_2/MoS_2等离子体复合光催化剂的制备及其增强光催化产氢活性

采用尿素沉积法制备了Au/Ti O_2/Mo S_2等离子体复合光催化剂。通过光催化产氢实验,在10%(φ,体积分数)甘油水溶液为牺牲剂条件下,研究了不同Mo S_2含量、Au固载2%(w,质量分数)时,Au/Ti O_2/Mo S_2(ATM)复合样品的光催化产氢活性。结果表明,当Mo S_2含量为0.1%(w)时,复合样品ATM0.1显示出最高的光催化产氢活性,其产氢速率达到708.85μmol·h~(-1),是Ti O_2/Mo S_2(TM)两相复合样品中光催化活性最高样品TM6.0产氢速率的11倍。三相复合样品显示增强光催化产氢活性主要是由于吸附在Ti O_2/Mo S_2层状复合材料上的Au纳米颗粒具有表面等离子共振效应,能强烈吸收波长范围550–560 nm的可见光,诱导产生光生电子,金纳米颗粒上的电子受到激发后转移到Ti O_2导带上,Ti O_2导带上的电子传递给片状Mo S_2,最终在Mo S_2上催化氢气产生。     

微波辅助快速制备2D/1D ZnIn2S4/TiO2 S型异质结及其光催化制氢性能

The threat and global concern of energy crises have significantly increased over the last two decades. Because solar light and water are abundant on earth, photocatalytic hydrogen evolution through water splitting has been considered as a promising route to produce green energy. Therefore, semiconductor photocatalysts play a key role in transforming sunlight and water to hydrogen energy. To date, various photocatalysts have been studied. Among them, TiO₂ has been extensively investigated because of its non-toxicity, high chemical stability, controllable morphology, and high photocatalytic activity. In particular, 1D TiO₂ nanofibers (NFs) have attracted increasing attention as effective photocatalysts because of their unique 1D electron transfer pathway, high adsorption capacity, and high photoinduced electron–hole pair transfer capability. However, TiO₂ NFs are considered as an inefficient photocatalyst for the hydrogen evolution reaction (HER) because of their disadvantages such as a large band gap (~3.2 eV) and fast recombination of photoinduced electron–hole pairs. Therefore, the development of a high-performance TiO₂ NF photocatalyst is required for efficient solar light conversion. In recent years, several strategies have been explored to improve the photocatalytic activity of TiO₂ NFs, including coupling with narrow-bandgap semiconductors (such as ZnIn₂S₄). Recently, microwave (MW)-assisted synthesis has been considered as an important strategy for the preparation of photocatalyst semiconductors because of its low cost, environment-friendliness, simplicity, and high reaction rate. Herein, to overcome the above-mentioned limiting properties of TiO₂ NFs, we report a 2D/1D ZnIn₂S₄/TiO₂ S-scheme heterojunction synthesized through a microwave (MW)-assisted process. Herein, the 2D/1D ZnIn₂S₄/TiO₂ S-scheme heterojunction was constructed rapidly by using in situ 2D ZnIn₂S₄nanosheets decorated on 1D TiO₂ NFs. The loading of ZnIn₂S₄ nanoplates on the TiO₂ NFs could be easily controlled by adjusting the molar ratios of ZnIn₂S₄ precursors to TiO₂ NFs. The photocatalytic activity of the as-prepared samples for water splitting under simulated solar light irradiation was assessed. The experimental results showed that the photocatalytic performance of the ZnIn₂S₄/TiO₂ composites was significantly improved, and the obtained ZnIn₂S₄/TiO₂ composites showed increased optical absorption. Under optimal conditions, the highest HER rate of the ZT-0.5 (molar ratio of ZnIn₂S₄/TiO₂= 0.5) sample was 8774 μmol·g^-1·h^-1, which is considerably higher than those of pure TiO₂ NFs (3312 μmol·g^-1·h^-1) and ZnIn₂S₄nanoplates (3114 μmol·g^-1·h^-1) by factors of 2.7 and 2.8, respectively. Based on the experimental data and Mott-Schottky analysis, a possible mechanism for the formation of the S-scheme heterojunction between ZnIn₂S₄ and TiO₂ was proposed to interpret the enhanced HER activity of the ZnIn₂S₄/TiO₂heterojunctionphotocatalysts.      

MoS_2/TiO_2复合催化剂的制备及其在紫外光下的光催化制氢活性

为了研究复合光催化剂在光催化中的制氢效率,采用水热法制备了Mo S2纳米片,然后通过水热法在Mo S2纳米片上负载了TiO_2纳米颗粒,形成了Mo S2/TiO_2异质结复合催化剂。采用冷场发射扫描电子显微镜(FE-SEM)、透射电子显微镜(TEM)、X射线衍射(XRD)、紫外-可见吸收光谱(UV-Vis)、拉曼光谱(Raman),X射线光电子能谱(XPS)对材料的结构和光学性能表征并进行分析。通过光催化制氢测试对光催化剂进行评价,实验结果表明,在波长为365 nm的紫外光照射下,最高光催化制氢速率为1004μmol·h-1·g-1,对应的催化剂的Mo S2含量为30%,其催化速率远大于单一的Mo S2和TiO_2,表明Mo S2/TiO_2复合催化剂在紫外光照下能显著提高光催化产氢性能。基于Mo S2/TiO_2复合光催化剂优越的光催化产氢性能,本文对复合光催化剂的产氢机理做了研究和分析。     

LaNiO3/TiO2纳米管阵列的电化学制备及其光催化性能

利用脉冲电沉积与高温退火相结合的方法制备了镍酸镧(LaNiO₃)纳米颗粒负载的二氧化钛(TiO₂)纳米管阵列. 修饰于TiO₂纳米管阵列上的LaNiO₃纳米颗粒粒径小（< 10 nm）、分布均匀、负载量可控,一些LaNiO₃纳米颗粒沉积于TiO₂纳米管内. 紫外可见吸收光谱显示,LaNiO₃/TiO₂纳米管阵列的吸收带边较TiO₂纳米管阵列明显红移,可见光吸收明显增强. 可见光下光催化降解罗丹明B（RhB）的结果表明,脉冲循环沉积500次制得的LaNiO₃/TiO₂纳米管阵列的光催化活性最佳,其对RhB光催化降解速率是TiO₂纳米管阵列的3.5倍,并且表现出极好的光催化稳定性.     

Pd修饰对Cd0.8Zn0.2S/SiO2光催化甘油水溶液制氢性能的影响

用等体积浸渍法制备了不同Pd负载量的Pd/Cd_0.8Zn_0.2S/SiO₂光催化材料,采用XRD、H₂-TPR、XPS、UV-vis DRS和光催化反应评价等方法对光催化材料的表面结构、光吸收性能以及光催化甘油水溶液制氢反应性能进行了考察。研究结果表明,ZnS与CdS在SiO₂表面形成了Cd_0.8Zn_0.2S固溶体,金属Pd负载未对固溶体Cd_0.8Zn_0.2S/SiO₂的结构造成影响;金属Pd修饰明显地提高了原固溶体的光响应性能,拓展了其吸光域,增强了吸光效率。金属Pd修饰后,Cd_0.8Zn_0.2S/SiO₂的光解甘油水溶液产氢速率显著提高,Pd负载量为0.5%的Pd/Cd_0.8Zn_0.2S/SiO₂具有最佳的光催化甘油水溶液制氢性能,其在紫外光照射下的氢气生成速率为831 μmol/h,较未负载时提高了近四倍;模拟太阳光下为153 μmol/h,较未负载时提高了近两倍。     

聚苯胺纳米线/SnO2复合光催化材料的光化学制备与性能

将具有确定形态的聚苯胺(PANI)纳米线作为复合单元, 直接分散在SnSO₄和H₂SO₄的混合溶液中, 通 过紫外光照射获得PANI纳米线/SnO₂纳米颗粒复合材料. 对复合材料的形态和成分进行了分析, 发现二者 相互交织在一起且部分颗粒直接生长在纳米线上. 以罗丹明B溶液为目标降解污染物研究了复合材料在低 功率紫外灯下的光催化活性. 结果表明, PANI纳米线可以明显增强SnO₂的光催化活性, 且增强效果与光照 复合时间呈规律性变化, 在最优复合时间下复合材料的光催化活性是纯SnO₂的近3倍. 通过对能级结构与光催化反应过程的测试分析, 认为Z型异质结的形成促进了光生电子-空穴的分离, 进而增强了材料的光催化活性.     

Preparation and Photocatalysis of Mesoporous TiO2 Nanofibers via an Electrospinning Technique

Mesoporous TiO₂ nanofibers have been synthesized by a new method that combines sol-gel chemistry and electrospinning technique. The obtained mesoporous TiO₂ nanofibers were characterized with scanning electron microscopy(SEM), X-ray diffraction(XRD), transmission electron microscopy(TEM) and nitrogen adsorption-desorption isotherms. The photocatalytic performance was evaluated by the photocatalytic degradation of Rhodamine B under UV light irradiation. The results show that mesoporous TiO₂ nanofibers exhibit higher photocatalytic activity compared with nonporous TiO₂ nanofibers.     

Enhanced Visible-light Photocatalytic Activity of g-C3N4/Nitrogen-doped Graphene Quantum Dots/TiO2 Ternary Heterojunctions for Ciprofloxacin Degradation with Narrow Band Gap and High Charge Carrier Mobility

Limited visible-light absorption and high recombination rate of photogenerated charges are two main drawbacks in g-C₃N₄-based photocatalysts. To solve these problems, g-C₃N₄/nitrogen-doped graphene quantum dots (NGQDs)/TiO₂ ternary heterojunctions were facilely prepared via a one-step calcining method. The morphology, structure, optical and electrochemical properties of g-C₃N₄/NGQDs/TiO₂ were characterized and explored. The optimal g-C₃N₄/NGQDs/TiO₂ composite exhibits enhanced photocatalytic degradation performance of ciprofloxacin (CIP) compared with the as-prepared g-C₃N₄, TiO₂(P25) and g-C₃N₄/TiO₂ heterojunction under visible light irradiation. The apparent rate constant of the composite is around 6.43, 4.03 and 2.30 times higher than those of g-C₃N₄, TiO₂ and g-C₃N₄/TiO₂, respectively. The enhanced photocatalytic efficiency should be mainly attributed to the improvement of light absorption and charge separation and transfer efficiency, originating from the narrow band gap and high charge carrier mobility. The active species trapping experiments results showed that the h⁺ and ^·O₂^- were the main active species in the degradation process. A possible photocatalytic reaction mechanism of the g-C₃N₄/NGQDs/TiO₂ composite for the enhanced degradation of CIP under visible light irradiation was also proposed.     

LaCoO_3-TiO_2纳米管阵列的构筑及可见光光催化性能

TiO_2纳米管阵列具有较高的光催化活性,但可见光吸收弱,限制了其太阳能利用和环境应用。窄带隙的钙钛矿(ABO3)型氧化物能够吸收大范围波段的可见光,且稳定性高,但光催化活性低。本文首先采用溶胶-凝胶法合成了LaCoO_3纳米颗粒,然后利用电泳沉积技术将LaCoO_3纳米颗粒修饰于TiO_2纳米管阵列表面,构筑了LaCoO_3-TiO_2纳米管阵列。扫描电子显微镜(SEM)、透射电子显微镜(SEM)、X射线衍射(XRD)和X射线光电子能谱(XPS)的表征结果显示溶胶-凝胶法合成的纳米颗粒为LaCoO_3,其尺寸均匀,结晶度高,平均粒径约为100nm。LaCoO_3纳米颗粒与TiO_2纳米管阵列之间的结合力好。紫外可见吸收光谱(DRS)显示,随着电泳沉积时间的延长,LaCoO_3-TiO_2纳米管阵列的吸收带边逐渐红移700nm。可见光下光催化降解甲基橙(MO)的结果表明,电泳沉积15 min制得的LaCoO_3-TiO_2纳米管阵列对MO的光催化效率最高,其降解速率是相同条件下TiO_2纳米管阵列的4倍。光致发光光谱和电化学阻抗谱证实LaCoO_3纳米颗粒的负载有效地促进了光生电荷的分离和传输,可见光光催化活性明显增强。